• 한국산업융합학회 논문집
• /
• 제26권4_2호
• /
• pp.585-589
• /
• 2023

Unlike general carbon steel, stainless steel's mechanical properties change depending on the content of chromium and nickel. In this study, since stainless steel for high-temperature pressure container parts is used as shafts, the fatigue strength and fatigue limit of the materials were evaluated using a rotational bending fatigue test. Meanwhile, fatigue analysis was conducted under the same conditions as the specimen for structural analysis and fatigue analysis of stainless steel for high-temperature pressure container parts. Using the fatigue analysis results, we tried to derive the life of the material and the safety factor for each part. As a result of performing a fatigue test by processing a specimen for the fatigue test of A182 F6A stainless steel, the fatigue limit was 548 MPa. The ratio between the tensile strength and fatigue limit of the material was 0.545, representing 54.5% of the tensile strength.

• 한국신뢰성학회:학술대회논문집
• /
• 한국신뢰성학회 2006년도 학술발표대회 논문집
• /
• pp.357-361
• /
• 2006

Fatigue fracture behavior of a hybrid joint part with bolting was evaluated in comparison to the case of static fracture. Hybrid joint part specimens for bending test were made with layers of CFRP and aluminum honeycomb. Characteristic fracture behaviors of those specimens were obviously different under static and cyclic loads. Static bending load showed the shear deformation at the honeycomb core, whereas cyclic bending load caused the delamination between CFRP skin layers and honeycomb core. Experimental results obtained by static and fatigue tests were considered in modifications of design parameters of the hybrid joint.

• Journal of Mechanical Science and Technology
• /
• 제15권7호
• /
• pp.1022-1031
• /
• 2001

The elastic modulus and fatigue properties of canine and human trabecular bone tissues (single trabecular) were experimentally determined on a microstructural level using four-point bending cyclic test, and they were compared based on microstructural characteristics and mineral density. The results showed that canine trabecular bone tissue had significantly lower modulus and lower fatigue strength than human tissue. The observed microstructural differences between the two tissues may be more responsible for the differences, although the lower mineral density in canine tissue might also have contributed to the lower modulus and fatigue strength.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.173-174
• /
• 2008

The four-point bending test is a widely used method to determine material parameters. The aim of the present study was to evaluate the flexural strength (or modulus of rupture) and the Weibull modulus of cordierite ceramic substrate by means of four-point bending tests. The strength data from experiments followed Weibull statistics. These data indicate that the fatigue effects are more severe when the substrate temperature in the peripheral region is near $200^{\circ}$. At temperatures well above $200^{\circ}C$ the available design strength can be as high as 65% as substrate's initial strength.

• 유체기계공업학회:학술대회논문집
• /
• 유체기계공업학회 2004년도 유체기계 연구개발 발표회 논문집
• /
• pp.385-389
• /
• 2004

Test facilities for the wind turbine performance monitoring and mechanical load measurements are installed in Vestas 100 kW wind turbine in Wollyong test site, Jeju island. The monitoring system consists of Garrad-Hassan T-MON system, telemetry system for blade load measurement, various sensors such as anemometer, wind vane, strain gauge, power meter, and etc. The experimental procedure for the measurement of wind turbine loads, such as edgewise(lead-lag) bending moment, flapwise bending moment, and tower base bending moment, has been established. Strain gauges are on-site calibrated against load cell prior to monitoring the wind turbine loads. Using the established monitoring system, the wind turbine is remotely monitored. From the measured load data, the load analysis has been performed to obtain the load power spectral density and the fatigue load spectra of the wind turbine.

• Journal of Mechanical Science and Technology
• /
• 제16권8호
• /
• pp.1109-1116
• /
• 2002

To investigate the effect of nitriding layer on both fatigue crack initiation and fatigue life, turbine rotor steel ( IC.- 1Mo-0.25V steel) specimens were nitrided by the nitemper method and then put to a rotary bending fatigue test at room and elevated temperatures. In nitriding, temperature and time were controlled to obtain a different nitrided thickness. Microstructure analysis, micro-Victors hardness test, and scanning electron microscope observation were carried out for evaluating experiments. In results, the fatigue cracks of nitrided specimens were initiated at inclusion near the interface between nitrided layer and substrate, which showed fish-eye type appearance in fractograph. The fatigue life of nitrided specimens at every temperature was prolonged compared to that of the non-nitrided. However, there was not observable improvement in fatigue characteristics with the increase of a nitrided thickness.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 추계학술대회논문집A
• /
• pp.231-237
• /
• 2000

A15052/AFRP laminates were developed principally to obtain a material with good fatigue strength, in which possible cracks would grow very slowly. Weight savings of more than 30% should be attainable in practice. Also, the crack bridging fibers could still was carry a significant part of the load over the crack, thus the COD and stress intensity factor was reduced at the crack tip. A15052/ AFRP laminates consists of three thin sheets of 5052-H34 aluminum alloy and two layers of [0] unidirectional aramid fiber prepreg. The cyclic-bending moment test was investigated based on applying the five kinds of bending moments. The size of the delamination zone produced between 5052-H34 aluminum alloy sheets and fiber-adhesive layers was measured from ultrasonic C-scan pictures taken around the fatigue crack. In addition, the relationship between the cyclic-bending moment and the delamination zone size was studied and the effect of fiber bridging mechanism was also considered.

• 대한기계학회논문집A
• /
• 제36권10호
• /
• pp.1227-1234
• /
• 2012

본 연구에서는 감육결함이 가공된 실배관 곡관 시편을 대상으로 10 MPa의 내압과 반복 굽힘하중 조건에서 피로 시험을 수행하였다. 시험에는 감육결함이 곡관의 외호부와 내호부에 존재하는 경우를 고려하였으며, 반복 하중으로는 완전 역방향의 변위제어 형태로 작용되는 In-plane 상의 굽힘하중이 고려되었다. 실험 결과, 감육결함이 곡관의 외호부에 존재하는 경우에는 결함부가 아닌 곡관의 측면에서 축방향 균열이 생성되었다. 또한, ASME Sec.III의 설계 피로곡선에서 예측된 건전 곡관의 피로수명보다 긴 피로수명을 보였으며, 피로수명이 결함 길이에 크게 영향을 받지 않았다. 반면, 결함이 내호부에 존재하는 곡관은 내호부에서 원주방향 균열이 발생하였으며, 피로수명은 ASME Sec.III의 설계 피로곡선에서 예측한 건전 곡관의 피로수명보다 짧은 값을 보였다. 또한, 내호부 감육 곡관의 피로수명은 결함 길이가 감소함에 따라 뚜렷이 감소하였다.

• 한국해양공학회지
• /
• 제25권6호
• /
• pp.72-79
• /
• 2011

In this paper, the fatigue characteristics of shot peened A7075-T651 alloy were compared with those of the specimens without the shot peening. The multi-spindle and single-spindle rotating bending fatigue testing machines were employed for the evaluation. Shot peening (SP) with various pressure (5 psi, 10 psi, 15 psi, 25 psi and 35 psi) were used in this test. In order to investigate the effect of the applied pressure during the SP, we carried out the surface roughness test, compressive residual stress test, hardness test, tensile test, VHCF (Very high cycle fatigue) test and SEM observation. SP induced the formation of remarkable compressive residual stress from the surface to certain depth of sample by means of the plastic deformation. The surface hardness and the fatigue characteristics of the specimens were also modified by the SP. According to the S-N curves, fatigue lives of shot peended sample with 25 psi measures 50 times higher than that of the untreated sample. The fatigue lives of shot peened sample with 15 psi and 35 psi measure approximately 10 times higher than that of the untreated ones.

• 한국재난정보학회 논문집
• /
• 제9권4호
• /
• pp.476-483
• /
• 2013

본 연구는 자동차 파쇄 잔재물의 활용성을 알아보고자 폐차과정에서 발생되는 폐나일론 섬유를 아스팔트 콘크리트에 첨가하여 일반 아스팔트 콘크리트와의 피로수명 비교, 경제성 분석을 실시하였다. 4점 휨 피로 시험을 수행한 결과 일반 아스팔트 대비 피로수명이 10% 향상되었으며, 이를 통해 경제성 분석을 실시하여 35년간 약 5.4억 원의 유지보수비용에 대한 비용 절감을 가져 오는 것으로 확인 되었다. 폐나일론 섬유 보강 아스팔트는 비용절감 효과와 더불어 폐자재의 환경처리비용 이점과 활용성 측면에서의 친환경적 공법으로 생애주기비용분석에서보다 더 큰 경제적, 사회적 효과가 발생 할 것으로 판단된다.