• Korean Journal of Materials Research
• /
• v.31 no.2
• /
• pp.61-67
• /
• 2021

Fabrication of a ferromagnetic composite powder for the magnesium and BaFe12O19 system by mechanical alloying (MA) is investigated at room temperature. Mixtures of Mg and BaFe12O19 powders with a weight ratio of Mg:BaFe12O19 = 4:1, 3:2, 2:3 and 1:4 are used. Optimal MA conditions to obtain a ferromagnetic composite with fine microstructure are investigated by X-ray diffraction, differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM) measurement. It is found that Mg-BaFe12O19 composite powders in which BaFe12O19 is dispersed in Mg matrix are successfully produced by MA of BaFe12O19 with Mg for 80 min. for all compositions. Magnetization of Mg-BaFe12O19 composite powders gradually increases with increasing the amounts of BaFe12O19, whereas coercive force of MA powders gradually decreases due to the refinement of BaFe12O19 powders with MA time for all compositions. However, it can be seen that the coercivity of Mg-BaFe12O19 MA composite powders with a weight ratio of Mg:BaFe12O19=4:1 and 3:2 for MA 80 min. are still high, with values of 1260 Oe and 1320 Oe compared to that of Mg:BaFe12O19=1:4. This clearly suggests that the refinement of BaFe12O19 powders during MA process for Mg:BaFe12O19=4:1 and 3:2 tends to be suppressed due to ductile Mg powders.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.34 no.4
• /
• pp.125-130
• /
• 2024

Preparation of ferromagnetic powders for the mixture of hematite and pure Mg powders by ball milling has been investigated. Also, consolidation of the ball-milled powders was performed in a spark plasma sintering machine at 800-1,000℃. It is found that a ferromagnetic Fe-MgO composite powders are obtained by ball milling of hematite and pure Mg powders before 1 hour. The magnetization and coercivity of ball-milled samples change at the results of the solid state reaction of hematite by pure Mg during ball milling. The saturation magnetization of ball-milled samples increases with increasing ball milling time and reaches to a maximum value of 93.4 emu/g after 5 hours of ball milling. Shrinkage change after sintering of ball-milled sample for 5 hours was significant above 300℃ and gradually increased with increasing temperature up to 800℃. X-ray diffraction result shows that the average grain size of Fe in Fe-MgO bulk sample sintered at 900℃ is 50 nm. It can be also seen that the coercivity of bulk sample sintered at 900℃ is still high value of 90 Oe, indicating that the grain growth of magnetic Fe phase during sintering process tend to be suppressed.

• Journal of Powder Materials
• /
• v.8 no.3
• /
• pp.151-156
• /
• 2001

MgO based nanocomposite powder including ferromagnetic iron particle dispersions, which can be available for the magnetic and catalytic applications, was fabricated by the spray pyrolysis process using ultra-sonic atomizer and reduction processes. Liquid source was prepared from iron (Fe)-nitrate, as a source of Fe nano-dispersion, and magnesium (Mg)-nitrate, as a source of MgO materials, with pure water solvent. After the chamber were heated to given temperatures (500~$^800{\circ}C$), the mist of liquid droplets generated by ultrasonic atomizer carried into the chamber by a carrier gas of air, and the ist was decomposed into Fe-oxide and MgO nano-powder. The obtained powders were reduced by hydrogen atmosphere at 600~$^800{\circ}C$. The reduction behavior was investigated by thermal gravity and hygrometry. After reduction, the aggregated sub-micron Fe/MgO powders were obtained, and each aggregated powder composed of nano-sized Fe/MgO materials. By the difference of the chamber temperature, the particle size of Fe and MgO was changed in a few 10 nm levels. Also, the nano-porous Fe-MgO sub-micron powders were obtained. Through this preparation process and the evaluation of phase and microstructure, it was concluded that the Fe/MgO nanocomposite powders with high surface area and the higher coercive force were successfully fabricated.