• Journal of Powder Materials
• /
• v.30 no.6
• /
• pp.470-477
• /
• 2023

The effects of annealing on the microstructure and mechanical properties of Al-Zn-Mg-Cu-Si alloys fabricated by high-energy ball milling (HEBM) and spark plasma sintering (SPS) were investigated. The HEBM-free sintered alloy primarily contained Mg₂Si, Q-AlCuMgSi, and Si phases. Meanwhile, the HEBM-sintered alloy contains Mg-free Si and θ-Al₂Cu phases due to the formation of MgO, which causes Mg depletion in the Al matrix. Annealing without and with HEBM at 500℃ causes partial dissolution and coarsening of the Q-AlCuMgSi and Mg₂Si phases in the alloy and dissolution of the θ-Al₂Cu phase in the alloy, respectively. In both alloys, a thermally stable α-AlFeSi phase was formed after long-term heat treatment. The grain size of the sintered alloys with and without HEBM increased from 0.5 to 1.0 ㎛ and from 2.9 to 6.3 ㎛, respectively. The hardness of the sintered alloy increases after annealing for 1 h but decreases significantly after 24 h of annealing. Extending the annealing time to 168 h improved the hardness of the alloy without HEBM but had little effect on the alloy with HEBM. The relationship between the microstructural factors and the hardness of the sintered and annealed alloys is discussed.

• Archives of Metallurgy and Materials
• /
• v.64 no.2
• /
• pp.539-542
• /
• 2019

Pre-alloyed Astaloy CrL^TM (Fe-1.5 wt% Cr-0.2 wt% Mo), a commercial Fe-based alloy powder for high strength powder metallurgy products, was sintered and hot forged with additions of 0.5 wt% C and 0~2 wt% Cu. To investigate the influence of various Cu contents, the microstructural evolution was characterized using density measurements, scanning electron microscope (SEM) and electron backscatter diffraction (EBSD). Transverse rupture strength (TRS) was measured for each composition and processing stage. The correlation between Cu additions and properties of sinter-forged Fe-Cr-Mo-C alloy was discussed in detail.

• Journal of Powder Materials
• /
• v.26 no.2
• /
• pp.112-118
• /
• 2019

Infiltration is a popular technique used to produce valve seat rings and guides to create dense parts. In order to develop valve seat material with a good thermal conductivity and thermal expansion coefficient, Cu-infiltrated properties of sintered Fe-Co-M(M=Mo,Cr) alloy systems are studied. It is shown that the copper network that forms inside the steel alloy skeleton during infiltration enhances the thermal conductivity and thermal expansion coefficient of the steel alloy composite. The hard phase of the CoMoCr and the network precipitated FeCrC phase are distributed homogeneously as the infiltrated Cu phase increases. The increase in hardness of the alloy composite due to the increase of the Co, Ni, Cr, and Cu contents in Fe matrix by the infiltrated Cu amount increases. Using infiltration, the thermal conductivity and thermal expansion coefficient were increased to 29.5 W/mK and $15.9um/m^{\circ}C$, respectively, for tempered alloy composite.

• Archives of Metallurgy and Materials
• /
• v.64 no.2
• /
• pp.613-616
• /
• 2019

The objective of the present research is to develop the novel multi-compaction technology to produce hybrid structure in powder metallurgy (P/M) components using dissimilar Fe-based alloys. Two distinct powder alloys with different compositions were are used in this study: Fe-Cr-Mo-C pre-alloyed powder for high strength and Fe-Cu-C mixed powder for enhanced machinability and lower material cost. Initially, Fe-Cu-C was pre-compacted using a bar-shaped die with lower compaction pressure. The green compact of Fe-Cu-C alloy was inserted into a die residing a half of the die, and another half of the die was filled with the Fe-Cr-Mo-C powder. Then they subsequently underwent re-compaction with higher pressure. The final compact was sintered at 1120℃ for 60 min. In order to determine the mechanical behavior, transverse rupture strength (TRS) and Vickers hardness of sintered materials were measured and correlated with density variations. The microstructure was characterized using optical microscope and scanning electron microscope to investigate the interfacial characteristics between dissimilar P/M alloys.

• Journal of Powder Materials
• /
• v.24 no.4
• /
• pp.302-307
• /
• 2017

In this study, Fe-Cu-C alloy is sintered by spark plasma sintering (SPS). The sintering conditions are 60 MPa pressure with heating rates of 30, 60 and $9^{\circ}C/min$ to determine the influence of heating rate on the mechanical and microstructure properties of the sintered alloys. The microstructure and mechanical properties of the sintered Fe-Cu-C alloy is investigated by X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM). The temperature of shrinkage displacement is changed at $450^{\circ}C$ with heating rates 30, 60, and $90^{\circ}C/min$. The temperature of the shrinkage displacement is finished at $650^{\circ}C$ when heating rate $30^{\circ}C/min$, at $700^{\circ}C$ when heating rate $60^{\circ}C/min$ and at $800^{\circ}C$ when heating rate $90^{\circ}C/min$. For the sintered alloy at heating rates of 30, 60, and $90^{\circ}C/min$, the apparent porosity is calculated to be 3.7%, 5.2%, and 7.7%, respectively. The hardness of the sintered alloys is investigated using Rockwell hardness measurements. The objective of this study is to investigate the densification behavior, porosity, and mechanical properties of the sintered Fe-Cu-C alloys depending on the heating rate.

• Journal of Powder Materials
• /
• v.23 no.3
• /
• pp.207-212
• /
• 2016

In this study, Fe-Cu-Ni-Mo-C low alloy steel powder is consolidated by spark plasma sintering (SPS) process. The internal structure and the surface fracture behavior are studied using field-emission scanning electron microscopy and optical microscopy techniques. The bulk samples are polished and etched in order to observe the internal structure. The sample sintered at $900^{\circ}C$ with holding time of 10 minutes achieves nearly full density of 98.9% while the density of the as-received conventionally sintered product is 90.3%. The fracture microstructures indicate that the sample prepared at $900^{\circ}C$ by the SPS process is hard to break out because of the presence of both grain boundaries and internal particle fractures. Moreover, the lamellar pearlite structure is also observed in this sample. The samples sintered at 1000 and $1100^{\circ}C$ exhibit a large number of tiny particles and pores due to the melting of Cu and aggregation of the alloy elements during the SPS process. The highest hardness value of 296.52 HV is observed for the sample sintered at $900^{\circ}C$ with holding time of 10 minutes.

• Journal of Powder Materials
• /
• v.19 no.4
• /
• pp.247-252
• /
• 2012

Effect of Cu and $DyF_3$ powder mixing with Cu-free (Nd, Dy)-Fe-B jet-milled powder on the magnetic properties of sintered magnets was investigated. The coercivity of a magnet prepared from the Cu-free (Nd, Dy)-Fe-B powder was about 10 kOe even though the alloy powder already contained some Dy (3.5 wt%). When small copper powder was blended, however, the coercivity of the magnet increased almost 100%, exhibiting about 20 kOe. On the contrary, the coercivity enhancement was moderate, about 4 kOe, when dysprosium content in the sintered magnet was simply increased to 4.9 wt% by the addition of small $DyF_3$3 powder.

• Journal of Powder Materials
• /
• v.27 no.1
• /
• pp.31-36
• /
• 2020

Phosphorus is an element that plays many important roles in powder metallurgy as an alloy element. The purpose of this study is to investigate the influence of phosphorus addition on the microstructures and mechanical properties of sintered low-alloy steel. The sintered low-alloy steels Fe-0.6%C-3.89%Ni-1.95%Cu-1.40%Mo-xP (x=0, 0.05, 0.10, 0.15, 0.20%) were manufactured by compacting at 700 MPa, sintering in H₂-N₂ at 1260 ℃, rapid cooling, and low-temperature tempering in Ar at 160 ℃. The microstructure, pore, density, hardness, and transverse rupture strength (TRS) of the sintered low-alloy steels were evaluated. The hardness increased as the phosphorus content increased, whereas the density and TRS showed maximum values when the content of P was 0.05%. Based on microstructure observation, the phase of the microstructure changed from bainite to martensite as the content of phosphorus is increased. Hence, the most appropriate addition of phosphorus in this study was 0.05%.

• Korean Journal of Materials Research
• /
• v.8 no.9
• /
• pp.819-824
• /
• 1998

The influence of casting cooling rate during the preparation of ingots on the grain size distribution and the magnetizing ability of $\textrm{Nd}_{16}\textrm{Fe}_{72}\textrm{V}_{4}\textrm{B}_{8}$ sintered magnets were investigated. Sintered magnets prepared from copper mold which allow a higher cooling rate, show a smaller grain size distribution and god magnetizing ability. The effects of adding bride forming elements, such as Cr, Mn, Nb, and W on the magnetic properties of Nd-Fe-B sintered magnets were also investigated. Both Cr and W addition increase coercivity and the resultant $\textrm{Nd}_{16}\textrm{Fe}_{72}\textrm{Cr}_{4}\textrm{B}_{9}$ alloy exhibits a similar magnetizing ability in comparison with $\textrm{Nd}_{16}\textrm{Fe}_{72}\textrm{V}_{4}\textrm{B}_{8}$ alloy.

• Journal of Powder Materials
• /
• v.1 no.1
• /
• pp.60-65
• /
• 1994

When a commercial prealloyed Fe-powder(Fe-5Cr-lMo-2Cu-0.5P-3C) is liquid phase sintered at 116$0^{\circ}C$, liquid precipitates with various shapes form within solid grains during the initial stage of sintering. The shape of a liquid precipitate changes pith the increment of their size from sphere(with radius<0.3$\mu\textrm{m}$), a transient polyhedron with more than 7 faces(1~2 $\mu\textrm{m}$), cuboid(3~5 $\mu\textrm{m}$), and finally to sphere(>5 $\mu\textrm{m}$). The shapes of liquid precipitates closely resemble the growth shapes predicted on the basis of solid-liquid interfacial energy and the coherency strain energy with anisotropic elastic constants in the diffusion zone around the precipitates.