• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.3
• /
• pp.199-205
• /
• 1999

The quaternary Ti-Al-V-N films have been grown on glass substrates by reactive dc and rf magnetron sputter deposition from a Ti-6Al-4V target in mixed Ar-$N_2$ discharges. The Ti-Al-V-N films were investigated by means of X-ray diffraction(XRD), electron probe microanalysis(EPMA) and scratch tester. Both XRD and EPMA results indicated that the Ti-Al-V-N films were of single B1 NaCl phase having columnar structure with the (111) preferred orientation. Scratch tester results showed that the adhesion strength of Ti-Al-V-N films which treated with substrate heating and vacuum annealing was superior to that of as-deposited film. The good adhesion strength was also achieved in the double-layer structure of Ti-Al-V-N/Ti-Al-V/Glass.

• The Transactions of the Korean Institute of Electrical Engineers P
• /
• v.52 no.2
• /
• pp.56-60
• /
• 2003

In this work, we have fabricated thin film resistors using the DC/RF magnetron sputter of 51wt%Ni-41wt%Cr-8wt%Si alloy target and studied the effect of the process parameters on the electrical properties. In fabrication process, sputtering power, substrate temperature and annealing temperature have been varied as controllable parameters. TCR decreases with increasing the substrate temperature, but TCR increases over 300 [$^{\circ}C$]. The films are annealed to 400 [$^{\circ}C$] in air atmosphere, TCR increases with increasing the annealing temperature. The resistivity was 172 [${\mu}{\Omega}{\cdot}cm$] and 209 [${\mu}{\Omega}{\cdot}cm$] for the RF and DC as a sputtering power sources, respectively. Also, TCR was -52 [$ppm/^{\circ}C$] and -25 [$ppm/^{\circ}C$]. As a results of them, it is suggested that the sheet resistance and TCR of thin films can be controlled by variation of sputter process parameter and annealing of thin film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.05a
• /
• pp.17-20
• /
• 1994

PTCRl(positive temperature coefficient of resistivity) thermistors in the thin file BaTiO$_3$ system were deposited by radio frequency (13.56 MHz) and dc radio frequency (13.56MHz) and dc magnerton sputter equipment. R-T(resistivity -temperature) properties was investigated as a function of substrate and the temperature variation. The specimens make a comperison between the thin films and the bulk in the resistivity variation. Substrate temperature. deposition time. and forward power are deposited at the 400$^{\circ}C$, 10 hours, and 210 watt. respectively. The aim of this work is to obtain lower than bulk specimen resistivity in thin films BaTiO$_3$ system thermistor by RF/DC magnetron sputter equipment.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.65 no.12
• /
• pp.2014-2018
• /
• 2016

Transparent, conductive electrode films, showing the particular characteristics of good conductivity and high transparency, are of considerable research interest because of their potential for use in opto-electronic applications, such as smart window, photovoltaic cells and flat panel displays. Multilayer transparent electrodes, having a much lower electrical resistance than widely-used transparent conducting oxide electrodes, were prepared by using RF/DC magnetron sputtering system. The multilayer structure consisted of three layers, [NiInZnO(NIZO)/Ag/NIZO]. The optical and electrical properties of the multilayered NIZO/Ag/NIZO structure were investigated in relation to the thickness of each layer. The optical and electrical characteristics of multilayer structures have been investigated as a function of the Ag and NIZO film thickness. High-quality transparent conductive films have been obtained, with sheet resistance of $9.8{\Omega}/sq$ for Ag film thickness of 8 nm. Also the multilayer films of inserted Ag 8 nm thickness showed a high optical transmittance above 93% in the visible range. The electrical and optical properties of the new multilayer films were mainly dependent on the thickness of Ag insertion layer.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.12
• /
• pp.1103-1109
• /
• 2003

Crystalline carbon nitride films have been deposited by RF reactive magnetron sputtering system with negative DC bias. The carbon nitride films deposited on various substrates showed ${\alpha}$- C$_3$N$_4$,${\beta}$-C$_3$N$_4$ and lonsdaleite structures through XRD and FTIR We can find the grain growth of hexagonal structure from SEMI photographs, which is coincident with the theoretical carbon nitride unit cell. When nitrogen gas ratio is 70 % and RF power is 200 W, the growth rate of carbon nitride film on quartz substrate is about 2.1 $\mu\textrm{m}$/hr.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.206-206
• /
• 2009

RF Magnetron Sputtering 방법을 통해 ZnS:Mn 박막 형광체를 증착한 다층 TFEL (Thin-Film Electroluminescent) Backlight 소자를 제작하였다. Alumina 기판 위에 Au 전극과 PMN 후막 유전체를 Screen printing 기법으로 층을 형성하였다. 그 위에 MgO 박막 유전체를 E-Beam 장비를 이용하여 증착 후, ZnS:Mn 박막 형광체를 50 W 의 저전력으로 약 8000 ${\AA}$ 두께로 증착하였다. 형광체는 Sputter 증착 시 Sulfur 부족 현상을 보상해주기 위해 ZnS:Mn (0.5%) Target 에 2 at % 의 Sulfur를 첨가하였으며, 상부 전극으로 사용할 ITO 는 DC Magnetron Sputter 를 이용하여 증착하였다. 어닐링 공정은 Air 분위기에서 급속 열처리 장치 (RTA, Rapid Thermal Annealing) 을 이용하여 600 $^{\circ}C$에서 20 분 진행하였다. 이러한 과정들을 통해 저전압 고휘도의 TFEL Backlight 소자를 제조할 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.446-447
• /
• 2007

The rapid thermal annealing effect of transparent IZTO(indium zinc oxide) and IAZO(indium alminium zinc oxide) films grown on glass substrate for solar cell or flat panel displays(FPDs) was studied. We prepared IZTO using RF magnetron sputtering and IAZO using DC co-sputtering method. Subsequently, using rapid thermal annealing(RTA) system, prepared IZTO and IAZO films were annealed at 300, 400, 500, $600^{\circ}C$ for 90sec. In addition, Electrical and optical characteristics were measured by Hall effect measurement and UV/Vis spectrometer examinations, respectively. To analyze structural properties and surface smoothness of the IZTO and IAZO films, XRD and SEM examinations were performed, respectively. It was shown that IZTO and IAZO films exhibited microcrystalline structure over $400^{\circ}C$ and amorphous structural regardless of RTA temperature, respectively.

• Transactions on Electrical and Electronic Materials
• /
• v.5 no.3
• /
• pp.122-125
• /
• 2004

ITO films were deposited on polyethylene terephthalate substrate by a dc reactive magnetron sputtering using rf bias without substrate heater and post-deposition thermal treatment. The dependency of rf substrate bias on plasma sputter processing was investigated to control energetic particles and improve ITO film properties. The substrate was applied negative rf bias voltage from 0 to -80 V. The composition of indium, tin, and oxygen atoms is strongly depended on the rf substrate bias. Oxygen deficiency is the highest at rf bias of -20 V. The electrical and optical properties of ITO films also are dominated obviously by negative rf bias.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.5
• /
• pp.257-261
• /
• 2006

Nano-structured carbon nitride $(CN_x)$ films were prepared by reactive RF magnetron sputtering with a DC bias at various deposition conditions, and the physical and electrical properties were investigated. FTIR spectrum indicated an ${alpha}C_3N_4$ peak in the films. The carbon nitride film deposited on Si substrate had a nano-structured surface morphology. The grain size was about 20 nm and the deposition rate was $1.7{\mu}m/hr$. When the $N_2/Ar$ ratio was 3/7, the level of nitrogen incorporation was 34.3 at%. The film had a low dielectric constant. The metal-insulator-semiconductor (MIS) capacitors that the carbon nitride was deposited as insulators, exhibited a typical C-V characteristics.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.52.2-52.2
• /
• 2011

본 연구의 목적은 CIGS 태양전지의 두 가지 TCO층 중 AZO를 제외한 intrinsic ZnO의 전자빔 처리 영향에 대한 특성 분석을 하고자 함이다. 또한 추후 CIGS 태양전지를 제조하여 적용 시 전자빔 처리 전후의 특성이 어떻게 변하는지를 알아보기 위한 사전 실험이다. Intrinsic ZnO는 RF magnetron sputter 를 이용하여 약 100nm의 두께로 증착 하였다. 이때 공정 압력을 변수로 RF power는 80W로 설정 하였으며 Ar 분압은 10mtorr, 5mtorr, 1mtorr로 각각 달리 하며 증착 하였다. 이후 전자빔 처리를 위해 각각의 시편에 Argon flow 7sccm 상태에서 DC power 3kW, RF power 300W의 세기로 전자빔 처리를 실시 하였다. 전자빔 처리에 따른 전기적, 구조적 특성을 분석하기위해 Hall measurement와 SEM, XRD, UV-vis spectroscopy을 사용하였다. 먼저 Hall measurement 측정을 통한 전기적 분석 결과 비저항이 무한대에서 약 $40m{\Omega}{\cdot}cm$로 감소된 결과를 도출 할 수 있었으며, $2{\sim}3.4{\times}10^{18}/cm^3$ 이상의 carrier density 가 측정 되었다. UV-vis spectroscopy를 이용한 투과도 측정결과 모든 시편에서 Band gap이 감소하는 결과를 보였다. SEM, XRD를 이용한 분석결과 결정성 및 grain의 크기가 증가하는 결과를 얻을 수 있었다.