• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.1
• /
• pp.73-81
• /
• 2010

The objective of this study was to evaluate the color stability of new silorane-based composite resin compared with methacrylate-based composite resins after immersion in 3 staining solutions. One silorane-based composite(Filtek P90) and 3 methacrylate -based composites(Filtek Z250, Filtek Z350, Tetric Ceram) were evaluated. Twenty disk-shaped specimens($10{\times}2mm$) of each of 4 composite resins were prepared. The specimens were then divided into 4 groups of 5 specimens each and immersed in 3 staining solutions( coffee, red wine, curry solution) or distilled water(control) for 28-day test period. Color of the specimens was measured with a spectrophotometer(Color Eye 7000A) using CIE $L^*a^*b^*$ color space relative to CIE standard illuminant D65 at baseline, 1day, 3days, 7days, 14days, 21days and 28days after staining. The color differences( ${\Delta}{E^*}_{ab}$) were calculated. The results were obtained as follows ; 1. The mean color changes(${\Delta}{E^*}_{ab}$) of the composites were greatest in curry solution, then red wine, coffee and distilled water, in decreasing order. 2. The mean color changes(${\Delta}{E^*}_{ab}$) of the composites were greatest in Z350, Z250, Tetric Ceram and P90, in decreasing order.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.3
• /
• pp.427-436
• /
• 2005

Topical application of APF gel can increase the surface roughness of resin composites and the roughened surfaces may allow increased bacterial accumulation and surface staining. Resin specimens of two proprietary resin composites, Filtek Z250(FZ) and Filtek Supreme Universal(FS), and experimental resin composites containing 0%, 3%, 6% nanofillers(E0, E3, E6) were fabricated and divided into two groups of the same number; APF treatment group and no treatment group. The amount of S. mutans adhered to specimens and the mean surface roughness(Ra) were measured. The results were as follows; 1. In no treatment group, the amount of S. mutans adhered to FS was the smallest. It was significantly different from those of FZ, E3, E6(p<0.05) although it was not significantly different from that of E0(p>0.05). 2. For all resin composites used, the amount of S. mutans adhesion in APF treatment group was significantly greater than that in no treatment group(p<0.05). 3. In APF treatment group, the amount of S. mutans adhesion was significantly different between materials(p<0.05), and increased in order of FS, FZ, E0, E3 and E6. 4. Difference of the surface roughness(Ra) between materials was not statistically significant in both no treatment group and APF treatment group(p>0.05)

• Journal of Convergence for Information Technology
• /
• v.9 no.7
• /
• pp.159-167
• /
• 2019

This study aimed to evaluate the effects of oral rinsing solution on the color stability, surface microhardness and surface roughness change of composite resin. In this in-vitro study, 80 disc-shaped specimens were fabricated of Filtek P60 and Filtek Z250(A2 shade). The samples of each group were randomly divided into eight subgroups (n=10). The baseline color values ($L^*$, $a^*$, $b^*$) of each specimen were measured according to CIE LAB system using a colorimeter. After baseline color measurements, the control samples were immersed in distilled water and the test groups were immersed colorless, green and purple mouthrinses three times a day for thirty minutes. This process was repeated for two weeks. Green and purple oral rinsing solutions displayed color, microhardness and roughness change of all composite resin after immersion in the mouthrinses. Therefore, prescription of oral rinsing solution for a minimum of two weeks is a common practice, which may cause discoloration of aesthetic composite restorations of patients.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.2
• /
• pp.133-141
• /
• 2004

Statement of problem : Porcelain restorations are widely used in restorative dentistry with a high degree of general success. However, porcelain is brittle and may fracture intraorally. Sometimes a repair may be attempted using composite resin and bonding system available. Color stability of porcelain repair resins affects esthetics and prognosis of prosthesis, so that provides important criteria for the choice of porcelain repair resins. Purpose : The purpose of this study was to investigate the color stability of composite resins used widely as porcelain repair system. Materials and method : Composite resins used for this study were Carisma(Kulzer, Germany), Tetric ceram(Ivoclar, Liechtenstein), Filtek Z250(3M, USA), and Arabesk Top(VOCO, Germany). Thirty disc-shaped specimens($10{\times}2mm$) were fabricated from each composite resin. Color changes of specimens after treatment using thermocycling system(KD-TCS30, Kwang-duk F.A. Korea) and after immersion in methylene blue(0.05% by Wt) were measured with colorimeter(Model Tc-6Fx, Tokyo Denshoku Co.) and obtained data were analyzed. Results and Conclusion: The results obtained from this study were as fo11ows. 1. The color change of Filtek Z250 was lesser than those of Tetric ceram and Arabesk Top after thermocycling (12000 times). 2. All of the composite resins in this study showed increase of color change according to increase of thermocycling frequency. 3. After treatment with methylene blue, the color change of Arabesk Top was greater than those of Carisma and Tetric ceram, and Tetric ceram was more stable than others.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.3
• /
• pp.288-297
• /
• 2010

The purpose of this study was to evaluate the effect of light cured fluoride-releasing materials on the inhibition of demineralization. In addition, the pattern of fluoride uptake of adjacent tooth structure was analyzed with EPMA. Eighty intact premolars were restored with $Filtek^{TM}$ Z250(control group, composite), Fuji Filling $LC^{TM}$(RMGI), Dyract $AP^{(R)}$ (compomer) and Beautifil II(giomer). Restored teeth were stored in distilled water for 30 days. Then sixty teeth(n=15) were exposed to demineralizing solution(pH 4.3). Demineralized teeth were bisected and polished. The specimens were observed with confocal laser scanning microscope. The depth of outer lesion and the thickness of inhibition zone were measured. Remained twenty teeth(n=5) were bisected for fluoride uptake analysis. The fluoride analysis were taken at enamel-restoration interface and dentin-restoration interface by electron probe micro-analyzer. The results are as follows: 1. The depth of outer lesion of Fuji Filling $LC^{TM}$ Dyract AP, Beautifil II was shallower than that of $Filtek^{TM}$ Z250 at the margin of restoration(p<0.05). 2. The thickness of caries inhibition zone of Fuji Filling $LC^{TM}$, Dyract AP, Beautifil II was greater than that of $Filtek^{TM}$ Z250 at the margin of restoration(p<0.05). 3. Fuji Filling $LC^{TM}$, Dyract AP, Beautifil II groups showed the greater fluoride uptake into enamel and dentine around restoration than $Filtek^{TM}$ Z250 group. 4. In dentin the difference of fluoride concentration were greater than in enamel, and Dyract AP showed the greatest fluoride concentration in dentin.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.4
• /
• pp.479-484
• /
• 2013

PURPOSE. The aim of this study was to evaluate the effects of additional acid etching and curing mechanism (light-curing or self-curing) of a composite resin on the dentin bond strength and compatibility of one-step self-etching adhesives. MATERIALS AND METHODS. Sixteen human permanent molars were randomly divided into eight groups according to the adhesives used (All-Bond Universal: ABU, Clearfil S3 Bond: CS3), additional acid etching (additional acid etching performed: EO, no additional acid etching performed: EX), and composite resins (Filtek Z-250: Z250, Clearfil FII New Bond: CFNB). Group 1: ABU-EO-Z250, Group 2: ABU-EO-CFNB, Group 3: ABU-EX-Z250, Group 4: ABU-EX-CFNB, Group 5: CS3-EO-Z250, Group 6: CS3-EO-CFNB, Group 7: CS3-EX-Z250, Group 8: CS3-EX-CFNB. After bonding procedures, composite resins were built up on dentin surfaces. After 24-hour water storage, the teeth were sectioned to make 10 specimens for each group. The microtensile bond strength test was performed using a microtensile testing machine. The failure mode of the fractured specimens was examined by means of an optical microscope at ${\times}20$ magnification. The data was analyzed using a one-way ANOVA and Scheffe's post-hoc test (${\alpha}$=.05). RESULTS. Additional etching groups showed significantly higher values than the no additional etching group when using All-Bond Universal. The light-cured composite resin groups showed significantly higher values than the self-cured composite resin groups in the Clearfil S3 Bond. CONCLUSION. The additional acid etching is beneficial for the dentin bond strength when using low acidic one-step self-etch adhesives, and low acidic one-step self-etch adhesives are compatible with self-cured composite resin. The acidity of the one-step self-etch adhesives is an influencing factor in terms of the dentin bonding strength and incompatibility with a self-cured composite resin.

• Restorative Dentistry and Endodontics
• /
• v.36 no.3
• /
• pp.188-195
• /
• 2011

Objectives: The purpose of this study was to evaluate the polymerization shrinkage stress among conventional methacrylate-based composite resins and a silorane-based composite resin. Materials and Methods: The strain gauge method was used for the determination of polymerization shrinkage strain. Specimens were divided by 3 groups according to various composite materials. Filtek Z-250 (3M ESPE) and Filtek P-60 (3M ESPE) were used as a conventional methacrylate-based composites and Filtek P-90 (3M ESPE) was used as a silorane-based composites. Measurements were recorded at each 1 second for the total of 800 seconds including the periods of light application. The results of polymerization shrinkage stress were statistically analyzed using One way ANOVA and Tukey test (p = 0.05). Results: The polymerization shrinkage stress of a silorane-based composite resin was lower than those of conventional methacrylate-based composite resins (p < 0.05). The shrinkage stress between methacrylate-based composite resin groups did not show significant difference (p > 0.05). Conclusions: Within the limitation of this study, silorane-based composites showed lower polymerization shrinkage stress than methacrylate-based composites. We need to investigate more into polymerization shrinkage stress with regard to elastic modulus of silorane-based composites for the precise result.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.2
• /
• pp.233-243
• /
• 2006

The aim of this study was to investigate the relationship between the C-factor and shrinkage strain values of composite resin and examine the strain values in different incremental filling techniques. Experiment consisted two aims. First, we compared with strain value in two different C-factors(3.7 and 1.0). Second, we examined the strain values in three different filling techniques. The results of the present study can be summarized as follows : 1. High C-factor groups showed higher contraction stress values than low C-factor groups at 900 sec after polymerization. 2. Hybrid resin showed higher contraction stress values than flowable resin in high C-factor cavities. But contraction stress was not revealed significant difference between hybrid resin and flowable resin in low C-factor cavities (P>0.05). 3. Bulk felling with hybrid resin(Group 1) showed high contraction stress and lining with flowable resin followed hybrid resin (Group 5) showed lower contraction stress. 4. Contraction stress were increased during 900 sec after polymerization in high C-factor groups but decreased gradually after 900 sec. 5. Low C-factor groups showed tight marginal seal between resin and cavity wall but high C-factor groups showed gaps formed between resin and cavity wall in part. On the basis above results, layering techniques in high C-factor cavity showed advantages in reducing contraction stress and gap formation between cavity wall and resin restoration.

• Restorative Dentistry and Endodontics
• /
• v.28 no.3
• /
• pp.222-231
• /
• 2003

The purpose of this study was to compare shear bond strength and interfacial pattern of composite bond-ed to dentin using self-etching adhesive systems. Sixty extracted human molars with exposed occlusal dentin were divided into four groups and bonded with four adhesives and composites. Single Bond/Filtek Z 350(SB), Tyrian SPE-One-Step Plus/Aelitefil(TY), Prompt L-Pop/Filtek Z 250(LP), and One-Up Bond F/palfique Toughwell(OU). The results of this study were as follows; 1 Shear bond strength for OU was significantly lower than that of other groups(p＜0.05). No significant difference was founded among SB, TY, and LP. 2. Failure modes to dentin showed adhesive and mixed for SB TY and LP, but them for OU showed adhesive in all spceimens. 3. Dentin-resin interface showed close adaptation for SB, TY, and LP, but it showed gap for OU. 4. The hybrid layers for TY, LP OU were thinner than that of SB. Adhesive layers were observed between composite and hybrid layer, which were 5 $\mu\textrm{m}$ thick for TY and 10 $\mu\textrm{m}$ thick for OU.

• Restorative Dentistry and Endodontics
• /
• v.39 no.4
• /
• pp.310-318
• /
• 2014

Objectives: This study examined the influence of the resin thickness on the polymerization of silorane- and methacrylate-based composites. Materials and Methods: One silorane-based (Filtek P90, 3M ESPE) and two methacrylate-based (Filtek Z250 and Z350, 3M ESPE) composite resins were used. The number of photons were detected using a photodiode detector at the different thicknesses (thickness, 1, 2 and 3 mm) specimens. The microhardness of the top and bottom surfaces was measured (n = 15) using a Vickers hardness with 200 gf load and 15 sec dwell time conditions. The degree of conversion (DC) of the specimens was determined using Fourier transform infrared spectroscopy (FTIR). Scratched powder of each top and bottom surface of the specimen dissolved in ethanol for transmission FTIR spectroscopy. The refractive index was measured using a Abbe-type refractometer. To measure the polymerization shrinkage, a linometer was used. The results were analyzed using two-way ANOVA and Tukey's test at p < 0.05 level. Results: The silorane-based resin composite showed the lowest filler content and light attenuation among the specimens. P90 showed the highest values in the DC and the lowest microhardness at all depth. In the polymerization shrinkage, P90 showed a significantly lower shrinkage than the rest two resin products (p < 0.05). P90 showed a significantly lower refractive index than the remaining two resin products (p < 0.05). Conclusions: DC, microhardness, polymerization rate and refractive index linearly decreased as specimen thickness linearly increased. P90 showed much less polymerization shrinkage compared to other specimens. P90, even though achieved the highest DC, showed the lowest microhardness and refractive index.