• Economic and Environmental Geology
• /
• v.17 no.2
• /
• pp.115-139
• /
• 1984

The Cu-Pb-Zn-Ag hydrothermal vein-type deposits which comprise the Sambong mine occur within calc-alkaline volcanics of the Cretaceous Gyeongsang Basin. The ore mineralization took place through three distinct stages of quartz (I and II stages) and calcite veins (III stage) which fill the pre-existing fault breccia zones. These stages were separated in time by tectonic fracturing and brecciation events. The reflection variations of one mineral depending on mineralization sequence are considered to be resulted from variation in its chemical composition due to different physico-chemical conditions in the hydrothermal system. The reflection power of sphalerite increases with the content of Fe substituted for Zn. Reflectances of the sphalerite grain are lower on (111) than on (100) surface. The spectral profiles depend on the internal reflection color. Sphalerite, showing green, yellow and reddish brown internal reflection, have the highest reflection power at $544m{\mu}$ (green), $593m{\mu}$ (yellow) and $615m{\mu}$ (red) wavelength, respectively. Chalcopyrite is recognized as biaxial negative from the reflectivity data of randomly oriented grains measured at the most sensitivity at $544m{\mu}$. The microindentation hardness against the Fe content (wt. %) for the sphalerite increases to 8.05% Fe and then decreases toward 9.5% Fe content. Vickers hardness of the sphalerite is considerably higher on surface of (100) than on (111). The relationship between Vickers hardness and crystal orientation of the galena was determined to be $VHN_{(111)}$ > $VHN_{(210)}$ > $VHN_{(100)}$. The softer sulfides have the wider variation of the diagonal length in the indentation. Diagonal length in the indentation is pyrite

• Journal of the korean academy of Pediatric Dentistry
• /
• v.26 no.4
• /
• pp.677-687
• /
• 1999

This study was performed to evaluate the effect of aging and thermal cycling on the tensile strength of six commercially available glass-ionomer materials: two chemically set glass-ionomer materials(Fuji II, Fuji IX), two resin-modified glass-ionomer materials(Fuji II LC, Vitremer), and two polyacid-modified composite resins(Compoglass, Dyract). Rectangular tension test specimens were fabricated in a teflon mold giving 5mm in gauge length and 2mm in thickness. All samples were divided into 3 groups. Group 1 was immersed in a $37^{\circ}C$ distilled water for 1 hour. Group 2 was immersed in a $37^{\circ}C$ distilled water for 30 days. Group 3 was subjected to 10,000 thermal cycles between $5^{\circ}C$ and $55^{\circ}C$, and the immersion time in each bath was 15 seconds per cycle. Tensile testing was carried out at a cross-head speed of 0.5mm/min and fracture surfaces were examined with scanning electron microscope. The results obtained were summarized as follows; 1. The polyacid-modified composite resins were stronger than the resin-modified glass-ionomer materials, which were much stronger than the conventional glass-ionomer materials. 2. Tensile strengths were slightly increased after aging treatments for 30days. 3. Tensile strengths of conventional glass ionomers were significantly increased after thermal cycling treatment(p<0.01). 4. The highest tensile strength value of 45.4MPa was observed in the Dyract group and the lowest value of 13.3MPa was observed in the Fuji II LC group after the thermal cycling test, and the strengths of polyacid-modified composite groups were significantly higher than those of other groups. 5. The highest characteristic strength value of 48.6MPa was obtained in the Dyract group, however the highest Weibull modulus value of 8.9MPa was obtained in the Compoglass group after thermal cycling test.