• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.3
• /
• pp.51-56
• /
• 2015

It has been used various pad finish materials to enhance the reliability of solder joint and recently Electroless Ni Electroless Pd Immersion Gold (the following : ENEPIG) pad has been used more than others. This study is about reliability according to being used in commercial Electrolytic Ni pad and ENEPIG pad, and was observed behavior of various Cu contents. After reflow, the inter-metallic compound (IMC) between solder and pad is composed of $Cu_6Sn_5$ (Ni substituted) by using EDS, and in case of ENEPIG, between IMC and Ni layer was observed the dark layer ($Ni_3P$ layer). Additional, it could be controlled the thickness of dark layer according to Cu contents. Investigated the different fracture mode between electrolytic Ni and ENEPIG pad after drop shock test, in case of soft Ni, accelerated stress propagated along the interface between $1^{st}$ IMC and $2^{nd}$ IMC, and in case of ENEPIG pad, accelerated stress propagated along the weaken surface such as dark layer. The unstable interface exists through IMC, pad material and solder bulk by the lattice mismatch, so that the thermal and physical stress due to the continuous exterior impact is transferred to the IMC interface. Therefore, it is strongly requested to control solder morphology, IMC shape and thickness to improve the solder reliability.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2011.06a
• /
• pp.153-154
• /
• 2011

• Journal of the Korean institute of surface engineering
• /
• v.43 no.3
• /
• pp.142-147
• /
• 2010

We evaluated characteristics of ENEPIG (Electroless Nickel Electroless Palladium Immersion Gold) surface treatment for mobile equipment that requires high reliability, in addition to investigating surface treatment processes for semiconductor boards that require high reliability such as regular PCB-package systems, board-on-chip, chip-scaled package (CSP), etc and application for semiconductor package board of SIP, BOC. As a result, it appeared that ENEPIG has superior properties compared to ENIG surface treatment in corrosion resistance, solder junction, wetting, etc. We anticipate that these results will be able to lend credibility to ENEPIG as a low-cost alternative for producing mobile devices such as the cell phones, especially when applied to mass production.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.179-180
• /
• 2009

본 연구에서는 ENIG, ENEPIG 의 Pad 표면처리가 고속전단시험에 미치는 영향에 대해 연구하고자 하였다. Pad의 표면처리를 ENIG와 ENEPIG로 하여 고속전단시험을 수행하여 그에 따른 Shear force와 Shear energy를 측정하였다. 고속전단시험결과 ENEPIG 표면처리 시편이 ENIG의 표면처리시편보다 shear force와 shear energy의 값이 높게 나타났다.

• Journal of Welding and Joining
• /
• v.35 no.3
• /
• pp.1-6
• /
• 2017

The effect of metal turnover (MTO) of electroless Ni plating bath on the brittle fracture behavior of electroless nickel electroless palladium immersion gold (ENEPIG)/Sn-3.0wt%Ag-0.5wt%Cu(SAC305) solder joint was evaluated in this study. The MTOs of the electroless Ni for the ENEPIG surface finish were 0 and 3. As the MTO increased, the interfacial IMC thickness increased. The brittle fracture behavior of the ENEPIG/SAC305 solder joint was evaluated with high speed shear (HSS) test. The HSS strength decreased with increasing the MTO of the electroless Ni bath. The brittle fracture increased with increasing the shear speed of the HSS test. The percentage of the brittle fracture for the 3 MTO sample was much higher than that for the 0 MTO sample.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.1
• /
• pp.83-90
• /
• 2017

In this paper, we evaluated the solderability of thin electroless nickel-electroless palladium-immersion gold (ENEPIG) plating layer for fine-pitch package applications. Firstly, the wetting behavior, interfacial reactions, and mechanical reliability of a Sn-3.0Ag-0.5Cu (SAC305) solder alloy on a thin ENEPIG coated substrate were evaluated. In the wetting test, maximum wetting force increased with increasing immersion time, and the wetting force remained a constant value after 5 s immersion time. In the initial soldering reaction, $(Cu,Ni)_6Sn_5$ intermetallic compound (IMC) and P-rich Ni layer formed at the SAC305/ENEPIG interface. After a prolonged reaction, the P-rich Ni layer was destroyed, and $(Cu,Ni)_3Sn$ IMC formed underneath the destroyed P-rich Ni layer. In the high-speed shear test, the percentage of brittle fracture increased with increasing shear speed.

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.3
• /
• pp.51-56
• /
• 2014

The reliability of solder joint is significantly affected by the property of surface finish. This paper reports on a study of high speed shear energy and failure mode for Sn-4.0wt%Ag-0.5wt%Cu (SAC405) solder joints with the time of Pd activation. The nodule size of electroless Ni-P deposit increased with increasing the time of Pd activation. The roughness (Ra) of electroless Ni-P deposit decreased with increasing the time of Pd activation. Then, with $HNO_3$ vapor, the quasi-brittle and brittle mode of SAC405 solder joint decreased with increasing the time of Pd activation. This results indicate that the increase in the Pd activation time for Electroless Ni/ Electroless Pd/ Immersion Au (ENEPIG) surface finish play a critical role for improving the robustness of SAC405 solder joint.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.3
• /
• pp.63-71
• /
• 2022

In this study, the interfacial reaction and drop impact reliability of Sn-Ag-Cu (SAC) solder and electroless nickel autocatalytic gold (ENAG) were studied. In addition, the solder joint properties with the ENAG surface finish was compared with electroless nickel immersion gold (ENIG) and electroless nickel electroless palladium immersion gold (ENEPIG). The IMC thickness of SAC/ENAG and SAC/ENEPIG were 1.15 and 1.12 ㎛, respectively, which were similar each other. The IMC thickness of the SAC/ENIG was 2.99 ㎛, which was about two times higher than that of SAC/ENAG. Moreover, it was found that the IMC thickness of the solder joint was affected by the metal turnover (MTO) condition of the electroless Ni(P) plating solution, and it was found that the IMC thickness increased when the MTO increased from 0 to 3. The shear strength of SAC/ENEPIG was the highest, followed by SAC/ENAG and SAC/ENIG. It was found that when the MTO increased, the shear strength was lowered. In terms of brittle fracture, SAC/ENEPIG was the lowest among the three joints, followed by SAC/ENAG and SAC/ENIG. Likewise, it was found that as MTO increased, brittle fracture increased. In the drop impact test, it was confirmed that the 0 MTO condition had a higher average number of failures than the 3 MTO condition, and the average number of failures was also higher in the order of SAC/ENEIG, SAC/ENAG, and SAC/ENIG. As a result of observing the fracture surface after the drop impact, it was found that the fracture was between the IMC and the Ni(P) layer.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.194-195
• /
• 2009

본 연구에서는 고속전단 강도에 표면 처리의 변화가 미치는 영향에 대해 연구하고자 하였다. 표면 처리를 ENIG, ENEPIG, OSP로 하여 고속전단시험을 수행하였다. 고속전단 결과 SAC105의 전단 강도 값은 ENIG가 가장 작았고, ENEPIG가 가장 높았다. SAC305의 전단 강도 값은 ENIG가 가장 작았고, OSP와 ENEPIG는 비슷한 값을 나타냈다.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.3
• /
• pp.11-17
• /
• 2009

The drop impact reliability comes to be important for evaluation of the life time of mobile electronic products such as cellular phone. The drop impact reliability of solder joint is generally affected by the kinds of pad and reflow number, therefore, the reliability evaluation is needed. Drop impact test proposed by JEDEC has been used as a standard method, however, which requires high cost and long time. The drop impact reliability can be indirectly evaluated by using high speed shear test of solder joints. Solder joints formed on 3 kinds of surface finishes OSP (Organic Solderability Preservation), ENIG (Electroless Nickel Immersion Gold) and ENEPIG (Electroless Nickel Electroless Palladium Immersion Gold) was investigated. The shear strength was analysed with the morphology change of intermetallic compound (IMC) layer according to reflow number. The layer thickness of IMC was increased with the increase of reflow number, which resulted in the decrease of the high speed shear strength and impact energy. The order of the high speed shear strength and impact energy was ENEPIG > ENIG > OSP after the 1st reflow, and ENEPIG > OSP > ENIG after 8th reflow.