An Evaluation of Plastic and Early Dry Shrinkage of Fiber Reinforced Concrete Using Recycled Aggregate

순환잔골재를 활용한 섬유 보강 콘크리트의 소성 및 초기 건조수축평가

Recently, the recycling and reusing of construction and demolition waste concrete is urgently required because generation quantity of construction and demolition waste concrete is greatly increased according to the rapid increasing of urban redevelopment project. On the other hand, the problem solution for demand and supply unbalance of fine aggregate is urgently required because of the restriction of collecting sea fine aggregate by intensification of environment influence evaluation and the shortage of river fine aggregate. but a quality of aggregate as building structure is not demonstrated. Therefore it is the objective of this study to estimate plastic and early dry shrink crack of fiber reinforced concrete using a recycled aggregate by plat-ring test and mock-up test of exposure to the air. as a result, in case of plat- ring test, developing crack is wider using recycled aggregate concrete than natural aggregate concrete, is wider using fiber reinforced concrete than non fiber. in case of mock-up test of exposure to the air, it is similar to plat-ring test.

골재자원의 부족과 폐기콘크리트의 증가로 인하여 순환골재사용의 필요성이 증가되고 있다. 그러나 순환골재의 건조수축으로 인한 균열등과 같은 문제점이 지적되어 이에 대한 연구가 요구되고 있다. 따라서 본 연구에서는 순환골재에 관한 연구의 일환으로 순환잔골재를 활용한 섬유 보강 콘크리트의 소성 및 초기 건조수축균열을 판상-링형구속수축시험 및 모의부재 옥외폭로시험을 통하여 측정하였다. 그 결과 판상-링형구속수축시험의 경우 순환잔골재를 사용한 콘크리트가 천연 잔골재보다 균열발생이 크게 나타났으며 섬유혼입의 경우 무혼입보다 높은 균열 저감성능을 나타내었다. 모의부재 실험에 있어서도 판상-링형구속수축시험과 유사하게 순환잔골재를 사용한 콘크리트가 균열발생이 큰 것으로 나타났으며 섬유 혼입의 경우 높은 저감 성능을 나타내었다.