• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.55-64
• /
• 1995

Metallizing method on ceramic surface is one of the compositing technology of ceramics and metal. The purpose of this study is to make HIC (Hybrid Intergrated Circuit) with copper metallizing method of which copper layer is formed on ceramic substrate by firing in atmosphere in lieu of conventional hybrid microcircuit systems based on noble metal. Metallizing pastes were made from various copper compounds such as Cu$_{2}$O, CuO, Cu, CuS and kaolin. And the screen printing method was used. The characteristics of metallized copper layers were analyzed through the measurement of sheet resistance, SEM, and EDZX. The results obtainted are summarized as follows; 1. The copper metallizing layers on ceramic surface can be formed by firing in air. 2. The metallized layer using Cu$_{2}$O paste showed the smallest sheet resistance among a group of copper chemical compounds. And optimum metallizing conditions are 15 minutes of firing time, 1000.deg.C of firig temperature, and 3 minutes of deoxidation time. 3. The results of EDAX analysis showed mutual diffusion of Cu and Al. 4. The kaolin plays a important role of deepening the penetration of Cu to $Al_{2}$O$_{3}$ ceramics. But if the kaolin content is too much, sheet resistance increases and copper metallizing layer becomes brittle.

• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.53-61
• /
• 1996

It was attempted to improve the wear resistance of Al alloy under the load condition by making a formation of the thicker surface hardening alloy layers. The thicker surface hardening alloy layers were formed on 6061 Al alloys overlayed by MIG and TIG welding process with Cu powders feeding. The characteristics of hardening and wear resistance have been investigated in relation to the microstructures of alloyed layers, with a selection of optimum alloying conditions for formation of overlaying layer. The results obtained were summarized as follows With increasing feeding rate of Cu powders by MIG welding, the hardness and specific wear of the overlay weld alloys were increased. It is considered that these high hardness and specific wear of overlay weld alloys were due to the formation of Θ($Al_2Cu$) phases. With increasing feeding rate of Cu powders by TIG welding, the hardness and specific wear of the overlay weld alloys were increased in feeding rates 12 and 18g/min. However, the hardness and specific wear were decreased in the powder feeding rate 38g/min. It is considered that considered that decrease of hardness and specific wear in the powder feeding rate 38g/min due to formation of ${\gamma}$($Al_4Cu_9$) phases.

• Journal of the Korean Vacuum Society
• /
• v.5 no.4
• /
• pp.341-347
• /
• 1996

We fabricated the effective $Cu_2S$/CdS solar cells with large area by a spray pyrolysis method. In preparation process, we investigated the process parameters which directly influenced the efficiency of solar cell, such as the grid contact for electrodes, the temperature condition of CdS spray and the junction characteristics of $Cu_2S$ layer, by scanning electron microscope(SEM), x-ray diffraction(XRD) and temperature dependent optical absorption and photoconductivity. The $Cu_2S$/CdS solar cell with area of 1$\textrm{cm}^2$ showed the efficient of 3.15% under air mass 2(AM2) spectrum irradiation with 75mW/$\textrm{cm}^2$.

• 연구논문집
• /
• s.24
• /
• pp.63-79
• /
• 1994

This article reports a experimental study of the method to achieve a bond joint at lower temperature in a short time. DC magnetron sputtering of Sn, Sn/Pb, Sn/In and Sn/Cu on copper substrate was provided as an interlayer for Cu to Cu bonding under the air environment. Various examination was conducted and investigated on the effect of experimental parameters such as coating materials, coating time(or coating thickness), bonding temperature and bonding time etc. Bonding was performed at the temperature of $210^\circC-320^\circC$ for 0sec and interfacial reaction between the coated layer and copper substrate was examined using optical, scanning electron microscope and x-ray diffractometer. From the obtained results, it was found that intermetallic compounds layer consisted of $\eta-phase(Cu_6Sn_5)$ and $\beta-phase(Cu_3Sn)$ was formed at the joint interface for almost all coating materials. But the dominant phase formed in the preetched Cu substrate coated with Sn was $\beta-phase$. A characteristic morphology looks like a reaction ring, which was believed as the strong interconnecting regions between two substrates, was found to be formed on the reaction surface of copper substrates. The morphologies and compositions of the intermetallics, which depends on the regions of the reaction surface, was appeared as greatly different. Based on above results, the new bonding process to make the joint at lower temperature for short time can be admitted as a feasible process.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.313.1-313.1
• /
• 2013

현재 결정질 실리콘 태양전지의 전 후면 전극의 형성은 스크린 프린팅 방법이 주를 이루고 있다. 스크린 프린팅 방법은 쉽고 빠르게 인쇄가 가능한 반면 단가가 높고 금속 페이스트에 첨가된 여러 혼합물에 의해서 전극과 기판 사이의 저항이 크다는 단점이 있다. 본 논문에서는 스크린 프린팅 방법으로 태양전지의 seed layer를 인쇄하고, Cu도금을 진행함으로써 태양전지의 전기적 특성을 비교하였다. 주요 전극 형성을 Cu 도금을 사용함으로써 전극과 기판사이의 저항을 감소시키고 값비싼 Ag페이스트를 값싼 Cu로 대체함으로써 가격을 낮출 수 있는 장점이 있다. 실험에 사용된 Si 웨이퍼 특성은 $156{\times}156$ mm2, 200 ${\mu}m$, 0.5-3.0 ${\Omega}{\cdot}cm$ and p-type 웨이퍼를 사용하였다. 웨이퍼는 표면조직화, p-n접합 형성, 반사방지막 코팅을 하였으며 스크린 프린팅 방법을 이용해 전 후면 전극을 인쇄하고 열처리 과정을 통해 전극을 형성하였다. 이 후 전면에 Cu도금을 실행하여 태양전지를 완성하였다. 완성된 태양전지는 솔라 시뮬레이터 및 TLM패턴을 이용하여 전기적 특성을 분석하였으며, SEM과 linescan, 광학현미경 등을 이용하여 전극을 분석하였다.

• Journal of Welding and Joining
• /
• v.24 no.6
• /
• pp.21-27
• /
• 2006

This study was focused on the evaluation of the thermo-mechanical board-level reliability of Pb-bearing and Pb-free surface mount assemblies. The composition of Pb-bearing solder was a typical Sn-37Pb and that of Pb-free solder used in this study was a representative Sn-3.0Ag-0.5Cu in mass %. Thermal shock test was chosen for the reliability evaluation of the solder joints. Typical $Cu_6Sn_5$ intermetallic compound (IMC) layer was formed between both solders and Cu lead frame at the as-reflowed state, while a layer of $Cu_3Sn$ was additionally formed between the $Cu_6Sn_5$ and Cu lead frame during the thermal shock testing. Thickness of the IMC layers increased with increasing thermal shock cycles, and this is very similar result with that of isothermal aging study of solder joints. Shear test of the multi layer ceramic capacitor(MLCC) joints was also performed to investigate the degradation of mechanical bonding strength of solder joints during the thermal shock testing. Failure mode of the joints after shear testing revealed that the degradation was mainly due to the excessive growth of the IMC layers during the thermal shock testing.

• Journal of Welding and Joining
• /
• v.30 no.2
• /
• pp.65-69
• /
• 2012

Environmental and health concerns over the lead have led to investigation of the alternative Pb-free solders to replace commonly used Pb-Sn solders in microelectronic packaging application. The leading candidates for lead-free solder alloys are presently the near eutectic Sn-Ag-Cu alloys. Therefore, extensive studies on reliability related with the composition have been reported. However, the insufficient drop property of the near eutectic Sn-Ag-Cu alloys has demanded solder compositions of low Ag content. In addition, the solder interconnections in automobile applications like a smart box require significantly improved vibration resistance. Therefore, this study investigated the effect of alloying elements (Ag, Bi, In) on the vibration fatigue strength. The vibration fatigue was conducted in 10~1000Hz frequency and 20Grms. The interface of the as-soldered cross section close to the Cu pad indicated the intermetallic compound ($Cu_6Sn_5$) regardless of solder composition. The type and thickness of IMC was not significantly changed after the vibration test. It indicates that no thermal activities occurred significantly during vibration. Furthermore, as a function of alloying composition, the vibration crack path was investigated with a focus on the IMCs. Vibration crack was initiated from the fillet surface of the heel for QFP parts and from the plating layer of chip parts. Regardless of the solder composition, the crack during a vibration test was propagated as same as that during a thermal fatigue test.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.449-449
• /
• 2013

최근 반도체 소자의 집적회로는 점점 복잡해지고 있는 반면, 소자의 크기는 작아지고 있으며 그로 인해 패드의 크기가 작아지고 패드사이의 간격 또한 협소해지고 있다. 따라서 웨이퍼 단계에서 제조된 집적회로의 불량여부를 판단하기위한 검사 장비인 프로브카드(Probe Card)의 높은 집적도가 요구되고 있다. 하지만 기존의 MEMS 공법으로 제작되는 프로브 빔은 복잡한 제조 공정과 높은 생산비용, 낮은 집적도의 문제점을 가지고 있다. 본 연구에서는 이러한 문제점을 해결하기 위하여 간단한 제조 공정과 낮은 생산비용, 높은 집적도를 가지는 프로브 빔을 개발하기 위하여 절연절단 방식으로 BeCu (Beryllium-Copper) 프로브 빔을 제작하였다. 낮은 소비 전력으로 우수한 프로브 빔 어레이를 제작하기 위해서 가장 고려해야할 대상은 프로브 빔의 재료와 구조(형상)이다. 절연전단 방식으로 프로브 빔을 형성할 때 요구되는 Fusing current는 프로브 빔의 구조(형상)에 크게 영향을 받는다. 낮은 Fusing current는 소비 전력을 줄여주고, 절연절단으로 형성되는 프로브 빔의 단면(끝)을 날카롭게 하여 프로브 빔과 집적회로의 패드 간의 접촉 저항을 감소시킨다. 프로브 빔의 제작은 BeCu 박판을 빔 형태로 식각하여 제작하였으며, 실리콘 비아 홀(Via hole) 구조의 기판위에 정렬하여 soldering 공정을 통해 실리콘 기판과 BeCu 박판을 접합시켰다. 접합된 프로브 빔의 끝부분을 들어 올린 상태로 전류를 인가하여 stress free 상태로 만들어 내부 응력을 제거하였으며, BeCu 박판에 fusing current를 인가하여 BeCu 박판 프레임으로부터 제거를 하였다. 제작된 프로브 빔의 길이는 1.7 mm, 폭은 $50{\mu}m$, 두께는 $15{\mu}m$, 절단부의 단면적은 1$50{\mu}m^2$로 제작되었다. 그리고 프로브 빔의 절단부의 길이는 $50{\mu}m$ 부터 $90{\mu}m$까지 $10{\mu}m$ 증가시켜 제작되었다. 이후에 절연절단 공정에 요구되는 Fusing current를 측정하였고, 절연절단 후의 절단면의 형상을 SEM (Scanning Electron Microscope)장비를 통하여 확인하였다. 절단부의 길이가 $50{\mu}m$일 때 5.98A의 fusing current를 얻었으며, 절연절단 후 절단부 상태 또한 가장 우수했다. 본 연구에서 제안된 프로브 빔 제작 방법은 프로브카드 및 테스트 소켓(Test socket) 생산에 응용이 가능하리라 기대한다.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.3
• /
• pp.9-18
• /
• 1999

In this study, Metallugical properties between Sn-3.5Ag, Sn-37Pb eutectic solders and Au/Ni/cu substrate according to time span above the melting point were investigated. A conventional reflow soldering machine wert used for this study and time span above the melting point was determined by changing peak soldering temperature and conveyor speed. As results, scallop type intermetallic compounds of $Ni_3Sn_4$ were formed at joint interface and no Cu-Sn compounds were found at all; Ni layer performed as a barrier for Cu diffusion. As the peak soldering temperature increased, thickness of the intermetallic compound layer increased; maximum thickness of the scallop-layer was 2.2$\mu\textrm{m}$. The shape of scallops were transformed from hemi-sphere type to elliptical shape with smaller size. Micro-hardness of the solder joint decreased as the eutectic structure of Sn-3.5Ag and Sn-37Pb increased.

• Journal of Welding and Joining
• /
• v.35 no.2
• /
• pp.23-29
• /
• 2017

Mechanical properties and hardness distributions in arc brazed joints of Dual phase steel using Cu-Al insert metal were investigated. The maximum tensile shear load was 10.4kN at the highest brazing current. It was about 54% compared to tensile load of base metal. This joint efficiency is higher than that of joint of DP steel using Cu-based filler metals which are Cu-Si, Cu-Sn. Fracture positions can be divided into two types. Crack initiation commonly occurred at three point junction among upper sheet, lower sheet and the fusion zone. However crack propagations were different with increasing the brazing current. In case of the lower current, it instantaneously propagated along with the interface between fusion zone and upper base material. On the other hand, in case of higher current, a crack propagation occurred through fusion zone. When the brazing current is low (60, 70A), the interface shape is flat type. However the interface shape is rough type, when the brazing current is high (80A). It is thought that the interface shapes were the reason why the crack propagations were different with brazing current. The interface was the intermetallic compounds which consisted of $(Fe,Al)_{0.85}Cu_{0.15}$ IMC formed by crystallization at $1200^{\circ}C$during cooling. Therefore the maximum tensile shear load and the fracture behavior were determined by a interface shape and effective sheet thickness of the fracture position.