• Corrosion Science and Technology
• /
• v.7 no.6
• /
• pp.370-374
• /
• 2008

In this study, we evaluated anti-corrosion properties of both commercial unleaded and lead epoxy primer for automotive substrate before applying to actual painting lines by salt spray test, and cyclic corrosion test, potentiodynamic test and electrochemical impedance spectroscopy. The difference in the corrosion resistance between automotive epoxy primers contained $Bi(OH)_{3}$ and leaded one was investigated. And it was also discussed the effect of zinc phosphate pretreatment to the epoxy primers. The specimen coated epoxy primer contained $Bi(OH)_{3}$ showed 0.5 V higher corrosion potential than that of bare steel. The result of salt spray test did not indicate remarkable difference of corrosion resistance in all specimens above $10{\mu}m$ thickness up to 1200 hours. In the cyclic corrosion test, epoxy primers contained $Bi(OH)_{3}$ on phosphated substrate performed good corrosion properties until 800 hours. The epoxy primer contained $Bi(OH)_{3}$ performed the equivalent corrosion resistance as leaded coating on phosphated steel, but slightly inferior to that of leaded on bare steel. These results show that the pre-treatment of zinc phosphate is effective as well as pigment changing in performing anti-corrosion properties in automotive bodies.

• Corrosion Science and Technology
• /
• v.9 no.5
• /
• pp.201-208
• /
• 2010

Epoxy coatings cured by different amine based curing agents have been prepared. Atomic force microscopy (AFM) has been used to monitor the surface topology changes of epoxy coatings before and after hygrothermal cyclic test. The glass transition temperature ($T_g$) and coefficient of thermal expansion (CTE) of the epoxy coating were measured by Thermo-mechanical Analysis (TMA). The Electrochemical impedance spectroscopy (EIS) with hygrothermal cyclic test has been introduced to evaluate the corrosion protection of the epoxy coatings. In conclusion, thermal properties of epoxy coatings were in good agreement with the results of corrosion protection of epoxy coated carbon steel obtained result by EIS with hygrothermal cyclic test. The relationship between thermal properties, surface roughness changes and corrosion protection of epoxy coatings are discussed in this study.

• Corrosion Science and Technology
• /
• v.10 no.3
• /
• pp.95-100
• /
• 2011

Protective coatings play an important role in the protection of metallic structures against corrosive environment. The main function of anticorrosive coating is to prevent the materials from corrosive agents, such as water, oxygen and ions. In the study, the corrosion protection properties of urethane and epoxy coating systems were evaluated using EIS methods exposed to the corrosion acceleration test such as Norsok M501, Prohesion and hygrothermal cyclic test. AFM analysis of the coating systems was carried out to monitor the change of roughness of coatings. Urethane coating system was more stable than the epoxy coating under given cyclic conditions. Water uptake into the urethane coatings was less than that into the epoxy coating. The urethane coating system showed better corrosion protection than epoxy coating system based on the changes of the impedance modulus at low frequency region with exposure time. Consequently, the corrosion protection properties of the epoxy and urethane coatings was well correspond with their surface roughness changes and water uptakes.

• Corrosion Science and Technology
• /
• v.8 no.6
• /
• pp.243-250
• /
• 2009

When a steel sheet pipe applied to marine environment, an anti-corrosive coating should be treated to obtain long-term life-time for steels, especially, splash zone. Although anti-corrosive property of coatings is required to be tested in real marine environment, it is difficult because of long test time such as 20 years or more time. Therefore, we used cyclic corrosion tester in a laboratory, which has similar conditions with salt-dry-wet process such as real marine environment. Anti-corrosive properties of the coatings and two steels were tested their anti-corrosive properties under cyclic corrosion test conditions(KS D ISO 14993) and the results were compared with estimate life-time in real marine environment. According to cyclic corrosion test, accelerated corrosive factor of each anti-corrosive coating was investigated accelerated corrosive factor from impedance with EIS method. Accelerated corrosive factor of type SS400 carbon steel and A690 was also investigated their accelerated corrosive factor from the regression curves of weigh loss results. One of the anti-corrosive coatings showed about 50 years life-time compared with standard sample life-time. Carbon steel SS400 showed from 0.1 mm/yr to 0.06 mm/yr as its corrosion rate.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.3
• /
• pp.211-218
• /
• 2013

Cyclic wet and dry conditions in the marine environment structures corrosion is known to be the fastest rising. For that reason, accelerated corrosion test methods for the reproduction of tidal environment has been actively conducted. However, many studies have estimated threshold value for steel corrosion or concentrated in chloride penetration analysis. In this study, cyclic wet and dry conditions to reproduce the structure of the environment in accelerated corrosion and chloride penetration test analysis was performed. Corrosion was determined by the result of reinforcement corrosion monitoring based on galvanic potential measurement and half-cell potential method. Accelerated corrosion test results for each formulation was different corrosion periods, the order OPC> FA> BS> High-strength concrete. FEM durability interpretation program DuCOM was conducted under the same conditions as in accelerated corrosion test. The experimental RCPT tests demonstrated the validity of the result.

• Corrosion Science and Technology
• /
• v.9 no.1
• /
• pp.34-38
• /
• 2010

Electrochemical study on cut edge corrosion of prepainted Zn coated (GI) and 55%Al-Zn coated (GL) steels has been performed in wet-dry cyclic conditions. Maximum width of delaminated polymer coating from the cut edge for GI and GL specimens was evaluated under wet-dry cyclic conditions. The cyclic tests were carried out for 1000 h by changing of relative humidity, where the salt of NaCl was deposited on the specimen every 48 h. The cut edge corrosion test under NaCl deposit indicated that the delamination of the GL specimen progresses at a higher rate than the GI. The electrochemical corrosion monitoring was also performed under condition of alternate exposure to immersion in NaCl solution and drying at 60%RH and $25^{\circ}C$. On the basis of the results of the delamination tests and electrochemical measurements, the mechanism of cut edge corrosion for GI and GL were discussed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.245-248
• /
• 2005

It should be noted that the critical chloride threshold level is not considered to be a unique value for all conditions. This value is dependent on concrete mixture proportions, cement type and constituents, presence of admixtures, environmental factors, steel reinforcement surface. conditions, and other factors. In this study, the accelerated corrosion test for reinforcing steel was conducted by electrochemical and cyclic wet and dry seawater method, respectively and during the test, corrosion monitoring by half cell potential method was carried out to estimate the chloride corrosion threshold value when corrosion for reinforcing steel in concrete was perceived. For this purpose, lollypop and right hexahedron test specimens were made for 31.4$\%$, 41.5$\%$ and 49.7$\%$ of w/c, respectively and then the accelerated corrosion test for reinforcing steel was executed. It was observed from the test that the time to initiation of corrosion was found to be different with water-cement ratio and accelerated corrosion test method, respectively and the chloride corrosion threshold value was found to range from 0.91 to 1.43 kg/$m^{3}$.

• Corrosion Science and Technology
• /
• v.5 no.5
• /
• pp.177-180
• /
• 2006

The anticorrosive performance of epoxy coating was examined by using the hygrothermal cyclic test and the degradation mechanism of the coating was investigated by using the AC impedance method. The relationship between the results obtained from different tests was studied. It was revealed that the hygrothermal cyclic test can be used as an effective acceleration test for the degradation of organic coating. It was also found in hygrothermal cyclic test that the epoxy coatings have the resistance to stresses at some extent. The degradation of organic coating seems to be caused by the decrease of resistance of coating and the increase of both capacitance and free volume in the organic coating.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.4
• /
• pp.136-143
• /
• 2016

There are various method for evaluating the durability life of concrete structures due to salt damage. The best way is to perform a corrosion test for a rebar embedded in concrete specimen was exposure to marine environment. However, this method has the disadvantage that it takes a long period of time. Also, accelerated corrosion test which was complemented complements the time-consuming weakness is limited to apply because it could not reveal a correlation between long-term exposure test. Accordingly, the purpose of this study is to derive a correlation coefficient between cycle drying-wetting accelerated corrosion test and long-term exposure test. Corrosion initiation time was measured in four types of concrete samples, i.e., two samples mixed with fly ash(FA) and blast furnace slag(BS), and the other two samples having two water/cement ratio(W/C = 0.6, 0.35) without admixture(OPC 60 and OPC 35). The accelerated corrosion test was carried out by two case, i.e., one is a cyclic drying-wetting method(case 1), and the other is a artificial seawater ponding test method(case 2). Whether corrosion occurs, it was measures using half-cell potential method. The results indicated that case 1 is to accelerated the corrosion of rebar about 24~36% as compared with case 2, then the corrosion of rebar embedded in concrete occurred according to the order of OPC60, FA, BS, OPC35. Correlation coefficient between accelerated corrosion test and long-term exposure test, case 1 is 4.23 to 5.42, and case 2 is 6.54 to 7.82.

• Journal of Ocean Engineering and Technology
• /
• v.14 no.1
• /
• pp.60-66
• /
• 2000

In order to study for corrosion behavior of reinforcing steel with oxidation layer. Experiments were done with various NaCl concentrations and with immersion time in simulated concrete pore solution(SPS) the characteristics of corrosion behavior were measured by polarization resistance method and cyclic potentiodynamic method. reinforcements were coated by epoxy except corrosion without oxidation layer and it also showed two anodic-nose. by the result of potention dynamic test the potential curve shift to low with time and anodic-nose was appeared with 3% NaCl solution after 15 days. By result of cyclic Potentiodynamic test the type of corrosion was different accoding to concentration.