• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2002년도 춘계학술강연 및 발표대회
• /
• pp.9-9
• /
• 2002

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 1997년도 Proceedings of the 12th KACG Technical Meeting and the 4th Korea-Japan EMGS (Electronic Materials Growth Symposium)
• /
• pp.79-85
• /
• 1997

Fe$_2$O$_3$ thin films were prepared on $Al_2$O$_3$ substrate by PECVD(Plasma-Enhanced Chemical Vapor Deposition) process. The phase transformation of iron oxide film was determined as the substrate temperature and reduction-oxidation process. $\alpha$-Fe$_2$O$_3$ was stable in deposition temperature ranges of 80~15$0^{\circ}C$. Fe$_3$O$_4$ phase was obtained by the reduction process of $\alpha$-Fe$_2$O$_3$ phase in H$_2$ ambient. Fe$_3$O$_4$ phase was transformed into a ${\gamma}$-Fe$_2$O$_3$ thin film under controlled oxidation conditions at 280~30$0^{\circ}C$.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.112-113
• /
• 2013

Thin CrAlMgSiN films, whose composition were 30.6Cr-11.1Al-7.3Mg-1.2Si-49.8N (at.%), were deposited on steel substrates in a cathodic arc plasma deposition system. They consisted of alternating crystalline Cr-N and AlMgSiN nanolayers. After oxidation at $800^{\circ}C$ for 200 h in air, a thin oxide layer formed by outward diffusion of Cr, Mg, Al, Fe, and N, and inward diffusion of O ions. Silicon ions were relatively immobile at $800^{\circ}C$. After oxidation at $900^{\circ}C$ for 10 h in air, a thin $Cr_2O_3$ layer containing dissolved ions of Al, Mg, Si, and Fe formed. Silicon ions became mobile at $900^{\circ}C$. After oxidation at $900^{\circ}C$ for 50 h in air, a thin $SiO_2-rich$ layer formed underneath the thin $Cr_2O_3$ layer. The film displayed good oxidation resistance. The main factor that decreased the oxidation resistance of the film was the outward diffusion and subsequent oxidation of Fe at the sample surface, particularly along the coated sample edge.

• 공업화학
• /
• 제21권3호
• /
• pp.333-336
• /
• 2010

합성가스에서 경질 올레핀을 합성하는 Fishcer-Tropsh 반응을 위하여 다양한 조성을 가지는 구형 철-알루미늄 촉매를 졸-겔 오일법으로 합성하였다. 합성된 구형 촉매를 이용하여 다양한 특성분석 및 반응성능을 측정하였다. 촉매의 비표 면적은 철의 비율이 증가할수록 감소하였고, CO 전환율은 Al/Fe비가 1.5인 촉매가 가장 우수하였다. 올레핀 선택도는 Al/Fe비에 영향을 받지 않았다. 함침법을 이용하여 K를 첨가한 경우 반응특성에 영향을 주었다. 첨가한 K의 농도가 증가할수록 초기 CO 전환율과 올레핀 선택도는 향상됐지만 촉매의 활성도는 급격히 감소하였다.

• 한국결정성장학회지
• /
• 제13권6호
• /
• pp.304-308
• /
• 2003

분리기 내 압력 조절을 통하여 압력 변화가 세라믹 입자 $Al_2O_3$, $Fe_2O_3$ 분급에 미치는 영향을 수치 해석적으로 분석하였다. 입자 분급 해석을 위해 3차원 Lagrangian approach를 이용하였으며, 이를 통해 입자의 분리기 내 거동 경로를 추적하여 각 압력에 따른 분리 가능한 최소 입자 크기(cut-diameter)와 분리율(separation rate)를 계산하였다. 압력 감소는 입자를 운반하는 아르곤 가스의 밀도를 감소시키면서, 분리기 내부 압력 손실을 줄이는 원인이 되었다. 이로 인해 상압에서 분리기 압력이 저압 상태로 변함에 따라, 더 미세한(수 $\mu\textrm{m}$) 입자가 분리 가능함이 예측되었다. 특히 50 torr의 저압 하에서 계산된 세라믹 입자의 분급 양상을 분석하면,$Al_2O_3$ 입자는 4 $\mu\textrm{m}$, $Fe_2O_3$경우는 3$\mu\textrm{m}$ 크기의 입자 분리가 가능하였다.

• 한국광물학회지
• /
• 제17권4호
• /
• pp.357-364
• /
• 2004

동양활석광상에서 산출되는 백운석기원 활석(활석 I)과 투각섬석기원 활석(활석 II)의 차이를 밝히기 위해 광물조성을 연구하였다. 활석 II의 철과 알루미늄 평균 함량이 각각 2.18 wt%와 0.31 wt%이고, 활석 각각 1.48 wt%와 0.08 wt%로서 전자의 경우가 높다. 활석 I보다 활석 II에서 Mg/(Mg+Fe+Mn)비가 일정한 값으로 꾸준히 낮고, 마찬가지로 Al 함량이 높은 것은 이들의 근원물질인 투각섬석과 백운석의 조성의 차이에서 기인된 것으로 보인다. 활석 II에서의 Al과 Fe가 투각섬석 경우보다 부화된 것은 변질작용 중에 이들 원소의 불유동성과 열수용액의 급격한 확산에 기인된 것으로 해석되며, 후자의 경우 활석 ll의 불완전성장과 함께 순간적인 성핵을 촉진시키게 된다. 광석 중에 투각섬석기원 활석의 양이 증가하면 투각섬석 자체의 함량과 Al과 Fe 등의 불순물 증가로 인해 광석의 품위는 저하된다.

• 한국분말재료학회지
• /
• 제12권6호
• /
• pp.393-398
• /
• 2005

In-situ processing route was adopted to disperse carbon nanotubes (CNTs) into $Al_2O_3$ powders homogeneously. The $Al_2O_3$ composite powders with homogeneous dispersion of CNTs could be synthesized by a catalytic route for in-situ formation of CNTs on nano-sized Fe dispersed $Al_2O_3$ powders. CNTs/Fe/$Al_2O_3$ nanopowders were densified by spark plasma sintering (SPS). The hardness and bending strength as well as electrical conductivity increased with increasing sintering temperature. However, the electrical conductivity of the composites sintered at above $1500^{\circ}C$ showed decreased value with increasing sintering temperature due to the oxidation of CNTs.

• 한국수소및신에너지학회논문집
• /
• 제22권4호
• /
• pp.443-450
• /
• 2011

The three-reactor chemical-looping process (TRCL) for the production of hydrogen from natural gas is attractive for both $CO_2$ capture and hydrogen production. In this study, redox property of $Fe_2O_3$ and $WO_3$ supported with $ZrO_2$ and $MgAl_2O_4$ were studied with temperature programmed oxidation/reduction (TPO/R) experiment. All metal oxides were prepared by ball mill method. Metal oxides supported with $ZrO_2$ showed the good redox property in TPO and TPR tests. Reduction behavior was matched well the theoretical reduction mechanism. Metal oxides supported with $MgAl_2O_4$ formed a solid solution ($MgFe_{0.6}Al_{1.4}O_4$, $MgWO_4$). $Fe_2O_3$ showed more narrow reaction range and lower reaction temperature than $WO_3$.

• 한국수소및신에너지학회논문집
• /
• 제14권3호
• /
• pp.268-275
• /
• 2003

The water-splitting process by the metal oxides using solar heat is one of the hydrogen production method. The hydrogen production process using the metal oxides (NiFe2O4/NiAl2O4,CoFe2O4/CoAl2O4, CoMnNiFerrite, CoMnSnFerrite, CoMnZnFerrite, CoSnZnFerrite) was carried out by two steps. The first step was carried out by the CH4-reduction to increase activation of metal oxides at operation temperature. And then, it was carried out the water-splitting reaction using the water at operation temperature for the second step. Hydrogen was produced in this step. The production rates of H2 were 110, 160, 72, 29, 17, $21m{\ell}/hr{\cdot}g-_{Metal\;Oxide}$ for NiFe2O4/NiAl2O4, CoFe2O4/CoAl2O4, CoMnNiFerrite, CoMnSnFerrite, CoMnZnFerrite, CoSnZnFerrite respectively in the second step. CoFe2O4/CoAl2O4 had higher H2 production rate than the other metal oxides.

• 한국자기학회지
• /
• 제12권1호
• /
• pp.1-6
• /
• 2002

Sol-gel법을 이용하여 $Y_3$Fe$_{5-x}$Al$_{x}$O$_{12}$ (x = 0.0, 0.25, 0.50, 0.75, 1.0) 분말을 합성하였다. 열시차 중량 분석장치(TG-DTA), x선회절기, 시료진동 자화율 측정기(VSM) 및 Mossbauer 분광기를 이용하여 물질의 결정구조 및 자기적 성질을 연구하였다. $Y_3$Fe$_{5-x}$Al$_{x}$O$_{12}$ 의 결정구조는 cubic이며, 격자상수는 x = 0.0에서 1.0까지 치환되었을 때 12.381부터 12.304 $\AA$으로 선형적으로 감소함을 보였다. Mossbauer spectrum을 13K부터 600K가지 여러 온도에서 측정을 하였다. x=0일 때 Mossbauer spectrum은 2 set으로 잘 구분할 수 있지만 치환량이 증가함에 따라 바깥쪽 팔면체 자리의 선폭이 점점 넓어지는 것을 관측할 수 있다. 이러한 현상은 사면체 자리에 존재하는 Fe$^{3+}$ 과 $Al^{3+}$ 이온의 확률적 분포에 따른 것으로 해석된다.