• 대한치과재료학회지
• /
• 제43권1호
• /
• pp.43-50
• /
• 2016

The aim of this study was to investigate the effect of multiwall carbon nanotube functionalized with carboxyl group (MWCNT-COOH) on the mechanical properties of dental glassionomer cement (GIC). MWCNT-COOH was prepared by the acid oxidative method. The MWCNT-COOH was incorporated into a commercial GIC powder or liquid at 0.5 wt% or 1.0 wt%. The net setting time of the cements was measured in accordance with ISO 9917 (Dental water-based cement). Specimens for compressive strength ($4mm{\varphi}{\times}6mm$), diametral tensile strength ($6mm{\varphi}{\times}4mm$) and flexure strength with modulus ($2mm{\times}2mm{\times}25mm$) were prepared by mixing with the cement liquid and kept in water bath of $(37{\pm}1)^{\circ}C$. Mechanical tests were conducted in 1 d, 7 d, and 14 days at a cross-head speed of 1 mm/min. Compressive strength of GIC mixed with 0.5 wt% MWCNT-COOH increased significantly at 7 d. However, overall mechanical properties of GIC modified with MWCNT were not significantly increased with a delayed setting time, in comparison with control cement. Overall results indicated that the MWCNT/GIC composite cements showed a limited strengthening effect for dental glassionomer cement.

• Restorative Dentistry and Endodontics
• /
• 제13권1호
• /
• pp.123-129
• /
• 1988

The purpose of this study was to evaluate the bond strength of glassionomer cement against cut dentin surface which was treated with various surface cleaning agents. 48 freshly extracted human 3rd molars were ground flat through the enamel into the dentin using 600 grit silicone carbide paper under a flow of water. The were divided into four groups by the following cleaning procedure on cut dentin surface; Group I : No surface treatment after grinding with 600 grit silicone carbide paper as control group Group II : Surface treatment with 50% citric acid for 30 seconds. Group III : Surface treatment with 37% phosphoric acid for 30 seconds. Group IV : Surface treatment with 10% poly acrylic acid for 30 seconds. The specimens in 4 groups were immersed in distilled water at $37^{\circ}C$ for 24 hours before testing after cleanising with water-spray and drying with air. Bond strength was measured with Instron Universal Testing Machine (Autograph S-100, Shimadzu, Kyoto, JAPAN). The results were as follows: 1. The bond strengths of group II, III & IV were not seemed to be shown more significant improvement than a group I. 2. The bond strengths in groups which were treated with 50% citric acid, 37% phosphoric acid and 10% polycrylic acid, were ranked 24.70kg/$cm^2$, 22.02kg/$cm^2$ and 31.13kg/$cm^2$, but its difference was not significant, statistically.

• Journal of Periodontal and Implant Science
• /
• 제30권4호
• /
• pp.793-803
• /
• 2000

Procedures for treatment of molar furcation invasion defects range from open flap debridement, apically repositioned flap surgery, hemisection, tunneling or extraction, to regenerative therapies using bone grafting or guided tissue regenerative therapy, or a combination of both. Several clinical evaluations using regenerative techniques have reported the potential for osseous repair of treated furcation invasions. Regenerative treatment of maxillary molars are more difficult due to the multiple root anatomy and multiple furcation entrances therefore, purpose of this study was to evaluated histologically self-curing glass-ionomer cement and light-curing glass-ionomer cement as a barrier in the treatment of a bi-furcated maxillary premolar. Five adult beagle dogs were used in this experiment. With intrasulcular and crestal incision, mucoperiosteal flap was elevated. Following decortication with 1/2 high speed round bur, degree II furcation defect was made on maxillary third(P3), forth(P4) and fifth(P5) premolar. 2 month later experimental group were self-curing glassionomer cement and light-curing glassionomer cement. After 4, 8 weeks, the animals were sacrificed by vascular perfusion. Tissue block was excised including the tooth and prepared for light microscope with Gomori's trichrome staining. Results were as follows. 1. In all experiment group, there were not epithelial down growth and glass ionomer cement were encapsulated connective tissue. 2. In 4 weeks experiment I group slighly infiltrated inflammatory cells but not disturb the new bone or new cementum formation. 3. In 8 weeks, experiment groups I, II were encapsulated fine connective tissue. 4. Therefore glass-ionomer cement filling to the grade III maxillary furcations with multiple root anatomy and multiple furcation entrances were possible clinical methods and this technique is useful method for Maxillary furcation involvement.

• 대한치과의사협회지
• /
• 제49권1호
• /
• pp.22-32
• /
• 2011

This paper reviewed the following subheadings and a few selected references in each section were discussed: ${\cdot}$ Sealant placed over caries; is it possible? Initial caries which is not sticky during proving is possible to be placed with sealants. ${\cdot}$ Prophylaxis of fissure; which method is most effective? Mechanical preparation with fissurotomy or resin polishing bur is one of the most effective method to clean the pit and fissure. ${\cdot}$ Glassionomer cement as a sealant; GIC, wheather it released fluoride or not, cannot be as cost-effective as resin-based sealants. ${\cdot}$ Sealant products; Color(white vs opaque), fluoride(containing vs not), filler component(filled vs non-filled) do not influenced the quality and retention of sealants. ${\cdot}$ Use of intermediate bonding agent to improve retention; Intermediate bonding may increase the retention rate of sealants ${\cdot}$ Penetration method of sealants; Several methods including waiting before light curing are recommended.

• 한국콘텐츠학회:학술대회논문집
• /
• 한국콘텐츠학회 2017년도 춘계 종합학술대회 논문집
• /
• pp.485-486
• /
• 2017

치과용 글라스아이오노머(GIC)는 치과에서 폭넓게 응용되고 있는 재료 중 하나이다. 그러나 GIC의 낮은 기계적 특성으로 인해 구강내 사용범위가 제한적이다. 이에 본 연구는 기능성 다중벽 탄소나노튜브(multi wall carbon nanotube; MWCNT-COOH)를 각 농도별(0.25-1.0 wt%)로 기존의 분말에 첨가하여 복합체를 제조한 후 제조사의 지시에 따란 분말(2):액(1)의 비율로 시편을 제작하여 다중벽탄소나노튜브가 GIC의 기계적 특성과 항균효과에 미치는 영향을 조사하였다.

• Restorative Dentistry and Endodontics
• /
• 제17권1호
• /
• pp.95-103
• /
• 1992

The purpose of this study was to evaluate the effect of the dentin pretreatment on the marginal leakage of a glassionomer cement. 1n this study, 60 molars with sound and healthy crown portion were used. The dentin surface of these teeth were exposed and polished with 600 grit silicon carbide paper. Square - shaped cavities were prepared on the flattened dentin surfaces and these were divided into 4 groups according to the dentin pretreatment procedures. Group I : Dentin pretreatment with distilled water as a control group. Group II : Dentin pretreatment with 5% sodium hypochlorite solution. Group III : Dentin pretreatment with Ketac conditioner. Group IV : Dentin pretreatment with 40% polyacrylic acid. The degrees of dye penetration in the cavity walls were assessed using a stereoscope at ${\times}40$ magnification according to the maximum dye penetration. The results were analyzed by using Mann - Whitney U test. The results were as follows : 1. All groups showed varying depth of dye penetration. 2. Distilled water group showed the most severe marginal leakage when compared with the other groups(P<0.05). 3. 40% polyacrylic acid group showed the least amount of marginal leakage compared with the other groups (P<0.05). 4. There were significant differences between Goup I(distilled water) and Group IV (40% polyacrylic acid)(P<0.05), but there were no significant differences among Group I(distilled water), Group II(sodium hypochlorite), Group III(Ketac conditioner) (P>0.05).

• 대한소아치과학회지
• /
• 제37권1호
• /
• pp.24-34
• /
• 2010

본 연구의 목적은 광중합형 글라스아이오노머 시멘트에 마이크로 입자의 하이드록시아파타이트와 나노미터 입자의 하이드록시아파타이트를 첨가하였을 때 물리적 성질과 탈회 저항, 결합 강도의 차이를 비교하기 위함이다. 실험에 사용된 광중합형 글라스아이오노머 시멘트는 Fuji II LC 였고 순수한 Fuji II LC GIC는 대조군으로, 15% micro HA- Fuji II LC GIC는 실험군 1, 15% nano HA- Fuji II LC GIC는 실험군 2로 설정한 후 실험을 진행하였고 다음과 같은 결론을 얻었다. 1. CLSM으로 탈회 표면 깊이를 관찰한 결과 대조군 보다 실험군에서 법랑질의 탈회가 덜 발생하였고, 실험군 1 보다 실험군 2에서 법랑질의 탈회가 적게 관찰되었다. 2. SEM을 이용한 탈회면 관찰시 대조군에서 법랑질의 탈회가 더 많이 일어났고, 실험군은 하이드록시아파타이트의 영향으로 탈회가 덜 일어나 표면입자가 보다 규칙적이었다. 두 실험군을 비교했을 때 실험군 2가 실험군 1 보다 탈회에 저항하였다. 3. 결합 강도는 대조군, 실험군 1, 실험군 2 순으로 증가했으며 세 군간에 통계학적으로 유의할 만한 차이가 있었다 (p < 0.05). 4. SEM 상에서 결합 강도 측정 후 파절된 면을 관찰한 결과 하이드록시아파타이트를 포함하는 실험군에서 골 유사 아파 타이트 추정 입자가 관찰되었으며 실험군 1 보다 실험군 2에서 더 많은 입자가 형성되었다.