• Journal of Periodontal and Implant Science
• /
• v.35 no.4
• /
• pp.891-905
• /
• 2005

The present study was performed to evaluate the effect of tetracycline-HCL on the change of implant surface microstructure according to application time. Implant with pure titanium machined surface. HA-coated surface and TiUniteTM surface were utilized. Implant surface was rubbed with 50mg/ml tetracycline-HCL solution for $\frac{1}{2}min.$, 1min., $1\frac{1}{2}min.$, 2min., and $2\frac{1}{2}min.$ respectively in the test group. Then, specimens were processed for scanning electron microscopic observation. The results of this study were as follows. 1. Both test and control group showed a few shallow grooves and ridges in pure titanium machined surface implants. There were not significant differences between two groups. 2. In HA-coated surfaces, round particles were deposited irregularly. The roughness of surfaces conditioned with tetracycline-HCL was lessened and the cracks were increased relative to the application time. 3. The anodic oxidized surfaces showed the craterous structures. The surface conditioning with tetracycline-HCl didn't influence on its micro-morphology. In conclusion, the detoxification with 50mg/ml tetracycline-HCL must be applied respectively with different time according to various implant surfaces.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2007.06a
• /
• pp.234-237
• /
• 2007

We fabricated nano-structures of the anodic aluminum oxides on sapphire substrates. Two processes of nano-structured sapphire surface have present: the one is the template mask and the other is the anodic oxidized aluminum deposited on sapphire substrate. The formation of nano-structures has investigated by FE-SEM measurement. The etched surface by the template showed periodic lattice but the deposited surface showed the randomly distributed phase of nanoholes instead of the periodic lattice.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.545-546
• /
• 2006

This study was performed to investigate the surface properties of electrochemically oxidized pure titanium by anodic spark discharging method. Commercially pure titanium plates of $10{\times}20{\times}1[mm]$ in dimensions were polished sequentially emery paper. Anodizing was performed at current density of $76.2\;[mA/cm^2]$, application voltage of 290, 350, 400 [V] using a regulated DC power supply, which allowed automatic transition constant current when a preset maximum voltage has been reached. The Ti surface oxided films was characterized by scanning electron microscope(SEM). The precipitation of HA(Hydroxyapatite) crystals on anodized surface was greatly accelerated by hydrothermal treatment. The concentrations of DL-$\alpha$-Glycerolphosphate Magnesiurn(DL-$\alpha$-GP-Mg) salt and Ca acetate in an electrolyte was highly affected the precipitation of HA crystals converted by Ti Anodized oxide films by Shape of Impulse Voltage.

• Carbon letters
• /
• v.8 no.1
• /
• pp.30-36
• /
• 2007

Oxidized PAN (OXI-PAN) fibers were used for the precursors of activated carbon fiber in study. How drying temperature affected the properties of carbon fibers on activating process of carbon fibers was investigated. The specific surface areas of activated carbon fibers have been determined on a series of chemically activated carbons with KOH and NaOH. The experimental data showed variations in specific surface area, iodine and silver adsorptions by the activated carbon fibers. The amount of iodine adsorption increases with increasing specific surface areas in both activation methods. This was because the ionic radius of iodine was smaller than the interior micropore size of activated carbon fibers. Silver adsorbed well in NaOH activated carbon fibers rather than KOH activated carbon fibers in this study.

• Korean Chemical Engineering Research
• /
• v.53 no.1
• /
• pp.83-90
• /
• 2015

In this study, we investigated optimum conditions for the introduction of a lot of free radical polymerizable methacrylate groups on the multi-walled carbon nanotube (MWCNT) surface. Carboxyl groups were introduced first on MWCNT surfaces by treating with a mixture of sulfuric acid and nitric acid with ultrasonic bath for 2 hours, and oxidized MWCNTs were reacted further with thionyl chloride followed by triethylenetetramine (TETA) to introduce amino groups on the oxidized MWCNT surface, to make MWCNT-$NH_2$. To introduce free radical polymerizable methacrylate groups on the MWCNT-$NH_2$, MWCNT-$NH_2$ was reacted with 3-(acryloyloxy)-2-hydroxypropyl methacrylate (AHM) by Michael addition reaction. We investigated progress of modification reactions for MWCNT by fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA) and elemental analysis (EA). We found maximum degree of Michael addition reactions between AHM and TETA grafted on MWCNT-$NH_2$ for 10:1 mol ratio and 8 hour reaction time in our reaction conditions.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.21 no.1
• /
• pp.33-42
• /
• 2005

This study was performed to investigate the surface properties and in vitro biocompatibility of electrochemically oxidized Ti-6Al-7Nb alloy by anodic spark discharge technique. Discs of Ti-6Al-7Nb alloy of 20 mm in diameter and 2 mm in thickness were polished sequentially from #300 to 1000 SiC paper, ultrasonically washed with acetone and distilled water for 5 min, and dried in an oven at $50^{\circ}C$ for 24 hours. Anodizing was performed using a regulated DC power supply. The applied voltages were given at 240, 280, 320, and 360 V and current density of $30mA/cm^2$. Hydrothermal treatment was conducted by high pressure steam at $300^{\circ}C$ for 2 hours using a autoclave. Samples were soaked in the Hanks' solution with pH 7.4 at $36.5^{\circ}C$ during 30 days. The results obtained were summarized as follows; 1. The oxide films were porous with pore size of $1{\sim}5{\mu}m$. The size of micropores increased with increasing the spark forming voltage. 2. The main crystal structure of the anodic oxide film was anatase type as analyzed with thin-film X-ray diffractometery. 3. Needle-like hydroxyapatite (HA) crystals were observed on anodic oxide films after hydrothermal treatment at $300^{\circ}C$ for 2 hours. The precipitation of HA crystals was accelerated with increasing the spark forming voltage. 4. The precipitation of the fine asperity-like HA crystals were observed after being immersed in Hanks' solution at $37^{\circ}C$. The precipitation of HA crystals was accelerated with increasing the spark forming voltage and the time of immersion in Hanks' solution. 5. The Ca/P ratio of the precipitated HA layer was equivalent to that of HA crystal as increasing the spark forming voltage and the time of immersion in Hanks' solution.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.22 no.1
• /
• pp.101-110
• /
• 2006

This study was performed to investigate the surface properties and in vitro biocompatibility of electrochemically oxidized Ti-6Al-7Nb alloy by anodic spark discharge technique. Discs of Ti-6Al-7Nb alloy of 20 mm in diameter and 2 mm in thickness were polished sequentially from #300 to 1000 SiC paper, ultrasonically washed with acetone and distilled water for 5 min, and dried in an oven at $50^{\circ}C$ for 24 hours. Anodizing was performed using a regulated DC power supply. The applied voltages were given at 240, 280, 320, and 360 V and current density of $30mA/cm^2$. Hydrothermal treatment was conducted by high pressure steam at $300^{\circ}C$ for 2 hours using a autoclave. Samples were soaked in the Hanks' solution with pH 7.4 at $36.5^{\circ}C$ during 30 days. The results obtained were summarized as follows; 1. The oxide films were porous with pore size of $1{\sim}5{\mu}m$. The size of micropores increased with increasing the spark forming voltage. 2. The main crystal structure of the anodic oxide film was anatase type as analyzed with thin-film X-ray diffractometery. 3. Needle-like hydroxyapatie (HA) crystals were observed on anodic oxide films after hydrothermal treatment at $300^{\circ}C$ for 2 hours. The precipitation of HA crystals was accelerated with increasing the spark forming voltage. 4. The precipitation of the fine asperity-like HA crystals were observed after being immersed in Hanks' solution at $37^{\circ}C$. The precipitation of HA crystals was accelerated with increasing the spark forming voltage and the time of immersion in Hanks' solution. 5. The Ca/P ration of the precipitated HA layer was equivalent to that of HA crystal as increasing the spark forming voltage and the time of immersion in Hanks' solution.

• Corrosion Science and Technology
• /
• v.19 no.3
• /
• pp.138-145
• /
• 2020

Immersion tests of Alloy 600 were conducted in simulated primary water environments of a pressurized water reactor at 325 ℃ for 10, 100, and 1000 h to obtain insight into effects of surface deformation on internal and intergranular (IG) oxidation behavior through precise characterization using various microscopic equipment. Oxidized samples after immersion tests were covered with polyhedral and filamentous oxides. It was found that oxides were abundant in mechanically ground (MG) samples the most. The number density of surface oxides increased with time irrespective of the method of surface finish. IG oxidation occurred in mechanically polished (MP) and chemically polished (CP) samples with thin internal oxidation layers. However, IG oxidation was suppressed with relatively thick internal oxidation layers in MG samples compared to MP and CP samples, suggesting that MG treatment could increase resistance to primary water stress corrosion cracking (PWSCC) from the standpoint of IG oxidation. As a result, appropriate surface treatment for Alloy 600 could prevent oxygen diffusion into grain boundaries, inhibit IG oxidation, and finally induce its high PWSCC resistance.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.44 no.4
• /
• pp.51-61
• /
• 2002

The objective of this study is to develop GLEANS-PADDY model to predict nutrients loading from paddy-field areas. This model is developed by modifying the GLEANS model which is used for uplands, and composed of hydrology and nutrient submodels. The optimal field size for CLEANS-PADDY model application is about up to 50 ha with mild slope, relatively homogeneous Soils and spatially rainfall, and a single crop farming. The CLEAMS model is modified to handle ponded soil surface condition and saturated soil profile in paddy field. In the hydrology submodel of the CLEAMS-PADDY model. the ponded depth routing method is used to handle the ponded water condition of paddy field. To compute potential evapotranspiration the FAO-24 Corrected Blaney-Criddle method is used for paddy field instead of Penman-Monteith method in the CLEAMS model. In the nutrients submodel of the CLEAMS-PADDY model, the soil was assumed saturated and soil profile in the root zone was divided into oxidized and reduced zones.

• Journal of Fashion Business
• /
• v.10 no.1
• /
• pp.94-105
• /
• 2006

Hair bleaching is a treatment process in which the melanic pigment is oxidized by hydrogen peroxide. With the increase of the number of treatments, $1{\sim}10$ levels of various colors develop, the hair luster diminishes, and the appearance becomes very rough. In this study, by changing the number of hair bleaching and bleaching conditions, the changes in the degree of hair damage and its process were observed through the use of scanning electron microscopy. The color changes were also compared through the use of spectrophotometer. In order to study the physical changes of the bleached hairs and to search for the optimum conditions to keep the hair damages minimum during bleaching, tensile properties were measured and reviewed. By increasing the number of hair bleaching and by the severe conditions, the scales became eroded and the protection layers were decreased, and the oxidation reached the inner sectors resulting in rough surface and fibrillation. The surface of the hairs became bright yellowish and transparent by the bleaching of melanic pigments or by the destruction of pigments. With the increase of bleaching degree, in terms of physical changes, the breaking strength decreased while the elongation increased a little.