• The Journal of Korean Academy of Prosthodontics
• /
• v.24 no.1
• /
• pp.55-65
• /
• 1986

An in vitro study was performed to evaluate adaptation of custom direct, custom indirect, and prefabricated post system on 15 extracted upper central incisors. 15 specimens were prepared and equally devided into 3 groups under random sampling. Each group of 5 cast posts was made with custom direct, custom indirect, and prefabricated post core method. Gap between inner wall of the dentin and outer wall of the cast post was measured on electron microphotographic prints at x500 magnification. The result were as follows ; 1. No significant difference of adaptation at cervical portion was found between each method. 2. Prefabricated post core method had poor adaptation compared with other methods. 3. Even distribution of adaptation was found in custom direct method between each portion. 4. Prefabricated post core method showed remarkable difference in adaptation between each portion.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.5
• /
• pp.640-649
• /
• 2000

In the restoration of endodontically treated teeth, carbon fiber post was recently introduced. The purpose of this in vitro study was to investigate the fracture strength of teeth restored with a pre-fabricated carbon fiber post in comparison with teeth restored with a prefabricated titanium post & custom cast gold post after cyclic loading in the different environment. A total of 30 recently extracted human central incisors of similar dimension with crowns removed were used. All teeth were placed into acrylic blocks and every steps for post and core fabrication were made accord-ing to manufacture's instruction. The post length and core dimensions were standardizd. All teeth were divided into 6 groups: 1) carbon fiber post / atmosphere, 2) titanium post / atmosphere, 3) gold post / atmosphere, 4) carbon fiber post / wet, 5) titanium post / wet, 6) gold post / wet. Carbon fiber post and titanium post were cemented in place using resin cement and cores were fabricated with Ti-Core. Custom cast gold post was made from Duralay pattern resin and cemented using resin cement, too. All specimens were thermocycled 10,000 times. After 50,000 cyclic loading, failure strength was measured using Instron testing machine. Kruskal-Wallis test followed by Mann-Whitney test was used to compare the mean fracture strength. Results were as follows : 1. All specimens showed lower fracture strength in wet environment after cyclic loading than in atmosphere condition, but did not reveal a significant difference. 2. There was no significant difference between carbon fiber post specimen and titanium post specimen in the same environment. 3. Gold cast post specimen showed significant different greater fracture strength than those of others in the same environment. 4. Carbon fiber post specimen showed no root fracture.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.3
• /
• pp.170-175
• /
• 2017

PURPOSE. The aim of the present study was to evaluate the fracture resistances of zirconia, cast nickel-chromium alloy (Ni-Cr), and fiber-composite post systems under all-ceramic crowns in endodontically treated mandibular first premolars. MATERIALS AND METHODS. A total of 36 extracted human mandibular premolars were selected, subjected to standard endodontic treatment, and divided into three groups (n=12) as follows: cast Ni-Cr post-and-core, one-piece custom-milled zirconia post-and-core, and prefabricated fiber-glass post with composite resin core. Each specimen had an all-ceramic crown with zirconia coping and was then loaded to failure using a universal testing machine at a cross-head speed of 0.5 mm/min, at an angle of 45 degrees to the long axis of the roots. Fracture resistance and modes of failure were analyzed. The significance of the results was assessed using analysis of variance (ANOVA) and Tukey honest significance difference (HSD) tests (${\alpha}=.05$). RESULTS. Fiber-glass posts with composite cores showed the highest fracture resistance values ($915.70{\pm}323N$), and the zirconia post system showed the lowest resistance ($435.34{\pm}220N$). The corresponding mean value for the Ni-Cr casting post and cores was reported as $780.59{\pm}270N$. The differences among the groups were statistically significant (P<.05) for the zirconia group, as tested by ANOVA and Tukey HSD tests. CONCLUSION. The fracture resistance of zirconia post-and-core systems was found to be significantly lower than those of fiber-glass and cast Ni-Cr post systems. Moreover, catastrophic and non-restorable fractures were more prevalent in teeth restored by zirconia posts.