• JSTS:Journal of Semiconductor Technology and Science
• /
• v.10 no.3
• /
• pp.213-224
• /
• 2010

An optically controlled silicon MESFET (OPFET) was fabricated by diffusion process to enhance the quantum efficiency, which is the most important optoelectronic device performance usually affected by ion implantation process due to large number of process induced defects. The desired impurity distribution profile and the junction depth were obtained solely with diffusion, and etching processes monitored by atomic force microscope, spreading resistance profiling and C-V measurements. With this approach fabrication induced defects are reduced, leading to significantly improved performance. The fabricated OPFET devices showed proper I-V characteristics with desired pinch-off voltage and threshold voltage for normally-on devices. The peak photoresponsivity was obtained at 620 nm wavelength and the extracted external quantum efficiency from the photoresponse plot was found to be approximately 87.9%. This result is evidence of enhancement of device quantum efficiency fabricated by the diffusion process. It also supports the fact that the diffusion process is an extremely suitable process for fabrication of high performance optoelectronic devices. The maximum gain of OPFET at optical modulated signal was obtained at the frequency of 1 MHz with rise time and fall time approximately of 480 nS. The extracted transconductance shows the possible potential of device speed performance improvements for shorter gate length. The results support the use of a diffusion process for fabrication of high performance optoelectronic devices.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.2
• /
• pp.93-98
• /
• 2001

YMnO$_3$ films are excellent gate dielectric materials of ferroelectric random access memories (FRAMs) with MFSFET (metal -ferroelectric-semiconductor field effect transistor) structure because YMnO$_3$ films can be deposited directly on Si substrate and have a relatively low permittivity. Although the patterning of YMnO$_3$ thin films is the requisite for the fabrication of FRAMs, the etch mechanism of YMnO$_3$ thin films has not been reported. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$ film is 285$\AA$/min under Cl$_2$/(Cl$_2$+Ar) of 1.0, RF power of 600 W, dc-bias voltage of -200V, chamber pressure of 15 mTorr and substrate temperature of $25^{\circ}C$. The selectivities of YMnO$_3$ over CeO$_2$ and $Y_2$O$_3$ are 2.85, 1.72, respectively. The selectivities of YMnO$_3$ over PR and Pt are quite low. Chemical reaction in surface of the etched YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy (XPS) surface of the selected YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy(XPS) and secondary ion mass spectrometry (SIMS). The etch profile was also investigated by scaning electron microscopy(SEM)

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.183-183
• /
• 2012

In the era of 45 nm or beyond technology, conventional etch mask using photoresist showed its limitation of etch mask pattern collapse as well as pattern erosion, thus hard mask in etching became necessary for precise control of etch pattern geometry. Currently available hard mask materials are amorphous carbon and polymetric materials spin-on containing carbon or silicon. Amorphous carbon layer (ACL) deposited by PECVD for etch hard mask has appeared in manufacturing, but spin-on carbon (SOC) was also suggested to alleviate concerns of particle, throughput, and cost of ownership (COO) [1]. SOC provides some benefits of reduced process steps, but it also faced with wiggling on a sidewall profile. Diamond like carbon (DLC) was also evaluated for substituting ACL, but etching selectivity of ACL was better than DLC although DLC has superior optical property [2]. Developing a novel material for pattern hard mask is very important in material research, but it is also worthwhile eliminating a potential issue to continuously develop currently existing technology. In this paper, we investigated in-situ dry-cleaning (ISD) monitoring of ACL coated process chamber. End time detection of chamber cleaning not only provides a confidence that the process chamber is being cleaned, but also contributes to minimize wait time waste (WOW). Employing Challenger 300ST, a 300mm ACL PECVD manufactured by TES, a series of experimental chamber cleaning runs was performed after several deposition processes in the deposited film thickness of $2000{\AA}$ and $5000{\AA}$. Ar Actinometry and principle component analysis (PCA) were applied to derive integrated and intuitive trace signal, and the result showed that previously operated cleaning run time can be reduced by more than 20% by employing real-time monitoring in ISD process.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.167-167
• /
• 2011

Magnetic random access memory (MRAM) is one of the prospective semiconductor memories for next generation. It has the excellent features including nonvolatility, fast access time, unlimited read/write endurance, low operating voltage, and high storage density. MRAM consists of magnetic tunnel junction (MTJ) stack and complementary metal-oxide semiconductor (CMOS). The MTJ stack is composed of various magnetic materials, metals, and a tunneling barrier layer. For the successful realization of high density MRAM, the etching process of magnetic materials should be developed. Among various magnetic materials, FePt has been used for pinned layer of MTJ stack. The previous etch study of FePt magnetic thin films was carried out using $CH_4/O_2/NH_3$. It reported only the etch characteristics with respect to the variation of RF bias powers. In this study, the etch characteristics of FePt thin films have been investigated using an inductively coupled plasma reactive ion etcher in various etch chemistries containing $CH_4$/Ar and $CH_4/O_2/Ar$ gas mixes. TiN thin film was employed as a hard mask. FePt thin films are etched by varying the gas concentration. The etch characteristics have been investigated in terms of etch rate, etch selectivity and etch profile. Furthermore, x-ray photoelectron spectroscopy is applied to elucidate the etch mechanism of FePt thin films in $CH_4$/Ar and $CH_4/O_2/Ar$ chemistries.

• Korean Journal of Materials Research
• /
• v.1 no.4
• /
• pp.214-220
• /
• 1991

The effects of $SiO_2$ reactive ion etching (RIE) in $CHF_{3/}C_2F_6$ on the surface properties of the underlying Si substrate were studied by X-ray photoelectron spectroscopy(XPS) and secondary ion mass spectrometry(SIMS) techniques. Angle-resolved XPS analysis was carried out as non-destructive depth profile one for investigating the chemical bonding states of silicion, carbon, oxygen and fluorine. The residue layer consists of C-F polymer. O-F bond was found on the top of the polymer layer and Si-O, Si-C and Si-F bonds were detected between Si substrate and polymer film. A 60nm thick damaged layer of silicon surface mainly contains carbon and fluorine.

• Journal of Surface Science and Engineering
• /
• v.56 no.2
• /
• pp.160-168
• /
• 2023

Recently, investigation on metallization is a key for a stretchable display. Amorphous metal such as Ni and Zr based amorphous metal compounds are introduced for a suitable material with superelastic property under certain stress condition. However, Ni and Zr based amorphous metals have too high resistivity for a display device's interconnectors. In addition, these metals are not suitable for display process chemicals. Therefore, we choose an aluminum based amprhous metal Al-Mo as a interconnector of stretchable display. In this paper, Amorphous Forming Composition Range (AFCR) for Al-Mo alloys are calculated by Midema's model, which is between 0.1 and 0.25 molybdenum, as confirmed by X-ray diffraction (XRD). The elongation tests revealed that amorphous Al-20Mo alloy thin films exhibit superior stretchability compared to pure Al thin films, with significantly less increase in resistivity at a 10% strain. This excellent resistance to hillock formation in the Al20Mo alloy is attributed to the recessed diffusion of aluminum atoms in the amorphous phase, rather than in the crystalline phase, as well as stress distribution and relaxation in the aluminum alloy. Furthermore, according to the AES depth profile analysis, the amorphous Al-Mo alloys are completely compatible with existing etching processes. The alloys exhibit fast etch rates, with a reasonable oxide layer thickness of 10 nm, and there is no diffusion of oxides in the matrix. This compatibility with existing etching processes is an important advantage for the industrial production of stretchable displays.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.213-216
• /
• 2001

Etching behaviors of ferroelectric $YMnO_3$ thin films were studied by an inductively coupled plasma (ICP). Etch characteristic on ferroelectric $YMnO_3$ thin film have been investigated in terms of etch rate, selectivity and etch profile. The maximum etch rate of $YMnO_3$ thin film is $300{\AA}/min$ at $Ar/Cl_2$ of 2/8, RF power of 800W, dc bias voltage of 200V, chamber pressure of 15mTorr and substrate temperature of $30^{\circ}C$. Addition of $CF_4$ gas decrease the etch rate of $YMnO_3$ thin film. From the results of XPS analysis, YFx compounds were found on the surface of $YMnO_3$ thin film which is etched in $Ar/Cl/CF_{4}$ plasma. The etch profile of $YMnO_3$ film is improved by addition of $CF_4$ gas into the $Ar/Cl_2$ plasma. These results suggest that fluoride yttrium acts as a sidewall passivants which reduce the sticking coefficient of chlorine on $YMnO_3$.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.30A no.7
• /
• pp.60-74
• /
• 1993

Experiments of RIE of tungsten films using SF$_{6}$ plasma were conducted to investigate the effect of process parameters on etch rate, uniformity, anisotropy, and selectivity. As power increased, the etch rate increased. Maximum etch rate was obtained at 200mtorr As interelectrode spacing increased the etch rate increased for P < 200mtorr while it decreased for P> 200mtorr. Etch rate was maximum at 20 sccm gas flow rate. As substrate temperature increased, the etch rate increased and activation energy was 0.046 eV. In addition, maximum etch rate was acquired at 20% $O_{2}$ addition. The etch rate slightly increased when Ar was added up to 20% while it continuously decreased when N$_{2}$ was added. Uniformity got improved as pressure decreased and was less than 4% for P <100mtorr. Mass spectrometer was utilized to analyze gas composition and S and F peaks were observed from XPS analysis with increasing power. The anisotropy was better for smaller power and spacing, and lower pressure and temperature. It improved when CH$_{4}$ was added and anisotropic etch profile was obtained when about 10% $O_{2}$ was added. The selectjvity was better for smaller power larger pressure and spacing, and lower temperature. Especially. low temperature processing was proposed as a novel method to improve the anisotropy and selectivity.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.69-69
• /
• 2003

최근 trench capacitor, isolation trench, micro-electromechanical system(MEMS), micro-opto-electromechanical system(MOEMS)등의 다양한 기술에 적용될 고종횡비(HAR) 실리콘 식각기술연구가 진행되어 지고 있다. 이는 기존의 습식식각시 발생하는 결정방향에 따른 식각률의 차이에 관한 문제와 standard reactive ion etching(RIE) 에서의 낮은 종횡비와 식각률에 기인한 문제점들을 개선하기 위해 고밀도 플라즈마를 이용한 건식식각 장비를 사용하여 고종횡비(depth/width), 높은 식각률을 가지는 이방성 트랜치 구조를 얻는 것이다. 초기에는 주로 HBr chemistry를 이용한 연구가 진행되었는데 이는 식각률이 낮고 많은양의 식각부산물이 챔버와 시편에 재증착되는 문제가 발생하였다. 또한 SF6 chemistry의 사용을 통해 식각률의 향상은 가져왔지만 화학적 식각에 기인한 local bowing과 같은 이방성 식각의 문제점들로 인해 최근까지 CHF3, C2F6, C4F8, CF4등의 첨가가스를 이용하여 측벽에 Polymer layer의 식각보호막을 형성시켜 이방성 구조를 얻는 multi_step 공정이 일반화 되었다. 이에 본 연구에서는 SF6 chemistry와 소량의 02/HBr의 첨가가스를 이용한 single_step 공정을 통해 공정의 간소화 및 식각 프로파일을 개선하여 최적의 HAR 실리콘 식각공정 조건을 확보하고자 하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.10
• /
• pp.747-751
• /
• 2010

In the study, the characteristics of the etched Zinc oxide (ZnO) thin films surface, the etch rate of ZnO thin film in $Cl_2/BCl_3/Ar$ plasma was investigated. The maximum ZnO etch rate of 53 nm/min was obtained for $Cl_2/BCl_3/Ar$=3:16:4 sccm gas mixture. According to the x-ray diffraction (XRD) and atomic force microscopy (AFM), the etched ZnO thin film was investigated to the chemical reaction of the ZnO surface in $Cl_2/BCl_3/Ar$ plasma. The field emission auger electron spectroscopy (FE-AES) analysis showed an elemental analysis from the etched surfaces. According to the etching time, the ZnO thin film of etched was obtained to The AES depth-profile analysis. We used to atomic force microscopy to determine the roughness of the surface. So, the root mean square of ZnO thin film was 17.02 in $Cl_2/BCl_3/Ar$ plasma. Based on these data, the ion-assisted chemical reaction was proposed as the main etch mechanism for the plasmas.