• 한국재료학회지
• /
• 제14권12호
• /
• pp.893-899
• /
• 2004

Even though Ti-6Al-4V has gained popularity as an implant material, the possible dissolution of Al and V ions in body fluids remains a matter of concern. Though commercially pure Ti (Cp-Ti) overcomes this problem, the mechanical strength of pure titanium remains very low. Thus, in this experiment Cp-Ti was processed by Equal channel angular processing (ECAP), in order to increase the mechanical strength. The biocompatibility of ECAP-Ti, Cp-Ti and Ti-6Al-4V was examined by the apatite formation on each sample surface, after treating the surface with 5M NaOH and soaking in Simulated body fluids (SBF). Initially, the samples were mechanically polished on silicone carbide paper (#2000). The polished samples were treated with 5M NaOH solution at $60^{\circ}C$ for 24 hours. The NaOH treated samples were washed gently with distill water and dried at $40^{\circ}C$ for 1 day. The dried samples were heat treated in air at $600^{\circ}C$ for 1 hour. The surface morphology of these samples were studied using SEM and XRD. The SEM studies showed network of pores in all samples. The XRD showed oxide layer formation on Cp-Ti and Ti-6Al-4V. samples. However the oxide layer in ECAP-Ti was not substantial. These samples were immersed in SBF, kept at $36.5^{\circ}C$ for seven days period. At the end of 7 days, the apatite formation was confirmed only on Cp-Ti and was not observed in Ti-6Al-4V and ECAP-Ti. These observations of apatite formation relate to the fact that Cp-Ti showed greater oxide layer than other samples. The apatite examined was confirmed as tricalcium phosphate (TCP) using EDS and XRD.

• 한국재료학회지
• /
• 제15권9호
• /
• pp.585-588
• /
• 2005

Titanium and Titanium alloys are widely used as an orthopedic and dental implant material because of their excellent biocompatibility and mechanical strength. In this study, ECAP Cp-Ti and Cp-Ti were heat treated for different annealing time of 30 min, 90 min and 3 hours. The grain size for each condition was studied. The micro-Vicker hardness test was carried out f3r each different heat treated samples. The micro-Vicker hardness test for ECAP Cp-Ti, Cp-Ti and Cp-Ti (3hr) revealed hardness values of 239.5, 182 and 144 Hv, respectively. The grain size was increased from approximately $70{\mu}m\;to\;300{\mu}m$ with the increase in heat treatment time from 30 min to 3 hours. The heat treated samples were tested for their biocompatibility in simulated body fluid (SBF) and corrosion rates was determined using Polarization Curve test (PCT). The PCT results showed Cp-Ti with comparatively high corrosion potential of -0.18 V and corresponding corrosion current of $2\times10^{-6}$ A, while the corrosion rate in ECAP Cp-Ti and Cp-Ti (30 min annealed) showed very similar results of corrosion potential about -0.47 V with corresponding corrosion current of $7\times10^{-8}$ A.

• 한국재료학회지
• /
• 제14권6호
• /
• pp.432-435
• /
• 2004

Ti and Ti alloys are important materials for medical and dental applications. The effect of equal channel angular process(ECAP) and addition of Fe in Ti were studied with optical microstructure and corrosion behavior. Fine grains in Ti was obtained after ECAP. Corrosion behavior of commercial pure(CP)-Ti and Ti alloys was studied by open circuit test and polarization curve test(PCT) at $36.5^{\circ}C$ with SBF in biological environment. The corrosion behavior of ECAP-Ti was similar to that of CP-Ti in PCT, but Ti-Fe alloys were observed to become more corrosive with increasing Fe content.

• 공학논문집
• /
• 제8권1호
• /
• pp.23-30
• /
• 2006

• 한국재료학회지
• /
• 제15권10호
• /
• pp.671-677
• /
• 2005

Ti and Ti alloys are known to have excellent corrosion properties, which is an important aspect for biocompability of these implants in human body. In our study, four types of samples (Cp-Ti, Ti-6Al-4V, $0.5wt.\%$ Fe-Ti and ECAP Ti) were tested for their apatite forming ability and corrosion properties. The micropolished samples were treated with 5M NaOH solution at $60^{\circ}C$ for 24 hours. Each samples was gently washed with distilled water and heat-treated at 600"C for 1 hour. The heat-treated samples were soaked in Simulated Body Fluid (SBF) solution at $36.5^{\circ}C$ in an incubator for different period of time. The test revealed that $0.5 wt.\%$ Fe-Ti showing faster apatite growth on the surface (7th day) compared to other samples. Polarization curve test (PCT) was also carried out to determine the corrosion resistance of each samples in SBF solution. ECAP-Ti showed highest corrosion resistance compared to any other samples. $0.5wt.\%Fe-Ti$ showed higher corrosion potential and corrosion current compared to other samples.