• Restorative Dentistry and Endodontics
• /
• v.19 no.2
• /
• pp.633-640
• /
• 1994

The tensile bond strength to dentin was measured for three glass-ionomer cement and composite resin combinations: two light-curing glass-ionomer cements(Vitrebond and XR - Ionomer) and one traditional glass - ionomer cement(Ketac - Bond), two adhesive systems(Scotchbond, and XR - Bonding System), and a corresponding composite resin. The bond strength of this "sandwich" was also compared with that of the same cements used in bulk. Vitredbond showed a significantly higher bond strength in bulk than did the other two cements. Of the sandwiches, the XR - Iomomer and XR - Bond combination showed a bond strength significantly higher than that of the Vitrebond and Scotchbond or Ketac- bond and Scotchbond combination. The fracture of the bond was mainly adhesive for Vitrebond, cohesive for XR - Ionomer when used in bulk and adhesive - cohesive when used in a sandwich, and cohesive for Ketac-Bond.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.1
• /
• pp.66-78
• /
• 2004

The objective of this study was to apply the vibration technique to reduce the viscosity of bonding adhesives and thereby compare the bond strength and resin penetration in enamel and dentin achieved with those gained using the conventional technique and vibration technique. For enamel specimens, thirty teeth were sectioned mesio-distally. Sectioned two parts were assigned to same adhesive system but different treatment(vibration vs. non-vibration). Each specimen was embedded in 1-inch inner diameter PVC pipe with a acrylic resin. The buccal and lingual surfaces were placed so that the tooth and the embedding medium were at the same level. The samples were subsequently polished silicon carbide abrasive papers. Each adhesive system was applied according to its manufacture's instruction. Vibration groups were additionally vibrated for 15 seconds before curing. For dentin specimen, except removing the coronal part and placing occlusal surface at the mold level, the remaining procedures were same as enamel specimen. Resin composite(Z250. 3M. U.S.A.) was condensed on to the prepared surface in two increments using a mold kit(Ultradent Inc., U.S.A.). Each increments was light cured for 40 seconds. After 24 hours in tap water at room temperature, the specimens were thermocycled for 1000cycles. Shear bond strengths were measured with a universal testing machine(Instron 4465, England). To investigate infiltration patterns of adhesive materials, the surface of specimens was examined with scanning electron microscope. The results were as follows: 1. In enamel the mean values of shear bond strengths in vibration groups(group 2, 4, 6) were greater than those of non-vibration group(group 1, 3, 5). The differences were statistically significant except AQ bond group. 2. In dentin, the mean values of shear bond strengths in vibration groups(group 2, 4, 6) were greater than those of non-vibration groups(group 1, 3, 5). But the differences were not statistically significant except One-Up Bond F group. 3. The vibration group showed more mineral loss in enamel and longer resin tag and greater number of lateral branches in dentin under SEM examination.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.576.2-576
• /
• 2001

The purpose of this study was to evaluate the effect of dentinal sclerosis and tubular orientation on Class V restoration bonded with three dentin bonding agents using confocal laser scanning microscope(CLSM). Class V cavities were prepared from freshly extracted caries-free human teeth. thirty of these cavities were divided into two groups based upon the status of class V cavities: Group 1, cervical abrasive lesions without preparation; Group 2, artificially-prepared wedge-shaped cavities.(omitted)

• Restorative Dentistry and Endodontics
• /
• v.30 no.3
• /
• pp.204-214
• /
• 2005

This study compared the microtensile bond strength (${\mu}$TBS) and microscopic change of two 2-step and two 1-step self-etching adhesives to dentin according to storage times in distilled water. Occlusal dentin was exposed in 48 human molars. They were divided to four groups by different adhesives: SE Bond group (Clearfil SE Bond), AdheSE group (AdheSE). Adper group (Adper Prompt L-Pop), and Xeno group (Xeno III) . Each group was stored in 37$^{\circ}C$ distilled water for 1, 15, and 30 days. Resin-bonded specimens were sectioned into beams and subjected to ${\mu}$TBS testing with a crosshead speed of 1 mm/minute. For SEM observation, one specimen was selected and sectioned in each group after each stroage time. Resin-dentin interface was observed under FE-SEM. In all storage times, mean ${\mu}$TBS of SE group was significantly higher than those of other groups (p < 0.05). There was no significant difference between mean ${\mu}$TBS of SE group and AdheSE group among all storage times, but significant difference between 1- and 30-day storage in mean y${\mu}$TBS of Adper group and Xeno group (p > 0.05). For 1-and 15-day storage, all groups showed the close adaptation between resin-dentin interfaces. For 30-day storage, resin-dentin interfaces showed wide gap in Adper group and separate pattern in Xeno III group.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.4
• /
• pp.636-644
• /
• 2004

Recently, self-etching adhesive system have been developed and bonding procedures simplified into one or two steps, which are simultaneously applied to both enamel and dentin. These systems are easy to use and have the potential for good clinical success. The purpose of this study is to evaluate in vitro the microleakage on the cementum/dentin and enamel walls in composite resin restoration of Class V cavities, regarding the use of different adhesive systems. 30 human premolars were divided into 3 groups. A standardized Class V preparation was prepared on the buccal and lingual surface of each premolar. The preparation were made parallel to the cementoenamel junctions, with the gingival half of the preparation extending 1mm apical to the cementoenamel junction. After adhesive system was applied to teeth as manufacture's recommendation, hybrid resin composite was filled in bulk into the preparation and light polymerized according to manufacturer's recommendations. Specimen were stored in distilled water at $37^{\circ}C$ for 5 days and thermocycled 1000 times ($5^{\circ}C{\pm}2^{\circ}C\;and\;55^{\circ}C{\pm}2^{\circ}C)$, then immersed in a 2% methylene blue solution for 12 hours. After sectioning mesio distally through the restorations, the degree of dye penetration was scored under a stereomicroscope at ${\times}\;25$ magnification. The data were analyzed statistically using t-test and one-way ANOVA. The results were as follows: ${\cdot}$ There is no adhesive system which can prevent microleakage perfectly. ${\cdot}$ There is significant difference in microleakage between enamel margin and dentin margin (p<0.0001). ${\cdot}$ In enamel margin, self-etching primer systems did not show any significant difference comparing total-etching system. In denin margin, self-etching primer systems did not show any significant difference comparing one-bottle adhesive system used in combination with total-etching.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.4
• /
• pp.619-627
• /
• 2008

The objective of this study was to compare the microleakage of five adhesive systems in the enamel and dentin of permanent teeth. Class V cavity preparations with occlusal margins in enamel and gingival margins in dentin were prepared on both buccal and lingual surfaces of 25 extracted human molar teeth. The tested adhesives were: Adper Scotchbond Multi-purpose Plus Adhesive (SM), Adper Single bond 2 (SB), Clearfil SE Bond (SE), Adper Prompt L-Pop (PL) and G-Bond (GB). The results were as follows: 1. At the enamel margins, PL showed the highest leakage value(0.85), and others showed values of SB(0.55), GB(0.50), SM(0.35) and SE(0.25) in decreasing order. There were statistically significant differences in PL vs. SM and PL vs. SE(p<0.05). 2. At the dentin margins, GB showed the highest leakage value(2.10), and others showed values of SE(1.45), PL(1.40), SB(1.05), SM(0.70) in decreasing order. There were statistically significant differences in GB vs. SB and GB vs. SM(p<0.05). 3. Dentin margins showed high dye penetration rate than enamel margins in all material tested groups and there were statistically significant differences for SE, PL and GB.

• Restorative Dentistry and Endodontics
• /
• v.27 no.3
• /
• pp.299-309
• /
• 2002

The purposes of this study were to evaluate the microtensile bond strength of one-step adhesives accord ing to various dentin surface treatments and to observe the interface between resin(Z-100$^{TM}$) and dentin under SEM. In this study forty-five non-caries extracted human molars and three adhesive systems were used ; AlI-Bond 2(AB), One-Up Bond F(OU), AQ-Bond(AQ). ; In Group 1, 2, 3, AB was used and tooth surfaces were treated by smearing(S), ultrasonic cleansing(US), etching(E) respectively. In Group 4. 5, 6, One-Up Bond F was used and tooth surfaces were also treated as the same way above. In Groups 7, 8, 9, AQ Bond was used and tooth surfaces wet$.$e treated as the same way. Each specimen was prepared for microtensile bond testing, and were stored for 24hrs in 37$^{\circ}C$ distilled water. After that, microtensile bond strength for each specimen was measured. Specimens were fabricated to examine the failure patterns of interface between resin and dentin and observed under the SEM. The results were as follows ; 1. The results(mean$\pm$SD) of microtensile test were group 1, 25.69$\pm$4.31MPa; group 2, 40.93$\pm$10.94MPa; group 3, 47.65$\pm$8.85MPa； group 4, 35.98$\pm$9.14MPa； group 5, 39.66$\pm$8.45MPa; group 6, 43.26$\pm$13.01MPa; group 7, 25.07$\pm$4.2MPa；group 8, 30.4$\pm$4.74MPa；group 9, 33.61$\pm$7.88MPa. 2. One-Up Bond F was showed the highest value of 36.98$\pm$9.14MPa in dentin surface treatment with smearing, and there were significant differences to the other groups (p<0.05). 3. All-Bond 2 was showed the highest value of 40.93$\pm$10.94MPa in dentin surface treatment with ultra-sonic cleansing, but was no significant difference to One-Up Bond F(p>0.05) 4. All-Bond 2 was showed the highest value of 47.65$\pm$8.85MPa in dentin surface treatment with etch ing(10%phosphoric acid), and there were significant differences to the other groups(p<0.05). 5. All-Bond 2 was showed the highest value of 47.65$\pm$8.85MPa in dentin surface treatment according to manufacture's directions. but was no significant difference to One-Up Bond F(p>0.05). 6. AQ Bond was skewed the lowest microtensile bond strength with various dentin surface treatment, and the were significant differences to the other groups(p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.28 no.3
• /
• pp.203-208
• /
• 2003

The purpose of this study was to evaluate the effect of salivary contamination of teeth on bonding efficacy of self-priming and self-etching DBSs. The materials used were Single Bond(SB, self-priming system, 3M), Unifil Bond(UB, self-etching system, GC), and Scotchbond Multi-Purpose Plus(SM, 3M) as control. Forty five human molars randomly allocated to three groups as dentin bonding systems tested and embedded in epoxy resin. Then the specimens were wet-ground to expose flat buccal enamel surface or flat occlusal dentin surface and cut bucco-lingually to form two halves with slow speed diamond saw. One of them was used under non-contamination, other under contamination with saliva. The bonding procedure was according to the manufacturer's directions and resin composite(Z-100, 3M Dental Products, St. Paul, MN) was built-up on the bonded surface 5mm high. The specimens were ground carefully at the enamel-composite interface with fine finishing round diamond bur to create an hour-glass shape yielding bonded surface areas of $1.5{\pm}0.1\textrm{mm}^2$. The specimens were bonded to the modified microtensile testing apparatus with cyanoacrylate, attached to the universal testing machine and stressed in tension at a CHS of 1mm/min. The tensile force at failure was recorded and converted to a tensile stress(MPa). Mean values and standard deviations of the bond strength are listed in table. One-way ANOVA was used to determine significant difference at the 95% level. The bond strength of SBMP and SB were not affected by salivary contamination, but that of UB was significantly affected by salivary contamination. These results indicate that DBSs with total etch technique seems less likely affected by salivary contamination in bonding procedure.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.45 no.4
• /
• pp.445-454
• /
• 2018

The aim of this study was to measure the shear bond strength (SBS) of different adhesive systems to calcium silicate-based materials (Biodentine and RetroMTA). Eighty cylindrical acrylic blocks, with a hole (5.0 mm diameter, 2.0 mm height) in each, were prepared. The holes were filled with Biodentine (BD) and RetroMTA (RMTA), and the specimens were divided into 2 groups. Each group was classified into 4 subgroups: Clearfil$^{TM}$ SE (CSE) ; AQ bond (AQ) ; All bond universal Self-etch (ABU-SE) ; and All bond universal Total-etch (ABU-TE). After the application of different adhesive systems, composite resin (Z350) was applied over BD and RMTA. The SBS was measured using a universal testing machine, and the data were compared using the Kruskal-Wallis test and the Mann-Whitney test. The highest and lowest values of SBS were observed for BD-ABU-SE and RMTA-AQ, respectively. No significant differences were found in the SBS between ABU-TE and ABU-SE and between ABU-TE and CSE to BD and RMTA. According to the data, BD showed a higher SBS than did RMTA when BD and RMTA are compared in the same adhesive agents. Further, among all groups, composite resin with ABU-SE showed better bond strength to BD and RMTA.

• Restorative Dentistry and Endodontics
• /
• v.34 no.1
• /
• pp.51-60
• /
• 2009

The purpose of this study was to perform quantitative comparisons of water permeable zones in both the adhesive and the hybrid layer before and after thermo cycling in order to assess the integrity of the bonding interface. Twenty eight flat dentin surfaces were bonded with a light-cured composite resin using one of four commercial adhesives [OptiBond FL (OP), AdheSE (AD), Clearfil SE Bond (CL). and Xeno III (XE)]. These were sectioned into halves and subsequently cut to yield 2-mm thick specimens; one specimen for control and the other subjected to thermocycling for 10,000 cycles. After specimens were immersed in ammoniacal silver nitrate for 24 h and exposed to a photo developing solution for 8 h, the bonded interface was analyzed by scanning electron microscopy (SEM) and wavelength dispersive spectrometry (WDS) at five locations per specimen. Immediately after bonding. the adhesive layer of OP showed the lowest silver uptake, followed by CL, AD. and XE in ascending order (p < 0.0001); the hybrid layer of CL had the lowest silver content among the groups (p = 0.0039). After thermocycling, none of the adhesives manifested a significant increase of silver in either the adhesive or the hybrid layer. SEM demonstrated the characteristic silver penetrated patterns within the interface. It was observed that integrity of bonding was well maintained in OP and CL throughout the thermocycling process. Adhesive-tooth interfaces are vulnerable to hydrolytic degradation and its permeability varies in different adhesive systems, which may be clinically related to the restoration longevity.