• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.5
• /
• pp.474-481
• /
• 2009

Fracture models and criteria of adhesive with two parameters, namely $G_C$ and ${\sigma}_{max}$, have been developed to describe the fracture process of adhesive joints. Cohesive zone model(CZM) is a representative two parameter failure criteria approach. In CZM, ${\sigma}_{max}$ is a critical, limiting maximum value of the stress in the damage zone ahead of the crack and is assumed to have some physical significance in adhesive failure. Based on CZM and finite element analysis method, the relationship between fracture load and adhesive properties, as $G_{IC)$ and $({\sigma}_{max})_I$, was investigated in adhesively bonded joint tensile test and T-peel test. The two parameters in tensile mode loading were evaluated by using the relationship. The value of $G_{\IC}$ evaluated by proposed method showed close agreement with analytical solution for tapered double cantilever beam(TDCB) test which proposed in an ASTM standard.

• Journal of Surface Science and Engineering
• /
• v.32 no.6
• /
• pp.647-657
• /
• 1999

Due to the inherently poor adhesion strength of Cu-based leadframe/EMC (Epoxy Molding Compound) interface, popcorn cracking of thin plastic packages frequently occurs during the solder reflow process. In the present work, in order to enhance the adhesion strength of Cu-based leadframe/EMC interface, black-oxide layer was formed on the leadframe surface by chemical oxidation of leadframe, and then oxidized leadframe sheets were molded with EMC and machined to form SDCB (Sandwiched Double-Cantilever Beam) and SBN (Sandwiched Brazil-Nut) specimens. SDCB and SBN specimens were designed to measure the adhesion strength between leadframe and EMC in terms of critical energy-release rate under quasi-Mode I ($G_{IC}$ ) and mixed Mode loading ($G_{C}$ /) conditions, respectively. Results showed that black-oxide treatment of Cu-based leadframe initially introduced pebble-like X$C_2$O crystals with smooth facets on its surface, and after the full growth of $Cu_2$O layer, acicular CuO crystals were formed atop of the $Cu_2$O layer. According to the result of SDCB test, $Cu_2$O crystals on the leadframe surface did not increase ($G_{IC}$), however, acicular CuO crystals on the $Cu_2$O layer enhanced $G_{IC}$ considerably. The main reason for the adhesion improvement seems to be associated with the adhesion of CuO to EMC by mechanical interlocking mechanism. On the other hand, as the Mode II component increased, $G_{C}$ was increased, and when the phase angle was -34$^{\circ}$, crack Kinking into EMC was occured.d.

• Advanced Composite Materials
• /
• v.16 no.2
• /
• pp.95-113
• /
• 2007

Experimental investigations of interlaminar mechanical properties for carbon fiber reinforced plastic (CFRP) laminates were carried out using aramid fiber ($Kevlar^{(R)}$-29 1000d) and carbon fiber (TR40-1K 612d, Mitsubishi Rayon) stitching. Various carbon fiber (CF) stitch densities were used to prepare a number of CF stitched CFRP laminates for double cantilever beam (DCB) tests. An insert tongue-type loading fixture, developed by the Japan Aerospace Exploration Agency (formerly the National Aerospace Laboratory of Japan), was also employed in the DCB test. Interlaminar tension tests were carried out under an out-of-plane directional loading using a single CF stitch thread in the CFRP laminates. The DCB test results clarified that the relationship between the volume fractions of the CF stitch thread ($V_{ft}$) and mode I critical energy release rate ($G_{Ic}$) showed a mostly linear function with a higher gradient than that of the $Kevlar^{(R)}$ stitched CFRP laminates. The CF stitched CFRP tension test results indicated that the consumption energy per unit area ($E_i$) was larger than that of $Kevlar^{(R)}$ stitched CFRP laminates.

• Journal of the Korean Society for Railway
• /
• v.8 no.6 s.31
• /
• pp.573-580
• /
• 2005

Model I interlaminar fracture behaviors of the carbon/epoxy composite, one of the candidate composites for a tilting train carbody, were investigate by the use of DCB(Double cantilever beam) specimens. These specimens were made of CF3327 plain woven fabric with epoxy resin, and an artificial starter delamination was fabricated by inserting Teflon film with the thickness of $12.5{\mu}m$ of $25.0{\mu}m$ at the one end of the specimen. Mode I interlaminar fracture toughness was evaluated for the specimens with the different thickness of an inserter. Also delamination propagating behaviors and interlaminar fracture surface were examined through an ooptical travelling scope and a scanning electron microscope. We found that abruptly unstable crack propagation called as stick-slip phenomena was observed. In addition, interlaminar fracture behaviors were affected on the location and the morphology of a crack tip as well as an interface region.

• Transactions on Electrical and Electronic Materials
• /
• v.1 no.3
• /
• pp.23-28
• /
• 2000

A block-oxide layer was formed on the surface of Cu-based leadframe by chamical oxidation method in order to enhance the adhesion strength between Cu-based leadframe and epoxy molding compound (EMC) Using sandwiched double cantilever beam (SDCB) specimens, the adesion strength was measured in terms of interfacial fracture toughness, G$\sub$IC//Results showed that the black-oxide layer was composed of two kinds of layers: pebble-like Cu$_2$O layer and acicular CuO layer, At the initial stage of oxidation the Cu$_2$O layer was preferentially formed and thickened up to around 200 nm whithin 1 minute of the oxidation time. Then the CuO layer started to from atop of the Cu$_2$O layer and thickened up to around 1300 nm until 20 minutes. As soon as the CuO layer formed, the thickness of Cu$_2$O layer began to reduce and finally reached to around 150 nm. The pre-cleaned and the Cu$_2$O coated leadframes showed almost no adhesion of EMC, however, as the CuO precipitates appeared and became continuous, G$\sub$IC/ increased up to around 80 J/㎡. Further oxidation raised G$\sub$IC/ up. to around 100 J/㎡.

• Journal of Surface Science and Engineering
• /
• v.36 no.6
• /
• pp.491-499
• /
• 2003

Copper-based leadframe sheets were oxidized in a hot alkaline solution to form brown-oxide layer on the surface and molded with epoxy molding compound (EMC). The brown-oxide-coated leadframe/EMC joints were machined to form sandwiched double-cantilever beam (SDCB) specimens and sandwiched Brazil-nut (SBN) specimens for the purpose of measuring the fracture toughness of leadframe/EMC interfaces. The SDCB and the SBN specimens were designed to measure the fracture toughness of the leadframe/EMC interfaces under nearly mode-I loading and mixed-mode (mode I ＋ mode II) loading conditions, respectively. Fracture surfaces were analyzed by various equipment such as glancing-angle XRD, SEM, AES, EDS and AFM to elucidate failure path. Results showed that failure occurred irregularly in the SDCB specimens, and oxidation time of 2 minutes divided the types of irregular failures into two classes. The failure in the SBN specimens was quite different from that in the SDCB specimens. The failure path in the SBN specimens was not dependent on the phase angle as well as the distance from tips of pre-cracks.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.4
• /
• pp.127-134
• /
• 2021

In this study, the adhesive fracturing characteristics of a DCB specimen due to single and heterogeneous bonding materials under tearing load was investigated. The experiments were conducted to examine the fracturing properties of the adhesive DCB specimen. As an experimental condition, a forced displacement of 3mm/min was applied to one side while the other side was fixed. As a result of the experiment, it was found that the AL6061-T6 material was superior to the CFRP material in terms of maximum stress, specific strength, and energy release rate when compared to the adhesive fracturing property of a single material. We tested CFRP-AL, a heterogeneous bonding material, and compared its experimental results to the results from the single materials. Based on these results, CFRP-AL with a heterogeneous bonding material was observed to have the superior structural safety compared to single materials for the mode III fracture type.

• Journal of Surface Science and Engineering
• /
• v.32 no.4
• /
• pp.531-537
• /
• 1999

A copper based leadframe was oxidized in brown-oxide forming solution, then the growth characteristics of brown oxide and the effect of brown-oxide formation on the adhesion strength of leadframe to epoxy molding compound (EMC) were studied by using sandwiched double cantilever beam (SDCB) specimens. The brown oxide is composed of fine acicular CuO, and its thickness increased up to ~150 nm within 2 minutes and saturated. Bare leadframe showed alomost no adhesion to EMC, while once the brown-oxide layer formed on the Surface of leadframe, the adhesion strength increased up to ~80 J/$\m^2$ within 2 minutes. Correlation between oxide thickness, $\delta$ and the adhesion strength in terms of interfacial fracture toughness, $G_{c}$ was linear. Considering the above results, we might conclude that the main adhesion mechanism of brown-oxide treated leadframe to EMC is mechanical interlocking, in which fine acicular CuO plays a major role.e.

• Composites Research
• /
• v.12 no.5
• /
• pp.40-53
• /
• 1999

The interlaminar facture behavior of multidirectional carbon-fiber/epoxy composite laminates under low and high rates of test, up to rate of about 11.4m/s has been investigated using the double cantilever beam specimens. The mode I loasing with rates above 1.0m/s had considerable dynamic effects on the load-time curves and thus revealed higher values of the average crack velocity than thet expected from a simple proportional relationship with the test rate. The modified beam analysis utilizing only the opening displacement and crack length exhibited an effective means for evaluating the dynamic fracture energy $G_{IC}$. Flexural modulus increased gradually with an increase of the test rate, which was utilized in the evaluation of $G_{IC}$. Values of $G_{IC}$ at the crack initiation and arrest were scarcely changed with increasing test rate up to 1.0m/s. However the maximum $G_{IC}$ was much enlarged at 11.4m/s due to the large amount of fiber bridging the crack tip. The larger the initial crack length, the smaller the maximum $G_{IC}$ at high rate.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.19 no.1
• /
• pp.79-84
• /
• 1983

The test specimen, designated the double cantilever beam, was employed for a fracture mechanics study of stress corrosion cracking (SCC) of type 5083 Al-alloy in seawater. Stress intensities for this DCB specimen were calculated by using compliance, strain energy release rate and relation between stress intensity and strain energy release rate. Analytical expression for compliance as a function of crack length was obtained by applying beam theory. It was investigated that the polarization potentials affected the growth rate and surface of stress corrosion cracking. The results are as follows, The critical stress intensity was 134.81-148.38kg/mm super(3/2) and K sub(Ii) under polarization potentials was 75.92-145.78kg/mm super(3/2). The minimum stress corrosion crack growth rate was occurred at-987mV SCE. Insoluble compound on $\beta$ phase was looked into through SCC. The greater anodic potential is, the larger insoluble compound on $\beta$ phase becomes.