• 한국세라믹학회지
• /
• 제40권12호
• /
• pp.1154-1158
• /
• 2003

Hydrothermal deposition of hydroxyapatite coatings on $Al_2$O$_3$ substrates was studied using aqueous solutions of Ca(NO$_3$)$_2$ㆍ4$H_2O$ and (NH$_4$)$_2$HPO$_4$ containing EDTA disodium salt as a chelating agent for $Ca^{2+}$. For the precipitation of the coatings the EDTA-Ca$^{2+}$ chelates were dissociated thermally at 20$0^{\circ}C$ or decomposed by oxidation with $H_2O$$_2$ at 9$0^{\circ}C$. Scanning electron microscopy and X-ray diffraction were used to investigate the deposition behavior and the phase of the coatings. Hydroxyapatite coatings were not deposited with the thermal dissociation method, whereas uniform deposition of the coatings (about 0.7 $\mu\textrm{m}$ thickness) was obtained with the oxidative decomposition method. The coatings consisted of fine rod-like hydroxyapatite crystals (hexagonal structure) with 60-80 nm diameters, having some preferred orientation with their length (i.e., the c axis) perpendicular to the substrate.ate.

• Korean Chemical Engineering Research
• /
• 제51권6호
• /
• pp.733-738
• /
• 2013

퇴적토는 미사 및 점토와 같은 미세토의 함량이 높으며, 유기물질이 많으며, 완충능이 크기 때문에 퇴적토로부터 중금속을 제거하는 것은 매우 어렵다. 본 연구에서는, 중금속으로 오염된 퇴적토에서 중금속을 제거하기 위해 2 V/cm의 일정한 전압경사를 적용한 실험실 규모의 전기동력학적 (EK) 정화공법을 사용하였다. 실험을 위해 적용한 음극 전해질로는 0.1 M의 ethylenediaminetetraacetic acid (EDTA), citric acid (CA), $HNO_3$, HCl, 그리고 수돗물을 사용하였으며, 양극 전해질로는 수돗물을 사용하여 순환시켜 주었다. 음극 전해질로 CA를 사용한 실험군에서 Ni, Cu, Zn, Pb는 각각 초기와 비교하여 92.4, 96.1, 97.1, 88.1%의 중금속 제거효율을 보였다. 높은 전압경사를 적용하게 되면, 음극 전해질내에 citrate 및 EDTA가 퇴적토로 이동이 용이하게 되며, 그로 인해 중금속-킬레이트 화합물을 형성하여 중금속의 추출률을 높일 수 있었다. 이러한 결과를 바탕으로, 높은 전압경사를 적용한 EK 실험에서 음극 전해질로 EDTA 혹은 CA를 사용하면 퇴적토로부터 중금속을 효과적으로 추출할 수 있다고 판단된다.

• 한국세라믹학회지
• /
• 제43권8호
• /
• pp.463-468
• /
• 2006

Hydrothermal deposition of hydroxyapatite coatings on two types of $ZrO_2$ substrates (3 mol% $Y_2O_3$-doped and 13 mol% $CeO_2$-doped tetragonal $ZrO_2s$) was studied using aqueous solutions of $Ca(NO_3)_2\;4H_2O$ and $(NH_4)_2HPO_4$ containing EDTA (ethylene diamine tetra acetic acid) disodium salt as a chelating agent for $Ca^{2+}$ ions. For the precipitation of the coatings, the $EDTA-Ca^{2+}$ chelates were decomposed by oxidation with $H_2O_2$ at $90^{\circ}C$. The deposition behavior, morphology, and orientation of the coatings were investigated while varying the solution pH using scanning electron microscopy and X-ray diffractometry. For the two sub-strates, sparse deposition of the coating was obtained at pH 5.5, whereas a uniform deposition was obtained at pH 7.1, 9.8, and 11.4 with a denser microstructure for the higher pH. The coating consisted of thin needle-like or plate-like crystals ($1-2{\mu}m$ length or diameter) at pH 7.1, but fine rod-like crystals ($1-2{\mu}m$ length, $0.1{\mu}m$ diameter) at pH 9.8 and 11.4. The coatings were $1-3{\mu}m$ thick and showed a preferred orientation of the hydroxyapatite crystals with their c axis (i.e., the elongated direction) perpendicular to the substrate surface especially for pH 9.8 and 11.4.

• 농업과학연구
• /
• 제32권1호
• /
• pp.71-80
• /
• 2005

본 연구에서는 phytic acid가 금속이온이나 양이온을 chelate시키는 작용이 탁월하며, 특히 $Fe^{2+}$나 $Ca^{2+}$에 대해서 친화성이 높다는 점을 착안하여, 사람이 평소에 쉽게 섭취하고 식용이 가능하며 인체에 무해한 장점이 있는PA가 EDTA를 대체할 수 있는지 여부를 알아보았고, 실제 동물 실험을 통해 생존율 효과에 얼마나 영향이 미치는지를 관찰한 결과이다. 1. 살균적 Osmotic Shock 및 Chelating Agent의 강화효과 1) 초기 실험에 투입된 균수를 측정한 결과 $1.7{\times}10^6cfu/ml$ 이었으며 증류수에 의한 osmotic shock을 받은 균의 생존균수는 $Mg^{2+}$ 경우 접종 후 1분에서 92.5%, 3분에서 91.8%, 5분에서 79.8%로 평균 88%로 큰 차이 없는 살균효과를 나타났다. 2) 증류수에 의한 osmotic shock을 받은 균은 접종 후 1분에서 83.5%, 3분에서 70.0%, 5분에서 60.2%로 평균 71.2%로 비교적 완만한 살균효과를 나타났다. 3) EDTA 및 PA 용액은 0.1mM 농도의 경우 보다 1mM 농도에서 osmotic shock가 극적으로 강화되는 경향을 알 수 있었다. 2. Phytic acid의 Vibrio vulnificus 패혈증 마우스 생존율에 미치는 영향 V. vulnificus 패혈증에 미치는 영향을 관찰한 결과 고농도의 경우 마우스의 평균 사망시간은 348분이였으나 저농도인 경우 마우스의 평균 사망시간이 1246분으로 고농도 보다 3.6배나 오랜시간 생존한 것으로 나타났다. CaEDTA의 처치군 고농도의 경우 평균 생존시간은 387분으로 대조군 348분으로 약간의 생존시간 증가의 경향을 관찰 할 수 있었고 저 농도의 경우 평균 생존시간은 669분으로 고농도에 비해 생존시간이 1.8배 정도 증가하는 경향을 관찰할 수 있었다. 그러나 phytic acid농도의 영향은 있지만 저농도에서는 생존시간이 훨씬 늘어났다. 따라서, 마우스의 접종실험결과 병원균인 V. vulnificus의 접종농도와 마우스의 치사속도가 정의 상관관계가 있는 것으로 나타났다. 3. phytic acid가 간이 손상된 마우스의 Vibrio vulnificus 패혈증에 미치는 영향 사염화탄소로 간을 파괴시킨 마우스를 사용하여 정상 마우스(대조군)와 비교한 결과, 간 손상이 없는 대조군에 비해 1.5배 빠른 사망 속도로 나타나, 기저질환인 간장질환 등을 앓고 있는 사람이 V. vulnificus에 감염될 경우 치사 속도가 치명적임을 간접적으로 관찰할 수 있었다. 마우스에 V. vulnificus의 접종량을 달리한 결과 $2.3{\times}10^7cfu/ml$에서는 접종 후 평균 생존시간은 226분이었고, $0.8{\times}10^6cfu/ml$에서는 접종 후 평균 생존시간은 300분으로 두 농도간 사망속도는 1.3배로 죽어가는 양상은 비슷하였으나, 기저 질환이 없을지라도 치사속도는 접종량에 크게 의존하고 있음을 알 수 있었다.