• Journal of Powder Materials
• /
• v.18 no.6
• /
• pp.546-551
• /
• 2011

Ag spot-coated Cu nanopowders were synthesized by a hydrothermal-attachment method (HA) using oleic acid capped Ag hydrosol. Cu nano powders were synthesized by pulsed wire exploding method using 0.4 mm in diameter of Cu wire (purity 99.9%). Synthesized Cu nano powders are seen with comparatively spherical shape having range in 50 nm to 150 nm in diameter. The oleic acid capped Ag hydrosol was synthesized by the precipitation-redispersion method. Oleic acid capped Ag nano particles showed the narrow size distribution and their particle size were less than 20 nm in diameter. In the case of nano Ag-spot coated Cu powders, nanosized Ag particles were adhered in the copper surface by HAA method. The components of C, O and Ag were distributed on the surface of copper powder.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.6
• /
• pp.493-501
• /
• 1998

$YBa_2Cu_3O_X$ samples were fabricated by MPMG(Melt Powdered Melt Growth). Intitial composition of the mixed powders were prepared as follow ; $YBa_2Cu_3O_X$ : $Y_2BaCuO_5$ = 1:0, 1:0.2, 1:0.3, 1:0.4. After the first melt and cooling, 5wt% to 20wt% fo Ag power was added to the powder. Effects of the different initial $Y_2BaCuO_5$ and Ag addition amount on $J_c$ and magnetization of $YBa_2Cu_3O_X$ fabricated by MPMG method were investigated. The critical current density increased with the amount of $Y_2BaCuO_5$ and Ag. It was also observed that the difference between negative and positive magnetization in the magnetization hysteresis measurement at 77K was larger than the case where $Y_2BaCuO_5$and Ag were not added to the $YBa_2Cu_3O_X$ powders. It is concluded that $Y_2BaCuO_5$ sample with 40wt% amount of $Y_2BaCuO_5$ and 20wt% amount of Ag has not only the largest $J_c$ but also the improved pinning effect.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.51-57
• /
• 2008

In this paper, wetting and interfacial reaction properties for low Ag containing Sn-Ag-Cu Pb-free solder alloy, i.e., Sn-0.3Ag-0.7Cu were investigated and compared with those of Sn-1.0Ag-0.5Cu and Sn-3.0Ag-0.5Cu. Melting behavior and stress-strain curves of some Sn-xAg-xCu alloys were also measured using a differential scanning calorimeter(DSC) and a tensile test machine, respectively. In order to enhance insufficient wetting properties of Sn-0.3Ag-0.7Cu alloy, the improvement of wetting properties were analyzed by applying fluxes containing higher content of halide or indium adding of 0.2wt.% into the solder alloy. It was concluded that the small addition of indium is more effective for the improvement of wettability in low temperature range of $230{\sim}240^{\circ}C$ than applying flux containing higher content of halide.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.2
• /
• pp.97-104
• /
• 2016

In the preparation of Ag-coated Cu flakes using L-ascorbic acid as a reductant for the electroless Ag plating, the effects of pretreatment methods and the reductant concentration on the uniformity of Ag coating layer and the anti-oxidation property of Ag-coated Cu flakes during the heating in air were evaluated. It was found that the removal degree of surface oxide layer during the pretreatment has great influence on the uniformity of Ag coating layer and the formation degree of hole defects in the flakes has slight effect on the anti-oxidation property of Ag-coated Cu flakes. It was also verified that the reductant concentration has great influence on the coverage uniformity and thickness of Ag coating, thus it was could be considered a main process parameter. When the reductant concentration was 0.04 M, high-quality Ag-coated Cu flakes was obtained. When the concentration increased to 0.06 M, however, the anti-oxidation property of Ag-coated Cu flakes became remarkably worse owing to remnant of Cu surface non-coated with Ag by the formation of pure Ag fine particles.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.235-237
• /
• 2007

In this paper, fabrication of Sn-3.0Ag-0.5Cu solder bumping having accurate composition and behavior of intermetallic compounds(IMCs) growth at interface between Sn-Ag-Cu bumps and Cu substrate were studied. The ternary alloy of the Sn-3.0Ag-0.5Cu solder was made by two binary(Sn-Cu, Sn-Ag) electroplating on Cu pad. For the manufacturing of the micro-bumps, photo-lithography and reflow process were carried out. After reflow process, the micro-bumps were aged at $150^{\circ}C$ during 1 hr to 500 hrs to observe behavior of IMCs growth at interface. As a different of Cu contents(0.5 or 2wt%) at Sn-Cu layer, behavior of IMCs was estimated. The interface were observed by FE-SEM and TEM for estimating of their each IMCs volume ratio and crystallographic-structure, respectively. From the results, it was found that the thickness of $Cu_3Sn$ layer formed at Sn-2.0Cu was thinner than the thickness of that layer be formed Sn-0.5Cu. After aging treatment $Cu_3Sn$ was formed at Sn-0.5Cu layer far thinner.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.450-455
• /
• 2002

Cu-cored Sn-Ag solder balls were fabricated by coating pure Sn and Ag on Cu balls. The melting behavior and the solderability of the BGA joint with the Ni/Au coated Cu pad were investigated and were compared with those of the commercial Sn-Ag and Sn-Ag-Cu balls. DSC analyses clarified the melting of Cu-cored solders to start at a rather low temperature, the eutectic temperature of Sn-Ag-Cu. It was ascribed to the diffusion of Cu and Ag into Sn plating during the heating process. After reflow soldering the microstructures of the solder and of the interfacial layer between the solder and the Cu pad were analyzed with SEM and EPMA. By EDX analysis, formation of a eutectic microstructure composing of $\beta$-Sn, Ag$_3$Sn, ad Cu$_{6}$Sn$_{5}$ phases was confirmed in the solder, and the η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer was found to form at the interface between the solder and the Cu pad. By conducting shear tests, it was found that the BGA joint using Cu-cored solder ball could prevent the degradation of joint strength during aging at 423K because of the slower growth me of η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer formed at the solder, pad interface. Furthermore, Cu-cored multi-component Sn-Ag-Bi balls were fabricated by sequentially coating the binary Sn-Ag and Sn-Bi solders on Cu balls. The reflow property of these solder balls was investigated. Melting of these solder balls was clarified to start at the almost same temperature as that of Sn-2Ag-0.75Cu-3Bi solder. A microstructure composing of (Sn), Ag$_3$Sn, Bi and Cu$_{6}$Sn$_{5}$ phases was found to form in the solder ball, and a reaction layer containing primarily η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ was found at the interface with Ni/Au coated Cu pad after reflow soldering. By conducting shear test, it was found that the BGA joints using this Cu-core solder balls hardly degraded their joint shear strength during aging at 423K due to the slower growth rate of the η'-(Au, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer at the solder/pad interface.he solder/pad interface.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.30-32
• /
• 2006

The interfacial reaction and reliability of eutectic Sn-Pb and Pb-free eutectic Sn-Ag ball-grid-array (BGA) solders with an immersion Ag-plated Cu substrate were evaluated following isothermal aging at $150^{\circ}C$. During reflowing, the topmost Ag layer was dissolved completely into the molten solder, leaving the Cu layer exposed to the molten solder for both solder systems. A typical scallop-type Cu-Sn intermetallic compound (IMC) layer was formed at both of the solder/Cu interfaces during reflowing. The thickness of the Cu-Sn IMCs for both solders was found to increase linearly with the square root of isothermal aging time. The growth of the $Cu_3Sn$ layer for the Sn-37Pb solder was faster than that for the Sn-3.5Ag solder, In the case of the Sn-37Pb solder, the formation of the Pb-rich layer on the Cu-Sn IMC layer retarded the growth of the $Cu_6Sn_5$ IMC layer, and thereby increased the growth rate of the $Cu_3Sn$ IMC layer. In the ball shear test conducted on the Sn-37Pb/Ag-plated Cu joint after aging for 500h, fracturing occurred at the solder/$Cu_6Sn_5$ interface. The shear failure was significantly related to the interfacial adhesion strength between the Pb-rich and $Cu_6Sn_5$ IMC layers. On the other hand, all fracturing occurred in the bulk solder for the Sn-3.5Ag/Ag-plated Cu joint, which confirmed its desirable joint reliability.

• Korean Journal of Materials Research
• /
• v.15 no.9
• /
• pp.598-603
• /
• 2005

To develope new lead-free solders with the melting temperature close to that of Sn-37Pb$(183^{\circ}C)$, Sn-0.7Cu-5Pb-1Ga, Sn-0.7Cu-5Pb-1Ag, Sn-0.7Cu-5Pb-5Bi-1Ag, and Sn-0.7Cu-SBi-1Ag alloys were composed by adding low-netting elements such as Ga, Bi, Pb, and Ag to Sn-0.7Cu. Then the melting temperatures, microstructures, wettability, and adhesion properties of these alloys were evaluated. DSC analysis showed that the melting temperature of Sn-0.7Cu-SPb-1Ga was $211^{\circ}C$, and those of other alloys was in the range of $192\~200^{\circ}C$. Microstructures of these alloys after heat-treatment at $150^{\circ}C$ for 24 hrs were basically composed of coarsely- grown $\beta-Sn$ grains, and $Cu_6Sn_5$ and $Ag_3Sn$ intermetallic precipitates. Sn-0.7Cu-5Pb-1Ga and Sn-0.7Cu-5Pb-5Bi-1Ag showed excellent wettability, while Sn-0.7Cu-5Bi-1Ag and Sn-0.7Cu-5Pb-5Bi-1Ag revealed good adhesion strength with the Cu substrates. Among 4 alloys, Sn-0.7Cu-5Pb-5Bi-1Ag with the lowest melting temperature $(192^{\circ}C)$ and relatively excellent wettability and adhesion strength was suggested to be the best candidate solder to replace Sn-37Pb.

• Journal of the Korean Vacuum Society
• /
• v.16 no.4
• /
• pp.291-297
• /
• 2007

The field emission properties of CNT-emitters coated with Ag-Cu alloy have been investigated. The vertical aligned multi-walled CNTs were synthesized by dc-plasma enhanced chemical vapor deposition (dc-PECVD) and the Ag-Cu alloy was coated by using dc-magnetron sputter. The morphology of alloy-coated and un-coated CNT-emitters was observed by using SEM and their field emission properties were also measured. Annealing the AgCu-coated CNTs at temperature more than ${\sim}700^{\circ}C$, the Ag-Cu alloy was diffused to and aggregated on the top of the CNT as a Q-tip. A significant progress on the field emission was not observed with coating Ag-Cu alloy on the CNTs, but a certain improvement in a resistance against oxygen gas was made confirmation. It seems to be due to inertness of Ag-Cu alloy on the CNTs.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.4
• /
• pp.17-23
• /
• 2013

As a basic research to develop stretchable electronic packaging technology, CNT-Ag composite pads were formed on top of Cu/Sn chip bumps and flip-chip bonded using anisotropic conductive adhesive. Average contact resistances of the flip-chip joints were measured with respect to bonding pressure and presence of the CNT-Ag composite pads. When Cu/Sn chip bumps with CNT-Ag composite pads were flip-chip bonded to substrate Cu pads at 25MPa or 50 MPa, contact resistance was too high to measure. The specimen processed by flip-chip bonding the Cu/Sn chip bumps with CNT-Ag composite pads to the substrate Cu pads exhibited an average contact resistance of $213m{\Omega}$. On the other hand, the flip-chip specimens processed by bonding Cu/Sn chip bumps without CNT-Ag composite pads to substrate Cu pads at 25MPa, 50MPa, and 100MPa exhibited average contact resistances of $370m{\Omega}$, $372m{\Omega}$, and $112m{\Omega}$, respectively.