• 한국세라믹학회지
• /
• 제31권1호
• /
• pp.17-24
• /
• 1994

Al2O3-ZrO2(ZTA) composites were fabricated by a surface-induced coating of the precursor for the ZrO2 phase on the kinetically stable colloid particles of Al2O3. The fabricated composites were characterized by a uniform spatial distribution of the dispersed ZrO2 phase and by the absence of large ZrO2 grains throughout the Al2O3 matrix. The fracture toughness (KIC) and the bending strength of ZTA composites sintered at 1$600^{\circ}C$, respectively, were 5.6 MPa.m1/2 (for 20 wt% ZrO2) and 600 MPa (for 15wt% ZrO2). The fraction of tetragonal ZrO2 phase decreases as the total content of ZrO2, suggesting that both the stress-induced tlongrightarrowm transformation and the microcrack nucleation contribute to the toughening of the ZTA composites fabricated by the surface-induced coating.

• 한국세라믹학회지
• /
• 제23권4호
• /
• pp.17-22
• /
• 1986

$\beta$-Sialon powders were prepared by the reduction-nitridation reaction from the mixture of Wando-pyrophyllite and graphite at 135$0^{\circ}C$ in $N_2-H_2$ atmosphere. The $\beta$-Sialon powders were sintered at 175$0^{\circ}C$ by the pressureless sintering for 90min and the hot-pressing for 60 min respectively. All the sintered bodies showed their relative densities higher than 94% The values of M.O.R fracture toughness(KIC) and hardness showed 32.9kpsi 2.9MN/$m^{1.5}$ , 12.1GN/$m^2$ for the pressure-less sitnered bodies and 48.6kpsi, 4.6 MN/4m^{1.5}$ 15.3GN/$m^2$ for the hot-pressed bodies respectively.

• 한국세라믹학회지
• /
• 제26권2호
• /
• pp.201-209
• /
• 1989

Fine Si-Al-OH coprecipitate powders were prepared from Si- and Al-alkoxides by the hydrolysis method. $\beta$-Sialon powder was obtained from prepared Si-Al-OH coprecipitate by the simultaneous reduction and nitridation method. The syntehsized Sialon powder was pressureless sintered at 175$0^{\circ}C$ for 90 min in N2 atmosphere. The characterization of the Sialon powder was performed with XRD, BET, SEM, TEM and particle size analysis. The sinterability and mechanical properties of sintered bodies were investigated in terms of relative density, M.O.R., fracture toughness, hardness and the morphology of microstructure. The highest values of their mechanical properties were obtained for the $\beta$-Sialon ceramics at Z=1 and those values are as follows : M.O.R., KIC and HV of $\beta$-Sialon ceramics(Z=1) are 499.1 MPa, 5.9MN/m3/2 and 18.7GPa, respectively.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.107-108
• /
• 2006

The effect of WC or NbC addition on various properties of Ti(C0.7N0.3)-Ni cermets was investigated. The microstructure oj Ti(C0.7N0.3)-xWC-20Ni showed a typical core/rim structure, irrespective of the WC content, whereas the structure oj Ti(C0.7N0.3)-xNbC-20Ni was different and was dependent on the NbC content. The hardness (HV) and the fracture toughness (KIC) had a tendency to increase marginally, while the coercive force (HC) and the magnetic saturation $(4{\pi}{\sigma})$ decreased gradually with an increase in WC or NbC content in the systems studied. In addition, increasing WC content in Ti(C0.7N0.3)-xWC-20Ni system, decarburization was retarded, while denitrification was accelerated

• 대한치과보철학회지
• /
• 제52권4호
• /
• pp.312-316
• /
• 2014

목적: 본 연구에서는 지르코니아 수복물의 접착에 사용되는 레진 시멘트의 파괴인성을 측정하고 각 레진 시멘트의 다양한 수중 보관 기간이 파괴 인성에 미치는 영향에 관하여 알아보고자 하였다. 재료 및 방법: 세가지 종류의 레진 시멘트(Panavia F2.0, Clearfil SA luting, Zirconite)를 사용하여 single edge notched 형태의 시편($3mm{\times}6mm{\times}25mm$)을 제작하였다. 각 시편은 $37^{\circ}C$ 증류수에서 1일 (대조군), 30일, 90일, 180일 동안 보관하였다 (n=5). 만능시험기를 이용하여 0.1 mm/s 속도로 삼점굽힘 시험을 시행하고, 파절 시의 최대하중으로 파괴인성($K_{IC}$)을 계산하였다. 측정값은 일원분산분석과 다중분석을 위한 $Scheff{\acute{e}}$ test를 사용하였고, 유의수준은 0.05로 하였다. 결과: 대조군에서 Panavia F2.0가 $3.41{\pm}0.64MN{\cdot}m^{-1.5}$로 가장 높은 $K_{IC}$를 보였으며 Zirconite가 $3.07{\pm}0.41MN{\cdot}m^{-1.5}$, Clearfil SA luting이 $2.58{\pm}0.30MN{\cdot}m^{-1.5}$으로 가장 낮은 $K_{IC}$를 보였으나, 재료간에 유의성 있는 차이는 없었다. 수중보관 기간이 증가함에 따라 Panavia F2.0의 값은 감소였고, Clearfil SA luting과 Zirconite는 증가하였으나, 통계적으로 유의한 차이를 보이지 않았다. 결론: 지르코니아 수복물 전용 레진 시멘트의 파괴인성은 다른 일반 시멘트에 비해 대체로 높으며, 이러한 파괴인성은 수중 보관에 영향을 받지 않는다.

• 한국세라믹학회지
• /
• 제36권10호
• /
• pp.1102-1107
• /
• 1999

SiC-Si3N4 composites were prepared by mixing $\alpha$-Si3N4 powder to $\alpha$-SiC powder in the range of 10 to 30 vol% with 10vol% interval. 6wg% Al2O3 and 6wt% Y2O3 were respectively added as sintering aids. Hot pressing was performed at 1,80$0^{\circ}C$ for 1 hour with 25 MPa pressure. In the case of adding 20vol% of $\alpha$-Si3N4 powder the relative density to theoretical value and the flexural strength were 99.1% and 34,420 MPa respectively and the worn amount was 2.09$\times$10-3 mm2 which were the highest values in the all range of he composition. Although the composite containig 10 vol% of $\alpha$-Si3N4 powder showed the highest fracture toughness(KIC) of 4.65MN/m3/2 the reduction of the wear resistance in this composite is likely to be affected by the homogeneity and the uniformity of the grain coalescence and growth during the sintering process.

• Journal of Welding and Joining
• /
• 제28권1호
• /
• pp.86-91
• /
• 2010

In the present study, two-dimensional plane deformation thermo elasto-plastic analysis has been carried out, in order to investigate the thermal and mechanical behaviour (residual stress, plastic strain, magnitude of stress and their distribution and production mechanism) on multi-pass FCA butt weldment of high strength EH36-TMCP ultra thick plate. Moreover, this study can be considered as a basis for analysing the fracture toughness, KIC, and its effect on welding residual stress redistribution with notch on multi-pass FCA butt weldment, in future. The results of welding residual stress obtained from thermo elasto-plastic analysis has been compared and verified with the results measured by XRD.

• 한국세라믹학회지
• /
• 제26권6호
• /
• pp.771-782
• /
• 1989

Synthesis of $\beta$-Sialon powder was attempted with carbothermal reduction of porous glass. The porous glass was prepared by heat and hydrothermal treatments of 9.32 Li2O.46.5B2O3.37.2SiO2.6.98Al2O3 glass. Carbon pyrolyzed from propane gas was deposited on the porous glass, thereafter activated carbon was added as reducing agents. The synthesized $\beta$-Sialon powder was pressureless sintered at 175$0^{\circ}C$ for 1hr in N2 atmosphere. The characterization of the $\beta$-Sialon powder was performed with XRD, BET, SEM and particle size analysis. The sinterability and mechanical properties of the sintered bodies were investigated in terms of bulk density, M.O.R., fracture toughness, morphology of microstructure and etc. The reduction effect of deposited carbon was better than that of activated carbon mechanically added. The formation of SiC was precominant over that of Si2ON2 and $\beta$-Sialon owing to low partial pressure of N2 inside the pore, wehreas on the surface of porous glass the formation of Si2ON2 and $\beta$-Sialon were predominant. Thereafter, SiC reduced unreacted glass to be $\beta$-Sialon. Single phase of $\beta$-Sialon(Z=1.92) was obtained from PGA porous glass having the largest pore radius by the simultaneous reduction and nitridation method at 145$0^{\circ}C$ for 5hrs. The bulk density, M.O.R., and KIC of the sitered body are 3.17g/cc, 434.4MPa and 4.1MPa.m1/2, respectively.