Ni-15at.% W coatings with film thicknesses of 20-40 ㎛ were electroplated on a steel substrate, and their oxidation behavior was investigated at 700 and 800℃ in air. For comparison, a pure Ni coating and a bulk Ni were also oxidized. The Ni-15at.%W coating displayed the worst oxidation resistance, due to the formation of less-protective NiO, Fe₂O₃, NiFe₂O₄ and NiWO₄. The corrosion behavior Ni-15at.%W coatings electroplated on a steel substrate was similarly investigated at 700 and 800℃ in the Ar-l%SO₂ atmosphere. For comparison, the uncoated steel substrate was also corrosion-tested in the Ar-l %SO₂ atmosphere. Severe scale spallation and the internal corrosion of the steel that occurred in the uncoated substrate were not observed in the coated specimen. However, it seemed that the Ni-15at.%W coating cannot be a potential candidate as a sulfidation-resistant coating, due to the formation of less-protective NiO, NiS, WO₃ and NiWO₄.

• 한국세라믹학회지
• /
• 제33권12호
• /
• pp.1421-1425
• /
• 1996

Sintered Si3N4 and Inconel composed of Ni(58-63%) Cr(21-25%) Al(1-17%) Mn(<1%) fe(balance) were pressurelessly joined by using Ag-Cu-Ti brazing filler metal at 950℃ and 1200℃ under N2 gas atmosphere of 1atm and their interfacial structures were investigated. In case that the reaction temperature was low as 950℃ its interfacial structure was "Inconel metal/Ti-rich phase layer/brazing filler metal layer/Si3N4 " Ti used as reactive metal existed in between inconel steel and brazing metal and moved to the interface of between brazing filler metal nd Si3N4 according as reaction temperature increased up to 1200℃. The interfacial structure of inconel steel-Si3N4 reacted at 1200℃ was ' inconel metal/Ni-rich phase layer containing of Fe. Cr and Si/Cu-rich phase layer containing of Mn and Si/Si3N4 " Cr Mn, Ni and Fe diffused to the interface of between brazing filler metal and Si3N4 and reacted with Si3N4 The most reactive components of ingredients of inconel metal were Cr and Mn. On the other hand Ti added as reactive components to Ag-Cu eutectic segregated into Ni-rich phase layer,.

• 한국표면공학회지
• /
• 제30권4호
• /
• pp.248-254
• /
• 1997

The sulfidation behavior of a sputter-deposited amorphous coating of 69.0%Nb-16.9Ni-11.9%Al-2.2%Si (at.%) has been investigated as a funtion of temperature.(973-1173K) in pure sulfur pressure of 0.01atm. The sulfidation kinetics of the casting obyed the parabolic rate low over the whole temperature ranges studied. The stlfidation rate increased with the temperature, as expected. The sulfide scale, the composition of which was $Al_2S_3,\;NbS_2,\;Ni_{3-x}S_2\;and\;FeCrS_4$, formed on the amorphous coating was primarily bilayered. Both the outer fastgrowing non-protective 4Al_2S_3$scale and the inner slowly-growing protective $NbS_2$,/TEX> scale and the inner slowly-growing protective $NbS_2$ scale had some Fe and Cr dissolution, which evidently came from the base substrate alloy of stainless steel type 304. Belows the coating, Kirkendall void formation was noticed. Nevertheless, a dramatic improvement of sulfidation resistance was achieved by sputter-depositing Nb-2 Ni-Al-Si layer on the stainless steel 304.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1998년도 하계학술대회 논문집 D
• /
• pp.1555-1557
• /
• 1998

In order to investigate the core material for over-head transmission line with non-magnetic and high strength nitrogen steel, microstructure and several basic properties of Fe-Mn-Cr-Ni-N steel have been studied. It is necessary that core material have a $\gamma$ phase to have a non-magnetic characteristics. To acquire a $\gamma$ phase, Mn, Ni and C are added as a alloying element. It was found that Fe-25Mn-16Cr-1Ni-N alloy have a stable $\gamma$ phase. The precipitate from this alloy system was $(Cr, Fe)_7C_3$. High Mn and N steel satisfies Sievert's relation that solubility of nitrogen increases with the square root of partial pressure of gas in metal-gas system and the hardness have proportional relation with nitrogen concentration.

• 한국표면공학회지
• /
• 제49권6호
• /
• pp.587-594
• /
• 2016

Various surface treatments and thin film coating processes on the surface of injection die steel have been developed to extend the life. Most of previous studies were mainly focused on investigating the wear and static bonding behavior of thin films. In this study complex surface treatments of DLC coating combined with ion nitriding were applied to increase fatigue life and wear resistance. Ion nitriding, DLC coating, and DLC coating following nitriding on the surface of Fe-3.0Ni-0.7Cr-1.4Mn-X steel were investigated to uncover the beneficial effect which is applicable to injection die. The effect of various surface treatments and coating conditions on high cycle fatigue resistance was studied. Surface morphology change during fatigue tests were observed with AFM. Fatigue life of the die steel increased by 10 to 1,000 times at the various level of stress amplitudes in the condition of DLC coating following the ion nitriding for 3 hrs comparing with the only DLC coated condition.

• 한국레이저가공학회:학술대회논문집
• /
• 한국레이저가공학회 2002년도 춘계학술발표대회 논문개요집
• /
• pp.65-70
• /
• 2002

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1993년도 추계학술강연 및 발표대회강연 및 발표논문 초록집
• /
• pp.48-48
• /
• 1993

• Nuclear Engineering and Technology
• /
• 제55권3호
• /
• pp.902-907
• /
• 2023

To understand the eutectic reaction mechanism and the relocation behavior of the core debris is indispensable for the safety assessment of core disruptive accidents (CDAs) in sodium-cooled fast reactors (SFRs). This paper addresses reaction products and their distribution of the eutectic melting/solidifying reaction of boron carbide (B₄C) and stainless-steel (SS). The influence of the existence of carbon on the B₄C-SS eutectic reaction was investigated by comparing the iron boride (FeB)-SS reaction by Raman spectroscopy with Multivariate Curve Resolution (MCR) analysis. The scanning electron microscopy with dispersive X-ray spectrometer was also used to investigate the elemental information of the pure metals such as Cr, Ni, and Fe. In the B₄C-SS samples, a new layer was formed between B₄C/SS interface, and the layer was confirmed that the formed layer corresponded to amorphous carbon (graphite) or FeB or Fe₂B. In contrast, a new layer was not clearly formed between FeB and SS interface in the FeB-SS samples. All samples observed the Cr-rich domain and Fe and Ni-rich domain after the reaction. These domains might be formed during the solidifying process.

• 열처리공학회지
• /
• 제12권1호
• /
• pp.55-65
• /
• 1999

Graphitization of cementite in high carbon steels at subcritical temperature is reported. We have studied about the effects of Ni in these steels on graphitization. The chemical compositions of the specimens were Fe-(0.54, 0.7)%-C-1.0%Si-0.1%Mn-(0.2~1.0)%Ni. After annealing at $650^{\circ}C$, $680^{\circ}C$ and $700^{\circ}C$ during various time the microstructures and hardness change were observed. In order to recover the initial hardness of high carbon steel, dissolution treatment of graphite was performed at $870^{\circ}C$. In case of 0.7%C steel, graphitization was accelerated rather 1.0%Ni addition steel than 0.2% and 0.54%Ni addition steels but the graphite is coarser. In case of 0.54%C-0.2%Ni steel, graphite particles were distributed relatively homogeniously and finely. Nickel addition promotes graphitization of these steels but makes graphite blocky.

• 한국주조공학회지
• /
• 제25권6호
• /
• pp.259-264
• /
• 2005

The copper clad steel wire is used extensively as lead wires of electronic components such as capacitors, diodes and glass sealing lamp because the wire combines the strength and low thermal expansion characteristic of Fe-Ni steel with the conductivity and corrosion resistance of copper. In order to fabricate the copper clad steel wire, several processes including electro-plating, tubecladding extrusion process and dip forming process have been introduced and applied. The electroplating process for the production of copper clad steel wire shows poor productivity and induces environmental load generation such as electroplating solution. The dip forming process is suitable to mass production of copper clad steel such as trolley wire. and need expensive manufacturing facilities. The present paper describes the improvement of the conventional continuous casting process to fabricate copper clad steel wire, which its core metal is low thermal expansion Fe-Ni alloy and its sheath material is copper. In particular, the formation of intermetallic compound at interface between core and sheath was investigated in order to introduce optimum continuous casting process parameter for fabrication of copper clad steel wire with higher electrical conductivity. The mechanical strength of copper clad steel wire was also investigated through wiredrawing process with of 95% in total reduction ratio.