For melt-spun Fe-Nd-C alloy variation of phase development and magnetic properties with the variety of small Al addition was investigated. As the amount of Al addition increased the amorphization of Fe$_{14}$/Nd$_{2}$/C or $\alpha$-Fe was retarded and the residual Fe$_{14}$/Nd$_{2}$/C or $\alpha$-Fe did not eliminated after heat treatment resulting in poor coercivities of the ribbons. The grain size of Fe$_{14}$/Nd$_{2}$/C increased with the increase of Al addition and the abnormal grain was often found out in the ribbon heat treated for more then 10 min. The enhancement of coercivity was the highest with the addition of 0.5at%Al. As the amount of Al addition increase the coercivities dropped rapidly. The highest coercivity obtained so far is 13.9kOe which about 16% higher than that(11.2kOe) obtained from the Al-free specimen.

• Journal of Magnetics
• /
• v.14 no.1
• /
• pp.7-10
• /
• 2009

In this work, we studied the effects of Sn addition on the ordering temperature of FePt thin film. The coercivity of FePtSn film was about 1000 Oe greater than the coercivity of FePt film for an annealing temperature of $600^{\circ}C$. Therefore, Sn addition was effective in promoting the $L1_0$ ordering and in reducing the ordering temperature of the FePt film. From our X-ray diffraction results, we found that in the as-deposited film, the addition of Sn induced a lattice expansion in disordered FePt thin films. After the annealing process, the excess Sn diffuses out from the ordered FePt thin film because of the difference in the solid solubility of Sn between the disordered and ordered phases. The existence of precipitates of Sn from the FePt lattice was deduced by Curie temperature measurements of the FePt and FePtSn films. Therefore, the key role played by the addition of Sn to the FePt film can be explained by a reduction in the activation energy for the $L1_0$ order-disorder transformation of FePt which originates from the high internal stress in the disordered phase induced by the supersaturated Sn atoms.

• Journal of Korea Foundry Society
• /
• v.24 no.6
• /
• pp.356-365
• /
• 2004

Mechanical properties and microstructures of the Ni-AI-Fe and Ni-AI-Fe-(B, Zr) alloys which containing $10{\sim}30at$.%Fe, 0.1at.%B and/or 0.1at.%Zr have been investigated. The experimental results showed that the microstructures of Ni25Al were changed from a single phase ${\gamma}$ to dual phase ${\gamma}$ and ${\beta}$ by addition of 27at.%Fe. Ni45Al, however, kept the single ${\beta}$ phase even though Fe was added upto 30at.%. The hardness of Ni25Al were increased from $H_RB$ 70 to $H_RC$ 39 by addition of 27at.%Fe. In the case of Ni45Al which have $H_RC$ 37, the hardness was decreased by lOat.%Fe addition, but increased with 30at.%Fe. The yield strength and ultimate compressive strength in the compressive test have showed a similar trend with the hardness change. The strain to fracture was 14% at maximum and achieved in Ni25Al-27at.%Fe and Ni25Al-27at.%Fe-0.1 at.%B alloys. The Ni45Al showed a relatively low strain to fracture as 4%. The impact absorption energy of Ni25Al increased from 0.74 kg-m to 1.81 kg-m by addition of 27at.%Fe. In case of Ni45Al, the addition of lOat.%Fe and lOat.%Fe with small amounts of Band Zr did not change significantly the impact absorption energy of 0.60 kg-m, whereas the addition of 30at.%Fe with small amounts of B and Zr increased it slightly. In fracture tests, both of two basic materials showed the same intergranular fracture but by adding Fe it changed to the cleavage fracture mode or co-existing of cleavage and intergranular fractures.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.2
• /
• pp.128-136
• /
• 2004

Effects of alloying elements on the surface characteristics of Fe-38Al intermetallic compounds were investigated using potentiostat. The specimens were casted by the vacuum arc melting. The subsequent homogenization and the stabilization led to the homogeneous DO$_3$ structure of the specimen. After the corrosion tests, the surface of the tested specimen was observed by the optical microscopy and scanning electron microscopy(SEM). For Fe-38 at.% Al intermetallic compound, the addition of Cr and Mo proved to be beneficial in decreasing the grain boundary attack by decreasing the active current density. Addition of Band Nb resulted in a higher active current density and also a higher passive current density. These results indicated the role of Cr and Mo in improving the pitting corrosion resistance of Fe-38 at.%Al intermetallic compound. Band Nb addition to Fe-38 at.%Al accelerated the granular corrosion. Fe-38 at.%Al containing Cr and Mo showed remarkably improved pitting corrosion resistance in comparison with Band Nb addition to Fe-38 at. %Al.

• Journal of the Korean Ceramic Society
• /
• v.34 no.11
• /
• pp.1159-1164
• /
• 1997

Magnetite(Fe3O4) powders were synthesized through glycothermal reaction by using crystalline $\alpha$-FeOOH as precursor and ethyleanne glycol as solvent. The phase, morphology and particle size of synthesized powders were characterized by XRD and an SEM. When only ethylene glycol was used as solvent, the phase was transformed from $\alpha$-FeOOH to $\alpha$-Fe2O3 and finally Fe3O4 at 27$0^{\circ}C$ for 6hr without morphological change. But by addition of water, Fe3O4 powders were synthesized at 23$0^{\circ}C$ for 3hr through solution-recrystalization process. As the content of water addition increased, the particle shape changed from sphere to octahedron and the partcle size increased. When the excess amount of water added, residual $\alpha$-FeOOH or $\alpha$-Fe2O3 was recrystalized.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.453-460
• /
• 1997

Sr-ferrite having magnetoplumbite structure is similar to Ba-ferrite in magnetic characteristics, but better magnetic characteristics for using motor application. To improve remanence magnetic flux density(Br) and coercive force(iHc), it is necessary that sintered ferrites must have high density and grain size less than 1 $\mu$m. By varying n values in SrO.nFe2O3 basic composition, calcination temperature, and BaO addition, Sr-ferrite powder and sintered specimen was prepared. The n values, calcination temperature, and BaO addition affected secondary phase formation, particle size, and particle shape. BaO addition enhanced Fe2O3 secondary phase and hexagonal shape particle. Fe2O3 phase reduced sintered density which greatly decreased Br.

• Journal of the Korean Ceramic Society
• /
• v.34 no.7
• /
• pp.738-746
• /
• 1997

MgO clinker and two kinds of dolomite clinkers with different microstructures and CaO contents were used as starting materials, and the effects of Fe2O3 addition on the properties of MgO and dolomite were investigated in the range of 2 to 8 wt% of Fe2O3 content. Secondary phases contributed to densification of MgO-Fe2O3 and dolomite-Fe2O3 were magnesioferrite and dicalciumferrite, respectively. Sinterabilities of MgO-Fe2O3 and dolomite-Fe2O3 were directly proportional to the amount of secondary phases. Also, sinterability of dolomite itself was dependent on the microstructure of starting material including distribution of CaO and MgO as well as the addition amount of Fe2O3. The flexural strength of MgO-Fe2O3 content was almost constant. The hydration resistance of dolomite with large size of MgO and discontinuous distribution of CaO was higher than that of dolomite with small size of MgO and continuous distribution of CaO. Also, the minimum content of Fe2O3 to prevent they hydration of dolomite was about 4wt%. As increasing Fe2O3 content, the penetration resistance of MgO-Fe2O3 was improved by the increment of magnesioferrite. On the other hand, the penetration resistance of dolomite-Fe2O3 was decreased because of the increment of dicalciumferrite having low melting point.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.6
• /
• pp.480-490
• /
• 2003

Effects of plasma-nitriding on the pitting corrosion of Fe-30at%Al-5at%Cr alloy containing Ti, Hf, and Zr were investigated using potentiostat in 0.1M HCl. The specimen was casted by the vacuum arc melting. The subsequent homogenization was carried out in Ar gas atmosphere at $1000^{\circ}C$ for 7days and phase stabilizing heat treatment was carried out in Ar gas atmosphere at $500^{\circ}C$ for 5 days. The specimen was nitrided in the $N_2$, and $H_2$, (1:1) mixed gas of $10^{-4}$ torr at $480^{\circ}C$ for 10 hrs. After the corrosion tests, the surface of the tested specimens were observed by the optical microscopy and scanning electron microscopy(SEM). For Fe-30at%Al-5Cr alloy, the addition of Hf has equi-axied structure and addition of Zr showed dendritic structure. For Fe-30at%Al-5Cr alloy containing Ti, plasma nitriding proved beneficial to decrease the pitting corrosion attack by increasing pitting potential due to formation of TiN film. Addition of Hf and Zr resulted in a higher activation current density and also a lower pitting potential. These results indicated the role of dendritic structure in decreasing the pitting corrosion resistance of Fe-30Al-5Cr alloy. Ti addition to Fe-30Al-5Cr decreased the number and size of pits. In the case of Zr and Hf addition, the pits nucleated remarkably at dendritic branches.

• Journal of Korea Foundry Society
• /
• v.25 no.3
• /
• pp.128-133
• /
• 2005

The effects of Mn and Cr on the crystallization behaviors of Fe-bearing intennetallics in A356 alloy were studied. Coarse and acicular ${\beta}-Al_{5}$FeSi phase in A356-0.20wt.%Fe alloy was modified into small ${\alpha}$-Al(Fe,Mn)Si and ${\alpha}$-Al(Fe,Cr)Si phases in response to Mn and Cr addition, respectively. Increasing of Mn addition amount elevates the crystallizing temperature of ${\alpha}$-Al(Fe,Mn)Si and the Mn/Fe ratio in the ${\alpha}$-Al(Fe,Mn)Si. Cr is more effective to modify ${\beta}-Al_{5}$FeSi in comparison with Mn. ${\alpha}$-Al(Fe,Mn)Si phase had BCC/SC dual structure.

• Korean Journal of Metals and Materials
• /
• v.49 no.12
• /
• pp.989-994
• /
• 2011

Samples with compositions of 80 wt% Mg-14 wt% Ni-6 wt% $Fe_2O_3$ (named $Mg-Ni-Fe_2O_3$), and 78 wt% Mg-14 wt% Ni-6 wt% $Fe_2O_3-2$ wt% CNT (named $Mg-Ni-Fe_2O_3-CNT$ ) were prepared by reactive mechanical grinding. Hydriding and dehydriding properties and effects of CNT addition on the hydriding and dehydriding rates of $Mg-Ni-Fe_2O_3$ were then investigated. Activation of the $Mg-14Ni-6Fe_2O_3$ sample was completed after three hydriding (under 12 bar $H_2$)-dehydriding (under 1.0 bar $H_2$) cycles at 573 K. The addition of CNT to the $Mg-14Ni-6Fe_2O_3$ sample made the activation process unnecessary, with a small decrease in the hydrogen-storage capacity.