• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.12
• /
• pp.2962-2969
• /
• 1993

Recently, a study on the mirror-like surface grinding of brittle materials is active and as branch of these study, new dressing method for superabrasive wheel, electrolytic inprocess dressing(Elid) was developed. Using Elid, the mirror-like surface of brittle material can be generated without polishing or lapping process. In the future, Elid grinding will take important place in industry. But so far the analysis on Elid grinding was not quantitative but qualitative. In this study, The purpose is the quantitative analysis on Elid grinding by computer simulation, For computer simulation, the mean and the variance of the abrasive distribution were measured by tracing of the grinding wheel with stylus in transverse direction in the case of respective dressing current condition. This measurement result in a density distribution of abrasive by mathematical formulation using statistical method. The prediction of the surface roughness in Elid grinding was based on this density distribution.

• Journal of the Korean Ceramic Society
• /
• v.31 no.11
• /
• pp.1355-1361
• /
• 1994

With the availability of ceramics (Al2O3, Al2O3-TiC), it is possible to machine very hard steel at different cutting conditions. When hardened steel STD 11 is turned using ceramic tools, chip formation is observed conical-herical and arc chips with a cyclic saw toothed type. The main cause of saw toothed chip formation is observed conical-herical and arc chips with a cyclic saw toothed type. The main cause of saw toothed chip formation is found to be periodic gross shear fracture extending from the free surface of the chip toward the tool tip. In regard to chip control, ceramic Al2O3 is superior to the other cutting tools. The roughness of machined surface was getting worse with increasing of cutting speed and feed.

• The Korean Journal of Ceramics
• /
• v.5 no.1
• /
• pp.19-24
• /
• 1999

The influences of TiB2 additions to the β-sialon on mechanical propeties and electrical discharge machinability were investigated. Samples were prepared by adding 15, 30 and 45 vol.% TiB2 particles as a second phase to a β-sialon matrix. The β-sialon-TiB2 composites were sintered by hot pressing in a nitrogen atmosphere at 1800℃ with pressure of 30 MPa. The fracture toughness of the composites was increased with TiB2 content except 45 vol.% TiB2 composite. The crack propagation and crack deflection were observed with a SEM for etched samples after vicker's indentation. The composites containing more than 30 vol.% TiB3 had resistivity lower than 10-3 Ω㎝. The electrical discharge machining (EDM) of composited was conducted with two kind of machines such as die-sinker and wire cutter. The machinability was evaluated with the cutting rate surface roughness after machining.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.04a
• /
• pp.927-931
• /
• 1997

In process of the finish face milling of the hardended STD11 steel(H /sab r/ c50,55) by CBN tool, the optimum tool shape is suggested,which can minimize the tool fracture and by chipping by impact. The obtained results are as follows. (1) The optimal chamfer angel was about 25 .deg. , and the suitable chamfer width was 0.2mm. (2) The nose radius of tool was most excellent at 1.2mm in the viewpoint of tool wear and surface roughness. (3) Wear speed was effected by sintering method of CBN tool B.U.E

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1992.11a
• /
• pp.97-101
• /
• 1992

Cordierite glass ceramic has become an electronic substrate material for electronic circuits and the use of whiskers for improving strength and toughness is evident. Green sheets of mixtures containing 15% silicon nitride were sintered to greater than 99 % density. The microstructure was analysed using optical microscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD). The toughness and hardness were improved with increasing the whisker vol. % and sintering temperature. Especially, it is assumed that toughening increasing at the more high sintering temperature relevants to the glass phase increasing, as showned in the roughness of the fracture surfaces. It was directionally dependent of whisker direction during processing.

• Electrical & Electronic Materials
• /
• v.7 no.1
• /
• pp.1-6
• /
• 1994

Cordierite based glass ceramics has become an electronic substrate material for electronic circuits and the use of whickers for improving strength and toughness is evident. Pure cordierite containing 15 vol.% silicon nitride were sintered by hot-prossing and it has above 99% density. Especially, it is assumed that toughening increasing at the more high sintering temperature relevants to the glass phase increasing, as showned in the roughness of the fracture surfaces. It was directionally dependent of whisker drirection during processing.

• Journal of the Korean Society of Industry Convergence
• /
• v.8 no.1
• /
• pp.25-29
• /
• 2005

Titanium specially has high specific strength, excellent mechanical properties as fatigue strength and fracture ductility, good corrosion resistance, and therefore are broadly applied to the various fields. It is required the developmennt for the skills of wire-cut electrical discharge machining(WEDM), but the WEDMed surface was found to be worst due to the attached components of wire. Therefore precision maching method like lapping is necessary for getting high quilty surface. Roughness of lapped surface, surface hardness to each process depth and improved method of surface shape were stuided experimentally, by changing of grain size of diamond lap material and lapping pressure with constant speed in lapping process.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.205-210
• /
• 2001

Fatigue crack growth tests were carried out using high manganese cast steel under constant amplitude loading. Average crystal grain sizes of the material are $200{\mu}m$ and $1000{\mu}m$. For this material, ${\Delta}K_{th}$ is about $8MPa{\sqrt{m}}$ which is quiet large as compared to the general structural steels and the crack growth rate is lower than the general structural steels especilly in the low ${\Delta}K$ regsion. The reason of this behavior is crack closure due to fracture surface roughness and fretting oxide. The relationship between da/dN and the ${\Delta}K_{eq}$ was represented by narrow band regardless of the stress ratio.

• Tribology and Lubricants
• /
• v.5 no.1
• /
• pp.28-35
• /
• 1989

The wear tests of ceramic materials in dry rolling contact were carried out at room temperature to investigate their macroscopic wear characteristics. Both point contact and line cootact were adapted in the wear tests of them. Ceramic materials used in these tests were silicon nitride, silicon carbide, cermet of TiN and TiC, titania, and alumina. The wear test of the bearing steel was carried out to compare to the wear test results of the ceramic materials. The results showed that the wear rate of silicon nitride was smaller than any other ceramic materials and bearing steel. In the steady wear, the wear volume of ceramic materials increases linearly with the rolling distance. It was also found from the experimental results that fracture toughness and surface roughness dominate the wear process of ceramic materials in dry rolling contact.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.320-325
• /
• 1996

The influences of ZrB$_2$additives to the SiC and pulse width on electrical discharge machining of SiC-ZrB$_2$electroconductive ceramic composites were investigated. IIigher-flexural strength materials show a trend toward smaller crater volumes, leaving a soother surface; the average surface roughness of the SiC-ZrB$_2$15 Vol.% Composite with the flexural strength of 375㎫ was 3.2${\mu}{\textrm}{m}$,whereas the SiC-ZrB$_2$30 Vol.% composite of 457㎫ was 1.35${\mu}{\textrm}{m}$. In the SEM micrographs of the fracture surface of SiC-ZrB$_2$composites, the SiC-ZrB$_2$two phaes are distinct; the white phase is the ZrB$_2$. In the micrograph of the EDM surface, however, these phases are no longer distinct because of thicker recast layer of resolidified-melt-formation droplets present.