• 한국표면공학회지
• /
• 제28권1호
• /
• pp.3-13
• /
• 1995

Electroless Ni and Cu platings were conducted on $B_4C$ and SiC. In the electroless Ni plating, the deposition rate on $B_4C$ was higher than on SiC. However, the electroless Cu deposition occured with high deposition rate regardless of the carbide substrates used in this study. Uniformity of the deposits was better in the electroless Cu deposition than in the electroless Ni deposition. In the topographies of the electroless depositions, Ni deposits have grown as colony, whereas Cu deposits have grown as fine individual grains.

• 한국표면공학회지
• /
• 제32권4호
• /
• pp.487-495
• /
• 1999

In order to form metallic electrodes on PZT (Pb (Zr, Ti)O$_3$) ceramics, plating conditions for optimal electroless Ni deposition were investigated. Pb in PZT is the major component to inhibit the electroless deposition, because it plays a active role of catalytic poison in plating solution. Adhesion of the electroless Ni deposits is measured by push-pull scale test and peel test. Results such as deposition ability, deposition rate, and thickness of deposits showed in terms of concentration of etchant, composition of catalyzing solution, and composition and pH of electroless bath solution.

• 한국표면공학회지
• /
• 제55권4호
• /
• pp.202-214
• /
• 2022

Internal connections between device, package and external terminals for connecting packaging and printed circuit board are normally manufactured by electroless Ni-P plating followed by immersion Au plating (ENIG process) to ensure the connection reliability. In this study, a new non-cyanide-based immersion and electroless Au plating solutions using thiomalic acid as a complexing agent and aminoethanethiol as a reducing agent was investigated on different underlayer electroless Ni-P plating layers. As a result, it was confirmed that the deposition behavior and film properties of electroless Au plating are affected by grain size and impurity of the electroless Ni-P film, which is used as the plating underlayer. Au plating on the electroless Ni-P plating film with a dense surface structure showed the highest bonding strength. In addition, the electroless Au plating film on the Ni-P plating film has a smaller particle size exhibited higher bonding strength than that on the large particle size.

• Corrosion Science and Technology
• /
• 제13권3호
• /
• pp.107-111
• /
• 2014

Electroless plated Ni-Co-P films have been used to suppress the electromagnetic waves from magnetic recording media, and the suppression is known to be achieved with films made with optimized plating composition and plating condition. Effects of complexing agents on the deposition rate and bath stability of Ni-Co-P film were studied using sodium citrate, sodium tartrate and multi-complex agents containing both of them. Deposition of electroless Ni-Co-P platings was dependent upon the complexing agents. Deposition rate was twice when using sodium tartrate compared to that using sodium citrate. And it was slightly slower with multi-complex agents than with sodium tartrate, bath stability being declined in the former. Deposition rate increased with increasing pH until pH 11. Excellent bath stability and good deposition rate were obtained using multi-complex agent as sodium citrate 0.10 mol/L and sodium tartrate 0.15 mol/L in the electroless Ni-Co-P plating films.

• 한국표면공학회지
• /
• 제55권5호
• /
• pp.299-307
• /
• 2022

Gold plating is used as a coating of connector in printed circuit boards, ceramic integrated circuit packages, semiconductor devices and so on, because the film has excellent electric conductivity, solderability and chemical properties such as durability to acid and other chemicals. In most cases, internal connection between device and package and external terminals for connecting packaging and printed circuit board are electroless Ni-P plating followed by immersion Au plating (ENIG) to ensure connection reliability. The deposition behavior and film properties of electroless Au plating are affected by P content, grain size and mixed impurity components in the electroless Ni-P alloy film used as the underlayer plating. In this study, the correlation between electroless nickel plating used as a underlayer layer and cyanide-free electroless Au plating using thiomalic acid as a complexing agent and aminoethanethiol as a reducing agent was investigated.

• 한국표면공학회지
• /
• 제36권5호
• /
• pp.393-397
• /
• 2003

The effects of the composition and additives on the blackening and deposition rate of electroless Ni-Zn plating have been examined. Hydrazine resulted in lower sheet resistance of the deposit than sodium hypophosphite. Zinc concentration more than 15 wt% and small amount of ammonium sulfate in the deposits were needed in obtaining Ni-Zn deposit with a black color. An optimum condition was obtained for the black Ni-Zn deposit at an appreciable deposition rate.

• 한국표면공학회지
• /
• 제36권4호
• /
• pp.317-323
• /
• 2003

The effect of additives such as complexing agents, stabilzers and boric acid on the bath stability and the deposition rate of electroless black Ni-Zn plating has been examined. The deposits obtained became black and showed an amorphous structure. The significant increasing in the deposition rate was not found when only glycine and citric acid were used as complexing agents. The deposition rate increased up to 3 and 4 times by adding malic acid and glycolic acid as an additional complexing agent, respectively. The stabilizers and the boric acid, however, had little influence on the deposition rate.

• 한국표면공학회지
• /
• 제47권5호
• /
• pp.269-274
• /
• 2014

Electroless plating process as a solution deposition method is a viable means of preparing conductive metal films on non-conducting substrates through chemical reactions. In the present study, the preparation and properties of electroless Ni-plating on flexible silicone rubber are described. The process has been performed using a conventional Ni(P) chemical bath. Additives and complexing agents such as ammonium chloride and glycine were added and the reaction pH was controlled by NaOH aqueous solution. Ni deposition rate and crystallinity have been found to vary with pH and temperature of the plating bath. It was shown that Ni-films having the high crystallinity, enhanced adhesion and optimum electric conductivity were formed uniformly on silicone rubber substrates under pH 7 at $70^{\circ}C$. The conductive Ni-plated silicone rubber showed a high electromagnetic interference shielding effect in the 400 MHz-1 GHz range.

• 한국재료학회지
• /
• 제24권11호
• /
• pp.632-638
• /
• 2014

We investigated the effects of DMAB (Borane dimethylamine complex, C2H10BN) in electroless Ni-B film with addition of DMAB as reducing agent for electroless Ni plating. The electroless Ni-B films were formed by electroless plating of near neutral pH (pH 6.5 and pH 7) at $50^{\circ}C$. The electroless plated Ni-B films were coated on screen printed Ag pattern/PET (polyethylene terephthalate). According to the increase of DMAB (from 0 to 1 mole), the deposition rate and the grain size of electroless Ni-B film increased and the boron (B) content also increased. In crystallinity of electroless Ni-B films, an amorphization reaction was enhanced in the formation of Ni-B film with an increasing content of DMAB; the Ni-B film with < 1 B at.% had a weak fcc structure with a nano crystalline size, and the Ni-B films with > 5 B at.% had an amorphous structure. In addition, the Ni-B film was selectively grown on the printed Ag paste layer without damage to the PET surface. From this result, we concluded that formation of electroless Ni-B film is possible by a neutral process (~green process) at a low temperature of $50^{\circ}C$.

• 한국분말재료학회지
• /
• 제10권3호
• /
• pp.195-200
• /
• 2003

Ni coated $Al_2O_3$ composite was successfully Prepared by the electroless deposition Process. The average size of Ni particles coated on the $Al_2O_3$ matrix powder was about 20 nm. It was hard to find any reaction compound as an impurity at interface between $Al_2O_3$ and Ni particles after sintering. The characterization of microstructure crystal structure and fracture behavior of the sintered body were investigated using XRD, TEM and Victors hardness tester, and compared with those of the sintered $Al_2O_3$ monolithic body. Many dislocations were observed in the Ni phase due to the difference of thermal expansion coefficient between $Al_2O_3$ and Ni phase, and no observed microcracks at their $Al_2O_3$ and Ni interface. In the $Al_2O_3$/Ni composite, the main fracture mode showed a mixed fracture with intergranular and transgranuluar type having some ,surface roughness. The fracture toughness was slightly increased due to the plastic deformation mechanism of Ni phase in the $Al_2O_3$/Ni composite.