• Structural Engineering and Mechanics
• /
• 제64권6권
• /
• pp.793-802
• /
• 2017

The damage of concrete due to the expansion of alkali-aggregate reaction (AAR) and thermal-chemical reactions affecting the strength of concrete is studied. The empirical equations for the variations of expansion of AAR, compressive strength and degradation of the modulus of elasticity with time, and compressive strength with degradation of the modulus of elasticity are proposed by analysing numerous experimental data. It is revealed that the expansion of AAR and compressive strength increase with time. The proposed combination of the time variations of chemical and mechanical parameters provides a satisfactory prediction of the concrete strength. Seismic analysis of the aged Koyna dam is conceded for two different long-term experimental data of concrete incorporating the proposed AAR based properties. The responses of aged Koyna dam reveal that the crest displacement of the Koyna dam significantly increases with time while the contour plots show that major principal stress at neck level reduces with time. As the modulus of elasticity decreases with ages the stress generated in the concrete structure get reduces. On the other hand with lesser value of modulus of elasticity the structure becomes more flexible and the crest displacement becomes very high that cause the seismic safety of the dam reduce.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.541-544
• /
• 2006

This study was performed to proof expansion effect of the mortar bar due to Alkali-silica Reaction (ASR) by ASTM C 1260 test. Recently, the failure case of cement concrete pavement by ASR was reported in Korea. Cement concrete structures are caused crack by ASR. The service life of cracked cement concrete structures by ASR will be shorted. In this study, crushed the slate rock producted Chungcheongnamdo Boryeong was caused 0.3% expansion at 14 days due to ASR by ASTM C 1260 test. The particular spectrum showed that the ASR gel was analyzed contents included Si, Na, K, and Ca by EDX (electron dispersive X-ray spectrometer). It was verified that the crushed aggregate was caused expansion by ASR in Korea.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 학회창립 10주년 기념 1999년도 가을 학술발표회 논문집
• /
• pp.143-146
• /
• 1999

This study is intended to investigate the properties of expansion of concrete under various curing environment with expansive additives. In construction field, expansive additives, which are anaiable to prevent from the diverse cracks caused by drying shrinkage are not expected to accomplish the expantion we expected because of both the absence of the know ledge change, loss of weight and dynamic of elasticty under various unit contents of expansive additives and curing condtion.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 봄 학술발표회 논문집
• /
• pp.613-618
• /
• 2002

Steel slag produced in steel making process is divided with electric arc furnace slag and converter slag. Compared with the blast furnace slag, converter slag has the expansibility due to the reaction with water and free CaO. Therefore it is specified in Standard Specification for Concrete in Korea that steel slag aggregate must not be used in concrete. In this study, we treat electric arc furnace slag aggregate(EAFSA) for concrete before and after several aging process to reduce expansibility. The fundamental properties are measured, which are specific gravity, unit weight, abrasion value and immersion expansion ratio, as concrete aggregate. To understand the suitability of EAFSA for concrete, we made the concrete with EAFSA and then determined the strength and the volume change in EAFSA concrete. From the results EAFSA treated with steam aging process has potentiality for concrete aggregate.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.93-98
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of clear waste glass grading, and by-products(fly ash, blast-furnace slag) and by-products content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum grading can be found. Also, when the by-products are used with waste glass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2010년도 춘계 학술대회 제22권1호
• /
• pp.269-270
• /
• 2010

구조물에서 건조수축에 따른 균열은 간과해서는 안되는 요소로, 팽창재를 사용함에 따라 초기수축균열을 줄여줄 수 있다. 따라서 본 연구에서는 팽창재를 사용한 SHCC의 변형 및 거동에 따른 성능을 평가하기 위하여 건조수축 및 압축 실험을 계획하였으며, 에트링자이트 생성반응에 따른 SHCC의 역학적 특성을 평가하고자 한다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 가을 학술논문 발표대회
• /
• pp.87-88
• /
• 2022

The use of converter slag as an aggregate for concrete is limited due to the risk of expansion. This study analyzed the substances causing the expansion of converter slag and evaluated the possibility of its use as an aggregate for concrete through separation and selection. As a result of the experiment, it was confirmed that CaO and MgO were concentrated in the slag particles inducing expansion, and it was confirmed that it was possible to separate them from non-expanded particles through magnetic.

• 콘크리트학회논문집
• /
• 제14권4호
• /
• pp.597-607
• /
• 2002

우리나라에서 2000년도에 발생된 전기로 및 전로슬래그를 합하면 약 600만 톤 정도로서 주로 도로포장재료 및 매립재 등과 같은 한정된 용도로만 활용되어 왔다. 그 이유는 제강과정 중 유리석회가 슬래그화 되지 않고 불안정한 상태로 슬래그 내부에 잔존하기 때문에 콘크리트 구조물 내에서 팽창을 일으킬 가능성이 클 뿐만 아니라, 팽창이 심할 경우 구조물의 균열 내지는 붕괴까지도 야기 시킬 수 있으므로 콘크리트용 골재로 사용해서는 안 된다고 규정하고 있다. 따라서 제강슬래그를 콘크리트용 골재로 사용하기 위해서는 제강슬래그 자체의 팽창성 억제 내지는 안정화 처리가 우선 해결되어야 할 과제로 생각된다. 본 연구에서는 제강슬래그 골재의 팽창성을 저감시키기 위한 목적으로 6종류의 에이징 방법을 선정하여 안정화의 효율에 대하여 비교 검토하였다. 전로슬래그 골재의 경우, 본 연구에서 실시한 에이징 처리 방법으로서는 콘크리트용 골재로서 요구되는 팽창률을 저감시키는데 한계가 있었을 뿐만 아니라, 에이징 처리한 전로슬래그 골재 사용 콘크리트의 강도도 재령과 더불어 감소하는 문제점이 있음을 확인하였다. 그러나 전기로슬래그 골재를 온수중 및 증기중 에이징 처리할 경우, 팽창률이 전로슬래그 골재의 약 2/3 정도에 지나지 않는 효율을 나타내었으며, 이를 사용한 콘크리트의 강도도 전로슬래그 골재 사용 콘크리트와는 달리 보통콘크리트의 강도에 상응하는 비교적 좋은 결과를 나타내므로 콘크리트용 골재로서 사용 가능성을 시사하였다.

• 콘크리트학회논문집
• /
• 제24권4호
• /
• pp.491-498
• /
• 2012

이 연구는 시멘트 콘크리트 포장의 보수나 프리캐스트 제품용으로 사용되는 UP-MMA 폴리머 콘크리트의 경화수축, 열팽창계수 및 탄성계수에 대한 연구이다. 이를 위해 UP-MMA비, SRA 첨가량, 시험온도 등을 변수로 하여 경화수축 시험과 UP-MMA비에 따른 열팽창과 압축응력-변형률에 대하여 시험을 실시하였다. 그 결과 경화수축은 29.2~$82.6{\times}10^{-4}$으로 UP 비율과 시험온도에 큰 영향을 받는 것으로 나타났다. 그리고 열팽창계수는 21.6~$31.2{\times}10^{-6}/^{\circ}C$, 탄성계수는 2.8~$3.3{\times}10^4MPa$, 극한변형률은 0.00381~0.00418이었으며, 이는 UP-MMA비에 크게 영향을 받는 것으로 나타났다. 이러한 결과들은 UP-MMA 폴리머 콘크리트의 적용을 위한 설계에 중요한 기초자료로 이용될 수 있을 것이다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 봄 학술발표회 논문집(I)
• /
• pp.255-260
• /
• 1998

As a part of the study on the development of augered pile method, this study is intended to investigate the properties of fresh and hardened mortar with the proportion of expansion additives. With the increase of proportion of expansion additives, the fluidity of mortar shows a decrease while air content increases and setting time gets retarded. It show the satisfactory property in strength at 5% of proportion, and shows more expansion with the increase of proportion of expansion additives and sand/cement ratio. In conclusion, both of strength and expansion reveal appropriate at 10% of proportion of expansion additives.