• Progress in Superconductivity and Cryogenics
• /
• v.4 no.2
• /
• pp.16-20
• /
• 2002

Bi-axially textured Ni tapes for YBCO coated conductors were Prepared by cold rolling and heat treatment of Ni Powder compacts. The Ni powder used in this study was 5 urn in particle size and 99.99 % in purity. The process of this study consists of filling of hi powder into a rubber mold, cold-isostatically Pressing and sintering of the powder compacts at 110$0^{\circ}C$ for 6h in 96 % Ar - 4 % H$_2$ atmosphere. The sintered compacts were cold rolled with a 5 % step reduction ratio into a 100 micron-thick tapes and then heat-treated at 100$0^{\circ}C$ for various time periods. The (200) texture of Ni tape was successfully developed through the recrystallization heat treatment of the cold rolled Ni tapes. At 100$0^{\circ}C$, the degree of texture of the heat-treated Ni tapes seems not to be significantly affected by the heat-treatment time. The short heat treatment of S min was sufficient to develop the complete (200) cube texture. The degree of in-Plane and out-of-plane texture of the prepared Ni tapes was 8-10$^{\circ}$. The heat treated Ni tapes consisted of equiaxed grains with a size 50-70 microns. and the AFM sol-face roughness was as smooth as 3 nm.

• Korean Journal of Materials Research
• /
• v.26 no.7
• /
• pp.388-392
• /
• 2016

A cold roll-bonding process was applied to fabricate an AA1050/AA6061/AA1050 laminate complex sheet. Two AA1050 and one AA6061 sheets of 2 mm thickness, 40 mm width and 300 mm length were stacked up after surface treatment that included degreasing and wire brushing; material was then reduced to a thickness of 3 mm by one-pass cold rolling. The laminate sheet bonded by the rolling was further reduced to 1.2 mm in thickness by conventional rolling. The rolling was performed at ambient temperature without lubricant using a 2-high mill with a roll diameter of 210 mm. The rolling speed was 5.0 m/sec. The AA1050/AA6061/AA1050 laminate complex sheet fabricated by roll bonding was then hardened by natural aging T4) and artificial aging (T6) treatments. The microstructures of the as-roll bonded and the age hardened Al complex sheets were revealed by optical microscope observation; the mechanical properties were investigated by tensile testing and hardness testing. The strength of the as-roll bonded complex sheet was found to increase by 2.9 times compared to that value of the starting material. In addition, the hardness of the complex sheets increased with cold rolling for AA1050 and age-hardening treatment for AA6061, respectively. After heat treatment, both AA1050 and AA6061 showed typical recrystallization structures in which the grains were equiaxed; however, the grain size was smaller in AA6061 than in AA1050.

• Nuclear Engineering and Technology
• /
• v.50 no.3
• /
• pp.416-424
• /
• 2018

Microstructure of oxide formed on Zr-Nb-Sn tube sample was intensively examined by scanning transmission electron microscopy after exposure to simulated primary water chemistry conditions of various concentrations of Zn (0 or 30 ppb) and dissolved hydrogen ($H_2$) (30 or 50 cc/kg) for various durations without applying desirable heat flux. Microstructural analysis indicated that there was no noticeable change in the microstructure of the oxide corresponding to water chemistry changes within the test duration of 100 days (pretransition stage) and no significant difference in the overall thickness of the oxide layer. Equiaxed grains with nano-size pores along the grain boundaries and microcracks were dominant near the water/oxide interface, regardless of water chemistry conditions. As the metal/oxide interface was approached, the number of pores tended to decrease. However, there was no significant effect of $H_2$ concentration between 30 cc/kg and 50 cc/kg on the corrosion of the oxide after free immersion in water at $360^{\circ}C$. The adsorption of Zn on the cladding surface was observed by X-ray photoelectron spectroscopy and detected as ZnO on the outer oxide surface. From the perspective of $OH^-$ ion diffusion and porosity formation, the absence of noticeable effects was discussed further.

• Korean Journal of Materials Research
• /
• v.4 no.7
• /
• pp.828-836
• /
• 1994

In order to investigate the high temperature deformation characteristics in YBaiCu307-, oxide superconductor, the compression test was performed at temperatures from $890^{\circ}C$ to $930^{\circ}C$ at initial strain rate between $1.0 x 10^{-5}s^{-1}\; and \; 1.0^{-4}s^{-1}$. As the temperature increased and the initial strain rate decreased, the flow stress decreased. The strain rate sensitivity exponent measured as 0.41-0.46, supporting occurence of a superplastic deformation. The activation energy for superplastic deformation was calculated as 500-580KJ/mol, which decreased with increasing Ag content. Microstructure of the superplastically-deformed specimens showed that a grain growth occurred during deformation, and it appeared to be considerable when Ag content increased, but most grains still remained equiaxed after deformation. In this study, the deformation mechanism of YBCO superconductor was the grain boundary sliding with the diffusional accommodation and the contribution of the gram boundary sliding to the total strain was estimated to be 65%.

• Korean Journal of Metals and Materials
• /
• v.49 no.9
• /
• pp.678-685
• /
• 2011

The aim of this study was to determine the effect of applied pressure and sintering temperature on the microstructure and mechanical properties for spark plasma sintering (SPS) from commercial pure titanium (CP-Ti) powders. Spark plasma sintering is a relatively new sintering technique in powder metallurgy which is capable of sintering metal and ceramic powers quickly to full density at a fairly low temperature due to its unique features. SPS of -200 mesh or -400 mesh CP-Ti powders was carried out in an $Ar+H_2$ mixed gas flowing atmosphere between $650^{\circ}C$ and $750^{\circ}C$ under 10 to 80 MPa pressure. When SPS was carried out at relatively low temperatures ($650^{\circ}C$ to $750^{\circ}C$), the high (>60 MPa) pressure had a marked effect on densification and grain growth suppression. The full density of titanium was achieved at temperatures and pressures above $700^{\circ}C$ and 60 MPa by spark plasma sintering. The crystalline phase and microstructure of titanium sintered up to $700^{\circ}C$ consisted of ${\alpha}$-Ti and equiaxed grains. Vickers hardness ranging from 293 to 362 Hv and strength ranging from 304 to 410 MPa were achieved for spark plasma sintered titanium.

• Transactions of Materials Processing
• /
• v.31 no.6
• /
• pp.365-375
• /
• 2022

The microstructure and high-temperature plastic deformation behavior of the modified Al-0.7Mn alloy were investigated and compared with the conventional Al-0.3Mn (Al3102) alloy. α-Al (matrix) and Al₆(Mn, Fe) phases were identified in both alloys. As a result of microstructure observation, both alloys showed equiaxed grains, and Al-0.7Mn alloy showed larger grain size and higher Al₆(Mn, Fe) fraction than Al-0.3Mn alloy. High temperature compressive tests, the deformation temperatures of 410℃, 450℃, 490℃, 530℃ and strain rats of 10^-2/s, 10^-1/s, 1/s, 10/s, were conducted using Gleeble equipment. The flow stress values of Al-0.7Mn alloy were higher than that of Al-0.3Mn alloy at all strain rates and temperature conditions. Constitutive equations were presented using the flow stresses obtained from experimental results and the Zener-Hollomon parameter. In the true stress-true strain curves of the two alloys, the experimental and predicted values were in good agreement with each other. Based on the dynamic material model, eutectic deformation maps of Al-0.7Mn and Al-0.3Mn alloys were suggested, and the plastic instability region was presented. The modified Al-0.7Mn alloy showed a wider plastic instability region than that Al-0.3Mn alloy. Based on the process deformation maps, the MPE tube parts could be manufactured through the actual extrusion process using the suggested conditions.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.8
• /
• pp.66-71
• /
• 2022

Metal additive manufacturing (AM) has revolutionized several manufacturing industries. AM can generate large-scale metal components and produce complex geometries close to net-shapes. WAAM is an AM technology that has garnered considerable interest among industries owing to its economics and relatively high deposition rates. However, the heat accumulation in the weld bead during deposition triggers distortion and residual stress. To address these problems, various methods of interpass pressure rolling systems have been suggested in recent research. In addition, combining the rolling and WAAM processes can mitigate residual stresses. The constant-pressure rolling of the interlayer also affect the microstructure. The coarse microstructure of the as-deposited sample was altered to finer equiaxed grains via these methods. However, the bead-shape accuracy of the interlayer constant-pressure method does not consider the heat accumulation in each layer. Therefore, this study develops an interpass variable pressure rolling system that considers the heat accumulation of each layer. The interpass variable pressure rolling system comprises deposition, detection, pressure, and transport units. Finally, verification tests are performed on the interpass variable-pressure rolling system (at 500 kg) with the WAAM process, and the obtained results are discussed.

• Journal of Korea Foundry Society
• /
• v.42 no.3
• /
• pp.153-160
• /
• 2022

The effect of thickness on the microstructure and the mechanical properties of centrifugal cast 625 was investigated. Centrifugal cast 625 with various thickness of 10, 17 and 50mm showed partially columnar grained structure 8, 12.3 and 18.5mm respectively from the outer surface. Secondary dendrite arm spacing in the columnar grains slightly increased with increasing casting thickness. Tensile strength of the columnar region was similar regardless of casting thickness. Solidification behavior of the columnar grained region is similar to that of directional solidification, thus solidification rate in the centrifugal cast tube was extrapolated from the secondary dendrite arm spacing data of the directionally solidified material. The equiax grained region formed interior of the thick castings. The tensile strength of the equiaxed region showed the average value of the columnar region which is presumably originated from the grain structure rather than secondary dendrite arm spacing.

• Korean Journal of Materials Research
• /
• v.32 no.3
• /
• pp.161-167
• /
• 2022

A cold roll-bonding process is applied to fabricate an AA6061/AA5052/AA6061/AA5052 layered sheet. Two AA6061 and one AA5052 sheets of 2mm thickness, 40mm width and 300mm length are alternately stacked, then reduced to a thickness of 2.0 mm by multi-pass cold rolling after surface treatment such as degreasing and wire brushing. The rolling is performed at ambient temperature without lubricant using a 2-high mill with a roll diameter of 400 mm at a rolling speed of 6.0 m/sec. The roll-bonded AA6061/AA5052/AA6061/AA5052 layered sheet is then hardened by natural aging (T4) and artificial aging (T6) treatments. The microstructure of the as-roll bonded and the age-hardened Al sheets was revealed by SEM observation; the mechanical properties were investigated by tensile testing and hardness testing. After T4 and T6 aging treatment, the specimens had a recrystallization structure consisting of coarse equiaxed grains in both AA5052 and AA6061 regions. The as-roll-bonded specimen showed a clad structure in which the hardness of AA5052 regions was higher than that of AA6061 regions. However, after T4 and T6 aging treatment, specimens exhibited different structures, with hardness of AA6061 regions higher than that of AA5052 regions. Strengths of T6 and T4 age-treated specimens were found to increase by 1.55 and 1.36 times, respectively, compared to the value of the starting material.

• Journal of the Korean Ceramic Society
• /
• v.40 no.8
• /
• pp.751-757
• /
• 2003

Rapid densification of a SiC-30 wt% TiC powder with additive 10 wt% A1$_2$O$_3$-Y$_2$O$_3$-CaO was conducted by Spark Plasma Sintering(SPS). The fully-densified materials can be obtain through the SPS process with very fast heating rate and short holding time. In the present work, the heating rate and applied pressure were kept to be $100^{\circ}C$/min and 40 MPa, while sintering temperature varied from $1600^{\circ}C$ to $1800^{\circ}C$ for 10 min. The full densification of SiC-30 wt% TiC composites with the addition of $Al_2$O$_3$, $Y_2$O$_3$ and CaO was achieved at the temperature above $1700^{\circ}C$ by spark plasma sintering. The XRD found that 3C-SiC and TiC were maintained the entire SPS process temperature, without phase transformation of SiC and formation of YAG phase to $1800^{\circ}C$. The microstructures of the rapidly densified SiC-30 wt% TiC composites consisted of smaller equiaxed SiC grains and larger TiC grains. The biaxial strength of 635.2 MPa and fracture toughness of 6.12 MPaㆍ$m^{1/2}$ were found for the specimen prepared at $1750^{\circ}C$.