• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.1
• /
• pp.25-32
• /
• 2016

The purpose of this study is to evaluate the performance on the compressive bonding shear strength of ultra-high strength steel fiber reinforced cementitous composites(UHSCC). As a result of compressive bonding shear strength through Direct shear test, It was found that the specimen($150{\times}150{\times}150mm$) of NC(Normal concrete) + NC showed similar compressive bonding shear strength at whole experimental level. On the other hand, the specimen of UHSCC + UHSCC showed decrease of compressive bonding shear strength from after 30 minutes of the retarded placement than 0 minute. As a result of analyzing failure mode of bonding interface, It was found that the specimen of NC + NC showed mixed failure at whole experimental level. In case of the specimen of UHSCC + UHSCC, it showed interface failure from the specimen that are 30 minutes, 60 minutes and 90 minutes of delay of concrete placing. As a result of analyzing XRD test in terms of the placement interface on the specimen of NC and UHSCC, relatively much amount of $SiO_2$ was detected from the specimen of UHSCC than that of NC. It is judged that the most of main components of coating film shown in the specimen of UHSCC is $SiO_2$. In conclusion, it is judged that UHSCC which is made from after 30 minutes of delay of concrete placing is unable to be used as structural member because of deterioration of bonding performance. From later study, it is judged that the improvement of bonding performance from the part of cold joint occurrence is necessary through the interface preparation method.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.279-286
• /
• 2019

In this study, an experimental study on the tensile properties of steel fiber-reinforced ultra high strength concrete(UHSC) with a standard compressive strength of 180MPa was performed. Steel fibers with a volume ratio of 1% were mixed to prepare direct tensile strength specimens and prism specimens for the three-point bending test. The fabricated specimens were set up in the middle section of the specimen to induce cracks, and the test was carried out according to each evaluation method. First, the stress-strain curves were analyzed by performing direct tensile strength tests to investigate the behavior characteristics of concrete after cracking. In addition, the load-CMOD curve was obtained through the three-point bending test, and the inverse analysis was performed to evaluate the stress-strain curve. Tensile behavior characteristics of the direct tensile test and the three-point bending test of the indirect test were similar. In addition, the tensile stress-strain curve modeling presented in the SC structural design guidelines was performed, and the comparative analysis of the measured and predicted values was performed. When the material reduction factor of 1.0 was applied, the predicted value was similar to the measured value up to the strain of 0.02, but when the material reduction factor of 0.8 was applied, the predicted value was close to the lower limit of the measured value. In addition, when the strain was greater than 0.02, the predicted value by SC structural design guideline to underestimated the measured value.

• Journal of the Korea Concrete Institute
• /
• v.28 no.1
• /
• pp.41-48
• /
• 2016

This research investigates the effects of shrinkage reducing agent (SRA) on the mechanical behavior of strain-hardening cement composite (SHCC). SHCC material with specified compressive strength of 50 MPa was mixed and tested in this study. All SHCC mixes reinforced with volume fraction of 2.2% polyvinyl alcohol (PVA) fiber and test variables are type and dosage of shrinkage reducing agents. The shrinkage reducing materials used in this study are phase change material as the thermal stress reducing materials that have the ability to absorb or release the heat. The effect of SRA was examined based on the change in length caused by shrinkage and hardened mechanical properties, specially compressive, tensile and flexural behaviors, of SHCC material. It was noted that SRA reduces change in length caused by shrinkage at early age. SRA can also improve the tensile and flexural strengths and toughness of SHCC material used in this study.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.8 no.2
• /
• pp.23-30
• /
• 2008

UHPC has high performance, high strength and excellent mechanical properties. Moreover UHPC(Ultra High Performance Cementitious Composite) has advantage to reduce cross section under the same load compared with other kinds of concrete. But silica fume which is imported from foreign country has a abundant portion in UHPC mixture in comparison with normal concrete. This is one of the main reason to raise the construction cost. Superior mechanical properties of UHPC due to the optimum filling composition can be changed by replacing the very fine ingredient. The purpose of this research is to grasp the characteristic of UHPC which silica fume and silica flour is replaced with limestone powder. This experiment can be divided into three classes according to the kinds of replacement. The compressive strength and flow of all types were measured and microstructure and hydration phenomena for comparing RPC were analyzed by SEM, XRD, NMR method. As a result, the replacement can be considered to be effective by for the decrease of the UHPC structure construction cost and improvement of the fresh UHPC.

• Journal of the Korea Concrete Institute
• /
• v.19 no.1
• /
• pp.47-56
• /
• 2007

Recently, tunnels are increasingly constructed in this country with the increased construction of highways, high-speed railways and subways. Shotcrete is one of the major processes in the tunnel construction. Many problems, however, exist in the current shotcrete practice. The purpose of the study is, therefore, to explore the trobles in the current shotcreting practice, and to develop high-quality silica fume shotcrete. For the purpose of security a long-term durability of shotcrete, this study conducted combined deterioration tests. In this study, a combined deterioration test in consideration of a variety of deterioration factors were proceeded. Especially, micro-silica fume that was used frequently in overseas because of a outstanding strength-promotion effect was applied to combined deterioration test, and a long-term durability of shotcrete was investigated according to additions mixing. As a result of test, the shotcrete mixed Micro-silica fume showed a good deterioration quality compared with the other mixes. And is shows that the Micro-silica fume has an outstanding strength-promotion effect and is effective to secure a long-term durability of shotcrete by means of decreasing a deterioration caused by steel fiber mixed.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.5 no.1
• /
• pp.23-31
• /
• 2003

Since the mid of 1990, permanent shotcrete tunnel linings such as Single-shell and NMT have been constructed in many countries for reducing the construction time and lowing construction costs instead of conventional in-situ concrete linings. Among essential technologies for successful application of permanent shotcrete linings, high performance shotcrete having high strength, high durability and better pumpability has to be developed in advance as an integral component. This paper presents the idea and first experimental attempts to increase early strength and bond strength of wet-mixed Steel Fiber Reinforced Shotcrete (SFRS) in spring water condition. In order to increase early behavior of SFRS, a new approach using high-early strength cement with alkali-free liquid accelerator has been investigated. From the test results, wet-mix SFRS with high-early strength cement and alkali-free accelerator exhibited excellent early compressive strength improvement compared to the ordinary portland cement and good bond strength even under spring water condition.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.1
• /
• pp.25-32
• /
• 2021

For developing the durable eco-concrete, water-repellent and hydrophobic emulsion were prepared by stirring and mixing polymethyl hydrosiloxane and polyvinyl alcohol. After adding the PMHS emulsion cement paste, the hydration reaction characteristics and the change in chemical composition were analyzed through BSE and EDS analysis, and the micropores were evaluated by MIP test. Cement mixed with PMHS emulsion was analyzed to increase the hydration reactivity and to decrease the capillary porosity, but it was found that the capillary porosity varies depending on the degree of dispersion of the emulsion in the cement paste. In the case of the emulsion containing metakaolin, there was little difference in hydration degree and porosity from the case of using only the PMHS emulsion. However, when the cement surface was coated with PMHS emulsion, the contact angle was found to increase significantly compared to OPC, and it was analyzed that especially when PVA fiber was used together, it changed to a hypohydrophobic surface.

• International Journal of Highway Engineering
• /
• v.20 no.1
• /
• pp.87-95
• /
• 2018

PURPOSES : A geo-grid pavement, e.g., a stress-absorbing membrane interlayer (SAMI), can be applied to an asphalt-overlay method on the existing surface-pavement layer for pavement maintenance related to reflection cracking. Reflection cracking can occur when a crack in the existing surface layer influences the overlay pavement. It can reduce the pavement life cycle and adversely affect traffic safety. Moreover, a failed overlay can reduce the economic value. In this regard, the objective of this study is to evaluate the bonding properties between the rigid pavement and a SAMI by using the direct shear test and the pull-off test. The predicted fractural energy functions with the shear stress were determined from a numerical analysis of the moving average method and the polynomial regression method. METHODS : In this research, the shear and pull-off tests were performed to evaluate the properties of mixtures constructed using no interlayer, a tack-coat, and SAMI with fabric and without fabric. The lower mixture parts (describing the existing pavement) were mixed using the 25-40-8 joint cement-concrete standard. The overlay layer was constructed especially using polymer-modified stone mastic asphalt (SMA) pavement. It was composed of an SMA aggregate gradation and applied as the modified agent. The sixth polynomial regression equation and the general moving average method were utilized to estimate the interlayer shear strength. These numerical analysis methods were also used to determine the predictive models for estimating the fracture energy. RESULTS : From the direct shear test and the pull-off test results, the mixture bonded using the tack-coat (applied as the interlayer between the overlay layer and the jointed cement concrete) had the strongest shear resistance and bonding strength. In contrast, the SAMI pavement without fiber has a strong need for fractural energy at failure. CONCLUSIONS : The effects of site-reflection cracking can be determined using the same tests on cored specimens. Further, an empirical-mechanical finite-element method (FEM) must be done to understand the appropriate SAMI application. In this regard, the FEM application analy pavement-design analysis using thesis and bonding property tests using cored specimens from public roads will be conducted in further research.

• Journal of The Korean Society of Grassland and Forage Science
• /
• v.4 no.1
• /
• pp.41-60
• /
• 1983

Experiments were conducted to study the effect of stage of maturity at harvest on the quality of silage. Herbage samples taken from the barley plant, rye plant, wheat plant, oat plant, Orchardgrass, Italian ryegrass, a mixed grass sward of Orchardgrass and Italian ryegrass and corn plant at different stages of maturity and ensiled in order to evaluate the effect of maturity on the chemical composition and feeding value as well as digestibility using sheep. Forage material were ensiled in small concrete silo. 1. The dry matter yield per 10a increased with advancing the maturity. Yield of brarley plant was 404, 635 and 900 kg at heading, milk and milk dough stage, respectively. Rye plant yield was 279, 589, 708, 10,000, 1,265, 1,376 and 1,492 kg at booting, before heading, early heading, late heading, early flowering, late flowering and after flowering stage, respectively. Italian ryegrass yield was 355, 613, 844 and 1,109 kg at vegetative, booting, heading and flowering, respectively. Orchardgrass/Italian ryegrass production was 477, 696, 891 and 1,027 kg at before was 458, 1,252, 1,534, 1,986 and 2,053 kg at tassel, early milk, yellow ripe and ripe stage, respectively. 2. Dry matter content increased with advancing maturity, but crude protein declined markedly. The NFE content decreased with advancing maturity of all the herbages except corn plant where NFE content increased, but corn plant increased. The content of crude fiber increased with advancing maturity except corn plant. The content of crude ash decreased with advancing maturity. In the rye plant, the content of neutral detergent fiber (NDF), acid detergent fiber (ADF) and cellulose increased with advancing maturity. 3. In vitro dry matter digestibilities of the rye plant was 53.6, 54.1, 50.7, 47.1, 44.9, 40.1 and 38.9% booting, before hcading, early heading, late heading, early flowering, late flowering and after flowering stage, respectively. The regression equation was $Y=56.22-0.74X+0.009X^2$ (X=cutting date from the first cut, Y=dry matter digestibilities). 4. In vitro digestible dry matter yield (kg/10a) of rye plant increased with advancing maturity, but declined from the flowering stage. The regression equation was $Y=168.88+26.09X-0.41X^2$ (X=cutting date from the first cut). 5. In vitro digestibility of dry matter in the corn plant was 69.2, 71.5, 69.8 and 69.9% at tassel, early milk, milk and yellow ripe stage, respectively. 6. The digestibility of crude protein and crude fiber of all plants decreased with advancing matuity, but NFE of the barley and corn generally increased. 7. The TDN contents on the dry matter basis decreased, but those of barley and corn silage were not different. TDN content of barley was 57.8, 57.1 and 57.9% at heading, milk and milk dough stage, respectively. That of rye silage was 50.0, 27.2 and 43.7% at early flowering, after flowering and milk stage, respectively. Italian ryegrass silage was 67.9, 63.7, and 54.9% at before heading, early heading and after heading, respectively. In case of Orchardgrass silage the TDN was 54.8, 52.9 and 46.1% at after heading, after flowering and milk, respectively. Corn shows TDN value of 59.5, 62.8 and 61.6% at milk, yellow ripe and ripe, respectively. 8. The pH value increased slightly by advancing maturity. 9. the content of organic acid decreased by advancing maturity and also increasing the DM content.