• Archives of Metallurgy and Materials
• /
• v.66 no.4
• /
• pp.1007-1011
• /
• 2021

The microstructure and mechanical properties of hot-rolled Fe-9Mn-0.2C medium-manganese steels with different Al, Cu, and Ni contents were investigated in this study. Based on the SEM, XRD, and EBSD analysis results, the microstructure was composed of martensite, band-type delta ferrite, and retained austenite phases depending on the Al, Cu, and Ni additions. The tensile and Charpy impact test results showed that the sole addition of Al reduced significantly impact toughness by the presence of delta-ferrite and the decrease of austenite stability although it increased yield strength. However, the combined addition of Al and Cu or Ni provided the best combination of high yield strength and good impact toughness because of solid solution strengthening and increased austenite stability.

• Korean Journal of Materials Research
• /
• v.6 no.12
• /
• pp.1221-1232
• /
• 1996

용접부 인성을 향상시키기 위해 Ti 산화물을 첨가한 Ti 산화물강에 대하여 용접시 최고가 열온도와 냉각속도의 변화가 용접열영향부의 미세조직에 미치는 영향을 조사하였다. 용접열영향부의 인성향상에 기여하는 acicular ferrite는 140$0^{\circ}C$ 이상의 최고가열온도와 $\Delta$t800-500가 40초보다 빠른 냉각속도에서 활발해 생성되었다. 오스테나이트 결정립내에서 개재물로부터 핵생성된 일차 acicular ferite의 생성량은 전체 aicular ferrite의 약 20% 정도로 적었으며 대부분의 acicular ferrite는 일차 acicular ferrite로부터 생성된 이차 acicular ferrite인 것으로 나타났다. 이차 acicular ferrite는 plate사이에 Fe3C층이 존재하는 것으로 보아 확산기구에 의해 생성되는 것으로 생각된다. 개재물은 TiO, TiO2, TiN, MnS, AI2O3 MnO(galaxite)등으로 구성된 복합상이었으며 개재물이 일차 acicular ferrite의 핵생성 site로 작용하기 위해서는 약 1$\mu\textrm{m}$이상의 크기가 효과적인 것으로 나타났다. Ti 산화물과 TiN는 직접적인 acicular ferrite의 핵생성 site로 작용하기보다는 MnS, galaxite 등의 석출 site로 작용하여 개재물의 크기를 증가시킴으로써 acicular ferrite의 생성을 촉진시키는 것으로 생각된다.

• Korean Journal of Materials Research
• /
• v.10 no.3
• /
• pp.223-226
• /
• 2000

The oxygen deficient ferrites $(Ni_x,\; Zn_{1-x})Fe_2O_{4-{\delta}}$ can decompose $CO_2$ as C and $O_2$ at a low temperature of about $300^{\circ}C$. Ultra powders of $(Ni_x,\; Zn_{1-x})Fe_2O_4$ for the $CO_2$ decomposition were prepared by the hydrothermal methods. The XRD result of synthesized ferries showed the spinel structure of ferrites and ICP-AES and EDS quantitative analyses showed the composition similar with the starting molar ratios of the mixed solution prior to reaction. The BET surface area of the synthesized(Ni, Zn)-ferrites was above $110\textrm{m}^2/g$ and its particle size was very as small as about 5~10 nm. The $CO_2$ decomposition efficiency of the oxygen deficient ferrites($(Ni_x,\;Zn_{1-x})Fe_2O_{4-{\delta}}$) was almost independent with composition and the $CO_2$ decomposition efficiency of ternary (Ni, Zn)-ferrites was better than of binary Ni-ferrites.

• Journal of Welding and Joining
• /
• v.33 no.4
• /
• pp.37-43
• /
• 2015

Characteristics of dissimilar metal welds between STS 316L and carbon steel ASTM A516 Gr.70 made with GTAW have been evaluated in terms of microstructure, ferrite content, chemical analysis, hardness and corrosion resistance. Three heat inputs of 9.00, 11.25, 13.00kJ/cm were employed to make joints of dissimilar metals with ER309 wire. Based on microstructural examination, the amount of vermicular type of ${\delta}$-ferrite was increased with increasing heat input due to the increase of Creq/Nieq in the second layer of welds. Based on the EDX analysis of weld metals, Cr and Ni content in the 2nd layer increased while those content in the first layer of welds decreased with heat inputs. Cellular solidification mode in the 1st layer and dendritic solidification mode in the 2nd layer due to different cooling rates were prevailed, respectively. Heat affected zone which formed hard microstructure showed higher hardness than the weld metal. The salt spray test of dissimilar metals weld joints showed that the carbon steel surfaces only corroded. The weight loss rate due to corrosion increased up to 100hours but it decreased above 100 hours. There was little difference in the weight loss caused by corrosion regardless of heat inputs.

• Journal of Welding and Joining
• /
• v.32 no.2
• /
• pp.29-36
• /
• 2014

Recently, in order to enhance the function and usefulness of products, cladding of dissimilar materials that maximizes the performance of the material is being widely used in all areas of industry as an important process. Clad steel plate, produced by cladding stainless steel plate, an anticorrosive material, on carbon steel plate, is being used to produce pressure vessels. Stainless steel plate has good corrosion resistance, and carbon steel plate has good rigidity and strength; clad steel can satisfy all of these qualities at once. This study aims to find the ${\delta}$-ferrite behavior, mechanical properties, structure change, integrity and reliability of clad steel weld on hot rolled steel plates. For this purpose, multi-layer welding, repair welding and post weld heat treatment were implemented according to welding procedure specifications (WPS). In order to observe the mechanical properties and toughness of clad steel weld zone, post weld heat treatment was carried out according to ASME Sec. VIII Div.1 UW-40 procedure for post weld heat treatment. With heat treatment at $625^{\circ}C$, the hold time was used as the process variable, increased by intervals that were doubled each time, from 80 to 1,280 min. The structure of weld part was typical cast structure; localized primary austenite areas appeared near central vermicular ferrite and fusion line. The heat affected zone showed rough austenite structure created by the weld heat input. Due to annealing effects of heat treatment, the mechanical properties (tensile strength, hardness, impact value) of the heat affected area tended to decrease. From the results of this study, it is possible to conclude the integrity of clad steel welds is not affected much in field welding, repair welding, multi-layer welding, post weld heat treatment, etc.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1491-1500
• /
• 1994

Nonstoichiometry($\delta$) and the phase stability region of a ferrite spinel (Mg0.29Fe0.71)3-$\delta$O4 have been investigated by a coulometric titration method as a function of temperature(T) and oxygen partial pressure(Po2). It has been found that the spinel is thermodynamically stable in the ranges -8.0$\leq$log(PO2/atm)$\leq$-2.4, -7.0$\leq$log(PO2/atm)$\leq$-1.7 respectvely at 100$0^{\circ}C$. The nonstoichiometry extends over the ranges of -0.004$\leq$$\delta$$\leq$0.007, -0.008$\leq$$\delta$$\leq$0.006, -0.033$\leq$$\delta$$\leq$0.004 at 100$0^{\circ}C$, 120$0^{\circ}C$, respectvely. The observed PO2-dependence of $\delta$ suggests that the majority ionic defects are cation interstitials in the low PO2 region and cation vacancies in the high PO2 region.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2001.05a
• /
• pp.294-294
• /
• 2001

• Journal of the Korean Ceramic Society
• /
• v.19 no.3
• /
• pp.223-228
• /
• 1982

For the preparation of ferroxidure BaO.5.5 $Fe_2O_3$ with high coercive force, the green and calcined coprecipitates, which were obtained by neutralizing the mixed salt solution $FeCl_2-BaCl_2$ and $FeCl_3-BaCl_2$ with alkali solution $NaOH-Na_2CO_3$, were investigated about the thermal reaction, crystal growth, and the magnetic properties of the sintered specimens. The very single-domain crystallites of Ba-ferrite with high coercive force are formed from the coprecipitate of amorphous $Fe(OH)_3$ and amorphous $BaCO_3$ at lower temperature than that of subnucleus crystalline $\delta$-FeOOH and amorphous $BaCO_3$.

• Journal of the Korean institute of surface engineering
• /
• v.21 no.4
• /
• pp.176-182
• /
• 1988

Effects of Cr, Ni and W on the anodic polarization behavior were investigated for Fe-Cr-Ni-W alloys in deaerated 1N HCI solution. Surface films formed on the polarization were analysed using AES, SEM and EDAX. A higerconcentration of tungten was found in the surface oxide film compared to the matrix. It played an importanet role on incresing the stability of the passive film. The presence of an adequate amount of Cr was essential to increase the pitting resistance of the alloys in acid chloride media. Under 12 wt%cr,alloys containing 6wt%W did not exhidit any passivity at all. The main role of Ni was to control the microstructure rather than to modify the corrosion resistance. In 23 cr-14Ni-^W alloy, the duplex microstructure of ferrite($\delta$-phase) in an austenic matrix was developed. The reson why proferred pitting appeared in austenite and ferrite/austenite interface was that ferrite had more amount of Cr and W than austenite.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.836-842
• /
• 1998

In this experiment well-know additives for Mn-Zn ferrites CaO and {{{{ { SiO}_{2 } }} were added at various content and their effects on microstructures and magnetic properties with sintering atmosphere were examined. By adding up to 0.04wt% {{{{ { SiO}_{2 } }} and and 0.06wt% CaO the sintered density was increased and then decreased gra-dually. Higher sintered density and initial permeability were observed by adding both CaO and {{{{ { SiO}_{2 } }} than by adding CaO or {{{{ { SiO}_{2 } }} alone. Without any additives initial permeability and tan$\delta$/${\mu}$ decreased at 1000kHz as oxidation degree(${\gamma}$) increased.