• 대한기계학회논문집A
• /
• 제26권5호
• /
• pp.960-968
• /
• 2002

In this research, the effects of fiber stacking sequence on damage behaviors of FML(Fiber Metal Laminates) subject to indentation loading. SOP (Singly Oriented Ply) FML and angle ply FML were fabricated to study fiber orientation effects and angle ply effects. FML were fabricated by using 1050 aluminum laminate and carbon/epoxy prepreg. To increase adhesive bonding strength, Al laminate was etched using FPL methods. The static indentation test were conducted by using UTM under the 2side clamped conditions. During the tests, load and displacement curve and crack initiation and propagation behaviors were investigated. As fiber orientation angle increases, the crack initiation load of SOP FML increases because the stiffness induced by fiber orientation is increased. The penetration load of SOP FML is influenced by the deformation tendency and boundary conditions. However, the macro-crack of angle ply FML was initiated by fiber breakage of lower ply because angle plies in Angle ply FML prevents the crack growth and consolidation. The Angle ply FML has a critical cross-angle which prevent crack growth and consolidation. Damage behavior of Angle ply FML is changed around the critical cross-angle.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 추계학술대회논문집A
• /
• pp.204-209
• /
• 2001

In this research, the effects of fiber stacking sequence on damage behaviors of FML(Fiber Metal Laminates) subject to indentation loading. SOP (Singly Oriented Ply) FML and angle ply FML were fabricated to study fiber orientation effects and angle ply effects. FML were fabricated by using 1050 aluminum laminate and carbon/epoxy prepreg. To increase adhesive bonding strength, Al laminate was etched using FPL methods. The static indentation test were conducted by using UTM(5ton, Shimadzu) under the 2side clamped conditions. During the tests, load and displacement curve and crack initiation and propagation behaviors were investigated. As fiber orientation angle increases, the crack initiation load of SOP FML increases because the stiffness induced by fiber orientation is increased. The penetration load of SOP FML is influenced by the deformation tendency and boundary conditions. However, the macro-crack of angle ply FML was initiated by fiber breakage of lower ply because angle plies in Angle ply FML prevents the crack growth and consolidation. The Angle ply FML has a critical cross-angle which prevent crack growth and consolidation. Damage behavior of Angle ply FML is changed around the critical cross-angle.

• The Plant Pathology Journal
• /
• 제18권1호
• /
• pp.6-11
• /
• 2002

An isolate of Cucumber mosaic virus (CMV), PaFMl-CMV causing malformation on the fruit of paprika (Capsicum annuum var, grossum) was characterized based on biological reactions, serological relationships, and partial nucleotide sequence analyses. PaFMl-CMV was distinguishable from other isolates of CMYI Mf-(subgroup I) and LS-CMV (subgroup II), in terms of its reactions to some host plants. Polyclonal antibody against PaFMl-CMV showed homologous antigenic relationship with LS-CMV, however, the antibody formed a spur between PaFMl- and Mf-CMV, In the comparison of molecular size of dsRNAs of PaFMl-CMV with Mf- and LS-CMV, PaFMl-CMV had a slightly smaller RNAl and larger RNA2, RNA3, and RNA4. When the CDNA product of PaFMl-CMV coat protein (CP) gene was digested with some restriction enzymes, the fragment pattern was identical with that of LS-CMV The nucleotide and amino acid sequences of PaFMl-CMV CP gene were 99.5% and 98.6% identical with LS-CMV respectively. The data indicate that PaFMl-CMV belongs to subgroup II of CMV, which is the first report in Korea.

• 대한기계학회논문집A
• /
• 제27권3호
• /
• pp.372-380
• /
• 2003

Impact tests were conducted to study the effect of angle ply and metal laminate on impact damage characteristics of Fiber Metal laminates (FML). Impact tests were conducted using drop weight impact machine and damage behavior were analyzed by comparing with load-displacement curve and surface observation and microscopic observation of cross sections. The effect of angle ply on impact characteristics of FML are influenced by property of metal laminate. i.e., when the metal laminate is not enough to strong to prevent fiber debonding, Angle ply FML is superior to singly oriented ply (SOP) FML because angle ply enhance the stiffness by fiber supports and prevent (rack propagation. However, when the metal laminate is enough to strong to prevent fiber debonding, SOP FML is superior to Angle ply FML because the fiber of lower ply in Angle ply FML are more stressed than that of SOP FML.

• Composites Research
• /
• 제14권5호
• /
• pp.46-53
• /
• 2001

집중하중을 받는 일방향 보강(singly oriented ply, SOP) 섬유 금속 적층판(fiber metal laminate, FML)의 손상 거동을 음향 방출법(acoustic emission, AE)을 이용하여 연구하였다. 섬유 방향의 영향을 연구하기 위하여 다양한 섬유 방향을 가지는 SOP FML을 제작하였으며, UTM을 이용하여 압입 하중을 가하였다. 압입 시험 시 발생하는 AE신호는 150kH의 공진 주파수를 가지는 AE센서를 이용하여 측정하였으며, 여기에서 발생된 신호를 하중-변위 선도와 비교하였다. SOP FML의 손상 과정은 균열 개시, 균열 전파, 관통에 따라 3구간으로 나누어 겼다. 균열 개시전까지의 AE 신호의 특성으로 보아 미소 균열이 시편의 하부에서 발생하고 이 균열이 시편의 두께 방향으로 전파되어 섬유 분리를 발생시키는 것으로 생각된다. 발생된 균열은 섬유 방향을 따라 성장하였으며, 이 때 60~80dB의 AE신호들이 발생되었다. 관통이 발생할 때는 80~100dB의 고진폭의 AE신호가 나타나 섬유의 파괴가 발생함을 보였으며, 섬유의 방향이 증가할수록 섬유의 파괴가 많이 발생되었다 누적 AE count선도는 FML의 압입 특성을 잘 나타내어 FML의 특성 변호 예측에 유용하게 사용될 수 있을 것으로 생각된다.

• 한국항공우주학회지
• /
• 제33권6호
• /
• pp.39-44
• /
• 2005

섬유금속적층판(Fiber Metal Laminates, 이하 FML)에서 알루미늄과 유리섬유/에폭시 복합재료 사이의 열팽창 계수의 차이는 경화공정 시 FML내부에 열 잔류응력을 남기게 되며, 이러한 열 잔류응력은 FML의 피로특성과 항복강도에 영향을 주게 된다. 잔류응력을 예측하기 위해 두 가지 실험법이 제안 되었으며, 이론식을 통해 그 결과를 예측하고, 실제 실험을 수행하여 그 값을 확인 하였다. 또한, 열 잔류응력의 제거 및 응력의 역전을 위하여 후-인발 가공이 수행 되었으며, 가공 이후 발생한 FML내의 잔류응력이 측정 되었다. 예측된 열 잔류응력 결과와 실험을 통한 값이 일치함을 보이며, 후-인발 가공을 통하여 열 잔류응력 제거 및 항복강도의 증가가 발생하였다.

• Journal of Ginseng Research
• /
• 제42권1호
• /
• pp.21-26
• /
• 2018

Background: Furosine (${\varepsilon}$-N-2-furoylmethyl-L-lysine, FML) is an amino acid derivative, which is considered to be an important indicator of the extent of damage (deteriorating the quality of amino acid and proteins due to a blockage of lysine and a decrease in the digestibility of proteins) during the early stages of the Maillard reaction. In addition, FML has been proven to be harmful because it is closely related to a variety of diseases such as diabetes. The qualitative analysis of FML in fresh and processed ginsengs was confirmed using HPLC-MS. Methods: An ion-pair reversed-phase LC method was used for the quantitative analysis of FML in various ginseng samples. Results: The contents of FML in the ginseng samples were 3.35-42.28 g/kg protein. The lowest value was observed in the freshly collected ginseng samples, and the highest value was found in the black ginseng concentrate. Heat treatment and honey addition significantly increased the FML content from 3.35 g/kg protein to 42.28 g/kg protein. Conclusion: These results indicate that FML is a promising indicator to estimate the heat treatment degree and honey addition level during the manufacture of ginseng products. The FML content is also an important parameter to identity the quality of ginseng products. In addition, the generation and regulation of potentially harmful Maillard reaction products-FML in ginseng processing was also investigated, providing a solid theoretical foundation and valuable reference for safe ginseng processing.

• Structural Engineering and Mechanics
• /
• 제57권1호
• /
• pp.45-63
• /
• 2016

Fiber metal laminates (FMLs) represent a high-performance family of hybrid materials which consist of thin metal sheets bonded together with alternating unidirectional fiber layers. In this study, the buckling behavior of a FML circular cylindrical shell under axial compression is investigated via both analytical and finite element approaches. The governing equations are derived based on the first-order shear deformation theory and solved by the Navier solution method. Also, the buckling load of a FML cylindrical shell is calculated using linear eigenvalue analysis in commercial finite element software, ABAQUS. Due to lack of experimental and analytical data for buckling behavior of FML cylindrical shells in the literature, the proposed model is simplified to the full-composite and full-metal cylindrical shells and buckling loads are compared with the available results. Afterwards, the effects of FML parameters such as metal volume fraction (MVF), composite fiber orientation, stacking sequence of layers and geometric parameters are studied on the buckling loads. Results show that the FML layup has the significant effect on the buckling loads of FML cylindrical shells in comparison to the full-composite and full-metal shells. Results of this paper hopefully provide a useful guideline for engineers to design an efficient and economical structure.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 춘계학술발표대회 논문집
• /
• pp.65-68
• /
• 2001

In this research, damage initiation in singly oriented ply (SOP) FML under concentrated loading conditions was studied. The finite element method (FEM) base on the first order shear deformation theory is used for the analysis of fiber orientation effect on FML under concentrated loading conditions. The failure indices were calculated for the variation of fiber orientation and the results were compared with indentation experiments. The failure indices were well matched with damage initiation of SOP FML. Indentation results shows that the crack initiation of SOP FML is determined by stiffness induced by fiber orientation and tile penetration load of SOP FML are influenced by the deformation tendency and boundary conditions.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.407-412
• /
• 2001

In this research, damage behavior of singly oriented ply (SOP) fiber metal laminate (FML) subject to concentrated load was studied. The static indentation tests were conducted to study fiber orientation effect on damage behavior of FML. During the static indentation tests, Acoustic Emission technique (AE) was adopted to study damage characteristics of FML. AE signals were obtained by using AE sensor with 150kHz resonance frequency and the signals were compared with indentation curves of FML. As fiber orientation angle increases, the crack initiation load of SOP FML increases because the stiffness induced by fiber orientation is increased. The penetration load of SOP FML is influenced by the deformation tendency and boundary conditions. Cumulative AE counts were well predicted crack initiation and crack propagation and AE amplitude were useful for prediction of damage failure mode. During the matrix cracking, fiber debonding and fiber breakage, AE amplitude has $45{\sim}60dB,\;60{\sim}80dB\;and\;90{\sim}100dB$, respectively.