• Journal of the Korean Society for Heat Treatment
• /
• v.25 no.3
• /
• pp.138-145
• /
• 2012

An ${\alpha}$-Ferrite (Fe) powder dispersed with 4 vol.% of $Al_2O_3$ was successfully produced by a simple miling at 210 K with a mixture of $Fe_2O_3$, Fe and Al ingredient powders, followed by 2 step high temperature consolidation: Hot Pressing (HP) at 1323 K and then Hot Isostatic Pressing at 1423 K. The microstructure of the consolidated material was characterized by standard metallographic techniques such as XRD (X-ray Diffraction), TEM and STEM-EDS. The results of STEM-EDS analysis showed that the HIPed materials comprised a mixture of pure Fe matrix with a grain size of ~20 nm and $Al_2O_3$ with a bimodal size distribution of extremely fine (~5 nm) and medium size dispersoids (~20 nm). The mechanical properties of the consolidated materials were characterized by compressive test and micro Vickers hardness test at room temperature. The results showed that the yield strength of the ODS (Oxide Dispersion Strengthened) Fe alloy are as much as $674{\pm}39$ MPa and the improvement of the yield strength is attributed to the presence of the fine $Al_2O_3$ dispersoid.

• Journal of the Korean Ceramic Society
• /
• v.16 no.3
• /
• pp.142-154
• /
• 1979

The effects of microstructures and some additives $(CoO and Al_2O_3$) on the magnetic properties such as initial permeability, $\mu$-T curve, coercive force, and magnetic induction of MnZn ferrites have been studied. The powder was prepared by Hot Petroleum Drying Method. The basic composition of MnZn ferrites was 25.5mole % MnO, 22.0 mole% ZnO, 52.5 mole% $Fe_2O_3$. CoO in a concentration range from 0.05 to 0.5 mole% and $Al_2O_3$ from 2.5 to 7.5 mole% were added. Sintered density increased up to 97.5% of theoretical density. Permeability increased as average grain size increased, and that coercive force decreased as average grian size increased. Magnetic induction increased as sintered density increased. The variation of initial permeability with temperature in a temperature range from 0$^{\circ}$ to $60^{\circ}C$ was lowered (a flatter $\mu-T$ curve) as sintering temperature decreased. The compensation temperature To ofmagnetocrystalline anisotropy constant K1 and initial permeability varied with the species and amount of additives. When 0.05 mole% CoO was added to the basic composition, initial permeability at $15^{\circ}C$ increased from 5200 to 5900. The variation ofinitial permeability with temperature in a temperature range from 0^{\circ}to $60^{\circ}C$ was smaller (a flatter $\mu$-T curve) than that of the basic composition of Mn Zn ferrites. When 2.5 mole% $Al_2O_3$ was added, initial permeability at $15^{\circ}C$ decreased from 5200 to 3000. But the variation of initial permeability with temperature in a temperature range from 0$^{\circ}$to $60^{\circ}C$ was smaller (a flat ter $\mu-T$ curve) than when 0.05 mole% CoO was added. Experimental results showed that the conditions necessary for the occurrence of a very high permeability and a flat $\mu$-T curve were controversial even in a temperature range from $0^{\circ}$to $60^{\circ}C$.

• Journal of Korea Foundry Society
• /
• v.29 no.6
• /
• pp.257-264
• /
• 2009

The effects of silicon and molybdenum on the temperature-dependent properties of high silicon and high molybdenum ductile cast iron were investigated. Microstructure was composed of ferrite, cell boundary complex carbide, carbide precipitated in the grain and graphite. The number and size of carbide decreased with the increase of silicon content and increased with the increase of molybdenum content, however, the size of cell boundary carbide increased above 0.81wt%Mo. The room temperature tensile strength increased with the increase of silicon and molybdenum contents. That did not increase with the latter with more than 0.8wt%. Meanwhile the high temperature tensile strength showed the similar trend to that of room temperature one, that of the specimen with 0.55wt%Mo was the highest. The $A_1$ transformation temperature increased with the silicon and molybdenum contents, and showed similar tendency with the variation of strength. It was discussed due to the solubility limit of Molybdenum in ferrite, of which value was assumed to be in the vicinity of 0.81wt%Mo. The weight after oxidation at 1,173K showed the result caused by the difference in solubility of molybdenum in the matrix. That and the thickness change after oxidation did not show any consistent trend with the silicon and molybdenum contents.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.263-266
• /
• 2009

Transformation induced plasticity (TRIP) steel consisting of ferrite, austenite, and bainite phases was regarded as an excellent candidate for automotive applications due to the good combination of ductility and strength. The aim of the present study was to understand the microstructural characteristics of ultrafine grained (UFG) TRIP low-carbon steel fabricated via equal channel angular pressing accompanied with intercritical- and isothermal-annealing treatments. When compared to coarse grained counterpart, only the volume fraction of austenite phase in UFG TRIP steel remained unchanged, but all other microstructural variables such as size and morphology were different. It was found that UFG TRIP steel showed the homogeneous distribution of each constituent phase, which was discussed in terms of annealing treatments done in this study.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.9 no.5
• /
• pp.564-571
• /
• 1985

The estimation of fracture toughness in inhomogeneous material is still insufficient because it is difficult to get information of fracture initiation at the crack tip. Therefore, martensite-ferrite dual phase steel was prepared for a model material and micro-fracture behavior was investigated in the region of pre-fatigue crack in order to understand the characteristic of fracture resistance in inhomogeneous materials. In the case of severely inhomogeneous state, micro-fracture appearance is not distributed homogenously so that the estimation of fracture toughness is hardly possible. On the other hand when the grain size is refined or the strength of martensite is lowered, micro-fracture appearance is distributed homogenously and fracture toughness remarkably increases.

• Journal of Welding and Joining
• /
• v.17 no.3
• /
• pp.50-54
• /
• 1999

Feasibility study of the application of a developed annealed austenitic stainless steel at cryogenic temperature has been performed for membrane tank of LNG ship. Chemical properties of developed stainless steel are compared with a domestic commercial stainless steel and a foreign stainless steel which are used for LNG ships. Tensile properties at cryogenic temperature and fatigue strength at room temperature are measured for but and lap joints which are TIG welded specimens. Developed stainless steel having a small amount of titanium component shows the finest grain size in the HAZ, compared with the other stainless steel studied. Tensile strength, elongation and fatigue strength of the developed stainless steel are equal to those of the foreign stainless steel studied and are higher than the domestic commercial stainless steel studied.

• Journal of the Korean Institute of Navigation
• /
• v.22 no.4
• /
• pp.69-75
• /
• 1998

The super wideband electromagnetic wave absorber in RF-A-PF type has been proposed, which can be used for an anechoic chamber, wall material to prevent TV ghost, etc, In this paper, $Ni_x-Mg_{0.1}-Zn_(1-x-0.1){\cdot}Fe_2O_4$ Ferrite Powder has been fabricated. Using this, then, [$Ni_x-Mg_{0.1}-Zn_(1-x-0.1){\cdot}Fe_2O_4$-Rubber composite for RF-layer in the RF-A-PF type absorber has been fabricated and its characteristics has been analyzed. As a result, it has been shown that the $Ni_x-Mg_{0.1}-Zn_(1-x-0.1){\cdot}Fe_2O_4$-Rubber composit with the quantity $_x$ of $Ni_x$ between 0.5 and 0.6 is suitable for the RF-layer in the case of which the grain size is sub-micrometer order.

• Journal of the Korean Society for Heat Treatment
• /
• v.3 no.2
• /
• pp.37-44
• /
• 1990

The effect of the microstructural change on the near threshold fatigue crack growth rate in SM40C steel has been studied using the ${\Delta}K$ decreasing method. Below the total strain amplitude of 0.56%, cyclic softening occured, whereas above this value cyclic hardening occurred in the pearlitic lamellar structure. However, in the spherodized structure the cyclic hardening solely occurred. The crack growth rate in the near-threshold region was decreased with increasing prior austenite grain size and this was due to surface roughness. The crack growth rate of the spherodized structure was lower than that of the pearlite lamellar structure and the ${\Delta}K_{th}$ of the former was higher than that of the latter. It was understood that the crack propagates preferentially through the ferrite phase. The intergranular facets in the near-threshold region appeared in the spherodized structure.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.824-827
• /
• 1995

Dielectromagnets are permanent magnets made from resin-bonded hard magnetic powders. Magnetic properties of dielectromagnets depend on kind of used hard magnetic materials as chemical compound, shape, size of grain and applied technology. Comparison of advantages and disadvantages of dielectromagnets made from different kind of magnetic powders induced us to try to prepare dielectromagnets from mixture of hard magnetic powders, not only one of them. The purpose of investigation on this kind of dielectromagnets is to find formula to prepare permanent magnets with properties adequate to different kind of electrical motors requirements. As hard magnetic materials we used powders of ferrite, melt-spun ribbon Nd-Fe-B and Alnico. Papers present results of investigation on technology of this kind of dielectromagnets. It shows also influence of kind of mixture and used technology on magnetic properties of dielectromagnets.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.6
• /
• pp.279-287
• /
• 2013

Oxide Dispersion Strengthened (ODS) Fe with $Al_2O_3$ dispersoid was successfully produced by reactive milling with a mixture of Fe, $Fe_3O_4$ (Magnetite), $Fe_2O_3$ (Hematite) and Al reactants at cryogenic temperature. The milled powders were consolidated by Vacuum Hot Press (HP) at 1323 K, and the consolidated materials were characterized by Transmission Electron Microscopy (TEM), Scanning Transmission Electron Microscopy (STEM), and Energy Dispersive Spectroscopy (EDS); the yield strength and the hardness of the consolidated materials were determined by compressive test and Vickers hardness test at room temperature. The grain size of the materials was estimated by X-ray Diffraction technique using the scherrer's formula. The TEM observations showed that the microstructure was comprised with a mixture of nanocrystalline Fe matrix and $Al_2O_3$ nano-dispersoids with a bimodal size distribution; the 0.2% off-set yield strength of the materials was as high as $758{\pm}29$ MPa and the Vickers hardness was $358{\pm}2$. The effect of the cryogenic milling and addition of extra Fe powder was discussed on the suppression of MSR (Mechanically induced Self-sustaining Reaction) for the desired microstructural evolution of ODS alloys.