• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.37 no.3
• /
• pp.274-279
• /
• 2024

Eu³⁺-doped BaZrO₃ (BaZrO₃:Eu³⁺) phosphor powders were prepared using a solid-state reaction by changing the molar concentration of Eu³⁺ within the range of 0.5 to 30 mol%. Irrespective of the molar concentration of Eu³⁺ ions, the crystal structures of all the phosphors were cubic. The excitation spectra of BaZrO₃:Eu³⁺ phosphors consisted of an intense broad band centered at 277 nm in the range of 230~320 nm. The emission spectra were composed of a dominant orange band at 595 nm arising from the ⁵D₀→⁷F₁ magnetic dipole transition of Eu³⁺ and two weak emission bands centered at 574 and 615 nm, respectively. As the concentration of Eu³⁺ increased from 0.5 to 10 mol%, the intensities of all the emission bands gradually increased, approached maxima at 10 mol% of Eu³⁺ ions, and then showed a decreasing tendency with further increase in the Eu³⁺ ions due to the concentration quenching. The critical distance between neighboring Eu³⁺ ions for concentration quenching was calculated to be 11.21 Å, indicating that dipole-dipole interaction was the main mechanism of concentration quenching of BaZrO₃:Eu³⁺ phosphors. The results suggest that the orange emission intensity can be modulated by doping the appropriate concentration of Eu³⁺ ions.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.3
• /
• pp.112-118
• /
• 2021

Dy³⁺- and Eu³⁺-codoped BaWO₄ phosphors for white light-emitting diode were synthesized with different activator ions via a solid-state reaction process. The structural, morphological, and optical properties of the BaWO₄:Dy³⁺,Eu³⁺ phosphors were investigated as a function of Eu³⁺ concentration at a fixed concentration of Dy³⁺ ions. XRD patterns exhibited that all the synthesized phosphors had a tetragonal system, irrespective of the concentrations of Dy³⁺ and Eu³⁺ ions. The excitation spectra of the synthesized phosphors were composed of three intense bands centered at 251, 355, and 393 nm and several weak peaks. For the BaWO₄:Dy³⁺,Eu³⁺ phosphors synthesized with 1 mol% of Eu³⁺, the emission spectra under ultraviolet excitation at 393 nm showed two strong blue and yellow bands at 485 and 577 nm corresponding to the ⁴F_9/2⁶H_15/2 and ⁴F_9/2⁶H_13/2 transitions of Dy³⁺ ions, respectively and several weak bands in the range of 600-700 nm resulting from the 4f transitions of Eu³⁺ ions. As the concentration of Eu³⁺ ions increased, intensities of the blue and yellow emission bands gradually decreased while those of the red emissions increased rapidly and the energy transfer efficiency from Dy³⁺ to Eu³⁺ ions was 95.3% at 20 mol% of Eu³⁺. The optimum white light emission with x=0.363, y=0.357 CIE 1931 chromaticity coordinates was obtained for the sample doped with 5 mol% Dy³⁺ and 1 mol% of Eu³⁺.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.533-538
• /
• 1998

추출제 Cyanex 301에 대한 NaN $O_3$ 매질에서 Am과 Eu의 추출 및 상호분리 거동에 대해 고찰하였다. Cyanex 301에 대한 Am과 Eu의 추출거동은 매우 유사하여 상호 분리할 수 없었으나 Cyanex 301을 8M NaOH로 비누화 처리하여 NaN $O_3$ 용액 매질에서 Eu에 대한 미량의 Am의 분배계수를 측정한 결과 Am에 대한 선택적 추출성이 높게 나타났다. Cyanex 301의 비누화을, 수용상의 pH 및 Eu 농도가 높아질수록 Am과 Eu의 상호 분리계수인 S $F_{AM}$Eu/는 930까지 증가되었으나 Cyanex 301에 옥탄올을 첨가할 경우에는 S $F_{Am}$ Eu/는 32.3까지 감소하였으며, Am과 Eu의 추출에 미치는 NaN $O_3$ 농도 영향은 없는 것으로 나타났다. Cyanex 301에 추출된 Am과 Eu은 pH가 4인 lM NaN $O_3$ 용액으로는 97.7% 그리고 0.05M DTPA/1.5M Lactic acid에 의해서 99% 이상 역추출되었다.

• Journal of the Korean Chemical Society
• /
• v.41 no.5
• /
• pp.251-255
• /
• 1997

Fluorescence spectra and life time of $Eu^{3+}$ ion in borosilicate glass medium are measured. Electronic transitions of $Eu^{3+}$ ion in borosilicate glass medium are found to come from $5D0{\rightarrow}7FJ$(J=0, 1, 2, 3, 4) transitions of SL coupling system in $f^b$ electrons configuration. From the number of Stark sublevels in spetra, crystal field for $Eu^{3+}$ ion is also found to have the symmetric character of low symmetry order, $n{\leq}2$. The fraction and the number of components of life times were varied depending on the composition of $Eu^{3+}$ in borosilicate glasses, from which the binding condition between the $Eu^{3+}$ ion and anionic oxygen of borosilicate glass can be deduced.

• Journal of the Korean Chemical Society
• /
• v.40 no.1
• /
• pp.59-64
• /
• 1996

The 7F0→5D0excitation spectra of Eu(Ⅲ) complexed with polyfunctional monocarboxylic acid(glycolic acid, glycine and thioglycolic acid) containing a terminal O, N and S neutral donors and propionic acid were investigated using Eu(Ⅲ) luminescence spectroscopy. In the excitation spectra of Eu(Ⅲ)-propionate system, the stepwise appearance of the peaks was observed at 579.0, 579.2 and 579.5 nm with increasing in the ligand-to-metal ratio, which correspond to the formation of Eu(propionate)2+, Eu(propionate)2+ and Eu(propionate)3 species. Three maximum peaks were also obtained for Eu(Ⅲ)-glycolate, Eu(Ⅲ)-glycinate and Eu(Ⅲ)-thioglycolate systems and were found to be quite similar to those of Eu(Ⅲ)-propionate system. The q values (number of coordinated water molecules of Eu(Ⅲ) ion) obtained from the luminescence decay constants of Eu(Ⅲ)-glycolate and Eu(Ⅲ)-thioglycolate were 7.0 and 7.1, and compare well with 7.3 for Eu(Ⅲ)-propionate: Each ligand units replace around two coordinated water molecules. These results show that the polyfunctional monocarboxylates behaves like the propionate for Eu(Ⅲ) ion coordination.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.3
• /
• pp.233-238
• /
• 2000

t-$ZrO_2/Al_2O_3$composites having a superior biocompatability and phase stability were prepared by adding 0~4 mol% of $Eu_2O_3$and sintered for 1 h at $1600^{\circ}C$ to evaluate phase stability, chromaticity and mechanical properties of the composites. No tetragonal to monoclinic phase transformation was observed for the composites containing $Eu_2O_3$after heat treatment for 20 h at $180^{\circ}C$ under 3.5 MPa water vapor pressure condition. As $Eu_2O_3$content increased, the color of the composites was changed from a slight white ivory to a light pink. The strength and the fracture toughness of the composites containing $Eu_2O_3$were above 620 MPa and 7.6 MPa.$m^{1/2}$, respectively, when $Eu_2O_3$was added up to 3 mol%.

• Journal of Powder Materials
• /
• v.24 no.6
• /
• pp.457-463
• /
• 2017

Nanosized $Gd_2O_3:Eu^{3+}$ red phosphor is prepared using a template method from metal salt impregnated into a crystalline cellulose and is dispersed using a bead mill wet process. The driving force of the surface coating between $Gd_2O_3:Eu^{3+}$ and mica is induced by the Coulomb force. The red phosphor nanosol is effectively coated on mica flakes by the electrostatic interaction between positively charged $Gd_2O_3:Eu^{3+}$ and negatively charged mica above pH 6. To prepare $Gd_2O_3:Eu^{3+}$-coated mica ($Gd_2O_3:Eu/mica$), the coating conditions are optimized, including the stirring temperature, pH, calcination temperature, and coating amount (wt%) of $Gd_2O_3:Eu^{3+}$. In spite of the low luminescence of the $Gd_2O_3:Eu/mica$, the luminescent property is recovered after calcination above $600^{\circ}C$ and is enhanced by increasing the $Gd_2O_3:Eu^{3+}$ coating amount. The $Gd_2O_3:Eu/mica$ is characterized using X-ray diffraction, field emission scanning electron microscopy, zeta potential measurements, and fluorescence spectrometer analysis.

• Korean Journal of Materials Research
• /
• v.22 no.5
• /
• pp.215-219
• /
• 2012

Red phosphors $Ca_{1-1.5x}WO_4:{Eu_x}^{3+}$ were synthesized with different concentrations of $Eu^{3+}$ ions by using a solid-state reaction method. The crystal structure of the red phosphors was found to be a tetragonal system. X-ray diffraction (XRD) results showed the (112) main diffraction peak centered at $2{\theta}=28.71^{\circ}$, and the size of crystalline particles exhibited an overall decreasing tendency according to the concentration of $Eu^{3+}$ ions. The excitation spectra of all the phosphors were composed of a broad band centered at 275 nm in the range of 230-310 nm due to $O^{2-}{\rightarrow}W^{6+}$ and a narrow band having a peak at 307 nm caused by $O^{2-}{\rightarrow}Eu^{3+}$. Also, the excitation spectrum presents several strong lines in the range of 305-420 nm, which are assigned to the 4f-4f transitions of the $Eu^{3+}$ ion. In the case of the emission spectrum, all the phosphor powders, irrespective of $Eu^{3+}$ ion concentration, indicated an orange emission peak at 594 nm and a strong red emission spectrum centered at 615 nm, with two weak lines at 648 and 700 nm. The highest red emission intensity occurred at x = 0.10 mol of Eu3+ ion concentration with an asymmetry ratio of 12.5. Especially, the presence of $Eu^{3+}$ in the $Ca_{1-1.5x}WO_4:{Eu_x}^{3+}$ shows very effective use of excitation energy in the range of 305-420 nm, and finally yields a strong emission of red light.

• Journal of the Korean Chemical Society
• /
• v.33 no.1
• /
• pp.82-89
• /
• 1989

The fluorescence of $Eu^{3+},\;Tb^{3+}$ substituted for $La^{3+}$ in Lanthanum Oxychloride (LaOCl) has been studied. The fluorescence intensity of the $Eu^{3+},\;Tb^{3+}$ in LaOCl excited by Ultra-violet light were investigated on its activator concentration and discussed as the energy transfer process. The energy transfer from $Tb^{3+}\;to\;Eu^{3+}$ take place in the $Eu^{3+}\;and\;Tb^{3+}$ codoped LaOCl crystal. This process was confirmed to the change of concentration and the measurement of fluorescence decay time.

• Journal of the Korean Society of Radiology
• /
• v.15 no.3
• /
• pp.391-399
• /
• 2021

Eu²⁺ doped polyphosphate NaSr(PO₃)₃ blue-emitting phosphors were synthesized by the conventional solid state method in a reductive atmosphere. The phase formation of NaSr(PO₃)₃ phosphors were characterized by using the X-ray powder diffraction (XRD) measurement. The photoluminescence emission and excitation spectra of the NaSr(PO₃)₃:Eu²⁺ phosphor, and decay curves were measured. Under the near-UV excitation, the phosphor exhibits a band emission around 420 nm assigned to the 4f⁶5d→f7(8S^7/2) transition of Eu²⁺. The temperature dependent emission spectra and decay curves were measured to elevate the thermal properties of the Eu²⁺ doped phosphors. The as-prepared NaSr(PO₃)₃:Eu²⁺ phosphors show a strong temperature dependent performance, which can serve as a promising temperature sensor.