• Journal of the Korean Magnetics Society
• /
• v.17 no.1
• /
• pp.1-5
• /
• 2007

The 1R(Infra-Red) spectrum and PL(Photoluminescence) of the antiferromagnetic pure $MnF_2$ and the single crystal $MnF_2(1.5%\;EuF_3)$ with the rutile structures were measured. The detailed analysis of the measured PL data showed the differences of the optical property between the single crystal $MnF_2(1.5%\;EuF_3)$ and the pure $MnF_2$. It was found that the additional PL peak by the doping of the $EuF_3$ in $MnF_2$ is originated from the f-d transition of $Eu^{3+}$ from the temperature dependent intensity measurement.

• Journal of the Korean Chemical Society
• /
• v.41 no.4
• /
• pp.175-179
• /
• 1997

Luminescence of $Eu^{3+}$ has been studied in $Sr_{2-2x}Eu_xK_xSnO_4$ with two-dimensional $K_2NiF_4$ structure. The $^5D_o$ → $^7F_o$$Eu^{3+}$ ion represents the J=0 → J=0 transition which is forbidden by a Judd-Ofelt selection rule for electric dipole transition in 4f shell of $Eu^{3+}$ ions. However, the emission line of $^5D_o$ → $^7F_o$$Eu^{3+}$ emission spectra of Sr2-2xEuxKxSnO4$Sr_{2-2x}Eu_xK_xSnO_4$structure around $Eu^{3+}$ ions.

• Journal of the Korean Magnetics Society
• /
• v.16 no.5
• /
• pp.261-263
• /
• 2006

In order to investigate the magnetic properties of Eu ions in the single crystal $MnF_2$, the temperature dependent magnetic susceptibilities of the antiferromagnetic $MnF_2$ and the single crystal $MnF_2$(1.5% $EuF_3$) with the rutile structures were measured in the temperature range from 4K to 300K. The detailed analysis of the measured susceptibilities showed that the magnetic susceptibility by the doping of the small amount $EuF_3$ in the antiferromagnetic single crystal $MnF_2$ follows the antiferromagnetic Curie-Weiss law with the negative paramagnetic Curie temperature similarly as in $MnF_2$. It was also found that Eu ion has +3 valence. This solves the long standing discrepancy on this problem.

• Korean Journal of Materials Research
• /
• v.21 no.12
• /
• pp.644-649
• /
• 2011

[ $A_{3-2x/3}Al_{1-z}In_{z}O_4F:Eu_x^{3+}$ ](A = Ca, Sr, Ba, x = -0.15, z = 0, 0.1) oxyfluoride phosphors were simply prepared by the solid-state method at $1050^{\circ}C$ in air. The phosphors had the bright red photoluminescence (PL) spectra of an $A_{3-2x/3}Al_{1-z}In_{z}O_4F$ for $Eu^{3+}$ activator. X-ray diffraction (XRD) patterns of the obtained red phosphors were exhibited for indexing peak positions and calculating unit-cell parameters. Dynamic excitation and emission spectra of $Eu^{3+}$ activated red oxyfluoride phosphors were clearly monitored. Red and blue shifts gradually occurred in the emission spectra of $Eu^{3+}$ activated $A_3AlO_4F$ oxyfluoride phosphors when $Sr^{2+}$ by $Ca^{2+}$ and $Ba^{2+}$ ions were substituted, respectively. The concentration quenching as a function of $Eu^{3+}$ contents in $A_{3-2x/3}AlO_4F:Eu^{3+}$ (A = Ca, Sr, Ba) was measured. The interesting behaviors of defect-induced $A_{3-2x/3}Al_{1-z}In_{z}O_{4-{\alpha}}F_{1-{\delta}}$ phosphors with $Eu^{3+}$ activator are discussed based on PL spectra and CIE coordinates. Substituting $In^{3+}$ into the $Al^{3+}$ position in the $A_{3-2x/3}AlO_4F:Eu^{3+}$ oxyfluorides resulted in the relative intensity of the red emitted phosphors noticeably increasing by seven times.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.1
• /
• pp.15-18
• /
• 2009

To enhance near UV-visible absorption region and to applied phosphor convert-white LEOs (PC-WLEDs), a red phosphor composed of ${Y_2}{SiO_5}:\;EU^{3+}$, $Bi^{3+}$ compounds was prepared by the conventional solid-state reaction. The photoluminescence (PL) shown that samples were excited by near UV light 395 nm for measurement of PL spectra. Emission spectra of samples have shown red emissions at 612 nm ($^5D_0{\to}^7F_2$). The enhanced near $UV{\sim}$ visible excitation spectrum with a broad band centered at 258 nm and 282 nm originated in the transitions toward the charge transfer state (CTS) due to the $Eu^{3+}-Bi^{3+}-O^{2-}$ interaction. The other excitation band at $350\;nm{\sim}480\;nm$, corresponding to the transitions $^7F_0{\to}^5L_9$ (364 nm), $^7F_0{\to}^5G_3$ (381 nm), $^7F_0{\to}^5L_6$ (395 nm), $^7F_0{\to}^5D_3$, (415 nm) and $^7F_0{\to}^5D_2$ (466 nm), occurred due to enhanced the f-f transition increasing $Bi^{3+}$ and $Eu^{3+}$ ions. The PL intensity increased with increased as concentration of $Bi^{3+}$ and the emission intensity becomes with a maximum at 0.125 mol.

• Korean Journal of Materials Research
• /
• v.22 no.5
• /
• pp.215-219
• /
• 2012

Red phosphors $Ca_{1-1.5x}WO_4:{Eu_x}^{3+}$ were synthesized with different concentrations of $Eu^{3+}$ ions by using a solid-state reaction method. The crystal structure of the red phosphors was found to be a tetragonal system. X-ray diffraction (XRD) results showed the (112) main diffraction peak centered at $2{\theta}=28.71^{\circ}$, and the size of crystalline particles exhibited an overall decreasing tendency according to the concentration of $Eu^{3+}$ ions. The excitation spectra of all the phosphors were composed of a broad band centered at 275 nm in the range of 230-310 nm due to $O^{2-}{\rightarrow}W^{6+}$ and a narrow band having a peak at 307 nm caused by $O^{2-}{\rightarrow}Eu^{3+}$. Also, the excitation spectrum presents several strong lines in the range of 305-420 nm, which are assigned to the 4f-4f transitions of the $Eu^{3+}$ ion. In the case of the emission spectrum, all the phosphor powders, irrespective of $Eu^{3+}$ ion concentration, indicated an orange emission peak at 594 nm and a strong red emission spectrum centered at 615 nm, with two weak lines at 648 and 700 nm. The highest red emission intensity occurred at x = 0.10 mol of Eu3+ ion concentration with an asymmetry ratio of 12.5. Especially, the presence of $Eu^{3+}$ in the $Ca_{1-1.5x}WO_4:{Eu_x}^{3+}$ shows very effective use of excitation energy in the range of 305-420 nm, and finally yields a strong emission of red light.

• Journal of the Korean Society of Radiology
• /
• v.13 no.3
• /
• pp.445-451
• /
• 2019

The fluorescence intensity and fluorescence lifetime of $Ba_2GdV_3O_{11}$, a vanadate compound based on $Ba^{2+}$ ion, were investigated by adding $Eu^{3+}$ as a rare earth ion which is an alkaline earth metal, which is distributed around active ions and has a large influence on fluorescent properties when used as a host in a phosphor. $Ba_2GdV_3O_{11}:Eu^{3+}$ phosphor was synthesized by solid state method and the crystallinity of the phosphor was confirmed by X - ray diffraction analysis. The fluorescence properties of the $Ba_2GdV_3O_{11}:Eu^{3+}$ phosphor were measured using optical and laser. The energy transfer and diffusion of the $Ba_2GdV_3O_{11}:Eu^{3+}$ phosphor are highly dependent on the concentration of $Eu^{3+}$. When the concentration of $Eu^{3+}$ is low, it shows strong fluorescence to the CT band. However, as the concentration of $Eu^{3+}$ increases, the fluorescence due to 4f - 4f transition is strong. The concentration of $Eu^{3+}$ ion increased and the energy between ions was diffused, and the lifetime of fluorescence decreased. Energy transfer occurs between two $Eu^{3+}$ ions at low $Eu^{3+}$ concentration and energy diffusion occurs at high $Eu^{3+}$ concentration.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.10
• /
• pp.31-36
• /
• 1999

The $CaSiN_2:Eu$ and $CaSiN_2:Tb$ phosphors were synthesized and analyzed to develop new nitride compound phosphors. $Ca_3N_2$, $Si_3N_4$ and $EuF_3$(or $TbF_3$) powders were mixed, cold-pressed, and sintered to synthesize $CaSiN_2:Eu$ and $CaSiN_2:Tb$ phosphors. Photoluminescence(PL) and electroluminescence(EL) characteristics of the synthesized phosphors were measured and found to be similar to general emission spectra of 뗘 and Tb ion, respecticely. Threshold voltage($V_{th)$) and luminance of the $CaSiN_2:Eu$ TFEL device fabricated by sputtering were 90 V and 1.62 $cd/m^2$ at 280 V, respectively. The charge-voltage(Q-V) and transferred charge-phosphor field($Q_t-F_p$) characteristics of the TFEL devices were also measured.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.3
• /
• pp.234-238
• /
• 2009

In the excitation spectra of $YNbO_4$ : $Eu^{3+}$, the charge transfer (CT) band around 270 nm due to $[NbO_4]^{3-}$$-Eu^{3+}$ interaction and sharp excitation peaks by f-f transition of $Eu^{3+}$ strongly appeared simultaneously. CT band depended on the structural properties of powders, showing the red-shift with increasing the crystallinity, while the f-f transition peaks were independent of the crystallinity. For $YNb_{1-x}Ta_xO_4$ : $Eu^{3+}$ (x = 0.05.0.2), $[TaO_4]^{3-}$. configuration was locally constructed, leading to the blue-shift in CT band and the decrease in the red emission intensity with increasing the Ta content.

• Korean Journal of Materials Research
• /
• v.18 no.3
• /
• pp.137-142
• /
• 2008

Blue-emitting BAM:Eu phosphor powders were formed by post-treatment of precursor powders with hollow or dense morphologies. The morphologies of the precursor powders obtained by spray pyrolysis were controlled by changing the preparation conditions and by changing the type of spray solution. The effects of the morphologies of the precursor powders on the characteristics of the BAM : Eu phosphor powders reacted with $AlF_3$ flux were investigated. Precursor powders with a spherical shape and a hollow morphology produced BAM : Eu phosphor powders with a plate-like morphology, a fine size and a narrow size distribution. On the other hand, precursor powders with a spherical shape and dense morphology produced BAM : Eu phosphor powders with a plate-like morphology and a large size. $AlF_3$ flux improved the photoluminescence intensities of the BAM : Eu phosphor powders. The photoluminescence intensity of the fine-sized BAM : Eu phosphor powders with a plate-like morphology was 90% of the commercial product under vacuum ultraviolet conditions.