• Journal of the Society of Disaster Information
• /
• v.12 no.3
• /
• pp.292-299
• /
• 2016

The insulation in buildings is very important. Insulation used in the building is largely divided into organic and inorganic insulation by its insulation material. Organic insulations material which are made of styrofoam or polyurethane are extremely vulnerable to fire. On the other hand, inorganic insulation such as mineral-wool and glass-wool are very week with moisture while they are non-flammable so that its usage is very limited. In this study, inorganic heat insulating material developed and the properties of thermal conductivity evaluated. The thermal conductivity and the water absorption of the sample in less than 50mm thickness of the board is less than 0.05W/mk, 3.0%. Bending strength and the water repellency is more than $25N/cm^2$, 98%.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.88-93
• /
• 2008

Ir-Re thin films with Ti interlayer were deposited onto the tungsten carbide substrate by ion beam assisted DC magnetron sputtering. The Ir-Re films were prepared with targets of having two atomic percent of 7:3 and 5:5. The microstructure and surface analysis of the specimen were conducted by using SEM, XRD and AFM. Mechanical properties such as hardness and adhesion strength of Ir-Re thin film also were examined. The interlayer of pure titanium was formed with 100 nm thickness. The film growth of Ir-30at.%Re was faster than that of Ir-50at.%Re in the same deposition conditions. Ir-Re thin films consisted of dense and columnar structure irrespective of the different target compositions. The values of hardness and adhesion strength of Ir-30at.%Re thin film coated on WC substrate were higher than those of Ir-50at.%Re thin film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.502-502
• /
• 2007

Current thin film process using memory device fabrication process use expensive processes such as manufacturing of photo mask, coating of photo resist, exposure, development, and etching. However, direct printing technology has the merits about simple and cost effective processes because inks are directly injective without mask. And also, this technology has the advantage about fabrication of fine pattern line on various substrates such as PCB, FCPB, glass, polymer and so on. In this work, we have fabricated the fine and thick metal pattern line for the electronic circuit board using metal ink contains Ag nano-particles. Metal lines are fabricated by two types of printing methods. One is a conventional printing method which is able to quick fabrication of fine pattern line, but has various difficulties about thick and high resolution DPI(Dot per Inch) pattern lines because of bulge and piling up phenomenon. Another(Second) methods is sequential printing method which has a various merits of fabrication for fine, thick and high resolution pattern lines without bulge. In this work, conductivities of metal pattern line are investigated with respect to printing methods and pattern thickness. As a result, conductivity of thick pattern is about several un.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.381-382
• /
• 2007

IZO/Ag/IZO (IAI) anode films for flexible organic light emitting diodes (OLEDs) were grown on PC (polycarbonate) substrate using DC sputter (IZO) and thermal evaporator (Ag) systems as a function of Ag thickness. To investigate electrical and optical properties of IAI stacked films, 4-point probe and UV/Vis spectrometer were used, respectively. From a IAI stacked film with 12nm-thick Ag, sheet resistance of $6.9\;{\Omega}/{\square}$ and transmittance of above 82 % at a range of 500-550 nm wavelength were obtained. In addition, structural and surface properties of IAI stacked films were analyzed by XRD (X-ray diffraction) and SEM (scanning electron microscopy), respectively. Moreover, IAI stacked films showed dramatically improved mechanical properties when subjected to bending both as a function of number of cycles to a fixed radius. Finally, OLEDs fabricated on both flexible IAI stacked anode and conventional ITO/Glass were fabricated and, J-V-L characteristics of those OLEDs were compared by Keithley 2400.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.396-399
• /
• 2003

In this paper, the purpose is to develop imaging technique of synchrotron radiation using CMOS image sensor. The detector using hybrid method to be research in this lab was used, in order to increase image signal. We made experiments with 1B2 Whitebeam/microprobe beamline in PAL (Pohang Accelerator Laboratory). Phosphor materials such as ZnS:(Ag,Li), ZnS:(Cu,Al), $Y_2O_2S:Eu$ were produced by spin coating on glass. Synchrotron radiation images were acquired and evaluated from monochromatic light from monochromoator in PAL 1B2line. From obtained object and phantom, MTF was 0.15 in ZnS:(Ag,Li) phosphor, and 0.178 in ZnS:( Cu,Al) at 151p/mm. MTFs were unsystematic because thickness of phosphor and uniformity of surface were not optimized. It's expected to improve MTF and the qualify of images as uniformity's optimized.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.448-449
• /
• 2006

For the possible applicative pearl pigment, multi-layered $TiO_2/Al/TiO_2$, $TiO_2/Cr/TiO_2$ thin film was deposited on glass substrate by using sputtering method. $TiO_2$ and Al or Cr was selected as a possible high and low refraction materials at the film interface respectively. Optical properties including color effect were systematically studied in terms of different film thickness and film layers by using spectrometer. In order to expect the experimental results, the simulation program, the Essential Macleod Program(EMP) was adopted and compared with the experimental data. The film consisting of $TiO_2/Al/TiO_2$, $TiO_2/Cr/TiO_2$ layers show the wavelength range of 430 - 760nm, typically color ranges between bluish purple and red. It was confirmed that this experimental result was quite well matched with the experimental one.

• 보존과학연구
• /
• s.23
• /
• pp.95-112
• /
• 2002

Seoul City built a facility for conservation of the Wongaksajisipcheungseoktap (Ten storied stone pagoda of Wongaksa Temple site, National treasure No. 2). It has speciality glass(thickness 21.5㎜) between steel-frames(8.4m, length 8.4m, height 15.4m). So we investigated the inside of facility to know whether the environment alvariation exists. We measured continuously the temperature and relative humidity, twice for the particulate, once for the $SO_2$(sulfur dioxide), $NO_2$(nitrogen dioxide)and $O_3$(ozone) from September $1_st$, 2000 to August $31_st$, 2001.The temperature and relative humidity, have a tendency to vary, and they have no difference between the inside and the outside. As dewy phenomenon doesn appear on the surface of the Pagoda and facility we know that the inside air is moving. As a result of the particulate is $64\mug$/$m_3$ of average concentration, the particulate fluxed inside don’t flow out because air-velocity of the outside is faster than that of the inside. The air pollutants are 0.036ppm/hr of SO$_2$average concentration, 0.028ppm/hr of $NO_2$ average concentration and 0.008ppm/hr of $O_3$ average concentration which are lower than the Environmental Air Quality Standards($SO_2$ : 0.15ppm/hr, $NO_2$ : 0.25ppm/hr,O3 : 0.1ppm/hr).

• Polymer(Korea)
• /
• v.28 no.4
• /
• pp.305-313
• /
• 2004

A vacuum pressure-difference technique for making a nano-precision replica is investigated for various applications. Master patterns for replication were fabricated using a nano-replication printing (nRP) process. In the nRP process, any picture and pattern can be replicated from a bitmap figure file in the range of several micrometers with resolution of 200nm. A liquid-state monomer is solidified by two-photon absorption (TPA) induced by a femto-second laser according to a voxel matrix scanning. After polymerization, the remaining monomers were removed simply by using ethanol droplets. And then, a gold metal layer of about 30nm thickness was deposited on the fabricated master patterns prior to polydimethylsiloxane molding for preventing bonding between the master and the polydimethylsiloxane mold. A few gold particles attached on the polydimethylsiloxane stamp during detaching process were removed by a gold selecting etchant. After fabricating the polydimethylsiloxane mold, a nano-precision polydimethylsiloxane replica was reproduced. More precise replica was produced by the vacuum pressure-difference technique that is proposed in this paper. Through this study, direct patterning on a glass plate, replicating a polydimethylsiloxane mold, and reproducing polydimethylsiloxane replica are demonstrated with a vacuum pressure-difference technique for various micro/nano-applications.

• Polymer(Korea)
• /
• v.33 no.1
• /
• pp.91-95
• /
• 2009

We fabricated the electromagnetic (EM) noise absorber films for high temperature use by blending a soft magnetic powder with poly(amide imide) (PAI). The EM noise absorber films of PAI/soft magnet composite were prepared by casting the solution of poly(amide amic acid)/soft magnet powder into glass substrate with casting applicator device and then thermal imidization. The obtained films were fully characterized and their physical properties including thermal behavior, thermal stability and mechanical properties were studied. The EM noise absorption ability was also investigated using micro-strip line method. At 1 GHz, the power loss of composite film with 150 ${\mu}m$ thickness was about 25%.

• Journal of the Korean Vacuum Society
• /
• v.20 no.3
• /
• pp.195-199
• /
• 2011

ITO thin films and gold (Au), copper (Cu) and nickel (Ni) intermediate ITO multilayer (ITO/Au/ITO, ITO/Cu/ITO, ITO/Ni/ITO) films were deposited on glass substrates with a reactive radio frequency and direct current magnetron sputtering system and then the effect of intermediate metal layer and annealing temperature on the methanol gas sensitivity of ITO films were investigated. Although both ITO and ITO/metal/ITO (IMI) film sensors have the same total thickness of 100 nm, IMI sensors have a sandwich structure of ITO 50 nm/metal 10 nm/ITO 40 nm. The change in the gas sensitivity of the film sensors caused by methanol gas ranging from 100 to 1000 ppm was measured at room temperature. The IAI film sensors showed the higher sensitivity than the other sensors. Finally, it is concluded that the ITO 50/Au 10/ITO 40 nm film sensors hasthe potential to be used as improved methanol gas sensor.