• Journal of the Korean Wood Science and Technology
• /
• v.47 no.3
• /
• pp.253-264
• /
• 2019

This study characterized the chemical compounds in tannin from mangium (Acacia mangium) bark extract and determined the physical-mechanical properties of glued laminated timber (glulam) made from sengon (Falcataria moluccana), jabon (Anthocephalus cadamba), and mangium wood. The adhesives used to prepare the glulam were based on mangium tannin and phenol resorcinol formaldehyde resin. Five-layer glulam beams measuring $5cm{\times}6cm{\times}120cm$ in thickness, width, and length, respectively, were made with a glue spread of $280g/m^2$ for each glue line, cold pressing at $10.5kgf/cm^2$ for 4 h and clamping for 20 h. Condensed mangium tannin consisted of 49.08% phenolic compounds with an average molecular weight of 4745. The degree of crystallinity was 14.8%. The Stiasny number was 47.22%. The density and the moisture content of the glulams differed from those of the corresponding solid woods with mangium having the lowest moisture content (9.58%) and the highest density ($0.66g/cm^3$). The modulus of rupture for all glulam beams met the JAS 234-2003 standard but the modulus of elasticity and the shear strength values did not. Glulam beams made with tannin had high delamination under dry and wet conditions, but glulam made from sengon and jabon wood met the standard's requirements. All glulam beams had low formaldehyde emissions and were classified as $F^{****}$ for formaldehyde emissions according to the JAS 234 (2003) standard.

• Korean Journal of Materials Research
• /
• v.9 no.2
• /
• pp.149-154
• /
• 1999

Alumina substrate was sealed by PbO-ZnO-$B_2O_3$glass using microwave heating. The crystallization behaviour of sealing glass and the state of sealing joint were investigated and were compared with those of conventionally sealed one. Compared to the conventional one, the microwave heat-treated sample had well-grown $\textrm{PbTiO}_3$ crystals and high degree of crystallinity even though it had shorter heat-treatment time and lower heat-treatment temperature. Also, the microwave sealed sample exhibited relatively a good sealing state and almost same bending strength.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.4
• /
• pp.84-92
• /
• 2008

Anatomical and physical characteristics of Pinus densiflora woods damaged by forest fire at Yangyang-gun, Kangwon-do were investigated in present study. Even though the bark was severly carbonized, no trace of carbonization in the xylem was found. The amount of resin exudation was different by the degree of fire damage. Green moisture content of sapwood in the damaged wood was lower than that in the sound wood, but vice versa in the heartwood. Green density of heartwood in the damaged wood was higher than that in the sound wood, but there was no significant difference in sapwood. Cambial activities were found stopped in the severely damaged wood but were identified in the lightly damaged wood. In safranine staining process, epithelial and ray parenchyma cell walls in the damaged woods showed darker hue than those in the sound wood. Granular substances were observed in the lumina of ray parenchyma and epithelial cells of the severely damaged wood. Relative crystallinity of the outermost growth ring in the severely damaged wood was slightly higher than that in the sound wood.

• Polymer(Korea)
• /
• v.34 no.6
• /
• pp.579-587
• /
• 2010

To investigate the properties of PET films, PET films were extruded at various temperature above $T_m$ and quenched at $18^{\circ}C$ for amorphous sheet, and stretched along a direction defined as the machine direction (MD) with a transverse direction (TD) above $T_g$ at various stretching ratios and then annealed at various temperatures produced by SKC PET line. Thermal shrinkage of MD and TD increased with decreasing annealing temperature and extruding temperature, and increasing stretching ratio. The degree of crystallinity, density, heat of fusion (${\Delta}H$) and pre-melting point ($T_m'$) increased with increasing annealing temperature and extruding temperature. Number average molecular weight ($M_n$) and intrinsic viscosity decreased with increasing extruding temperature. Tensile strength and modulus increased with increasing stretching ratio, however decreased with increasing annealing temperature. Reflective index of both stretching and thickness direction increased with increasing stretching ratio and annealing temperature.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.14 no.1
• /
• pp.191-196
• /
• 2010

Aluminum doped zinc oxide (AZO) films have been prepared on Coming 7059 glass substrates by r.f. magnetron sputtering method. A powder target instead of a conventional sintered ceramic target was used in order to improve the utilization efficiency of the target and reduce the cost of the film deposition process. The influence of sputter pressure on the structural, electrical, and optical properties of AZO films were studied. The AZO films had hexagonal wurtzite structure with a preferred c-axis orientation, regardless of sputter pressure and target types. The crystallinity and degree of orientation was increased by increasing the sputter pressure. For higher sputtering pressures, a reduction of the resistivity was observed due to a increase on the mobility and the carrier concentration. The lowest resistivity of $6.5{\times}10^{-3}\;{\Omega}-cm$ and the average transmittance of 80% can be obtained for films deposited at 15 mTorr.

• Journal of the East Asian Society of Dietary Life
• /
• v.24 no.3
• /
• pp.400-406
• /
• 2014

Apios (Apios americana Medikus) belongs to Leguminosae and is called 'American groundnut', 'Potato bean', and 'wild bean'. Apios is native to the Northern United States but is not widely distributed in Korea. In this study, cross-linked apios starch was prepared by reaction with epichlorohydrin, followed by characterization. FT-IR spectroscopy confirmed the degree of cross-linking of apios starch. X-ray diffraction patterns of native apios showed typical 'A' type as peaks at 15.1, 17.1, 17.9 and $23.2^{\circ}$, and cross-linking did not affect relative crystallinity and X-ray diffraction patterns of the starch. Scanning electron micrographs showed that apios starch granules were smooth with a globular shape, and there was little damage to starch granules after cross-linking. The lightness value of cross-linked apios starch was lower than that of native apios starch, whereas the redness value was not significantly different between cross-linked apios starch and native apios starch. Blue value showed that cross-linking of starch did not affect the iodine reaction of starch.

• Applied Chemistry for Engineering
• /
• v.26 no.6
• /
• pp.659-665
• /
• 2015

Loading of hydrophobic ${\alpha}$-tocopherol into nanostructured lipid carrier (NLC) was performed for improving its oxidative stability. First, various NLCs with different constituents and mixing ratios were prepared and their characteristics were investigated. While the stable NLCs were made when cetyl palmitate (CP) or glyceryl monosterate (GMS) was used as a solid lipid, the phase separation occurred in the NLCs consisting of stearic acid. Particle sizes of the NLCs were several hundreds of nanometers and the size decreased with increasing the ratio of solvent to lipid. It was examined from DSC thermogram and anisotropy test that the degree of crystallinity of the lipid phase decreased and the lipid matrix became less ordered when octyldodecanol, a long chain fatty alcohol, was added into the solid lipid. The oxidative stability of ${\alpha}$-tocopherol in NLC was remarkably improved compared to that in solution or emulsion under high temperature ($45^{\circ}C$) and UV radiation, which was verified through DPPH test and peroxide value measurement.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.1
• /
• pp.12-16
• /
• 2020

Indium tin oxide (ITO) films were prepared onto transparent polyimide (PI) substrates by RF magnetron sputtering at room temperature. The deposited ITO films were heat-treated at various temperatures (50, 100, 150, and 200℃). The effect of post heat-treatment temperature on structural, electrical and optical properties of ITO films were investigated. It was found that the as-deposited ITO films were amorphous and the degree of crystallinity and the grain size increased with an increasing heat-treatment temperature, which led to the increase in carrier concentration and mobility. The electrical resistivity of as-deposited ITO films was 2.73 × 10^-3 Ω·cm. With the heat-treatment temperature increasing from 50 to 200℃, the electrical resistivity decreased from 2.93 × 10^-3 to 1.21 × 10^-4 Ω·cm. The average transmittance (400~800 nm) of the ITO deposited PI substrates was decreasing with post heat-treatment temperature and was above 81 % for the temperatures 50~150℃ and decreased considerably to 78 % at 200℃.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.5
• /
• pp.197-202
• /
• 2001

The influence of thermal treatment and cold drawing was investigated for poly(ethy1ene terephthalate) films fabricated with various experimental conditions. Samples were elongated at room temperature under stepwise-drawing condition with the cross-head speed kom 0.5 to 500 mrdmin in an universal tester. Stress oscillation was observed in the stress-stnin curve of the samples heat-treatd at 50, 72 and $129^{\circ}C$ for 30 min, but it was not observed in the samples heat-treatd at $83^{\circ}C$ for 30 min. Thermal analyses of the samples were carried out in differential scanning calorimeter at the heating rate df $10^{\circ}C$/min/min, and the glass transition temperature, crystallization peak, enthalpy of fusion and degree of crystallinity were measured. The dynamic mechanical analyses of the samples were also carried out in a multiplefimction internal kiction pendulum at 1 Hz with the heating rate of $1.5^{\circ}C$/min, and it was found that the elastic modulus increases in the order of non-treated, heat-treated, and elongated samples.

• Polymer(Korea)
• /
• v.38 no.4
• /
• pp.457-463
• /
• 2014

In this study, the changes in the chemical structure and the physical property of fluoropolymer films (PTFE, FEP, PFA, PVDF, and ETFE) induced by $Co^{60}$ gamma ray in air, $N_2$, and vacuum environments were investigated. FTIR spectra of the irradiated fluoropolymers indicate that the oxidation proceeded by the reaction of radicals generated by irradiation with oxygen in air. The changes in the heat of fusion and the degree of crystallinity of the irradiated fluoropolymers were investigated using DSC and the results indicate that the scission and crosslinking reactions of the irradiated fluoropolymers were largely influenced by the chemical structure. It was also found that the mechanical property of the irradiated fluoropolymer films under an air atmosphere was significantly decreased.