• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.11 no.6
• /
• pp.725-732
• /
• 1999

It is usual to use hydrophilic-coated aluminum foil for evaporator fin of air-conditioners to reduce air flow resistance caused by the water droplets condensed on the fin surface. The major effect of a hydrophilic coating is to reduce the contact angle of the condensate and prevent bridging of the condensate between the adjacent fins. The performance of hydrophilic coating generally tends to be degraded as it is used since the coating material is washed down by the condensate. In the present work, several types of hydrophilic coatings were evaluated in terms of durability of hydrophilicity, corrosion resistance and heat resistance. Results showed that an improved hydrophilic coating of resin type presented superb qualify in terms of durability and corrosion resistance while having almost the same level of qualify in heat resistance compared with the others.

• Textile Coloration and Finishing
• /
• v.15 no.4
• /
• pp.51-56
• /
• 2003

Poly(ethylene terephthalate) (PET) fabrics were dyed with a series of ethoxylated alkylaminoanthraquinone dyes synthesized by the reaction of 1-aminoanthraquinone with poly(ethylene glycol) via a series of methylene spacer, and their hydrophilicity and durability to laundering were investigated. The results obtained are as follows: 1) Ethoxylated alkylaminoanthraquinone were successfully exhausted on PET fabric without any aid of chemical auxiliary. 2) The wettability of the dyed PET fabric was increased with the length of ethoxylate chain. 3) The durability of the wettability was good enough as to maintain the initial wettability even after 30 repeated launderings.

• Computers and Concrete
• /
• v.23 no.5
• /
• pp.351-359
• /
• 2019

In this study, the calcium hydroxide, an inherent product of cement hydration, was treated using biomimetic carbonation method of incorporating stearic acid to generate the hydrophobic calcium carbonate on concrete surface. Carbonation reaction was carried out at various $CO_2$ pressure and temperatures and utilizing the Scanning Electron Microscope (SEM), chloride-ion penetration test apparatus, and compression test machine to investigate the hydrophobicity, durability, and mechanical properties of the synthesized products. Experimental results indicate that the calcium stearate may change the surface property of concrete from hydrophilicity to hydrophobicity. Increasing reaction temperature can change the particles from irregular shapes to needle-rod structures with increased shear stress and thus favorable to hydrophobicity and microhardness. The contact angle against water for the concrete surface was found to increase with increasing $CO_2$ pressure and temperature, and reached to an optimum value at around $90^{\circ}C$. The maximum static water contact angle of 128.7 degree was obtained at the $CO_2$ pressure of 2 atm and temperature of $90^{\circ}C$. It was also found that biomimetic carbonation increased the permeability, acid resistance and chloride-ion permeability of the concrete material. These unique results demonstrate that the needle-rod structures of $CaCO_3$ synthetized on concrete surface could enhance hydrophobicity, durability, and mechanical properties of concrete.

• Tribology and Lubricants
• /
• v.40 no.3
• /
• pp.71-77
• /
• 2024

Hydrogen has emerged as an eco-friendly and sustainable alternative to fossil fuels. However, the utilization of hydrogen requires high-pressure compression, storage, and transportation, which poses challenges to the durability of compressor components, particularly the diaphragm. This study aims to improve the durability of 304 stainless steel diaphragms in hydrogen compressors by optimizing their surface roughness and corrosion resistance through wet etching. The specimens were prepared by immersing 304 stainless steel in a mixture of sulfuric acid and hydrogen peroxide, followed by etching in hydrochloric acid for various durations. The surface morphology, roughness, and wettability of the etched specimens were characterized using optical microscopy, surface profilometry, and water contact angle measurements. The friction and wear characteristics were evaluated using reciprocating sliding tests. The results showed that increasing the etching time led to the development of micro/nanostructures on the surface, thereby increasing surface roughness and hydrophilicity. The friction coefficient initially decreased with increasing surface roughness owing to the reduced contact area but increased during long-term wear owing to the destruction and delamination of surface protrusions. HCl-30M exhibited the lowest average friction coefficient and a balance between the surface roughness and oxide film formation, resulting in improved wear resistance. These findings highlight the importance of controlling the surface roughness and oxide film formation through etching optimization to obtain a uniform and wear-resistant surface for the enhanced durability of 304 stainless steel diaphragms in hydrogen compressors.

• Journal of the Korean Applied Science and Technology
• /
• v.31 no.4
• /
• pp.584-594
• /
• 2014

To increase of surface hydrophilicity of polymeric thin films is an important approaching technique for introduction of self-cleaning and/or antifogging properties on the surfaces of those films. In general, hydrophilic surface can be produced by coating non ionic surfactants or by increasing surface energy. Various non-ionic surfactants, such as Tween, Span, and PEG-PPG block copolymers were selected for our experiments, because they are cheap and well soluble in toluene system as well as they contain several reactive hydroxy fuctional groups with coupling agents. Blending conditions influence the PET film surface hydrophilicities. However, the introduction of only these surfactants on the surface of PET films did not show the high durability of hydrophilic properties after washing with water. To improve the durability two types of coupling agents such as epoxide and diisocyanate were adopted. Contact angle of water on hydrophilically coated PET film surface with 6 wt% of isophrone diisocyanate(IPDI) containing coating solution was reached to $8.7^{\circ}$, which was an indirect evidence for very high surface hydrophilicity. A light(500 nm of wavelength) transmittance value of coated PET film was changed only from 87% to 85% with keeping a good transparent property. This film can be usable for self-cleaning film industries.

• The Journal of Advanced Prosthodontics
• /
• v.16 no.2
• /
• pp.105-114
• /
• 2024

PURPOSE. This study aimed to evaluate the effect of pretreatment of three different universal adhesives (Single Bond Universal [SBU], All-Bond Universal [ABU], and Prime&Bond universal [PBU]) on the bonding durability of an adhesive (Panavia F 2.0, PF) and a conventional (Duo-Link, DL) resin cements to air-abraded zirconia. MATERIALS AND METHODS. Rectangular-shaped zirconia specimens were prepared. The chemical composition and surface energy parameters of the materials were studied by Fourier transform infrared spectroscopy and contact angle measurement, respectively. To evaluate resin bonding to the zirconia, all the bonding specimens were immersed in water for 24 h and the specimens to be aged were additionally thermocycled 10000 times before the shear bond strength (SBS) test. RESULTS. The materials showed different surface energy parameters, including the degree of hydrophilicity/hydrophobicity. While the DL/CON (no pretreatment) showed the lowest SBS and a significant decrease in the value after thermocycling (P < .001), the PF/CON obtained a higher SBS value than the DL/CON (P < .001) and no decrease even after thermocycling (P = .839). When the universal adhesives were used with DL, their SBS values were higher than the CON (P < .05), but the trend was adhesive-specific. In conjunction with PF, the PF/SBU produced the highest SBS followed by the PF/ABU (P = .002), showing no significant decrease after thermocycling (P > .05). The initial SBS of the PF/PBU was similar to the PF/CON (P = .999), but the value decreased after thermocycling (P < .001). CONCLUSION. The universal adhesive pretreatment did not necessarily show a synergistic effect on the bonding performance of an adhesive resin cement, whereas the pretreatment was beneficial to bond strength and durability of a conventional resin cement.

• Textile Coloration and Finishing
• /
• v.17 no.2 s.81
• /
• pp.26-30
• /
• 2005

Nylon fabric is widely used in stocking, inner wear, sports wear, and casual wear, but has a defect of easy electric static charging. Accordingly there has been great demand for the hydrophillic finishing technology that could be applied to nylon fiber more easily and efficiently. In this study, ethoxylated hexylantinoanthraquinones were exhausted onto nylon from aqueous bath, and hydrophillicity of the nylon was discussed. In the treatment of nylon fabrics with ethoxylated hexylaminoanthraquinones, they were successfully exhausted onto nylon fabric without any aid of chemical auxiliary. The hydrophilicity of the dyed nylon fabrics were increased with the length of ethoxylate chain. The durability of antistatic and hydrophilic characteristics was good enough as to maintain the initial properties even after 30 repeated launderings.

• Membrane and Water Treatment
• /
• v.5 no.2
• /
• pp.147-170
• /
• 2014

This paper focuses on the study of the most recent ultra-filtration techniques, based on porous polymer membranes, used for the treatment of wastewater from oil, mine and hydrometallurgical industries. The performance of porous membranes used in separation and recovery of oil and heavy metals from wastewater, was evaluated by the polymer composition and by the membrane characteristics, as it follows: hydrophobicity or hydrophilicity, porosity, carrier (composition and concentration), selectivity, fouling, durability, separation efficiency and operating conditions. The oil/water efficient separation was observed on ultra-filtration (UF) techniques, with porous membranes, whereas heavy metals recovery from wastewater was observed using porous membranes with carrier. It can be concluded, that in the ultra-filtration wastewater treatments, a hybrid system, with porous polymer membranes with or without carrier, can be used for these two applications: oil/water separation and heavy metals recovery.

• Corrosion Science and Technology
• /
• v.21 no.4
• /
• pp.290-299
• /
• 2022

Anodizing is an electrochemical surface treatment method conferring corrosion resistance and durability by forming a thick anodization film on the metal surface. Aluminum has a long service life and high thermal conductivity and formability, as well as excellent corrosion resistance. Aluminum 3003 alloy has improved formability, strength, and corrosion resistance due to the addition of a small amount of manganese. However, corrosion occurs in seawater and environments polluted with corrosion-inducing substances, which reduce corrosion resistance. Therefore, it is necessary to artificially form a thick anodized film to improve corrosion resistance. In this study, the anodization treatment time was 4 minutes, and voltages of 10 V, 20 V, 30 V, 40 V, 50 V, 60 V, 70 V, 80 V, 90 V, and 100 V were applied. The thickness and pore size of the oxide film increased according to the applied voltage. A barrier film was formed under voltage conditions from 10 V to 50 V, and a porous film was formed under voltage conditions from 60 V to 100 V. After anodizing, coating was applied. Wettability and corrosion resistance were observed before and after coating according to the surface shape and thickness of the oxide film.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.101-101
• /
• 2018

Quantitative measurement of chloride ion concentration has an important role in various fields of electrochemistry, medical science, biology, metallurgy, architecture, etc. Among them, its importance of architecture is ever-growing due to unexpected degradations of building structure. These situations are caused by corrosion of reinforced concrete (RC) structure of buildings. And chloride ions are the most powerful factors of RC structure corrosion. Therefore, precise inspection of chloride ion concentration must be required to increase the accuracy of durability monitoring. Multi-walled Carbon nanotubes (MWCNTs) have high chemical resistivity, large surface area and superior electrical property. Thus, it is suitable for the channels of electrical signals made by the sensor. Silver nanoparticles were added to giving the sensing property. CuBTC, one of the metal organic frameworks (MOFs), was employed as a material to improve the sensing property because of its hydrophilicity and high surface area to volume ratio. In this study, sensing element was synthesized by various chemical reaction procedures. At first, MWCNTs were functionalized with a mixture of sulfuric acid and nitric acid because of enhancement of solubility in solution and surface activation. And functionalized MWCNTs, silver nanoparticles, and CuBTC were synthesized on PTFE membrane, one by one. Electroless deposition process was performed to deposit the silver nanoparticles. CuBTC was produced by room temperature synthesis. Surface morphology and composition analysis were characterized by scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDS), respectively. X-ray photoelectron spectroscopy (XPS) was also performed to confirm the existence of sensing materials. The electrical properties of sensor were measured by semiconductor analyzer. The chloride ion sensing characteristics were confirmed with the variation of the resistance at 1 V.