• 한국기계연구소 소보
• /
• s.13
• /
• pp.3-13
• /
• 1984

Fatigue failure of axle housing could cause many injuries and much financial loss. This challenges the engineer to improve design decisions involving fatigue. Endurance evaluation of axle housing is great interest to auto-mobile manufacturers for the sake of safety and reliability. Axle housing is subjected to gross vehicle weight(G.V.W)as mean load and alternating load. Theoretical design diagram involving mean and alternating stresses is used for the evaluation of axle housing fatigue endurance with the equivalent stress of fatigue critical area on the axle housing. Four point bending fatigue tests on axle housing with constant amplitude loading at approximately R=0 were performed with 50 ton servohydraulic strucural fatigue testing machine developed at KIMM. Specimens were made with the same material STKM 13B as the axle housing and tested to obtain S_N data. Five specimens of STKM 13B were tested at 253.61 MPa and weibull distribution was obtained at the same stress level. Material data and structural data were compares and fatigue stress property factor and fatigue life property factor were obtained.

• Journal of the Korean Society of Safety
• /
• v.25 no.6
• /
• pp.53-59
• /
• 2010

A fatigue damage caused by cyclic load is considered as one of the important failure mechanisms that threaten the integrity of structures and components in a nuclear power plant. In ASME code section III NB, the fatigue analysis procedure and standard S-N curves for the class 1 components are described and these criteria should be met at the design step of components. As the current ASME S-N curves are based on the very conservative assumptions such as a local stress concentration effect, immoderate transient frequencies and a constant Young's modulus, however, they can not precisely address the fatigue behavior of components. In order to find out the technical solution for these problems, a number of researches and discussion have been carried out continuously at home and abroad over the decades. In this study, detailed fatigue analyses for DVI nozzle with various mesh density of finite elements were performed to evaluate effect of stress concentration factors on the fatigue analysis procedure and the excessive conservatism of stress concentration factors are confirmed through the analysis results.

• Journal of the Korean Society of Safety
• /
• v.11 no.2
• /
• pp.3-8
• /
• 1996

Fatigue fracture is the cyclic fracture phenomena at a very small local area near a crack tip. Therefore, the detailed quantitative experimental analysis about local cyclic strain distribution near a crack tip is prerequisite In order to make an effective parameter able to account for fatigue fracture problems. However, there are few reports on detailed quantitative experimental analysis of a local cyclic strain distribution near a crack tip, because of experimental difficulties. In this study, the distribution of local fatigue strains near a fatigue crack tip was in detail studied using by fine dot grid strain measurement method. From these results, a single parameter, which characterizes local fatigue strain field, was proposed. In addition, this parameter was applied to evaluate the fatigue crack propagation rate.

• Journal of the Korean Society of Safety
• /
• v.12 no.2
• /
• pp.17-21
• /
• 1997

The fatigue crack propagation rate has so far been measured by the effective stress intensity factor range Δ K/sub eff/. But no research has been done to study how much the crack opening ratio influences the expectation of the fatigue crack propagation. Therefore, this paper evaluates of the crack opening ratio on the fatigue crack propagation life by using the method of parameter sensitivity study. Summarizing the result ; ( 1 ) When the crack opening ratio U' is high, the effect of U' gets larger than any other except for the material factor m. But when U' is low, the effect is also diminished. Therefore, the selection of the lowest value possible is desirable in the evaluation of life. (2) When the value of the material factor m is high, the effect of crack opening ratio U' is increased, at the same time the effect of the other parameters also increased wholly. The effect of material factor m itself on life is high, but in case the material factor m is high, that the effect of each parameter on life get higher is unique. In designing, better attention to the material selection should be drawn. (3) In case the stress ratio R gets smaller, the effect of crack opening ratio U' is unchangeable. But the effect of R itself remarkably decreases, and the effect of material factor m somewhat decreases.

• Journal of Ocean Engineering and Technology
• /
• v.35 no.5
• /
• pp.327-335
• /
• 2021

Microcracks can rapidly grow and develop in high-strength steels used in offshore structures. It is important to render these microcracks harmless to ensure the safety and reliability of offshore structures. Here, the dependence of the aspect ratio (As) of the maximum depth of harmless crack (a_hlm) was evaluated under three different conditions considering the threshold stress intensity factor (Δk_th) and residual stress of offshore structural steel F690. The threshold stress intensity factor and fatigue limit of fatigue crack propagation, dependent on crack dimensions, were evaluated using Ando's equation, which considers the plastic behavior of fatigue and the stress ratio. a_hlm by peening was analyzed using the relationship between Δk_th obtained by Ando's equation and Δk_th obtained by the sum of applied stress and residual stress. The plate specimen had a width 2W = 12 mm and thickness t = 20 mm, and four value of As were considered: 1.0, 0.6, 0.3, and 0.1. The a_hlm was larger as the compressive residual stress distribution increased. Additionally, an increase in the values of As and Δk_th(l) led to a larger a_hlm. With a safety factor (N) of 2.0, the long-term safety and reliability of structures constructed using F690 can be secured with needle peening. It is necessary to apply a more sensitive non-destructive inspection technique as a non-destructive inspection method for crack detection could not be used to observe fatigue cracks that reduced the fatigue limit of smooth specimens by 50% in the three types of residual stresses considered. The usefulness of non-destructive inspection and non-damaging techniques was reviewed based on the relationship between a_hlm, a_NDI (minimum crack depth detectable in non-destructive inspection), a_{cr N} (crack depth that reduces the fatigue limit to 1/N), and As.

• Journal of the Korean Society of Safety
• /
• v.15 no.2
• /
• pp.8-12
• /
• 2000

The fatigue crack propagation tests were performed in triangular and holding-time stress waveforms at $650^{\circ}C$. The behavior of fatigue crack propagation was investigated according to waveform. The analysis of high temperature fatigue crack propagation by the stress intensity factor range ${\Delta}K$, elastic fracture mechanics parameter, was not available. The behaviors of high temperature fatigue crack propagation by the J-integral(${\Delta}J_f$, J' and ${\Delta}J_c$), elasto-plastic fracture mechanics parameter, were investigated in a number of stress waveforms. The fast-fast waveform exhibited cycle-dependent(fatigue type), the slow-fast and the hold time with 500sec waveforms appear to be time-dependent(creep type) and the fast-slow and the hold time with 5, 25sec waveforms exhibited conbined behavior of both types(fatigue-creep conbined type).

• Journal of the Korean Society of Safety
• /
• v.16 no.1
• /
• pp.18-24
• /
• 2001

The fatigue crack growth behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, $-60^{\circ}C$,$-80^{\circ}C$ and $-100^{\circ}C$ with stress ratio of R=0.05, 0.1 and 0.3. Fatigue crack propagation rate da/dN related with stress intensity factor range ${\Delta}K$ was influenced by stress ratio in stable of fatigue crack growth (Region II) with an increase in ${\Delta}K$. The resistance of fatigue crack growth at low temperature is higher compared with that at room temperature, which is attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and low temperatures are mainly explained by the crack closure and the strengthening due to the plasticity induced and roughness induced.

• Journal of the Korean Society of Safety
• /
• v.21 no.4 s.76
• /
• pp.19-24
• /
• 2006

Fatigue crack propagation tests for the brake disc cast iron were conducted for investigating fatigue crack propagation rate(da/dN), crack propagation path and fracture toughness($K_c$) of the material. The threshold stress intensity factor range, ${\Delta}K_{th}$, was found to be about $6MPa{\sqrt{m}}$ at the stress ratio of R = 0.1. Also, fracture toughness value was determined to be $24.7MPa{\sqrt{m}}$. Irregular fatigue fracture surfaces were observed, indicating that fatigue crack growth occurred at the interface between randomly scattered flak graphite and ferrite, where the interfacial strength was relatively weak.

• Journal of the Korean Society of Safety
• /
• v.22 no.2 s.80
• /
• pp.8-14
• /
• 2007

In this study, tensile and fatigue crack propagation tests machined from actual wheels were performed. FEM analysis also was performed on the crack that was assumed to be 15 mm in depth under the wheel tread surface. The stress intensity factors K I and K II at the crack tip under the stress($P_{max}=911.5MPa$) due to a rolling contact were analyzed for crack growth characteristics. As a result, the perpendicular crack was found to be more dangerous compared to the parallel one. It is found that in the wheel fatigue crack, parallel to the wheel tread surface, the crack with its length 2a = 2.4mm starts to propagate due to the fact that the effective stress intensity factor access to the threshold stress intensity factor($K_{th}=16.04MPa{\sqrt{m}}$) of the wheel.

• Structural Engineering and Mechanics
• /
• v.47 no.5
• /
• pp.643-660
• /
• 2013

In the present work, the capacity ratings of steel truss bridges have been carried out incorporating dynamic effect of moving vehicles and its accumulating effect as fatigue. Further, corrosion in the steel members has been taken into account to examine the rating factor. Dynamic effect has been considered in the rating procedure making use of impact factors obtained from simulation studies as well as from codal guidelines. A steel truss bridge has been considered to illustrate the approach. Two levels of capacity ratings- the upper load level capacity rating (called operating rating) and the lower load level capacity rating (called inventory rating) were found out using Load and Resistance Factor Design (LRFD) method and a proposal has been made which incorporates fatigue in the rating formula. Random nature of corrosion on the steel member has been taken into account in the rating by considering reduced member strength. Partial safety factor for each truss member has been obtained from the fatigue reliability index considering random variables on the fatigue parameters, traffic growth rate and accumulated number of stress cycle using appropriate probability density function. The bridge has been modeled using Finite Element software. Regressions of rating factor versus vehicle gross weight have been obtained. Results show that rating factor decreases when the impact factor other than those in the codal provisions are considered. The consideration of fatigue and member corrosion gives a lower value of rating factor compared to those when both the effects are ignored. In addition to this, the study reveals that rating factor decreases when the vehicle gross weight is increased.