• Journal of the Korean Chemical Society
• /
• v.34 no.6
• /
• pp.548-554
• /
• 1990

Temperature effects on the fluorescence emission spectra of 0.01 M Eu(III) ion with ClO$_4$, Cl$^-$, NO$_3$ were studied. Relative intensity change of hypersensitive band ($^5D0\; {\to}\;^7F_2$) and nonhypersensitive band ($^5D0 \;{\to}\;^7F_1$) was quite remarkable with temperature and ligand. The relative intensity change was interpreted as the change of formation constant and used to calculation the enthalpy change of $Eu(H_2O)_X^{3+}$+ to EuL(H$_2O)_{X-1}^{2+}$ complex. $\Delta{H}$ of $Eu(H_2O)_X^{3+}$ to EuCl(H$_2O)_{X-1}^{2+}$ was roughly 15 kJ/mol and temperature independent, but $\Delta{H}$ of EuNO$_3(H_2O)_{X-1}^{2+}$ was changed with temperature; -11 kJ/mol at 25$^{\circ}C$ and 47 kJ/mol at 250$^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.1
• /
• pp.67-74
• /
• 2002

A phosphor for Plasma Display Panel, BaMgAl$_{10}$ O$_{17}$ :Eu$^{2+}$, showing a blue emission band at about 450nm was prepared by a solid-state reaction using BaCO$_3$, $Al_2$O$_3$, MgO, Eu$_2$O$_3$ as starting materials wish flux AlF$_3$. The study of the behaviour of Eu in BAM phosphor was carried out by the photoluminescence spectra and the Rietveld method with X-ray and neutron powder diffraction data to refine the structural parameters such as lattice constants, the valence state of Eu, the preferential site of Mg atom and the site fraction of each atom. The phenomenon of the concentration quenching was abound 2.25~2.3wt% of Eu due to a decrease in the critical distance for energy transfer of inter-atomic Eu. Through the combined Rietveld refinement, R-factor, R$_{wp}$, was 8.11%, and the occupancy of Eu and Mg was 0.0882 and 0.526 at critical concentration. The critical distance of Eu$^{2+}$ in BAM was 18.8$\AA$ at 2.25% Eu of the concentration quenching. Furthermore, c/a ratio was decreased to 3.0wt% and no more change was observed over that concentration. The maximum entropy electron density was found that the modeling of $\beta$-alumina structure in BaMgAl$_{10}$ O$_{17}$ :Eu$^{2+}$correct coincided showing Ba, Eu, O atoms of z= 1/4 mirror plane.e.ane.e.

• Korean Chemical Engineering Research
• /
• v.43 no.1
• /
• pp.80-84
• /
• 2005

Nano-sized $Y_2O_3:Eu$ phosphor particles were prepared by ultrasonic spray pyrolysis. The effect of polymeric precursor and lithium carbonate flux on the morphology and luminescence characteristics of nano-sized $Y_2O_3:Eu$ phosphor particles was investigated. When using the spray solution containing both the polymeric precursor and the flux, the $Y_2O_3:Eu$ particles with spherical shape and micron size were turned into nano-sized $Y_2O_3:Eu$ phosphor particles during the post-treatment at high temperature. The mean size of $Y_2O_3:Eu$ phosphor particles was affected by the contents of polymeric precursors and lithium carbonate flux, and preparation temperature. The as-prepared particles by spray pyrolysis at high temperature from solution containing high contents of polymeric precursors had good photoluminescence intensity under vacuum ultraviolet after post-treatment above $1,000^{\circ}C$. The prepared nano-sized $Y_2O_3:Eu$ phosphor particles had comparable photoluminescence intensity under vacuum ultraviolet light with that of the commercial $Y_2O_3:Eu$ phosphor particles prepared by solid state reaction method.

• Korean Journal of Materials Research
• /
• v.27 no.2
• /
• pp.100-106
• /
• 2017

Nanosized and aggregated $Y_2O_3:Eu$ Red phosphors were prepared by template method from metal salt impregnated into crystalline cellulose. The particle size and photoluminescent property of $Y_2O_3:Eu$ red phosphors were controlled by variation of the calcination temperature and time. Dispersed nanosol was also obtained from the aggregated $Y_2O_3:Eu$ Red phosphor under bead mill wet process. The dispersion property of the $Y_2O_3:Eu$ nanosol was optimized by controlling the bead size, bead content ratio and milling time. The median particle size ($D_{50}$) of $Y_2O_3:Eu$ nanosol was found to be around 100 nm, and to be below 90 nm after centrifuging. In spite of the low photoluminescent properties of $Y_2O_3:Eu$ nanosol, it was observed that the photoluminescent property recovered after re-calcination. The dispersion and photoluminescent properties of $Y_2O_3:Eu$ nanosol were investigated using a particle size analyzer, FE-SEM, and a fluorescence spectrometer.

• Journal of the Korean Ceramic Society
• /
• v.43 no.1 s.284
• /
• pp.10-15
• /
• 2006

Photoluminescence (PL) and crystal structures of the $(l-x)CaWO_4-xLi_2WO_4$ binary system added with $Eu_2O_3$ activator have been characterized. The $CaWO_4\;and\;Li_2WO_4$ have the scheelite and phenakite structures respectively. The $CaWO_4-Li_2WO_4-Eu_2O_3$ phosphors show the red luminescence of 613 nm peak wavelength. The wavelength range of excitation spectral band is $380\~470$ nm with the peak wavelength of 397 nm. The $0.88(0.5CaWO_4-0.5Li_2WO_4)-0.12Eu_2O_3$ showed the most superior luminescence characteristics. The effect of co-doping elements such as $Al_2O_3$ and rare-earth oxides on PL has been characterized. The co-doping elements deteriorated the luminescence intensity except the $Al_2O_3$ and $Gd_2O_3$. The PL characteristics of $CaWO_4-Li_2WO_4-Eu_2O_3$ phosphors have been compared to those of the alkali europium double molybdates (tungstates) of scheelite-related structure such as $LiEu(MoO_4)_2$ and $CsEu(MoO_4)_2$. The crystal structures of $(l-y)[(l-x)CaWO_4-xLi_2WO_4]-yEu_2O_3$ phosphors have been characterized using XRD data and rietveld refinement.

• Korean Journal of Materials Research
• /
• v.27 no.10
• /
• pp.534-543
• /
• 2017

$Gd_2O_3:Eu^{3+}$ red phosphors were prepared by template method from crystalline cellulose impregnated by metal salt. The crystallite size and photoluminescence(PL) property of $Gd_2O_3:Eu^{3+}$ red phosphors were controlled by varying the calcination temperature and $Eu^{3+}$ mol ratio. The nano dispersion of $Gd_2O_3:Eu^{3+}$ was also conducted with a bead mill wet process. Dependent on the time of bead milling, $Gd_2O_3:Eu^{3+}$ nanosol of around 100 nm (median particle size : $D_{50}$) was produced. As the bead milling process proceeded, the luminescent efficiency decreased due to the low crystallinity of the $Gd_2O_3:Eu^{3+}$ nanoparticles. In spite of the low PL property of $Gd_2O_3:Eu^{3+}$ nanosol, it was observed that the photoluminescent property was recovered after re-calcination. In addition, in the dispersed nanosol treated at $85^{\circ}C$, a self assembly phenomenon between particles appeared, and the particles changed from spherical to rod-shaped. These results indicate that particle growth occurs due to mutual assembly of $Gd(OH)_3$ particles, which is the hydration of $Gd_2O_3$ particles, in aqueous solvent at $85^{\circ}C$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.3
• /
• pp.123-128
• /
• 2004

Both photoluminescence and the long-phosphorescent properties for $SrAl_2O_4$ : Eu$^{+2}$, $Dy^{+3}$ phosphor powder synthesized by the solid phase reaction were investigated as a function of $B_2O_3$ composition (0-10 wt%). The highest emission wavelength (520nm) of photoluminescence spectra was not affected by $B_2O_3$concentration. The highest emission intensity was obtained by the concentration of 3 wt% $B_2O_3$.After the removal of the Xenon lamp excitation (360nm), also, the excellent long-phosphorescent property of the phosphors was obtained by the concentration of 3 wt% $B_2O_3$ although the decay times for all phosphors decreased exponentially.

• Journal of Sensor Science and Technology
• /
• v.18 no.1
• /
• pp.48-53
• /
• 2009

$Eu^{2+}$-doped ${SrAl_2}{O_4}$ and $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors have been synthesized by conventional solid state method. Photocurrent properties of $Eu^{2+}$ doped ${SrAl_2}{O_4}$ and $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors, in order to elucidate $Dy^{3+}$ co-doping effect, during and after ceasing ultraviolet-ray (UV) irradiation have been investigated. The photocurrent of $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors during UV irradiation was 4-times lower than that of $Eu^{2+}$-doped ${SrAl_2}{O_4}$ during UV irradiation, and 7-times higher than that of $Eu^{2+}$-doped ${SrAl_2}{O_4}$ after ceasing UV irradiation. The photocurrent results indicated that holes of charge carriers captured in hole trapping center during the UV irradiation and liberated after-glow process, and made clear that $Dy^{3+}$ of co-dopant acted as a hole trap. The photocurrent of ${SrAl_2}{O_4}$ showed a good proportional relationship to UV intensity in the range of $1{\sim}5mW/cm^2$, and $Eu^{2+}$-doped ${SrAl_2}{O_4}$ was confirmed to be a possible UV sensor.

• Journal of the Korean Chemical Society
• /
• v.47 no.6
• /
• pp.619-624
• /
• 2003

The $Gd_{1.9-x}Li_{0.1}Eu_xO_3$ (x=0.02, 0.05, 0.08, and 0.12) powders (${\thickapprox}1{\mu}m$) synthesized by sol-gel method, whose surfaces are modified in a colloidal silica suspension (size of $SiO_2$ particles: ${\sim}30$ nm), have been fabricated to highly stable and effective luminescent films on the glass substrates. Thanks to the fused $SiO_2$ nano particles in the vicinity of the glass softening temperature (at around $700^{\circ}C$), $Gd_{1.9-x}Li_{0.1}Eu_xO_3$ powders are strongly attached onto the surface of glass substrate (>9H, pencil hardness tester). This simple and low-cost method to get $Gd_{1.9-x}Li_{0.1}Eu_xO_3$ phosphor films without any loss of luminescence brightness would promise for applications to display devices.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.801-806
• /
• 1998

$Eu^{3+}$ -doped $Y_2$$O_3$ phosphors has been prepared by a polymerized complex method and investigated their powder and luminescence properties. They were compared with phosphors prepared by a solid state reac-thion method. The phosphors synthesized have been characterized by X-ray diffraction low-voltage lu-minescent emission spectroscopy etc. Under low-voltage electron excitation $Eu^{3+}$-doped $Y_2$$O_3$ exhibited a strong narrow-band red emission peaking at 612nm. On the other hand the critical value for concentration quenching of sample prepared by the polymerized complex method fired at $1400^{\circ}C$ is x=0.05 for $(Y_{1-x}Eu_x__2O_3$ The emission intensity of phosphors prepared by the polymerized complex method was higher than that of phosphors prepared by the solid state reaction method.