• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 제37회 하계학술대회 논문집 C
• /
• pp.1418-1419
• /
• 2006

PZT(80/20) powder was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The coating and drying procedure was repeated 4 times. And then the PZT(20/80) precursor solution was spin-coated on the multilayered thick films. A concentration of a coating solution was 0.5 mol/L and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about 60-65 ${\mu}m$. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant and the dielectric loss of the PZT-6 thick film were 275 and 3.5, respectively. And the PZT-6 film shows the remanent polarization of 22.1 $C/cm^2$ and coercive field of 13.7 kV/cm.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 1998년도 PROCEEDINGS OF THE 15TH KACG TECHNICAL MEETING-PACIFIC RIM 3 SATELLITE SYMPOSIUM SESSION 4, HOTEL HYUNDAI, KYONGJU, SEPTEMBER 20-23, 1998
• /
• pp.79-83
• /
• 1998

Plasma display panel is a potential candidate for HDTV, due to the fact hat the expansion of screen size is much easier using thick film technology. In this study, transparent dielectric materials using lead borosilicate glasses is developed, which satisfy the requirements of dielectrics for PDP. Paste is made of this glass composition. The paste has thixotropic behavior suitable for screen printing. The paste shows more thixotropic behavior as the particle size decrease. After firing, cross sectional area was analyzed by SEM. The void of fired thick film was removed using bimodal particle system. The dielectric showed good adhesion characteristics.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.760-763
• /
• 2003

Low Temperature Cofired Ceramics (LTCC) technology is a promising technology to integrate many devices in a module by embedding passive components. For the module substrate, most LTCC structures have dielectric constants below 10 to reduce signal delay time. Some components, which need high dielectric constants, have not been yet embedded in LTCC module. So, embedding capacitor with high capacitance by applying another dielectrics with high dielectric constants in LTCC is an important issue to maximize circuit density in LTCC module. In this study, electrical properties of embedded capacitor fabricated by dielectric paste of high dielectric constants (K-100) and co-firing behavior with LTCC were investigated. To prevent camber development of co-fired structure, constrained sintering process was tested. Dielectric properties of embedded capacitors were calculated from their capacitance and impedance value. Temperature coefficient of capacitance were also measured.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 제5회 영호남 학술대회 논문집
• /
• pp.31-34
• /
• 2003

($Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$ (BSCT) (x=0.10, 0.15, 0.20) powder, prepared by the sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen-printing techniques on alumina substrates using the BSCT paste. The structural and the electrical properties were investigated for various composition ratio and sintering temperature. BSCT thick film thickness, obtained by four printings, was approximately 110 ~ 120 ${\mu}m$. The Curie temperature and dielectric constant at room temperature were decreased with increasing Ca content. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) specimen, which was sintered at $1420^{\circ}C$ and measured at 1MHz, were about 910, 0.46% and 9.28% at 5kV/cm, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.685-688
• /
• 2003

[ $(Ba,Sr,Ca)TiO_3$ ] powders, prepared by the sol-gel method, were mixed with an organic vehicle and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. The grain size decreased with increasing amounts of $MnO_2$, and the BSCT(50/40/10) thick film doped with 1wt% $MnO_2$ showed a value of 6.5mm. The thickness of thick films by four-cycle on printing/drying was approximately 100mm. The relative dielectric constant, dielectric loss and tunability of the BSCT(S0/40/10) thick films doped with 1.0wt% $MnO_2$ were 1296, 0.61% and 11.18%, respectively.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제55권12호
• /
• pp.555-559
• /
• 2006

Using the $Ba_{0.5}Sr_{0.5}TiO_3$(BST) powders prepared by the Sol-Gel method, the BST thick films were fabricated on the $Al_2O_3 $substrates coated with Pt by the screen printing method. Compared with pure BST thick films, the structural and dielectric properties of the BST thick films doped with $1{\sim}10$ wt % MgO were investigated. It was observed that the Mg substitution into BST causes a shift in the cubic-tetragonal BST phase transition peak to a lower temperature. The microstructure of the BST substituted with Mg was homogeneous and dense. Mg substitution into BST had a significant effect on the grain size reduction. Dielectric constant was decreased with increasing the MgO content and temperature. In the case of BST thick films doped with 1 wt% MgO, the relative permittivity and dielectric loss were 1581 and 1.4 % at 1 MHz.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2004년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.58-60
• /
• 2004

The $BaTiO_3/SrTiO_3$ heterolayered thick films were fabricated on alumina substrate by screening printing method. The obtained films were sintered at $1400^{\circ}C$ with bottom electrode of Pt for 2 hours. The structural and electrical properties of $BaTiO_3/SrTiO_3$ heterolayered thick films were compared with pure $BaTiO_3$ and $SrTiO_3$ films. The (Ba,Sr)$TiO_3$ phase was appeared at the $BaTiO_3/SrTiO_3$ heterolayered thick films. The thickness of $BaTiO_3/SrTiO_3$ heterolayered thick film, obtained by one printing, was about $50{\mu}m$. The dielectric constant and dielectric loss of the $BaTiO_3/SrTiO_3$ heterolayered thick films were about 1964, 5.5% at 1KHz, respectively.

• 한국전기전자재료학회논문지
• /
• 제20권7호
• /
• pp.581-586
• /
• 2007

[ $(Ba_{0.57}Sr_{0.33}Ca_{0.10})TiO_3$ ] (BSCT) powders, prepared by sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen printing method. The structural and dielectric properties were investigated as a function of the $Yb_2O_3$ doping contents. As a result of the TG-DTA, exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All BSCT thick films showed the typical XRD patterns of a cubic polycrystalline structure. The average thickness of all BSCT thick films was about $70{\mu}m$. The grain size of the BSCT thick film doped with 0.7 mol% $Yb_2O_3$ was approximately $6.2{\mu}m$. The Curie temperature and relative dielectric constant at room temperature decreased with increasing $Yb_2O_3$ amount. Relative dielectric constant and dielectric loss of the specimen doped with 0.1 mol% $Yb_2O_3$ were 4637 and 19 % at Curie temperature, respectively.

• 한국세라믹학회지
• /
• 제33권6호
• /
• pp.665-671
• /
• 1996

Ferroelectric Pb(Fe1/2Nb1/2)O3 thin films were successfully fabricated on ITO/Glass substrate by sol-gel proces-sing and characterized to determine the dielectric and electric properties. Viscosity of PEN sol measured to investigate rheological properties was 3.25 cP which was proper for coating. The sol also showed Newtonian behavior. RTA(Rapid Thermal Annealing) was used for the annealing of the thin film and 1200~1700$\AA$ thick PEN thin films were fabricated by repeating the intermediate and the final annealing. After the deposition of Pt as top electrode by vacuum evaporation dielectric and electric properties were measured. Dielectric properties of FFN thin film were enhanced by increasing the perovskite phase fraction with increasing the annealing temperature. Measured dielectric constant of 1700$\AA$ PFN thin film annealed at $650^{\circ}C$ was 890 at 1kHz Capacitatnce density and dielectric loss were 47 fF/${\mu}{\textrm}{m}$2 and 0.47 respectively. As a result of measuring Curie temperature PFN thin films had Curie point with a rang of 110~12$0^{\circ}C$ and showed broad dielectric peak at that point. Leakage current of the PFN thin films were increased with increasing the annealing tempera-ture.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.7-9
• /
• 2006

$(BaSr)TiO_3$ thick films were prepared by tape casting method using $BaTiO_3$ and $SrTiO_3$ powder slurry in order to investigate dielectric properties and low temperature sintering. Sintering density was $5.7\;g/cm^3$ and the BST sample exhibited the maximum dielectric constant, tunability at temperatures near phase transition point. The dielectric constant was increased and curie temperature was shifted to higher temperature with increasing of annealing temperature.