Tribological Properties of Hot Pressed $SiC/Si_3N_4$ Composites

가압소결 $SiC/Si_3N_4$ 복합체의 마찰마모특성

  • Baik, Yong-Hyuck (Department of Ceramic Eng. Advanced Materials Research Institute. Chonnam National University) ;
  • Choi, Woong (Department of Ceramic Eng. Advanced Materials Research Institute. Chonnam National University) ;
  • Park, Yong-Kap (Department of Materials Science and Eng., Sunmoon University)
  • 백용혁 (전남대학교 세라믹공학과.신소재기술연구소) ;
  • 최웅 (전남대학교 세라믹공학과.신소재기술연구소) ;
  • 박용갑 (선문대학교 재료공학과)
  • Published : 1999.10.01
Download PDF
⟨ Previous Next ⟩

Abstract

SiC-Si3N4 composites were prepared by mixing $\alpha$-Si3N4 powder to $\alpha$-SiC powder in the range of 10 to 30 vol% with 10vol% interval. 6wg% Al2O3 and 6wt% Y2O3 were respectively added as sintering aids. Hot pressing was performed at 1,80$0^{\circ}C$ for 1 hour with 25 MPa pressure. In the case of adding 20vol% of $\alpha$-Si3N4 powder the relative density to theoretical value and the flexural strength were 99.1% and 34,420 MPa respectively and the worn amount was 2.09$\times$10-3 mm2 which were the highest values in the all range of he composition. Although the composite containig 10 vol% of $\alpha$-Si3N4 powder showed the highest fracture toughness(KIC) of 4.65MN/m3/2 the reduction of the wear resistance in this composite is likely to be affected by the homogeneity and the uniformity of the grain coalescence and growth during the sintering process.

Keywords

References

  1. Yogyo Kyokai-Shi v.94 no.3 Friction and Wear of Ceramics Measured by a Pin-on-Disk Tester M. Iwasa;Y. Toibana
  2. Structural Ceramics v.29 B. Wachtman Jr.
  3. Rokakuho SiC Ceramics S. Somiya;Y. Inomata
  4. Am. Ceram. Bull. v.64 no.2 International Perspective on Ceramic Heat Engines E. M. Lenoe;J. L. Meglen
  5. Am. Ceram. Bull v.64 no.2 Ceramic Technology for Advanced Heat Engines Project D. R. Johnson;A. C. Schaffhauser;V. J. Tennery;E. L. Long
  6. Adv. Ceram. Mater. v.2 no.4 Applications of High-Technology Ceramics in Japanese Automobiles M. Taguchi
  7. J. Ceram. Soc. Jan. v.100 no.4 Mechanical Properties and Microstructure of$Si_3N_4$Matrix Composite with Nano-Meter Scale SiC Particles G. Sasaki;H. Nakase;K. Suganuma;T. Fujita;K. Niihara
  8. J. Ceram. Soc. Jan. v.100 no.4 Influence of Starting Powder Characteristics on Mechanical Properties of SiC-Particle/Si₃N₄Composites Y. Akimune;T. Ogasawara;N. Hirosaki
  9. J. Am. Ceram. Soc. v.56 no.9 Effect of Microstructure on Strength of$Si_3N_4$-SiC Composite System F. F. Lange
  10. J. Mat. Sci. v.27 Mechanical Properties and Microstructure in Sintered and HIPed SiC Particle/$Si_3N_4$Composites Y. Akimune;N. Hirosaki;T. Ogasawara
  11. J. Mater. Sci. v.10 no.12 Equilibrium Penny-Like Crack in Indentation Fracture B. R. Lawn;E. R. Fuller
  12. 요업학회지 v.30 no.12 고강도$Si_3N_4$/SiC 구조세라믹스에 관한 연구 김병수;김인술;장윤식;박홍채;오기동
  13. 요업학회지 v.33 no.10 반응소결 탄화규소의 제조 및 특성에 관한 연구 Ⅱ 박현철;박상환;최승철
  14. 요업학회지 v.34 no.12 출발상제어에 의한 자기복합화 미세구조의 탄화규소 세라믹스 제조 이종국;강현희;이의구;김환