• Proceedings of the KSR Conference
• /
• 2001.10a
• /
• pp.273-278
• /
• 2001

The transmission system of high speed train serve in the severe condition compared with those of other trains, namely, they have to transmit high power to run with high speed and they have to make maximum use of the limited space. To clarify the strength of gear for Korea High-speed train, a bending fatigue test is performed for the output gear of axle gear reduction unit. This paper reports the reviews of bending fatigue strength test method and the test results of output gear of axle gear reduction unit for high speed train.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1740-1743
• /
• 2007

In this study, two types of fatigue tests were conducted. First, cyclic bending tests were performed using the micro-bending tester. A four-point bending test method was adopted, because it induces uniform stress fields within a loading span. Second, thermal fatigue tests were conducted using a pseudo power cycling machine which was newly developed for a realistic testing condition. The pseudo-power cycling method makes up for the weak points in a power cycling and a chamber cycling method. Two compositions of solder are tested in all test condition, one is lead-free solder (95.5Sn4.0Ag0.5Cu) and the other is eutectic lead-contained solder (63Sn37Pb). In the cyclic bending test, the solder that exhibits a good reliability can be reversed depending on the load conditions. The lead-contained solders have a longer fatigue life in the region where the applied load is high. On the contrary, the lead-free solder sustained more cyclic loads in the small load region. A similar trend was detected at the thermal cycling test. A three-dimensional finite element analysis model was constructed. A finite element analysis using ABAQUS was performed to extract the applied stress and strain in the solder joints. A constitutive model which includes both creep and plasticity was employed. Thermal fatigue was occurred due to the creep. And plastic deformation is main damage for bending failure. From the inelastic energy dissipation per cycle versus fatigue life curve, it can be found that the bending fatigue life is longer than the thermal fatigue life.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2000.04a
• /
• pp.71-75
• /
• 2000

The effects of stitching thread on fatigue characteristics of polyurethane foam cored sandwich structures are investigated. Fatigue test and static test, being used in four point bending test, are performed with various diameters and distances of stitching thread. The Results show that the maximum load for bending tests is similar to each other, but after $1O^6$ fatigue cycles, the stiffness degradation of the stitching thread diameter $\emptyset$ 3mm specimen is a much larger than that of the $\emptyset$ 5mm specimen.

• Journal of the Korean Society of Safety
• /
• v.12 no.2
• /
• pp.27-36
• /
• 1997

This paper evaluates the static and fatigue bending strengths of CFRP (carbon fiber reinforced plastic) laminates subjected to hygrothermals. The specimens which had different stacking composition, orthotropic and quasi-isotropic laminated plates, were prepared for this experiment. A steel ball launched by the air gun collides against CFRP laminates to generate impact damages, and the 3-point fatigue bending test is carried out by using the impacted laminates to investigate the influence of hygrothermals on the effect on the residual bending fatigue strength of CFRP laminates.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.2 no.6
• /
• pp.1-8
• /
• 1994

To enhance the strength of gears for transmission, Generally caburizing heat treatment is applied. But there are some problems in this technology the distortion of gears during heat treatment process, and the discontinuity of manufacturing process. For these reasons, the high frequency induction hardening process is widely used. This method is one of the surface hardening process to improve the wear resistance and fatigue life of the machine components. In this study, to compare the bending fatigue strength of caburized gear with that of induction hardened gear, bending fatigue testing of gears with two different cases was performed by using an electrohydraulic servo-controlled fatigue testing machine and double tooth bending fatigue test fixture. Fatigue life distributions at constant stress levels were established directly from fatigue data. For gear design, the fatigue strength distribution at specified life is more important. This distribution is obtained by statical transformation from fatigue life distribution. Reliability of bending fatigue strength was estimated by P-S-N curves and Weibull distribution.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2000.05a
• /
• pp.93-99
• /
• 2000

This study deals with the evaluation of bending fatigue strength in shaving gears, We manufactured gears using manufacture processes that are currently used in most gears manufacturing companies. The test gears are hobbed then the tooth surface are treated by a combination of shaving carbonizing and shot peening. The constant stress amplitude fatigue test is performed by using an electrohydraulic servo-controlled pulsating tester. The S-N curves are obtained and illustrated. In this study we investigated the effect of shaving process and shot peening on fatigue strength, The effect of shaving process ad shot peening on the fatigue strength is evaluated quantitatively,. The enhancement of fatigue strength due to shaving process and shot peening is clarified

• Journal of Mechanical Science and Technology
• /
• v.17 no.3
• /
• pp.343-349
• /
• 2003

The fuselage-wing intersection suffers from the cyclic bending moment of variable amplitude. Therefore, the influence of cyclic bending moment on the delamination and the fatigue crack propagation behavior in AFRP/Al laminate of fuselage-wing was investigated in this study. The cyclic bending moment fatigue test in AFRP/Al laminate was performed with five levels of bending moment. The shape and size of the delamination Lone formed along the fatigue crack between aluminum sheet and aramid fiber-adhesive layer were measured by an ultrasonic C-scan. The relationships between da/dN and ΔK, between the cyclic bending moment and the delamination zone size, and between the fiber bridging behavior and the delamination zone were studied. As results, fiber failures were not observed in the delamination zone in this study, the fiber bridging modification factor increases and the fatigue crack growth rate decrease and the shape of delamination zone is semi-elliptic with the contour decreasing non-linearly toward the crack tip.

• Journal of Advanced Marine Engineering and Technology
• /
• v.21 no.5
• /
• pp.482-490
• /
• 1997

The effects of strain amplitude. test temperature and stress on the fatigue properties for Ti-Ni wires were investigated using a rotary bending fatigue tester specially designed for wires. The fatigue test results were discussed in connection with the static tensile properties. The DSC measurement was conducted after fatigue test in order to clarify the change of transformation behavior due to the progress of fatigue. Under the temperature below or near the Af, the strain amplitude($\varepsilon_a$)-failure life (Nf) curve showed to be composed of three straight lines with two turning points. Of the 2 turning points, the upper one was coincident with the elastic limit strain and the lower one with the proportional limit strain. With rising of the test temperature above Af, the pattern of $\varepsilon_a$-Nf curve changed gradually to composition of 2 straight lines. The $\varepsilon_a$-Nf curve shifted depending on test temperature. In the short and medium life zones, the higher the temperature was, the shorter the fatigue life. However, in the long life zone, above the Af temperature, the fatigue life was not affected by the temperature. The transformation enthalpy measured after fatigue test was dependent on Nf, $\varepsilon_a$, and test temperature.

• Journal of Advanced Marine Engineering and Technology
• /
• v.26 no.3
• /
• pp.337-343
• /
• 2002

This study deals with evaluation of bending fatigue strength in shaving gears. The saying gears were manufactured by processes that are currently used in most gears manufacturing companies. The test gears are bobbed, then the tooth surface are treated by a combination of shaving, carburizing and shot peening. The constant stress amplitude fatigue test is performed by using an electro-hydraulic servo-controlled pulsating tester. The S-N curves are obtained and illustrated. In this study, the effect of shaving process and shot peening was investigated and evaluated quantitatively on the fatigue strength. The enhancement of fatigue strength due to shaving process and shot peening is clarified.

• Journal of Welding and Joining
• /
• v.16 no.5
• /
• pp.134-141
• /
• 1998

In this study, a fillet size for bending fatigue strength of one side fillet welded T-joint, used in box type girder and other welding structure, was investigated by bending fatigue test with or without edge preparation and burn through, with variation of joint shape. As a result, the following conclusions were obtained. (1) In one side fillet welded T-joint, the larger the leg length, the greater the bending fatigue strength. The increase in bending fatigue strength. (2) One side filet welded T-joint with edge preparation showed higher bending fatigue strength than that with twofold-large leg length and without edge preparation. (3) In one side fillet welded T-joint without edge preparation, both manual welding and automatic welding were carried out with same condition. In this case, automatic welding shoed deeper penetration and more increased horizontal leg length than manual welding, so that automatic welding offers grater bending fatigue strength. (4) For one side fillet welded T-joint without edge preparation, the ratio(h/t) of the leg length (h) and the main plate thickness (t) in which toe crack can occur was 1.2 over. (5) In one side fillet welded T-joint with edge preparation, the burn through led to reduced bending fatigue strength. However, this bending fatigue strength was higher than that of one side fillet welded T-joint without edge preparation and with a larger leg length.