• Restorative Dentistry and Endodontics
• /
• v.24 no.1
• /
• pp.55-66
• /
• 1999

The purpose of this study was to evaluate the microleakage of 5 current dentin bonding systems which are composed of 2 multi-bottle systems(Scotchbond Multi-Purpose, All Bond2) and 3 one-bottle systems(Single bond, One-Step, Prime & Bond). In this in vitro study, class V cavities were prepared on buccal and lingual surfaces of sixty extracted human premolars and molars on cementum margin. The experimental teeth were randomly divided into six groups of 10 samples (20 surfaces) each, Group 1 : Scotchbond Multi-Purpose ; Group 2 : All Bond 2 ; Group 3 : Single Bond ; Group 4 : One-Step ; Group 5 : Prime & Bond ; Group 6 : no bonding agent(control). The bonding agent and composite resin were applied for each group following the manufacturer's instructions. After 500 thermocycling between $5^{\circ}C$ and $55^{\circ}C$, the 60 teeth were placed in 2% Methylene blue dye for 24 hours, then rinsed with tab water. The specimen were embedded in clear resin, then sectioned buccolingually through the center of restoration with a low speed diamond saw. The dye penetration on each of the specimen were then observed with a stereomicroscope at ${\times}20$. The results of study were statistically analyzed using the Student-Newmann-Keul's Methods and the Mann-Whitney Rank Sum Test. The resin/dentin interfaces were examined under Scanning Electron Microscopy. The results of this study were as follows. 1. None of the dentin bonding systems used in this study showed significant difference in leakage values at both the enamel and the dentin margins (P>0.05). 2. In all groups except the control, leakage value seen at the enamel margin was significantly lower than that seen at the dentin margin (P<0.05). 3. Compared to the control group, all the groups treated with dentin bonding systems showed significantly lower leakage value at both enamel and dentin margins (P<0.05). 4. In the SEM view, gaps were observed in the composite resin / dentin interface in group 6 where no dentin bonding agent was used, and in all the other groups (group 1, 2, 3, 4, 5) composite resin, hybrid layer, and dentin were seen to be closely adhering to each other where there were no leakages. Well-developed resin tags 3~100${\mu}m$ in length infiltrated dentinal tubules past the hybrid layer and a hybrid layer 1~5${\mu}m$ thick had developed between the dentinal surface and the composite resin surface.

• Restorative Dentistry and Endodontics
• /
• v.28 no.3
• /
• pp.209-221
• /
• 2003

The objectiveness of this study was to evaluate whether low-viscosity composite can bond effectively to dentin surface without bonding resin. The low-viscosity composites being 50wt% filler content were made by the inclusion of bonding resin of two self-etching systems(Cleafil SE Bond, Unifil Bond) varied with contents as 0, 10, 20, 30, 40, 50wt%. Exposed dentin surfaces of extracted 3rd molars are used. Dentin bond strengths were measured. The tests were carried out with a micro-shear device placed testing machine at a CHS of 1mm/min after a low-viscosity composite was filled into an iris cut from micro tygon tubing with internal diameter approximately 0.8mm and height of 1.0mm. 1 Flexural strength and modulus was increased with the addition of bonding resin. 2. Micro-shear bond strength to dentin was improved according to content of bonding resin irrespective of applying or not bonding resin in bonding procedure, and that of Clearfil SE Bond groups was higher than Unifil Bond. 3. There were no significant difference whether use of each bonding resin in bonding procedure for S-40, S-50, U-50(p＞0.05). 4. In SEM examination, resin was well infiltrated into dentin after primed with self-etching primer only for S-50 and U-50 in spite of the formation of thinner hybrid layer. Low viscosity composite including some functional monomer may be used as dentin bonding resin without an intermediary bonding agent. It makes a simplified bonding procedure and foresees the possibility of self-adhesive restorative material.

• Restorative Dentistry and Endodontics
• /
• v.46 no.2
• /
• pp.30.1-30.13
• /
• 2021

Objectives: This study was conducted to compare the microleakage and characteristics of the resin-tooth tissue interface between self-etch and etch-and-rinse adhesive systems after 48 hours and 3 months. Materials and Methods: 40 extracted premolar teeth were randomly divided into 2 groups: 1-step self-etch adhesive system - Optibond^TM All-In-One, and 2-step etch-and-rinse adhesive system - Adper^TM Single Bond 2. Both groups were subjected to 500 thermocycles (5℃-55℃) before scanning electron microscope (SEM) analysis or microleakage trial at 48-hour and 3-month time periods. Results: SEM images showed the hybrid layer thickness, diameter, and length of resin tags of the self-etch adhesive (0.42 ± 0.14 ㎛; 1.49 ± 0.45 ㎛; 16.35 ± 14.26 ㎛) were smaller than those of the etch-and-rinse adhesive (4.39 ± 1.52 ㎛; 3.49 ± 1 ㎛; 52.81 ± 35.81 ㎛). In dentin, the microleakage scores of the 2 adhesives were not different in both time periods (48 hours/3 months). However, the microleakage score of etch-and-rinse adhesive increased significantly after 3 months (0.8 ± 0.63 and 1.9 ± 0.88, p < 0.05). Conclusions: The self-etch adhesive exhibited better long-term sealing ability in dentin when compared to that of the etch-and-rinse adhesive. The greater hybrid layer thickness and dimensions of resin tags did not guarantee reliable, long-lasting sealing in the bonding area.

• Restorative Dentistry and Endodontics
• /
• v.33 no.6
• /
• pp.526-536
• /
• 2008

The purpose of this study was to compare the effect of various dentin bonding systems on microtensile bond strength of immediate dentin sealing (IDS) and delayed dentin sealing (DDS). Eighteen extracted permanent molars were used in this study. The teeth for DDS group were restored with a provisional restorations, and immersed in saline solution for 1 week, and divided into 3 subgroups according to various dentin bonding adhesives; SB subgroup (3 step total-etch adhesive), SE subgroup (2 step self-etch adhesive), XE subgroup (1 step self-etch adhesive). In IDS group, the teeth were divided into 3 subgroups, and applied with bonding adhesives as in DDS group. The teeth were restored with provisional restorations, and immersed in saline solution for 1 week. Indirect composite disc was cemented with resin cement, and all specimens were subjected to microtensile bond strength. The data were statistically analyzed with oneway ANOVA and Student t-test. The results were as follows: 1. The IDS group showed significantly higher ${\mu}TBS$ than DDS group in 3 step total-etch and 2 step selfetch adhesive (p < 0.05). 2. In IDS and DDS group, 3 step total-etch adhesive showed the highest ${\mu}TBS$ value, followed by 2 step self-etch, and 1 step self-etch adhesive. In IDS group, the ${\mu}TBS$ value for 1 step self-etch adhesive was significantly different from those of the other subgroups (p < 0.05), and in DDS group, there were statistical differences in all subgroup (p < 0.05). 3. Failure modes of tested dentin bonding adhesives were mostly mixed failure and only 1 step self-etch adhesive showed adhesive failure.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.580-580
• /
• 2001

Before resin composites can serve as durable substitutes for amalgam restorations, the adhesive system used to retain them and add to seal dentin must be improved. The recent observations, using the newly developed LVDT (linear variable differential transformer) probe, that all commercial bonding systems cause a collapse of the demineralized dentin matrix, simulated a re-evaluation of the effects of these formulations on the matrix. The experiment was begun by examining solvents such as water-HEMA mixtures. These produced the same shrinkages as did the complete formulations.(omitted)

• Proceedings of the KACD Conference
• /
• 2002.11a
• /
• pp.717-717
• /
• 2002

No Abstract, See Full Text

• Restorative Dentistry and Endodontics
• /
• v.28 no.5
• /
• pp.392-401
• /
• 2003

The purpose of this study was to evaluate the penetration pattern of dentin adhesives according to the orientation of dentinal tubules with confocal laser scanning microscopy. Specimens having perpendicular. parallel and oblique surface to dentinal tubules were fabricated. The primer of dentin adhesives (ALL $BOND^{\circledR}{\;}2,{\;}CLEARFIL^{TM}$ SE BOND and PQ1) was mixed with fluorescent material. rhodamine B isothio-cyanate (Aldrich Cherm. CO., Milw., USA), It was applied to the specimens according to the instructions of manufactures. The specimens were covered with composite resin (Estelite, shade A2) and then cut to a thickness of 500$\mu\textrm{m}$ with low speed saw (Isomet^{TM}, Buehler. USA). The adhesive pattern of dentin adhesives were observed by fluorescence image using confocal laser scanning microscopy. The results were as follows. 1. For the groups with tubules perpendicular to bonded surface. funnel shape of resin tag was observed in all specimen. However. resin tags were more prominent in phosphoric acid etching system (ALL $BOND^{\circledR}$ 2 and PQ1) than self etching system ($CLEARFIL^{TM}$ SE BOND). 2. For the groups with tubules parallel to bonded surface. rhodamine-labeled primer penetrated into peritubular dentin parallel to the orientation of dentinal tubules. But rhodamine-labeled primer of PQ1 diffused more radially into surrounding intertubular dentin than other dentin adhesive systems. 3. For the groups with tubules oblique to bonded surface. resin tags appeared irregular and discontinuous. But they penetrated deeper into dentinal tubules than other groups.

• Restorative Dentistry and Endodontics
• /
• v.29 no.5
• /
• pp.430-438
• /
• 2004

This study evaluated the influence of application time of self-etching primers on microtensile bond strength (${\mu}$TBS) to dentin using three self-etching primer adhesive systems. Dentin surfaces were exposed from forty-eight human molars. They were conditioned with three self-etching primers (Clearfil SE Bond [SE], Unifil Bond [UF], Tyrian SPE + One Step Plus [TY]) and different primining times (10s, 20s, 30s and 40s). Composite resins were bonded to dentin surfaces and specimens were made. ${\mu}TBS$ was tested and statistically compared using by one-way ANOVA and Tukey's Test. The results of this study presented that priming time for 10s in SE and UF groups and for 30s and 40s in TY group was highly decreased ${\mu}TBS$ to dentin.

• Restorative Dentistry and Endodontics
• /
• v.24 no.2
• /
• pp.310-321
• /
• 1999

In this in vitro study, confocal laser scanning microscopic morphology of dentin-resin interface and its relationship to shear bond strength were investigated after the exposed dentin surfaces were treated with 3 different kinds of dentin adhesive systems[three-step; Scotchbond Multi-Purpose Plus(SMPP), self-priming bonding resin; Single Bond(SB), self-etching primer; Clearfil Liner Bond 2(LB2)]. 52 extracted human molar teeth without caries and/or restorations. The experimental teeth were randomly divided into three groups of seventeen teeth each. In five teeth of each group, class V cavities(depth: 1.5mm) with 900 cavosurface angles were prepared at the cementoenamel junction on buccal and lingual surfaces. Bonding resins of each dentin adhesive system were mixed with rhodamine B. Primer of SMPP was mixed with fluorescein. In group 1. the exposed dentin was conditioned with etchant, applied with above primer and bonding resin of SMPP. In group 2, with etchant and self-priming bonding agent of SB. In group 3, with self-etching primer and bonding agent of LB2. After treatment with dentin adhesive systems, composite resin were applied and photocured. The experimental teeth were cut longitudinally through the center line of restoration and grounded so that about $90{\mu}m$-thick wafers of buccolingually orientated dentin were obtained. And, $70{\sim}80{\mu}m$-thick wafers sectioned horizontally, thus presenting a dentinal tubules at 900 to the cut surface of a remaining tooth, were obtained. Primer of SMPP mixed with rhodamine B was applied to these wafers. Confocal laser scanning microscopic investigations of these wafers were done within of 24 hours after treatment. To measure shear bond strength, the remaining twelve teeth of each group were grounded horizontally below the dentinoenamel junction, so that no enamel remained. After applying dentin adhesive systems on the dentin surface, composite was applied in the shape of cylinder. The cylinder was 5mm in diameter, and 2mm in thickness. Shear bond strength was measured using Instron with a cross-head speed of 0.5mm/min. It was concluded as follows ; 1. Hybrid layer of SMPP(mean: $4.56{\mu}m$) was thicker than that of any other groups. This value was not statistically significant thicker than that of SB(mean: $3.41{\mu}m$, p>0.05), and significant thicker than that of LB2(mean: $1.56{\mu}m$, p<0.05). There was a statistical difference between SB and LB2(p<0.05). 2. Although there were variations in the length of resin tag even in a sample, and in a group, most samples in SMPP and SB showed resin tags extending above $20{\mu}m$. But samples in LB2 showed resin tags of $10{\mu}m$ at best. 3. Besides primer's infiltration into demineralized peritubular dentin and dentinal tubules, fluorophore of primer was detected in the lateral branches of dentinal tubules. 4. All groups demonstrated statistically significant differences from one another(p<0.05), with shear bond strengths given in descending order as follows: SMPP(18.3MPa), SB(16.0MPa) and LB2(12.4MPa). 5. LB2 having thinnest hybrid layer($1.56{\mu}m$) showed the lowest shear bond strength(12.4MPa).

• Restorative Dentistry and Endodontics
• /
• v.39 no.1
• /
• pp.24-31
• /
• 2014

Objectives: The purpose of present study was to evaluate the internal adaptation of composite restorations using different adhesive systems. Materials and Methods: Typical class I cavities were prepared in 32 human third molars. The teeth were divided into the following four groups: 3-step etch-and-rinse, 2-step etch-and-rinse, 2-step self-etch and 1-step self-etch system were used. After the dentin adhesives were applied, composite resins were filled and light-cured in two layers. Then, silver nitrate solution was infiltrated, and all of the samples were scanned by micro-CT before and after thermo-mechanical load cycling. For each image, the length to which silver nitrate infiltrated, as a percentage of the whole pulpal floor length, was calculated (%SP). To evaluate the internal adaptation using conventional method, the samples were cut into 3 pieces by two sectioning at an interval of 1 mm in the middle of the cavity and they were dyed with Rhodamine-B. The cross sections of the specimens were examined by stereomicroscope. The lengths of the parts where actual leakage was shown were measured and calculated as a percentage of real leakage (%RP). The values for %SP and %RP were compared. Results: After thermo-mechanical loading, all specimens showed significantly increased %SP compared to before thermo-mechanical loading and 1-step self-etch system had the highest %SP (p < 0.05). There was a tendency for %SP and %RP to show similar microleakage percentage depending on its sectioning. Conclusions: After thermo-mechanical load cycling, there were differences in internal adaptation among the groups using different adhesive systems.