In this study, fire resistance and residual strength were examined after the addition of PF fiber and bonding fireproofing gypsum board to a high strength concrete-model column of 50 MPa grade. At the beginning of the experiment, all the properties of base concrete appeared to satisfy the target range. In terms of the internal temperature record, a trend of slightly high temperature was shown when the fireproofing gypsum board was not bonding, and when the fireproofing gypsum board was bonding, as PF content increased gradually, the temperature was gradually lowered. In terms of the relationship, as time elapsed a low temperature was shown when fiber was mixed, and when the board was bonding, the trend of lower temperature could be confirmed. Meanwhile, in terms of spalling property, a severe explosive fracture was generated at PF 0%, and falling off was prevented as the fiber content was increased; however, discoloration and a multitude of cracks were discovered, and when the board was bonding, the trend in which the exterior became satisfactory when the content was increased emerged. In terms of the residual compressive strength, measuring of strength could not be performed at PF 0% without bonding of board, and the strength was increased as the fiber content was increased; however, there was a decrease in strength of about 30 ~ 40%, and in the case of PF 0% with the bonding of board, the strength could be measured; however, about an 80% decrease in strength was shown, and only about a 10 ~ 20% decline in strength was displayed, as the range of decrease was reduced as the fiber content was increased. Considering all of these factors, it was determined that a more efficient enhancement of fire resistance was obtained when two methods are applied in combination rather than when the PF fiber content and bonding of fireproofing gypsum board are utilized individually.

• Tunnel and Underground Space
• /
• v.14 no.5
• /
• pp.353-362
• /
• 2004

Prediction of fragmentation in bench blasting is one of the most important factors to establish the production plan. It is widely accepted that fragmentation could be accurately predicted using the Kuz-Ram model in bench blasting. Nevertheless, the model has an ambiguous or subjective aspect in evaluating the model parameters such as joint condition, rock strength, density, burden, explosive strength and spacing. This study proposes a new method to evaluate the parameters of Kuz-Ram model, and the predicted mean fragment sizes using the proposed method are examined by comparing the measured sizes in the field. The results show that the predictions using Kuz-Ram model with the proposed method coincide with field measurements, but Kuz-Ram model does not reflect the in-situ rock condition and hence needs to be improved.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.119-120
• /
• 2011

Recently, the effects of high temperature and fiber content on the residual mechnical properties of high-strength concrete were experimentally investigated. In this paper, residual mechanical properties of concrete with water to cement (w/c) ratios of 55%, 42% and 32% exposed to high temperature are compared with those obtained in fiber reinforced concretes of similar characteristics with the ranging of 0,05% to 0,20% polypropylene (PP) fibers by volume of concrete, and considered factors include pre-load levels (20% and 40% of the maximum load at room temperature). Outbreak time and water contents were tested and were determined the compressive strength. In the result, it is showed that to prevent the explosive spalling of 50MPa grade concretes exposed to high temperature need more than 0.05Vol.% PP fibers. Also, the cross-sectional area of PP fiber can influence on the residual mechanical properties and the spalling tendency of fiber reinforced concrete exposed to high temperature. Especially, the external loading increases not only the residual mechanical properties of concrete but also the risk of spalling and the brittle tendency.

• Fire Science and Engineering
• /
• v.25 no.5
• /
• pp.8-13
• /
• 2011

High strength concrete is the occurrence of explosive spalling associated with high temperature such as a fire. The spalling causes the sever reduction of the cross sectional area with the exposure of the reinforcing steel, which originates a problem in the structural behaviour. The purpose of this study is to investigate the mechanical properties of lightweight mortar using perlite and polypropylene fiber for fire protection covering material. For this purpose, selected test variables were the ratio of water to cement, the ratio of cement to perlite, contents of polypropylene fiber. As a result of this study, it has been found that addition of perlite and polypropylene fiber to mortar modifies its pore structure and reduces its density. And it has been found that a new lightweight mortar can be used in the fire protection covering material.

• Advances in concrete construction
• /
• v.9 no.6
• /
• pp.597-610
• /
• 2020

Stress-strain models of fibre reinforced polymer (FRP) confined concrete have been widely investigated; however, the existing load which is always supported by structures during the retrofitting phase, namely 'preload', has been neglected. Thus, preload effects should be clarified, providing insightful information for FRP retrofitting of structures with preload conditions. Towards this aim, experiments were performed for 27 cylinder concrete specimens with the diameter 150 mm and the height 300 mm. Three specimens were used to test the compressive strength of concrete to compute the preloads 20%, 30% and 40% of the average strength of these specimens. Other 24 specimens were divided into 2 groups; each group included 4 subgroups. Four subgroups were subjected to the above preloads and no preload, and were then wrapped by 2 FRP layers. Similar designation is applied to group 2, but wrapped by 3 FRP layers. All specimens were tested under axial compression to failure. Explosive failure is found to be the characteristic of specimens wrapped by FRP. Experimental results indicated that the preload decreases 12-13% the elastic and second stiffness of concrete specimens wrapped by 2 FRP layers. The stiffness reduction can be mitigated by the increase of FRP layers. Preload negligibly reduces the ultimate force and unclearly affects the ultimate displacement probably due to complicated cracks developed in concrete. A mechanism of preload effects is presented in the paper. Finally, to take into account preload effects, a modification of the widely used model of un-preload FRP confined concrete is proposed and the modified model demonstrated with a reasonable accuracy.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.11a
• /
• pp.95-98
• /
• 2006

This study investigates spalling properties of high performance concrete, 60MPa clan, made with the various types of coarse aggregate and adding ratio of polypropylene(PP) fiber. As experimental parameters, totally sixteen specimens of ${\phi}100{\times}200mm$ in size are prepared: one specimen for control without fiber, ten specimens with different coarse aggregate types, along with 0.05, 0.1, 0.15 percent of PP fiber in each. 1 hour fire test is conducted and then spalling appearance, spalling degree and residual compressive strength are examined. In addition, sit specimens made with two types of coarse aggregate site, along with same adding ratio of fiber are supplementally done, and only spalling properties is examined. Test results showed that control concrete and most specimens containing 0.05% of PP fiber exhibited 4 to 3 level of spalling degree, resulting severe explosive spalling, except for the specimen using basalt aggregate(Bc) showing 2 to 3 level of that. Especially, the Bc specimen containing 0.1% of the fiber exhibited that residual compressive strength value was 32%, which is 10% higher than other specimens using limestone or granite. Spalling resistance performance was also effective as aggregate size increase.

• Journal of Fisheries and Marine Sciences Education
• /
• v.26 no.3
• /
• pp.525-534
• /
• 2014

This study has examined the effect of after-school physical activity on body composition and health related fitness of middle school students. The duration of after-school physical activity training program of this study is 12 weeks, the training time in 1 hours warming-up 10 minutes, the skill training 45 minutes and cool down did in 5 minutes. Exercise frequency is 5 time per week. Height basketball class, soccer class, subject class showed statistically meaningful increase between group variance showed statistically meaningful. Weight basketball class, soccer class, showed statistically meaningful decrease. Muscle mass basketball class showed statistically meaningful increase, soccer class showed statistically meaningful decrease. Cardiopulmonary basketball class, soccer class, showed statistically meaningful decrease. Explosive muscular strength basketball class, soccer class, showed statistically meaningful decrease. subject class showed statistically meaningful increase, between group variance showed statistically meaningful. Flexibility basketball class showed statistically meaningful increase, soccer class. Muscular strength basketball class, soccer class, subject class showed not statistically meaningful different.

• The Journal of Korea Robotics Society
• /
• v.17 no.2
• /
• pp.191-197
• /
• 2022

In this research, we developed the muscle-strength-assistant device, named as LEXO-W, and conducted suitability test for army when transporting high weights. LEXO-W relieves the burden when carrying heavy weights by distributing the load concentrated on the arms throughout the body. LEXO-W weighs 4 kg and is designed to handle objects weighing up to 55 kg. To verify the effectiveness of the device, object handling tests (high explosive shell, simple assembly bridges, and ammunition boxes) were conducted. Working time, metabolic rate, and electromyogram (EMG) signals were measured in each test. As a result, it was confirmed that the working time, metabolic rate and EMG signal before and after wearing LEXO-W were decreased. This research has great significance in that it verified the performance of the wearable device from the perspective of military operation.

• Journal of the Korean Ceramic Society
• /
• v.47 no.3
• /
• pp.223-231
• /
• 2010

The serious issue of tall building is to ensure the fire-resistance of high strength concrete. The fire resistant finishing method is necessarily essential in order to satisfy the fire resistance time of 3 h required by the law. The fire resistant finishing method is installed by applying a fire resistant material as a method of shotcrete or a fire resistant board to high strength concrete surface. This method can reduce the temperature increase of the reinforcement embedded in high strength concrete at high temperature due to the installation thickness control. This study is interested in identifying the effectiveness of inorganic alumino-silicate compounds including the inorganic admixture such as fly ash and meta-kaolin as the fire resistant finishing materials through the analysis of fire resistance and components properties at high temperature. The study results show that the fire resistant finishing material composed of fly ash and meta-kaolin has the thermal stability of the slight decrease of compressive strength at high temperature. These thermal stability is caused by the ceramic binding capacity induced by alkali activation reaction by the reason of the thermal analysis result not showing the decomposition of calcium hydrate. Inorganic compounds composed of fly ash and meta-kaolin is evaluated to be very effective as the fire resistance material for finishing to protect the concrete substrate by the reason of those simplicity in both application and manufacture. The additional study about the adhesion in the interface with concrete substrate is necessary for the purpose of the practical application.

• Journal of the Korea Institute of Building Construction
• /
• v.10 no.6
• /
• pp.67-75
• /
• 2010

In this paper, by using steel fiber, polypropylene fiber and these two hybrid fibers, the fire resistance performance and explosive properties of High Strength Concrete (HSC) with specified compressive strength of 40MPa are discussed. The paper also examines the bending resistance of the beam and the shearing resistance properties of non-reinforced HSC beam. This research helps to clarify the fire resistance of fiber HSC and its anti-explosion methods. The test results show that crack generation, explosion and carbonization can be effectively restrained when HSC is mixed with hybrid fibers under high temperature; furthermore, the maximum internal force and ductility are increased and the initial cracking can be restrained in the mechanical test.