• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 춘계학술대회 논문집
• /
• pp.491-492
• /
• 2008

The effect of B on the hot ductility of Fe-29Ni-17Co Kovar alloy and the mechanism of high temperature deformation behavior were investigated. Hot-tensile test was carried out at the temperature range of $900^{\circ}C-1200^{\circ}C$. Optical microscopy and scanning electron microscopy were used to investigate the microstructure and fracture during hot deformation. The hot ductility of Kovar alloy was drastically increased with the addition of Boron. The improvement of hot ductility results from the grain boundary migration mainly due to the dynamic recrystallization at lower temperature range($900^{\circ}C$).

• 한국재료학회지
• /
• 제24권9호
• /
• pp.481-487
• /
• 2014

The effect of alpha phase on the fatigue properties of Fe-29%Ni-17%Co low thermal expansion alloy was investigated. Two kinds of alloys (Base alloy and Alpha alloy) were prepared by controlling the minimal alloy composition. Microstructure observation, tensile, high-cycle fatigue, and low-cycle fatigue results were measured in this study. The Base alloy microstructure showed typical austenite ${\gamma}$ phase. Alpha alloy represented the dispersed phase in the austenite ${\gamma}$ matrix. As a result of tensile testing, Alpha alloy was found to have higher strengths (Y.S. & T.S.) and lower elongation compared to those of the Base alloy. High cycle fatigue results showed that Alpha alloy had a higher fatigue limit (360MPa) than that (330MPa) of the Base alloy. The Alpha alloy exhibited the superior high cycle fatigue property in all of the fatigue stress conditions. SEM fractography results showed that the alpha phase could act to effectively retard both fatigue crack initiation and crack propagation. In the case of low-cycle fatigue, the Base alloy had longer fatigue life in the high plastic strain amplitude region and the Alpha alloy showed better fatigue property only in the low plastic strain amplitude region. The fatigue deformation behavior of the Fe-29%Ni-17%Co alloy was also discussed as related with its microstructure.

• 한국주조공학회지
• /
• 제22권4호
• /
• pp.160-166
• /
• 2002

The structure and properties of Fe-29Ni-17Co alloy which had been melted using induction furnace in air atmosphere and than electroslag-remelted were investigated. The oxygen content was reduced to 0.03% when the ingot was refined from $0.09{\sim}0.12%$ of that air melted. The amounts of spheroidal oxides inclusions and gas porosities of ingot were markedly reduced by the ESR process. CTE of ESR ingot contained small amount of oxides and porosities was found to be lower than that of AIM ingot, and tensile properties of ESR ingot and plate were found to be superior than that of AIM ingot and plate.

• 열처리공학회지
• /
• 제18권3호
• /
• pp.177-182
• /
• 2005

The steady state cyclic mechanism, and the behaviour of Nicoseal(Fe-29Ni-17Co) have been examined under the condition of square wave stress cyclic tension creep test at the temperature, stress and frequency range of $430{\sim}470^{\circ}C$($0.41{\sim}0.43T_m$), 353~383 MPa, and 3 cpm, respectively. Also, the relationship between cyclic creep and static creep have been examined. The stress exponents(n) for the static creep deformation of this alloy were 11.6, 10.0, 8.4 and 7.9 at the temperature of 430, 445, 460 and $470^{\circ}C$, respectively. The apparent activation energies (Q) for the static creep deformation were 54.2, 51.8, 49.7 and 46.8 kcal/mole for the stress of 353, 363, 373 and 383 MPa, From the above results, it could be considered that the cyclic creep accelaration phenomena was obtained and that the cyclic deformation for Nicoseal seemed to be controlled by dislocation climb over the range of experimental conditions. Nicoseal alloy under the cyclic creep conditions was obtained as P=(T+460)(logt+17). The failure plane observed by SEM showed up transgranular fracture at all range.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 춘계학술대회 논문집
• /
• pp.355-356
• /
• 2009

The change of thermal expansion and mechanical behaviors by cold working has been investigated in Fe-29%Ni-17%Co low thermal expansion Kovar alloy. Fe-29%Ni-17%Co alloy was cold rolled gradually and prepared to plates having reduction ratio of 0%, 20%, 40%, 60%, and 80%. Annealing effect on the properties was also studied. Thermal expansion was measured from $25^{\circ}C$ to $600^{\circ}C$ with a heating rate of $5^{\circ}C$/min by using vacuum differential dilatometer. It was found that thermal expansion coefficient ($\alpha_{30{\sim}400}$) slightly decreased (reduction ration of 20%) and then remarkably increased (above reduction ration of 40%) with increasing reduction ratio of cold rolling. Thermal expansion coefficient ($\alpha_{30{\sim}400}$) was sharply decreased after annealing heat-treatment. Yield and tensile strengths were continuously increased and elongation was decreased by cold roiling. Microstructural observation and X-ray diffraction analysis results showed that the $\alpha$ phase significantly increased as the reduction ratio increased. The slight decrease of thermal expansion coefficient bellow reduction ration of 20% could be explained by the destroying short-range ordering and the decreasing of grain size. The significant increase of thermal expansion coefficient with cold rolling mainly attributed to the appearance of $\alpha$ phase. The correlation between the microstructural cause and invar phenomena for the low thermal expansion behavior was also discussed.

• 소성∙가공
• /
• 제17권4호
• /
• pp.240-248
• /
• 2008

The effect of alloying elements(Mn, S, Mo, B) on the high temperature deformation behavior of Fe-29%Ni-17%Co (Kovar) alloy were investigated. And the effect of high temperature oxidation on the hot ductility was also studied. The hot ductility of Kovar alloy was drastically increased with the addition of Mn and lowering of S content. It has been found that the brittle intergranular fracture at high temperature cracking is closely associated with the FeS sulfide along the grain boundary. When Mn was added, the type of sulfide was changed to MnS from FeS and ductile intergranular fracture and transgranular fracture were promoted. The formation of oxide layer was found to have minimized the hot ductility of the Kovar alloy significantly. Grain boundary micro-cracks in the internal oxide region were noted following deformation due to high temperature, one of which acting as a notch that caused the poor hot workability of the oxidized specimen. The addition of Mo to the Kovar alloy could also retard the decrease in the hot ductility of the oxidized specimen through the prevention of notching due to internal oxidation. Hot ductility was remarkably improved by the addition of Boron. The improvement of hot ductility results from the grain boundary migration mainly due to the dynamic recrystallization at lower temperature range ($900{\sim}1000^{\circ}C$).

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2004년도 춘계학술대회 논문집
• /
• pp.129-135
• /
• 2004

This study was to evaluate the effect of carbon content on metallic change and fatigue characteristics with Fe-29% Ni-17% Co, low heat expansion alloy, widely using electronic components, precision machines, and sealing with glass and metal etc. The steels were fabricated with variation of carbon content, 0, 0.03, 0.06, 0.1, and 0.20% with VIM and tensile test and fatigue test were performed to achieve the above purpose. The more carbon content, the higher hardness value and yield strength. But elongation of 0.03%C, 0.06%C, and 0.10%C specimen decreased about 2.2%, 1.5% and 0.8% respectively mote than that of the base metal. Especially the strength and elongation of 0.20%C specimen increased simultaneously about 14.4% and 7.5%. Fatigue life of 0.03%C specimen decreased but the more carbon content, the higher fatigue life over 0.06% carbon content more than that of base metal.

• 한국공작기계학회논문집
• /
• 제15권5호
• /
• pp.7-13
• /
• 2006

This study was to evaluate the effect of carbon content on metallic change and fatigue characteristics with Fe-29%Ni-17%Co, low heat expansion alloy, widely using electronic components, precision machines, and sealing with glass and metal etc. The steels were fabricated with variation of carbon content, 0, 0.03, 0.06, 0.1, and 0.20% with VIM and tensile test and fatigue test were performed to achieve the above purpose. The more carbon content, the higher hardness value and yield strength. But elongation of 0.03%C, 0.06%C, and 0.10%C specimen decreased about 2.2%, 1.5% and 0.8% respectively more than that of the base metal. Especially the strength and elongation of 0.20%C specimen increased simultaneously about 14.4% and 7.5%. Fatigue life of 0.03%C specimen decreased but the more carbon content, the higher fatigue life over 0.06% carbon content more than that of base metal.

• 한국세라믹학회지
• /
• 제49권2호
• /
• pp.167-172
• /
• 2012

Fine diamond powders are synthesized with a 420 ${\phi}$ cubic press and stack-cell composed of Kovar ($Fe_{54}Ni_{29}Co_{17}$) (or Kovar+7 ${\mu}m$-thick Zn electroplated) alloy and graphite disks. The high pressure high temperature (HPHT) process condition was executed at $1500^{\circ}C$ for 280 seconds by varying the nominal pressure of 5.7~10.6 GPa. The density of formation, size, shape, and phase of diamonds are determined by optical microscopy, field emission scanning electron microscopy, thermal gravimetric analysis-differential thermal ammnlysis (TGA-DTA), X-ray diffraction (XRD), and micro-Raman spectroscopy. Through the microscopy analyses, we found that 1.5 ${\mu}m$ super-fine tetrahedral diamonds were synthesized for Zn coated Kovar cell with whole range of pressure while ~3 ${\mu}m$ super-fine diamond for conventional Kovar cell with < 10.6 GPa. Based on $750^{\circ}C$ exothermic reaction of diamonds in TGA-DTA, and characteristic peaks of the diamonds in XRD and micro-Raman analysis, we could confirm that the diamonds were successfully formed with the whole pressure range in this research. Finally, we propose a new process for super-fine diamonds by lowering the pressure condition and employing Zn electroplated Kovar disks.