The behavior of abrasive wear on counterpart roughness of glass fiber reinforcement polyurethane resin (GF/PUR) composites were investigated at ambient temperature by pin-on-disc friction test. The friction coefficient, cumulative wear volume and surface roughness of these materials against SiC abrasive paper were determined experimentally. The major failure mechanisms were lapping layers, ploughing, delamination, deformation of resin and cracking by scanning electric microscopy (SEM) photograph of the tested surface. As increasing the counterpart roughness the GF/PUR composites indicated higher friction coefficient. The surface roughness of the GF/PUR composites was increased as the sliding velocity was higher and the counterpart roughness was rougher in wear test.

• 수산해양기술연구
• /
• 제48권3호
• /
• pp.277-283
• /
• 2012

The characteristics of abrasive wear on sliding speed of glass fiber reinforcement (GF/PUR) composites were investigated at ambient temperature by pin-on-disc friction test. The cumulative wear volume, friction coefficient and surface roughness of these materials on sliding speed were determined experimentally. The major failure mechanisms were lapping layers, deformation of resin, ploughing, delamination, and cracking by scanning electric microscopy (SEM) photograph of the tested surface. As increasing the sliding speed the GF/PUR composites indicated higher friction coefficient. The surface roughness of the GF/PUR composites was increased as the sliding speed was higher in wear test.

• 수산해양기술연구
• /
• 제46권4호
• /
• pp.495-502
• /
• 2010

The effect of load and sliding speed on abrasive wear characteristics of glass fiber/polyurethane (GF/PUR) composites were investigated at ambient temperature by pin-on-disc friction test. The friction coefficient, cumulative wear volume and surface roughness of these materials against SiC abrasive paper were determined experimentally. Experimental results showed that the surface roughness of the GF/PUR composites was increased as applied load was higher in wear test. The cumulative wear volume tended to increase nonlinearly with increase of sliding distance and depended on applied load and sliding speed for these composites. It could be verified by scanning electric microscopy (SEM) photograph of surface tested that major failure mechanisms were lapping layers, ploughing, delamination, deformation of resin and cracking.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.547-552
• /
• 2001

An intensity-based optical fiber vibration sensor is applied to detect and evaluate damages and fiber failure of composites. The optical fiber vibration sensor is constructed by placing two cleaved fiber end, one of which is cantilevered in a hollow glass tube. The movement of the cantilevered section lags behind the rest of the sensor in response to an applied vibration and the amount of light coupled between the two fibers is thereby modulated. Vibration characteristics of the optical fiber vibration sensor are investigated. Surface mounted optical fiber vibration sensor is used in tensile and indentation test. Experimental results show that the optical fiber sensor can detect damages and fiber failure of composites correctly.

• Elastomers and Composites
• /
• 제50권3호
• /
• pp.184-188
• /
• 2015

There is a need for light weight and high stiffness characteristics in the building structure as well as aircraft and cars. So fiber reinforced plastic with the addition of reinforcing agent such as glass fiber, carbon fiber, aramid fiber is utilized in this regard. In this study, mechanical strength, flow property and part shrinkage of glass fiber and carbon fiber reinforced PA6 were examined according to reinforcement content such as 10%, 20%, and 30%, and reinforcement type. The mechanical property was measured by a tensile test with specimen fabricated by injection molding and the flow property was measured by spiral test. In addition, we measured the part shrinkage of fiber reinforced PA6 that affects part quality. As glass fiber content increases, mechanical property increased by 75.4 to 182%, and flow property decreased by 18.9 to 39.5%. And part shrinkage decreased by 52.9 to 60.8% in the flow direction, and decreased by 48.2 to 58.1% in the perpendicular to the flow direction. As carbon fiber content increases, mechanical property increased by 180 to 276%, flow property decreased by 26.8 to 42.8%, and part shrinkage decreased by 65.0 to 71.8% and 69.5 to 72.7% in the flow direction and the direction perpendicular to the flow respectively.

• 수산해양기술연구
• /
• 제35권4호
• /
• pp.421-427
• /
• 1999

The critical fracture energy and failure mechanisms of GF/PP composites are investigated in the temperatures range of the ambient temperature to $-50^{\circ}C$ The critical fracture energy increase as fiber volume fraction ratio increased The critical fracture energy shows a maximum at ambient temperature and it tends to decrease as temperature goes up. Major failure mechanisms can be classfied such as fiber matrix debonding, fiber pull-out and/or delamination and matrix deformation.

• 폴리머
• /
• 제24권5호
• /
• pp.701-712
• /
• 2000

인발수지 함침장치를 사용하여 장섬유 강화 GF/PA 연속섬유를 제조한 후, 이에 PP 수지를 부가하는 새로운 방법으로 GF/PA/PP 삼성분계 복합재료를 제조하였다. 이들 복합재료의 기계적 특성을 비교한 결과, 제조 공정에 따라 물성이 다르게 나타났다. 예측한 대로 단일 사출 공정으로 제조한 GF/PA/PP(I) 복합재료 시편이 압출 후 사출 공정을 거친 GF/PA/PP(EI) 복합재료 시편보다 장섬유 함량이 높아 우수한 물성을 보여 주었다. 각 상 간의 계면 결합력을 개선시키기 위하여 상용화제로 PP-MAH를 첨가한 복합재료 제조 연구를 수행한 결과, 상용화제가 첨가되지 않은 복합재료보다 상용화제가 도입된 복합재료가 각 상 간의 계면 결합력이 향상되어 점도 및 기계적 특성이 크게 증가함을 볼 수 있었다. 특히, 이들 복합재료의 모폴로지를 관찰한 결과 상용화제가 첨가되지 않은 GF/PA/PP 복합재료의 경우는 가공 방법에 관계없이 유리섬유 주변에 PA 수지가 남아 있는 형태학적 구조를 나타내었으나, 상용화제로 PP-MAH가 도입된 경우는 PA 수지와 PP 수지 및 기지재와 유리섬유 사이에 계면 결합력이 증가됨으로 인해 유리섬유 계면에 인접한 수지가 PA 수지외에 PP 수지도 남아 있는 복잡한 구조를 보여 주었다.

• Composites Research
• /
• 제27권3호
• /
• pp.83-89
• /
• 2014

본 연구는 엔지니어링 플라스틱인 Polybutylene terephthalate(PBT)에 첨가물을 넣어 강도와 열전도성, 열충격내구성을 개선시키는 것을 목적으로 한다. 그에 따라 PBT에 유리섬유(Glass Fiber)와 Boron nitride(BN)을 복합적으로 첨가하여, 각각의 조성비에 따른 기계적 특성과 열전도 특성변화를 실험적으로 분석하였다. 시험 결과 BN의 함유량이 증가함에 따라 열전도도는 증가하였고, 기계적 강도는 작아졌다. 열충격싸이클을 가한 결과, 비충전 PBT는 파단 신장률이 작아졌으나 충전 PBT는 강도와 열전도율이 별다른 성질변화가 거의 없었다. BN의 첨가에 따라 PBT 복합재의 열전도도도는 크게 향상되었다.

• 대한기계학회논문집A
• /
• 제31권3호
• /
• pp.295-303
• /
• 2007

Degradation behaviors of filament-winded composites have been evaluated under the accelerated environmental test of high temperature, water immersion and thermal impact conditions. Two kinds of laminated composites coated by an urethane resin have been used: carbon-fiber reinforced epoxy(T700/Epon-826, CFRP) and glass-fiber reinforced phenolic (E-glass/phenolic, GFRP). For tensile strength of $0^{\circ}$ composites, CFRP showed little degradation while GFRP did high reduction by 25% under the influence of high temperature and water However for water-immersed $90^{\circ}$ composites tensile strength of both CFRP and GFRP showed high reduction. Bending strength and modulus of $90^{\circ}$ composites were largely reduced in water-immersion as well as high temperature environment. Urethane coating on the composite surface improved the bending properties by 20%, however hardly showed such improvement for water-immersed $90^{\circ}$ composites. In case of shear strength and modulus, both CFRP and GFRP showed high reduction by water-Immersion test but did a slight increase by high temperature and thermal impact conditions.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2004년도 추계학술대회 논문집
• /
• pp.1331-1334
• /
• 2004

The research on electromagnetic shielding has been advanced for military applications as well as for commercial products. Utilizing the reflective properties and absorptive properties of shielding material, the replied signal measured at the rear surface or at the signal source can be minimized. The shielding effect was obtained from materials having special absorptive properties or from structural characteristics such as stacking sequence. Recently researchers studied the electromagnetic properties of nano size particles. In this research {glass fiber}/{epoxy}/{nano particle} composites(GFR-Nano composites), was fabricated using various nano particles, and their properties in electromagnetic shielding were compared. For the visual observation of the nano composite materials, SEM(Scanning Electron Microscope) and TEM(Transmission Electron Microscope) were used. For the measurement of electromagnetic shielding, HP8719ES S-parameter Vector Network Analyser System was used on the frequency range of 8 GHz～12GHz. Among the nano particles, carbon black and Multi-Walled Carbon Nano-Tube (MWCNT) revealed outstanding electromagnetic shielding. Although silver nano particles (flake and powder) were expected to have effective electromagnetic shielding due to their excellent electric conductivities, test showed little shielding effect.