• Corrosion Science and Technology
• /
• 제7권6호
• /
• pp.370-374
• /
• 2008

In this study, we evaluated anti-corrosion properties of both commercial unleaded and lead epoxy primer for automotive substrate before applying to actual painting lines by salt spray test, and cyclic corrosion test, potentiodynamic test and electrochemical impedance spectroscopy. The difference in the corrosion resistance between automotive epoxy primers contained $Bi(OH)_{3}$ and leaded one was investigated. And it was also discussed the effect of zinc phosphate pretreatment to the epoxy primers. The specimen coated epoxy primer contained $Bi(OH)_{3}$ showed 0.5 V higher corrosion potential than that of bare steel. The result of salt spray test did not indicate remarkable difference of corrosion resistance in all specimens above $10{\mu}m$ thickness up to 1200 hours. In the cyclic corrosion test, epoxy primers contained $Bi(OH)_{3}$ on phosphated substrate performed good corrosion properties until 800 hours. The epoxy primer contained $Bi(OH)_{3}$ performed the equivalent corrosion resistance as leaded coating on phosphated steel, but slightly inferior to that of leaded on bare steel. These results show that the pre-treatment of zinc phosphate is effective as well as pigment changing in performing anti-corrosion properties in automotive bodies.

• Corrosion Science and Technology
• /
• 제9권5호
• /
• pp.201-208
• /
• 2010

Epoxy coatings cured by different amine based curing agents have been prepared. Atomic force microscopy (AFM) has been used to monitor the surface topology changes of epoxy coatings before and after hygrothermal cyclic test. The glass transition temperature ($T_g$) and coefficient of thermal expansion (CTE) of the epoxy coating were measured by Thermo-mechanical Analysis (TMA). The Electrochemical impedance spectroscopy (EIS) with hygrothermal cyclic test has been introduced to evaluate the corrosion protection of the epoxy coatings. In conclusion, thermal properties of epoxy coatings were in good agreement with the results of corrosion protection of epoxy coated carbon steel obtained result by EIS with hygrothermal cyclic test. The relationship between thermal properties, surface roughness changes and corrosion protection of epoxy coatings are discussed in this study.

• Corrosion Science and Technology
• /
• 제10권3호
• /
• pp.95-100
• /
• 2011

Protective coatings play an important role in the protection of metallic structures against corrosive environment. The main function of anticorrosive coating is to prevent the materials from corrosive agents, such as water, oxygen and ions. In the study, the corrosion protection properties of urethane and epoxy coating systems were evaluated using EIS methods exposed to the corrosion acceleration test such as Norsok M501, Prohesion and hygrothermal cyclic test. AFM analysis of the coating systems was carried out to monitor the change of roughness of coatings. Urethane coating system was more stable than the epoxy coating under given cyclic conditions. Water uptake into the urethane coatings was less than that into the epoxy coating. The urethane coating system showed better corrosion protection than epoxy coating system based on the changes of the impedance modulus at low frequency region with exposure time. Consequently, the corrosion protection properties of the epoxy and urethane coatings was well correspond with their surface roughness changes and water uptakes.

• Corrosion Science and Technology
• /
• 제8권6호
• /
• pp.243-250
• /
• 2009

When a steel sheet pipe applied to marine environment, an anti-corrosive coating should be treated to obtain long-term life-time for steels, especially, splash zone. Although anti-corrosive property of coatings is required to be tested in real marine environment, it is difficult because of long test time such as 20 years or more time. Therefore, we used cyclic corrosion tester in a laboratory, which has similar conditions with salt-dry-wet process such as real marine environment. Anti-corrosive properties of the coatings and two steels were tested their anti-corrosive properties under cyclic corrosion test conditions(KS D ISO 14993) and the results were compared with estimate life-time in real marine environment. According to cyclic corrosion test, accelerated corrosive factor of each anti-corrosive coating was investigated accelerated corrosive factor from impedance with EIS method. Accelerated corrosive factor of type SS400 carbon steel and A690 was also investigated their accelerated corrosive factor from the regression curves of weigh loss results. One of the anti-corrosive coatings showed about 50 years life-time compared with standard sample life-time. Carbon steel SS400 showed from 0.1 mm/yr to 0.06 mm/yr as its corrosion rate.

• 한국건설순환자원학회논문집
• /
• 제1권3호
• /
• pp.211-218
• /
• 2013

해양환경 조건 중 건습반복환경인 간만대는 구조물내 철근부식이 가장 빨리 일어나는 것으로 알려져 있다. 때문에 부식촉진시험 방법 중 간만대 환경을 재현한 시험방법이 가장 활발하게 진행되어왔다. 그러나 많은 연구들이 부식임계농도 추정이나 염화물침투해석에 집중되어 있는 상황이다. 본 논문에서는 건습반복조건의 환경을 재현하여 구조물내 철근부식촉진시험과 염화물 침투해석을 실시하였다. 배합에 사용된 재료의 종류를 변수로 시험을 실시하였으며, 철근부식모니터링 방법으로 갈바닉 전위측정법과 반전지전위법을 사용하여 철근부식의 유무를 판단하였다. 부식촉진시험결과 각 배합별로 부식기간이 차이가 났으며, 순서는 OPC > FA > BS > 고강도 순으로 나타났다. 부식촉진시험과 동일한 조건으로 FEM 내구성 해석 프로그램인 DuCOM, RCPT 시험을 실시하여 실험결과 값에 대한 타당성을 입증하였다.

• Corrosion Science and Technology
• /
• 제9권1호
• /
• pp.34-38
• /
• 2010

Electrochemical study on cut edge corrosion of prepainted Zn coated (GI) and 55%Al-Zn coated (GL) steels has been performed in wet-dry cyclic conditions. Maximum width of delaminated polymer coating from the cut edge for GI and GL specimens was evaluated under wet-dry cyclic conditions. The cyclic tests were carried out for 1000 h by changing of relative humidity, where the salt of NaCl was deposited on the specimen every 48 h. The cut edge corrosion test under NaCl deposit indicated that the delamination of the GL specimen progresses at a higher rate than the GI. The electrochemical corrosion monitoring was also performed under condition of alternate exposure to immersion in NaCl solution and drying at 60%RH and $25^{\circ}C$. On the basis of the results of the delamination tests and electrochemical measurements, the mechanism of cut edge corrosion for GI and GL were discussed.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.245-248
• /
• 2005

It should be noted that the critical chloride threshold level is not considered to be a unique value for all conditions. This value is dependent on concrete mixture proportions, cement type and constituents, presence of admixtures, environmental factors, steel reinforcement surface. conditions, and other factors. In this study, the accelerated corrosion test for reinforcing steel was conducted by electrochemical and cyclic wet and dry seawater method, respectively and during the test, corrosion monitoring by half cell potential method was carried out to estimate the chloride corrosion threshold value when corrosion for reinforcing steel in concrete was perceived. For this purpose, lollypop and right hexahedron test specimens were made for 31.4$\%$, 41.5$\%$ and 49.7$\%$ of w/c, respectively and then the accelerated corrosion test for reinforcing steel was executed. It was observed from the test that the time to initiation of corrosion was found to be different with water-cement ratio and accelerated corrosion test method, respectively and the chloride corrosion threshold value was found to range from 0.91 to 1.43 kg/$m^{3}$.

• Corrosion Science and Technology
• /
• 제5권5호
• /
• pp.177-180
• /
• 2006

The anticorrosive performance of epoxy coating was examined by using the hygrothermal cyclic test and the degradation mechanism of the coating was investigated by using the AC impedance method. The relationship between the results obtained from different tests was studied. It was revealed that the hygrothermal cyclic test can be used as an effective acceleration test for the degradation of organic coating. It was also found in hygrothermal cyclic test that the epoxy coatings have the resistance to stresses at some extent. The degradation of organic coating seems to be caused by the decrease of resistance of coating and the increase of both capacitance and free volume in the organic coating.

• 한국구조물진단유지관리공학회 논문집
• /
• 제20권4호
• /
• pp.136-143
• /
• 2016

염해에 의한 철근콘크리트 구조물의 내구수명을 평가하는 방법에는 여러 가지가 있지만, 가장 확실한 방법은 염해환경에 노출된 시편에 대한 철근 부식시험을 시행하는 것이다. 그러나 이러한 방법은 장기간이 소요된다는 단점이 있으며 이를 보완한 촉진부식시험 결과는 장기시험과의 상관성이 규명되지 않아 적용에 한계가 따른다. 따라서 본 연구에서는 부식촉진시험과 장기폭로시험간의 상관성을 분석하는 것을 연구의 목표로 한다. 부식속도가 가장 빠른 간만대 환경을 모사한 최적 건습반복시험방법을 찾고 해양환경폭로시험장의 간만대에 장기간 노출된 시편의 철근부식모니터링 시험결과와의 비교를 통해 촉진부식시험과 장기폭로시험간의 상관계수를 도출하였다. 또한 재료의 배합별 특성을 파악하기 위해 물,결합재비 60%를 기준으로 플라이애시를 20% 치환한 배합과 고로슬래그 미분말을 30% 치환한 배합을 비교하였으며, 물-결합재비가 35%인 고강도 배합에 대해서도 시험을 실시하였다. 반전지전위법에 의한 부식 모니터링 결과 일정기간의 건조와 습윤의 반복 조건보다는 염수를 시편 상부에 침지시켜 염수 및 산소의 공급이 계속되는 염수 ponding 시험법이 24~36% 정도 부식을 촉진시키는 것으로 나타났다. 각 배합별로는 모든 시험법에서 OPC60, FA, BS, OPC35 순으로 부식이 발생하였다. 간만대의 장기폭로시험과의 상관성 분석 결과 건습반복 부식촉진시험의 경우 4.23~5.52의 상관계수를 가지고 있었으며, 염수 ponding 시험법의 경우 6.54~7.82의 상관계수를 나타내었다.

• 한국해양공학회지
• /
• 제14권1호
• /
• pp.60-66
• /
• 2000

In order to study for corrosion behavior of reinforcing steel with oxidation layer. Experiments were done with various NaCl concentrations and with immersion time in simulated concrete pore solution(SPS) the characteristics of corrosion behavior were measured by polarization resistance method and cyclic potentiodynamic method. reinforcements were coated by epoxy except corrosion without oxidation layer and it also showed two anodic-nose. by the result of potention dynamic test the potential curve shift to low with time and anodic-nose was appeared with 3% NaCl solution after 15 days. By result of cyclic Potentiodynamic test the type of corrosion was different accoding to concentration.