• Journal of the Korean Ceramic Society
• /
• v.40 no.6
• /
• pp.553-559
• /
• 2003

PDP rib is one of the important parts of manufacturing process and the sintering degree of rib plays an important role to prevent some problems such as cross talk. Nowadays, the screen-printing method, which is a low price and high production, is used to make a rib. However, it is hard to judge and value the sintering ratio of sintered body itself. In this study, we measured the sintering degree by the dielectric breakdown of pores with the potentiostat. We conformed that this has similar tendency to density of sintered samples and an error being expected by open and closed pores was inspected by change of the microstructure to scanning electron microscope. This result showed that the sintering degree of PDP rib could be analyzed into the electro-chemical method.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.1
• /
• pp.18-25
• /
• 1998

G $d_{0.2}$C $e_{0.8}$ $O_{1.9}$(CGO) for electrolyte and L $a_{0.5}$S $r_{0.5}$Mn $O_3$(LSM50) for cathode in Solid Oxide Fuel Cells(SOFC) were synthesized by citrate process. Specimens were prepared with sintering temperatures at 110$0^{\circ}C$, 120$0^{\circ}C$ and 130$0^{\circ}C$, which were fabricated by slurry coating with citric acid contents. Interfacial resistance was measured between cathode and electrolyte using AC-impedance analyzer. With various citric acid content, the degree of agglomeration for the initial particles changed. Also sintering temperature changed the particle size and the degree of densification of cathode. Factors affecting the interfacial resistance were adherent degree of the electrolyte and cathode, distribution of TPB(three phase boundaries, TPB i.e., electrolyte/electrode/gas phase area) and porosity of cathode. By increasing the sintering temperature, particle size and densification of the cathode were increased. And then, TPB area which occurs catalytic reaction was reduced and so interfacial resistance was increased.sed.sed.d.

• Journal of Powder Materials
• /
• v.7 no.4
• /
• pp.218-227
• /
• 2000

It is well known that the Cu-Cr alloys are very difficult to be made by conventional sintering methods. This difficulty originates both from limited solubility of Cr in the Cu matrix and from limited sintering temperature due to high vapor pressures of Cr and Cu components at the high temperature. Densification of Cu-50%Cr Powder compacts by conventional Powder metallurgy Process has been studied. Three kinds of sintering methods were tested in order to obtain high-density sintered compacts. Completely densified Cu-Cr compacts could be obtained neither by solid state sintering method nor by liquid phase sintering method. Both low degree of shrinkage and evolution of large pores in the Cu matrix during the solid state sintering are attributed to the anchoring effect of large Cr particles, which inhibits homogeneous densification of Cu matrix and induces pore generation in the Cu matrix. In addition, the effect of undiffusible gas coming from the reduction of Cu-oxide and Cr-oxide was observed during liquid phase sintering. A two-step sintering method, solid state sintering followed by liquid phase sintering, was proved to have beneficial effect on the fabrication of high-dendsity Cu-Cr sintered compacts. The sintered compacts have properties similar to those of commercial products.

• The Korean Journal of Ceramics
• /
• v.5 no.3
• /
• pp.235-238
• /
• 1999

In a ceramic green body, some degree of nonuniformity in density always presents. These differences in green density will appear as nonuniform shrinkage after sintering takes place. For the complex ceramic bodies with various curves and angles, therefore, it is quite difficult to foresee the final dimensions precisely after sintering. This simulation study shows that, considering the sintering process as a thermal shrinkage phenomenon, the use of NASTRAN enables to predict the precise shape of a sintered body. Based on this result, 'the reverse engineering technique' has been developed that can unfold the exact dimensions of a green body to have the desired shape after sintering. This approach will provide a simple and useful tool for ceramic engineers to fabricate complicate bodies with tight dimensional tolerances.

• Electrical & Electronic Materials
• /
• v.8 no.2
• /
• pp.158-164
• /
• 1995

Solid solutions Sr$_{2}$(Ta$_{1-x}$ Nb$_{x}$)$_{2}$O$_{7}$, (x=0.0-1.0), composed of strontium tantalate(Tc=-107.deg. C) and strontium-niobate(Tc=1342.deg. C) were prepared by the conventional mixed oxide method and the flux method(molten salt synthesis method). Phase relation, sintering temperature, grain-orientation and dielectric properties for sintered ceramic samples were investigated with different compositions. Both Curie temperature and dielectric constant at Curie temperature were increased, and sintering behavior and the degree of grain-orientation were improved with the increase of Nb content. The single phase Sr$_{2}$(Ta/sib 1-x/Nb$_{x}$)$_{2}$O$_{7}$ powder was synthesized by using the flux method at lower temperatures, and sintering temperature was also reduced by using the flux method-derived powder than using the mixed oxide-derived powder. Sintering characteristics and dielectric properties of the specimens prepared by the flux method were better than those derived through the conventional mixed oxide method.thod.hod.

• Journal of the Korean Ceramic Society
• /
• v.23 no.1
• /
• pp.13-20
• /
• 1986

Zirconia soild electrolytes containing 4~10mol% of yttria were prepared by wet-blending of oxides and rea-ction-sintering, Sinterbility and degree of stabilization were optimized for the development of oxygen sensor. Fracture strength thermal expansion coefficient electrical conductivity and galvanic potential were measured and discussed with respect to the amount of ytria addition phase transformation microstructure and degree of stabilization. It was found that sintering and stabilization occurred when the composition was designed to be near the boundary region of $ZrO_2-Y_2O_3$ binary system. In such away a good zirconia solid electrolyte suitable for oxygen sensor could be developed.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.327-328
• /
• 2006

We have demonstrated that textured $Al_2O_3-mullite-SiC$ nanocomposites can be fabricated by slip casting followed by partial oxidation - reaction sintering of mixed suspensions of $Al_2O_3$ and SiC powders in a high magnetic field. The sintered density was changed by the degree of oxidation at 1200C and 1300C. The degree of orientation of alumina in the nanocomposite was examined on the basis of the X-ray diffraction patterns and scanning electron micrographs. It is confirmed that alumina-oriented nanocomposites were fabricated. The three-point bending strength at room temperature was observed for the nanocomposites.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.455-456
• /
• 2006

We have demonstrated that textured $Al_2O_3-mullite-SiC$ nanocomposites can be fabricated by slip casting followed by partial oxidation. reaction sintering of mixed suspensions of $Al_2O_3$ and SiC powders in a high magnetic field. The sintered density was changed by the degree of oxidation at 1200C and 1300C. The degree of orientation of alumina in the nanocomposite was examined on the basis of the X-ray diffraction patterns and scanning electron micrographs. It is confirmed that aluminaoriented nanocomposites were fabricated. The three-point bending strength at room temperature was observed for the nanocomposites.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.836-842
• /
• 1998

In this experiment well-know additives for Mn-Zn ferrites CaO and {{{{ { SiO}_{2 } }} were added at various content and their effects on microstructures and magnetic properties with sintering atmosphere were examined. By adding up to 0.04wt% {{{{ { SiO}_{2 } }} and and 0.06wt% CaO the sintered density was increased and then decreased gra-dually. Higher sintered density and initial permeability were observed by adding both CaO and {{{{ { SiO}_{2 } }} than by adding CaO or {{{{ { SiO}_{2 } }} alone. Without any additives initial permeability and tan$\delta$/${\mu}$ decreased at 1000kHz as oxidation degree(${\gamma}$) increased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.693-696
• /
• 2001

The (Ba$_{0.3}$Bi$_{0.3}$Sr$_{0.4}$)TiO$_3$[BBST] ceramics were prepared by conventional mixed oxide method. The structural properties of the BBST ceramics with sintering temperature were investigated by XRD, SEM, EDS. In the case of BBST ceramics sintered at 1150~135$0^{\circ}C$, the $Ba_{0.5}$Sr$_{0.5}$TiO$_3$and SrBi$_4$Ti$_4$O$_{15}$ phase were coexisted. The 2$\theta$ value of the BST (110) peaks were shifted to the lower degree at the sintering temperature of 130$0^{\circ}C$ and 135$0^{\circ}C$. The grains of the BBST ceramics sintered at 130$0^{\circ}C$ and 135$0^{\circ}C$ were not appeared. Increasing the sintering temperature, the densities of the BBST ceramics were increased. In the BBST ceramics sintered at 130$0^{\circ}C$ and 135$0^{\circ}C$, the mole ratio of Bi was decreased.d.ed.d.d.d.