A Study on the Fracture Resistance at the Crack Tip in Dual Phase Steel

복합조직강 의 균열선단 에서의 파괴저항 에 관한 연구

The estimation of fracture toughness in inhomogeneous material is still insufficient because it is difficult to get information of fracture initiation at the crack tip. Therefore, martensite-ferrite dual phase steel was prepared for a model material and micro-fracture behavior was investigated in the region of pre-fatigue crack in order to understand the characteristic of fracture resistance in inhomogeneous materials. In the case of severely inhomogeneous state, micro-fracture appearance is not distributed homogenously so that the estimation of fracture toughness is hardly possible. On the other hand when the grain size is refined or the strength of martensite is lowered, micro-fracture appearance is distributed homogenously and fracture toughness remarkably increases.

본 논문에서는 미시조직인자를 변화시킨 마르텐사이트-페라이트 복합조직강을 준비하여 균열선단 및 안정영역의 파괴양상과 파괴저항과의 관계를 검토하였다.