The microstructural characteristics and low temperature tensile properties between $25^{\circ}C$ and $-196^{\circ}C$ for as-welded and age hardened specimen by using Al 5083-H321 for base metal, 5083-5356 and 5083-4043 weldments have been investigated. The hardness of 5083-5356 weldment decreases with aging treatment, whereas the weld region of 5083-4043 weldment shows remarkable increase in hardness after aging due to the precipitation of fine Si particle at the grain boundaries and interiors. Low temperature tensile properties of 5083 AI base metal, 5083-5356 and 5083-4043 weldments appear to be the increment of tensile strengths and elongations at the room temperature and $-196^{\circ}C$, while the decrement of tensile properties around $-50^{\circ}C$ is shown. Through the observation of fine serration to fracture in the stress-strain curve and tensile fractography, the increment of localized deformation leading to promote the neck initiation and the increment of the dimple size cause to decrease in tensile strengths and elongations around $-50^{\circ}C$. For the tensile specimen of the 5083 base metal, 5083-5356 and 5083-4043 weldments, the reason to increase in elongation after solution and aging treatment is the diminishment of fine pit, the resolution of Mg into the matrix and the spheridization of the eutectic Si.

• 한국주조공학회지
• /
• 제38권5호
• /
• pp.87-94
• /
• 2018

The effects of Sr and (Ti-B) additives on the tensile properties of AC4A recycled (35% scrap content) aluminum alloys were investigated. An acicular morphology of the eutectic Si phase of as-cast specimens was converted to a fibrous morphology upon the addition of Sr. Moreover, morphology of the Sr modified eutectic Si phase became finer due to a T6 heat treatment. The grain size of the ${\alpha}$-solid solution was decreased by the addition of (Ti-B) additives. Depending on the treatment conditions of the as-cast specimens, i.e., no addition, a Sr addition and a (Ti-B)+Sr addition, the tensile strength levels of the as-cast specimens were 182, 192, and 204MPa, respectively. The corresponding strengths of T6 heat-treated specimens were 293, 308, and 318MPa. Elongations of the as-cast specimens were 2.2, 3.1, and 5.6%, and the corresponding elongations of the T6 heat-treated specimens were 4.6, 6.1, and 7.6%. The percentage of the reduced section area in the tensile specimens was also increased by the Sr and (Ti-B) additives. Sr and (Ti-B) additives changed the microstructure and the distribution of defects in the castings, resulting in an improvement of the tensile properties of AC4A aluminum alloys. According to our test results, recycled (35% scrap content) AC4A aluminum alloy met all of the KS requirements of the tensile strength and elongation values of AC4A aluminum alloy except for the elongation value of the one specimen condition, in this case the as-cast no-addition condition.

• 한국식품과학회지
• /
• 제42권5호
• /
• pp.559-564
• /
• 2010

도복 백미와 무도복 백미로부터 쌀 단백질을 추출하고 쌀 단백질과 curdlan 또는 ${\kappa}$-carrageenan을 일정 비율(3:0, 2:1, 1.5:1.5, 1:2, 0:3)로 혼합하여 복합 필름을 제조한 후 물리적 성질을 비교하였다. 쌀 단백질/curdlan 복합 필름의 경우 인장강도는 curdlan의 혼합비율이 증가할수록 증가하였고, 신장율은 혼합비율이 1.5:1.5일 때 가장 큰 것으로 나타났으며, 수증기투과도는 curdlan의 혼합비율이 증가할수록 감소하는 경향을 보였지만 감소폭은 크지 않았다. 도복미와 무도복미 사이에 물리적 성질의 유의차는 없었다. 쌀 단백질/${\kappa}$-carrageenan 복합 필름의 경우 인장강도는 ${\kappa}$-carrageenan의 혼합비율이 증가할수록 증가하였고, 신장율은 감소하였다. 수증기투과도는 일정한 경향을 보이지 않았다. 또한 도복미와 무도복미로 제조한 쌀 단백질 복합 필름의 물리적 성질사이에 유의차는 없었다.

• 한국작물학회지
• /
• 제51권4호
• /
• pp.287-294
• /
• 2006

Germination and early elongation of rice after germination were investigated in anoxic air treatment, nitric oxide gas treatment, and six concentrations of mercuric chloride solutions to determine the effects of limited oxygen environment, nitric oxide, and inhibited water flux through cell membrane in $17^{\circ}C$. Anoxic air treatment affected germination of tested six varieties very little. However root elongation rates were severely inhibited while shoot growth was affected less. Reductions in shoot and root elongations demonstrated genotypic variations. Nitric oxide delayed the germination of rice even though it didn't affect the final percent germination. Elongations of root and shoot were inhibited in nitric oxide treatment. The inhibitor effect of nitric oxide on the shoot elongation of rice was less severe, while nitric oxide completely inhibited the root emergence of rice. Concentrations of $HgCl_2$ greater than $300{\mu}M$ dramatically reduced the rate and percentage of germination when compared to distilled water treatment. The reduced percent germination showed the greatest variation among rice varieties in $500{\mu}M$ solution of mercuric chloride. Ansanbyeo, Jinheung, and Odaebyeo were affected less by $HgCl_2$, Nonganbyeo and Sangmibyeo were intermediate, and the germination of Andabyeo was greatly reduced by $HgCl_2$. Root elongation of germinated rice seedlings was more sensitive to oxygen deficits, nitric oxide, and $HgCl_2$ treatments than germination and shoot elongation. In conclusion, poor seedling establishment of rice sown in flooded paddy soils, in which the oxygen supply to the seeds is restricted, appears to the result of limited root elongation rate.

• 한국재료학회지
• /
• 제2권4호
• /
• pp.306-310
• /
• 1992

Effects of hafnium, boron and zirconium on the ductility of Ni$_3$(Al, Fe) intermetallic compounds were studied using tensile test and SIMS analysis. Ni$_3$(Al, Fe) alloy with 0.1 at.% Hf, 0.05 at.% B and 0.1 at.% Zr additions showed maximum elongations of about 30% at 300K, 10% at 300K and 14% at 473K, respectively. The fracture mode of the alloy without the additive was the mixture of intergranular and transgranular fractures, but the addition of Hf, Zr or B changed the fracture mode to transgranular only. SIMS analysis showed that the beneficial effects of Hf, Zr or B segregation on the grain boundary strength are consistent with the grain boundary cohesion theory.

• 소성∙가공
• /
• 제24권4호
• /
• pp.241-247
• /
• 2015

In order to prevent shape defects such as fluting and stretcher strains during press forming of aged low carbon steel sheets, roller leveling conditions for reducing yield point elongation were studied. Yield point elongations of leveled sheets were determined as a function of leveling, which is defined as the plastic fraction or the ratio of plastically deformed part in sheet thickness section to the whole thickness of the sheet. By adjusting this plastic fraction during leveling to more than 78%, yield point elongation in the leveled sheets was reduced so no fluting occurred during subsequent tangential bending. Stretcher strains can be avoided by leveling the sheet to an 84% plastic fraction condition.

• 소성∙가공
• /
• 제23권6호
• /
• pp.351-356
• /
• 2014

The current study aims to predict the forming limits considering the deformation characteristics of tailor rolled blank(TRB) during hot stamping. The formability of TRB is affected by the TRB line orientation because elongations change due to the intrinsic geometry within the sheet. To evaluate the forming limits, Nakazima tests were conducted at elevated temperatures with different TRB line orientations. Forming limit diagrams(FLD) of TRB can be predicted by an interpolating equation based on the Nakazima test. Predicted FLDs were used in FE-simulations of a rectangular drawing. The predicted limit drawing height was compared with experimental results. The simulation results show good agreement with the experimental ones with an error range of 3%.

• 한국철도학회논문집
• /
• 제5권1호
• /
• pp.32-39
• /
• 2002

As most railways are gradually electrified with modernized electric cars, the demand for catenary wires and their facilities are also increased. Catenary Wires are exposed to the marine area with air-borne salt or severely polluted industrial area with much corrosive emission gases depending on the locations. Corrosion of catenaty wires can make their actual lifetime shorter than that originally designed. Thus, the messenger and ACSR wires, kinds of catenary wire system, were investigated with respect to corrosion, which include new and used ones collected at the field. Tensile strengths and elongations appeared to decrease when the wires were exposed to corrosive environments. The amount of decrease was more prominent as environmental conditions became more corrosive. They are also vibrated with some amplitude everytime pentographs touch contact line. The frequent cyclic load on the wire may result in a fatigue damage. Surface damage by corrosion can make fatigue crack initiate with ease. In the present study, the fatigue life of the used wire was measured 50 to 60% compared with that of new one in average.

• 제어로봇시스템학회논문지
• /
• 제10권11호
• /
• pp.976-980
• /
• 2004

This study has introduced how to make conducting shape memory polyurethane(CSMPu) as a possible application to smart actuators. Different from conventional polyurethane, CSMPu can have a high conductivity and then electric power supplies enough energy to deform. To prepare conducting polyurethane, carbon nanotubes were incorporated into shape memory polyurethane. Basic experiments to reveal its characteristics have been conducted for a development of actuators. From the results conducted in the present study, optimized conditions for the process of actuating deformation were found. Thermo-electric characteristics such as the relation between temperature and specific resistance and trend curves of resistance variations according to elongations were measured. These data provided a strong possibility of CSMPu as a smart actuator.

• Nuclear Engineering and Technology
• /
• 제52권2호
• /
• pp.352-359
• /
• 2020

The effects of hydrogen precipitation on the mechanical properties of Zircaloy-4 and Zirlo alloys were examined with uniaxial tensile tests at room temperature and at 400 ℃ and accompanying microstructural changes in the Zircaloy-4 and Zirlo alloy specimens were discussed. The elastic moduli of Zircaloy-4 and Zirlo alloys decreased with increasing hydrogen concentrations. Yield strengths of both materials tended to decrease gradually. The reductions of yield stress seems to be caused by the dissipation of yield point phenomena shown in stress-strain curves. Ultimate tensile strengths (UTS) of Zircaloy-4 and Zirlo slightly increased at low hydrogen contents, and then decreased when the concentrations exceeded 500 and 700 wppm, respectively. Uniform elongations were stable until 600 wppm and drops to 0% around 1400 wppm at room temperature.