• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.937-940
• /
• 2008

골재자원의 부족과 폐기콘크리트의 증가로 인하여 순환골재사용의 필요성이 증가되고 있다. 그러나 순환골재의 건조수축으로 인한 균열등과 같은 문제점이 지적되어 이에 대한 연구가 요구되고 있다. 따라서 본 연구에서는 순환골재에 관한 연구의 일환으로 순환잔골재를 활용한 섬유 보강 콘크리트의 소성 및 초기 건조수축균열을 판상-링형구속수축시험 및 모의부재 옥외폭로시험을 통하여 측정하였다. 그 결과 판상-링형구속수축시험의 경우 순환잔골재를 사용한 콘크리트가 천연 잔골재보다 균열발생이 크게 나타났으며 섬유혼입의 경우 무혼입보다 높은 균열 저감성능을 나타내었다. 모의부재 실험에 있어서도 판상-링형구속수축시험과 유사하게 순환잔골재를 사용한 콘크리트가 균열발생이 큰 것으로 나타났으며 섬유 혼입의 경우 높은 저감 성능을 나타내었다.

• Journal of the Korean Wood Science and Technology
• /
• 제25권4호
• /
• pp.99-107
• /
• 1997

This study was executed to test the possibility of replacement for domestic Japanese larch(Larix leptolepis) for hardwoods and to acquire the information about the effects of drying temperature on internal temperature, moisture content and drying defects. In high-temperature drying, internal temperature increased rapidly to boiling point, immediately after that point the internal temperature rising rate was reduced. In the case of drying at temperature of $125^{\circ}C$, internal temperature could reach at boiling point in a very short time. Moisture content in high-temperature drying showed constant drying rate period and first period of falling rate drying together in 4 hours since experiment begun. There was no strong correlation between initial moisture content and final moisture content. Average drying rate at $115^{\circ}C$, $120^{\circ}C$ and $125^{\circ}C$ was 1.42%/hr, 1.88%/hr and 2.02%/hr, respectively; the case of drying temperature of $125^{\circ}C$ showed most rapid drying rate. Drying rate of $125^{\circ}C$ was so rapid that it showed more severe shrinkage, bow, collapse, end check, and internal check development than in other drying conditions. The result of this study showed the strong possibility of high-temperature drying for Japanese larch, and to dry Japanese larch optimally, dry bulb temperature should not exceed $120^{\circ}C$.

• 원예과학기술지
• /
• 제19권2호
• /
• pp.179-185
• /
• 2001

원예용 배지의 물리화학적 특성을 파악하기 위해 전세계적으로 다양한 분석 방법이 사용되고 있다. 유럽은 배지 분석방법의 표준화 연구를 지속적으로 수행해왔다. 유럽표준화 위원회에서는 유럽표준방법으로 CEN methods를 최종안까지 제출하였으며 사실상 유럽표준 배지분석방법의 제정을 확립하는 단계에 있다. 물리적 특성 중 건물함량과 수분함량은 건조 후 분석하였고, 실험 가밀도는 일정한 부피에 채워진 시료의 무게로 측정하였다. 가밀도, 진밀도, 공극률, 액상, 기상, 부피 감소율은 double ring과 sand suction table이라는 장치를 사용하여 배지를 포화, 배수시킨 후 건조시켜 분석하였다. 화학적 특성 중 pH와 EC는 부피 기준 1:5로 침출하여 분석하였다. 유기물과 회분함량은 건조와 연소 과정을 통해 분석하였다. CEN methods는 유럽표준방법으로 확립을 앞두고 있으나 더 지속적인 연구가 필요할 것이다.

• Journal of the Korean Wood Science and Technology
• /
• 제10권3호
• /
• pp.13-44
• /
• 1982

7.1 옛날부터 재목(材木)을 오래 불에 담그어 쓰면 덜트로 덜 휜다고 하였는데 말로서 전(傳)하여 왔을 뿐 그 연구결과(硏究結果)나 또는 그 원인(原因)에 대한 것은 분명(分明)치 못하였다. 한편 재목(材木)의 추출성분(抽出成分)이 그 재목(材木)의 물리적(物理的) 성질(性質)에 영향(影響)할 것이라는 추측(推測)은 많었으나 실지로 그 영향(影響)에 대한 연구(硏究)를 하여 그 결과(結果)와 그 원인(原因)을 밝힌 것도 극(極)히 적었다. 이 연구(硏究)는 이와같은 입장(立場)에 놓여있는 그 간미지(間未知)한 점(点)을 밝히기 위(爲)하여 다시말하면 재목(材木)을 물에 담그어 그 수용성(水溶性) 추출물(抽出物)을 추출(抽出)하므로써 일어나는 물리적(物理的) 성질(性質)에 대한 결과(結果)를 조사(調査)하고 이 결과(結果)를 통(通)하여 얻는 진리(眞理)를 응용(應用)하여 재목(材木)의 일대 흠점(欠点)인 수축(收縮), 팽창(膨脹) 이에따라 일어나는 트는것, 휘는것, 틀어지는 것 등(等)을 막아 재목이용(材木利用)의 합리화(合理化)를 기(期)할 목적(目的)으로써 시작(始作)된 것이며 Yale 재과대학(材科大學) 목재이용학(木材利用學) 연구실(硏究室)에서 담당교수 F.F.Wangaard 박사(博士) 지도하(指導下)에 재료(材料)는 동(同) 연구실(硏究室)에 준비(準備)되어 있는 북미(北美)산 스트로 - 부 소나무 참나무 그리고 남방열대(南方熱帶)산 하이메나에아의 삼(三) 종류(種類)에 대하여 연구(硏究)되었다. 7.2 연구(硏究)의 대상이 된 물리적(物理的) 성질(性質)은 목재(木材)의 실용적 사용(使用)에 있어서 가장 관계가 깊은 다시 말하면 트고 휘고 틀어지는등(等)의 관계가 깊은 평형함수량(平衡含水量), 수축(收縮), 팽창(膨脹) 그리고 강도(强度)의 지표(紙票)가 되는 비중(比重)등이 있다. 7.3 시험(試驗)은 위에 말한 세 가지 종류(種類)를 가지고 추출처리(抽出處理)를 하여 추출(抽出)한것과 반대로 추출성(抽出性) 물질(物質)은 침투(浸透)시킨것에 대하여 비교(比較)될 무처리(無處理)한 세 다른 공시재(供試在)를 준비(準備)하여 실시되었다. 다음 시험결과(試驗結果)는 7.4 수용성(水溶性) 추출물(抽出物)이 추출량(抽出量)과 그 추출액중(抽出液中)의 성분(成分)그룹은 Table 36에 표시(表示)된것과 같으며 나무 종류(種類)에 따라 추출량(抽出量)에 그리고 각(各) 성분(成分)그룹의 종류(種類)와 그 양(量)에 차이(差異)를 볼수 있었다. 7.5 평형함수량(平衡含水量)에 있어서는 a) 추출처리(抽出處理)를 하여 그 추출성분(抽出成分)이 빠져버린 공시재(供試材)와 그와 반대의 공시재(供試材) 사이에는 확실한 차이(差異)가 있어 추출성분(抽出成分)을 재내(材內)에 포함(包含)하고 있으므로써 같은 관계흡도에서 80%방습시(放濕時)는 이와 반대 평형함수량(平衡含水量)은 많아졌다. b) 설탕액(雪糖液)에 담그어 침투처리(浸透處理)를 하여 당분(糖分)이 재내(材內)에 침입(侵入)된 공시재(供試材)는 대체(大體) 추출처리(抽出處理)를 하지 않은 공시재(供試材)와 거의 같은 경향(傾向)의 결과(結果)를 나타내고 있다. c) 나무의 종류(種類)에 따른 차이(差異)는 일정한 경향(傾向)을 볼 수 없으나 스트로-부 소나무의 심재부(心材部)와 변재부를 비교(比較)하면 심재부(心材部)는 그 평형함수량(平衡含水量)이 적다. 이것은 원래(元來)의 함수량(含水量)에 있어서 심재부(心材部)가 적은데 이와같은 차이(差異)는 식물생리학적(植物生理學的) 또는 그 해부학적(解剖學的) 구조(構造)의 차이(差異)에서 생기는 것이다. 7.6 수축(收縮)에 있어서는 a) 추출처리(抽出處理)를 한 공시재(供試材)의 수축량(收縮量)은 그와 반대로 추출처리(抽出處理)를 않어 추출성분(抽出成分)이 그대로 남어있는 공시재(供試材)에 비교(比較)하여 그 수축량(收縮量)이 모두 크다. b) 설탕액(雪糖液)에 담그어 침투처리(浸透處理)를 한 공시재(供試材)는 그 수축량(收縮量)은 다른것에 비교(比較)하여 제일 적고 모두 침투처리(浸透處理)를 하지않은 공시재(供試材)와 거의 같은 결과(結果)를 보이고 있는데 이것은 재목(材木)을 사용전(使用前)에 특수(特殊)한 침투처리(浸透處理)를 하여 쓰면 재목(材木)의 일대 흠점(欠点)인 수축(收縮)을 막을수 있다는 것을 실증하는 것이다. c) 나무의 종류별(種類別)로보면 스트로-부 소나무의 심재부(心材部)는 그 변재부보다 수축량(收縮量)이 적으며 참나무의 수축량(收縮量)은 제일 크로 스토로-부 소나무에 비교(比較)하여 약(約)2배(倍) Hymenaea는 참나무 보다 적고 스트로 - 부 소나무 보다는 컸다. d) 각(各) 수종(樹種)을 통(通)하여 방향성(方向性)에 따른 수축량(收縮量)을 보면 촉단면방향(觸斷面方向)의 수축량(收縮量)은 경단방향(徑斷方向)의 수축량(收縮量)보다 큰 것은 다른 모든 나무에서 보느 결과(結果)와 같다. e) 추출량(抽出量)과의 관계를 보면 추출량(抽出量)이 많은 것일수록 추출처리(抽出處理)를 않은 것과의 수축량(收縮量)의 차이(差異)는 컸다. 7.7 팽창(膨脹)에 있어서는 a) 추출처리(抽出處理)로 그 성분(成分)을 추출(抽出)하여 낸 공시재(供試材)의 팽창량(膨脹量)은 그와 반대의 것에 비교(比較)하여 모두 팽창량(膨脹量)이 컸다. b) 재목(材木)의 방향성(方向性)에 따라보면 모두 촉단(觸斷) 방향(方向)의 팽창량(膨脹量)은 경단방향(徑斷方向)의 팽창량(膨脹量)에 비(比)하여 크다. c) 수축(收縮)에서 본것과 같이 팽창(膨脹)에 있어서도 나무의 종류(種類)에 따라 그 팽창량(膨脹量)에 차이(差異)를 볼수 있으며 그 팽창량(膨脹量)은 참나무 하이메나에아 스트로-부 소나무의 변재 그리고 동심재(同心材)의 순서(順序)도 적어졌으며, 수축량(收縮量)이 큰 것은 팽창량(膨脹量)에 있어서도 크다는 것을 실증하였다. 7.8 비중(比重)에 있어서는 a) 추출처리(抽出處理)를 한 공시재(供試材)의 비중(比重)이 추출처리(抽出處理)를 않은 공시재(供試材)의 비중(比重)에 비교(比較)하여 컸다. 이것은 비중(比重)을 결정(決定)할 때 사용(使用)된 용적(容積)에 기인(起因)하였으며 사실은 이와 반대의 결과(結果)가 나타나야 할 것이다. b) 나무의 종류별(種類別)로 보면 스트로-부 소나무의 심재(心材)는 변재보다는 그 비중(比重)이 크며 두 참나무의 비중(比重)은 소나무의 그것보다 배(倍)나 크고 하이메나에아는 그 비중(比重)이 제일 컷다. (9) 이상(以上) ; 모-든 시험결과(試驗結果)를 종합(綜合)하여 생각할 때 막연(漠然)히 재목(材木)을 물에 오래 담그어 쓴다는 생각은 오히려 잘못하면 목재(木材)의 성질(性質)을 더욱 악화(惡化)시킬 우려(憂慮)가 있으며 물에 담그어 쓰되 설탕질등(雪糖質等)으로 재목내부(材木內部)에 침투(浸透)할 수 있는 성질(性質)의 성분(成分)이 용해(溶解)되어 있는 액중(液中)에 담그어 쓰는 것은 재목(材木)의 일대 흠점(欠点)인 수축(收縮)과 팽창(膨脹) 그리고 이에 따라 일어나는 트고 휘는 일이며 틀어지는 등(等)의 흠점(欠点)을 막을 수 있다는 것을 실증하게 되었다. 만고(萬苦) 물속에 오래 담그어 쓰는 것이 다시 말하면 수용성(水溶性) 추출물(抽出物)을 빼내어 쓰는 것이 그 결과(結果)에 있어 확실히 양호(良好)하였다는 사실이 있었다면 그것은 수용성성분(水溶性成分)을 제출(提出)함으로써 균일(均一)한 수축(收縮)과 팽창(膨脹)이 일어나는데 기인(起因)하였을 것이다.

• 한국가구학회지
• /
• 제21권1호
• /
• pp.62-71
• /
• 2010

This study was carried out to investigate the physical and mechanical properties of 6 hardwoods before and after heat treatment in an effort to produce the high quality industrial lumber product. The object of the research was to design living products with heat treated woods. The results were as follows. Specific gravities of green woods were in range from 0.87 to 1.12. The specific gravities of never treated woods showed higher than those of the heat treated woods. The shrinkage of heat treated woods when green to air & oven dry was significantly low, compared to never treated woods. The compression strengths parallel to grain of heat treated woods showed higher than those of never treated woods. The moduli of rupture (MOR) of never treated and heat treated woods were $170.37N/mm^2~107.07N/mm^2$ and $122.78N/mm^2~61.27N/mm^2$ respectively. MORs of heat treated woods showed lower than those of never treated woods. The modulus of elasticity (MOE) of heat treated woods showed higher than those of never treated woods.

• 한국가구학회지
• /
• 제18권1호
• /
• pp.39-46
• /
• 2007

This study was carried out to investigate the wood properties for efficient utilization of warm temperate tree species of Quercus acuta Thunb. grown in Korea. Fundamental wood properties in the anatomical, physical, mechanical and chemical characteristics were examined. Quercus acuta Thunb. is a radial-porous, straight grained and fine textured wood. The heartwood is not clearly distinguished from the sapwood. In physical properties, it has a high oven-dry specific gravity of $0.85{\pm}0.02$, and high shrinkage from green to air-dried condition of $7.05{\pm}0.52%$ in radial and $11.13{\pm}0.48%$ in tangential direction. Mechanical properties determined are strong with the MOR of $1,065{\pm}90kgf/cm^2$, and tensile strength parallel to grain of $1,490{\pm}258kgf/cm^2$ and shear strength of $175{\pm}13kgf/cm^2$. Also, this wood has high extractive contents: 11.11% for cold and 13.51% for hot water.

• Geomechanics and Engineering
• /
• 제15권2호
• /
• pp.729-738
• /
• 2018

Soft clay soils due to their various geotechnical problems, stabilized with different additives. Traditional additives such as cement and lime will not able to increase the soil strength properties significantly. So, it seems necessary to use new additives for increasing strength parameters of soft clay soils significantly. Among the new additives, epoxy resins have excellent physical and mechanical properties, low shrinkage, excellent resistance to chemicals and corrosive materials, etc. So, in this research, epoxy resin used for stabilization of soft clay soils. For comprehensive study, three clay soil samples with different PI and various clay mineral types were studied. A series of uniaxial tests, SEM and XRD analysis conducted on the samples. The results show that using epoxy resin increases the strength parameters such as UCS, elastic modulus and material toughness about 100 to 500 times which the increase was dependent on the type of clay minerals type in the soil. Also, In addition to water conservation, the best efficiency in the weakest and most sensitive soils is the prominent results of stabilization by epoxy resin which can be used in different climatic zones, especially in hot and dry and equatorial climate which will be faced with water scarcity.

• Geomechanics and Engineering
• /
• 제12권1호
• /
• pp.111-125
• /
• 2017

Swelling and shrinkage characteristics of expansive fine grained soil cause volumetric changes followed by distress and damage to the structures. Soil stabilization can be explained as the alteration of the soil properties by chemical, mechanical or any other means in order to enhance the engineering properties of the soil. Utilization of industrial wastes in soil stabilization is cost effective and environment friendly. This paper presents an experimental study on stabilization of expansive soil using industrial wastes, viz. fly ash and dolochar. The paper includes the evaluation of engineering properties like unconfined compressive strength and California bearing ratio (CBR) of expansive soil collected from Balasore district of Odisha stabilized with fly ash and dolochar in different proportions and to predict the influence of these additives on engineering properties and strength characteristics of expansive soil. Both fly ash and dolochar were found to increase the CBR and decrease many index properties such as liquid limit, plastic limit, plasticity index, swelling index and UCS, thus enhancing the strength parameters of expansive soil.

• 한국식품영양과학회지
• /
• 제28권6호
• /
• pp.1283-1287
• /
• 1999

This study was carried out to develop new processed food from cherry tomatoes. The dried cherry tomatoes were prepared by using a sequence of osmotic dehydration, air drying, vacuum drying and freeze drying. The moisture contents of dried cherry tomato products by nontreatment and osmosis treatment were about 11~13% and 7.5~ 10%, respectively. The vitamin C contents of the dried product after osmotic dehydration were higher than those of the dried products by nontreatment. The vitamin C content of the freezing dried product was the highest of the others. The vacuum dried product by nontreatment was retained color of fresh fruit in the change of color. The ΔE value of the air dried product was lower than those of the others. As a result to microscopic analysis, fresh cherry tomato was observed regular tissue, while cherry tomato treated by osmosis was observed a cell collapse following the loss of water. The dried product had cell shrinkage and dense tissue. And the cell wall of dried products after osmotic dehydration were much more damage than those of nontreatment dried product. The palatability of the air dried product was the best of three drying methods. The dried cherry tomatoes treated by osmosis were superior to the dried cherry tomatoes by nontreatment.

• 한국의류산업학회지
• /
• 제18권6호
• /
• pp.878-888
• /
• 2016

In this study, wool/nylon(50/50%) blend yarn and its fabrics for tra-biz(complex word of travel+business) garment were prepared, and its wear comfort characteristics were investigated through thermal manikin and human-body wearing experiment. In addition, tactile wearing performance from fabric mechanical properties and the dimensional stability and the pilling of the fabric specimen during wearing and dry-cleaning were measured and compared with those of wool 100% fabric specimen. Heat keepability of the wool/nylon(50/50%) blend fabric by thermal manikin experiment was superior than that of wool 100% fabric, this result was verified with human-body wearing experiment and its result coincided well with this experimental result. Tactile wearing performance of the wool/nylon(50/50%) fabric from fabric mechanical properties measured by FAST system was better than that of the wool 100% fabric. The dimensional stability of the wool/nylon(50/50%) fabric was more stable than that of the wool 100% fabric. Because relaxation shrinkage was lower and hygral expansion of wool 100% fabric was more high. However, the breathability and pilling property of the wool/nylon(50/50%) fabric were inferior than those of the wool 100% fabric. The possibility of application for tra-biz garment of wool/nylon(50/50%) blend fabric was observed because of good heat keepability, tactile wearing performance and washing fastness.